CN102720335A - PVC (polyvinyl chloride) nano-floor - Google Patents

PVC (polyvinyl chloride) nano-floor Download PDF

Info

Publication number
CN102720335A
CN102720335A CN 201210198807 CN201210198807A CN102720335A CN 102720335 A CN102720335 A CN 102720335A CN 201210198807 CN201210198807 CN 201210198807 CN 201210198807 A CN201210198807 A CN 201210198807A CN 102720335 A CN102720335 A CN 102720335A
Authority
CN
China
Prior art keywords
pvc
flaggy
floor
calcium carbonate
nano
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201210198807
Other languages
Chinese (zh)
Inventor
张轩豪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 201210198807 priority Critical patent/CN102720335A/en
Priority to PCT/CN2012/078021 priority patent/WO2013185391A1/en
Publication of CN102720335A publication Critical patent/CN102720335A/en
Pending legal-status Critical Current

Abstract

The invention discloses a PVC (polyvinyl chloride) nano-floor which comprises an UV (ultraviolet) surface layer, a PVC wear-resistant layer, a PVC printed film layer, a PVC upper board layer, a PVC middle board layer and a PVC lower board layer from top to bottom. By weight percent, the PVC upper board layer is made from 45%-55% of PVC material, 35%-45% of calcium carbonate, 4%-6% of nano-material, and 4%-6% of plasticizer; the PVC middle board layer is made from 35%-45% of PVC material, 45%-55% of calcium carbonate, and 8%-10% of firming agent; and the PVC lower board layer is made from 55%-60% of PVC material, 25%-35% of calcium carbonate, 4%-6% of nano-material, and 4%-5% of plasticizer. The PVC nano-floor has the advantages of high strength, shock resistance, no peculiar odor and high antibiotic property.

Description

A kind of PVC nanometer floor
Technical field:
The present invention relates to technical field of construction and decoration materials, especially relate to a kind of PVC floor that use on ground that is layed in.
Background technology:
Cost of production is low because of having on the PVC floor, long service life, environment protecting are good etc., and advantage is used widely day by day; But; The present PVC floor part that also comes with some shortcomings; Show mainly that intensity is not high, not shock-resistant, frowziness, breed bacteria etc. easily, these problems are brought many puzzlements to the user, have also hindered popularizing of PVC floor to a certain extent.
Summary of the invention:
The objective of the invention is to the weak point that exists to prior art and a kind of PVC nanometer floor is provided, it has intensity height, shock-resistant, no stink, characteristics that antibiotic property is good.
Be to realize that above-mentioned purpose, PVC nanometer of the present invention floor include among UV surface course, PVC wearing layer, PVC printing rete, the last flaggy of PVC, the PVC flaggy under flaggy and the PVC from top to bottom successively; By weight percentage: the last flaggy of PVC is made up of 45%～55% PVC material, 35%～45% calcium carbonate, 4%～6% nano material, 4%～6% fluidizer; Flaggy is made up of 35%～45% PVC material, 45%～55% calcium carbonate, 8%～10% curing compound among the PVC; Flaggy is made up of 55%～60% PVC material, 25%～35% calcium carbonate, 4%～6% nano material, 4%～5% fluidizer under the PVC.
Preferred as technique scheme, described fluidizer is phthalate, citric acid ester type, phosphoric acid ester, epoxies, adipate ester class or polyesters compound.
Preferred as technique scheme, described curing compound is cumyl peroxide, benzoyl peroxide or 2, the 4-dichlorobenzoperoxide.
Preferred as technique scheme, described nano material is the silicon material.
Preferred as technique scheme, by weight percentage: the last flaggy of PVC (40) is made up of 50% PVC material, 40% calcium carbonate, 5% nano material, 5% fluidizer; Flaggy among the PVC (50) is made up of 40% PVC material, 50% calcium carbonate, 10% curing compound; Flaggy under the PVC (60) is made up of 60% PVC material, 30% calcium carbonate, 5% nano material, 5% fluidizer.
Beneficial effect of the present invention is: the PVC below its wearing layer goes up among flaggy, the PVC that layer structure can improve the intensity and the resistance to impact on PVC floor under flaggy and the PVC; Its inner nano material has good deodorizing and bactericidal effect; Thereby solved the stink of traditional P VC floor existence and the problem of easy breed bacteria, result of use is very good.
Description of drawings:
Below in conjunction with accompanying drawing the present invention is done further explanation:
Fig. 1 is a sectional structure sketch map of the present invention.
The specific embodiment:
The following stated is merely the preferred embodiment that embodies the principle of the invention, does not therefore limit protection scope of the present invention.
See shown in Figure 1: PVC nanometer of the present invention floor includes among the last flaggy of UV surface course 10, PVC wearing layer 20, PVC printing rete 30, PVC 40, the PVC flaggy 60 under flaggy 50 and the PVC from top to bottom successively; UV surface course 10, PVC wearing layer 20 and PVC printing rete 30 are the common structure in PVC floor, repeat no more here.
By weight percentage: the last flaggy 40 of PVC is made up of 45%～55% PVC material, 35%～45% calcium carbonate, 4%～6% nano material, 4%～6% fluidizer; Flaggy 50 is made up of 35%～45% PVC material, 45%～55% calcium carbonate, 8%～10% curing compound among the PVC; Flaggy 60 is made up of 55%～60% PVC material, 25%～35% calcium carbonate, 4%～6% nano material, 4%～5% fluidizer under the PVC.Fluidizer is the foaming binding material of PVC, and its kind can be phthalate, citric acid ester type, phosphoric acid ester, epoxies, adipate ester class or polyesters compound.Curing compound is cumyl peroxide, benzoyl peroxide or 2, the 4-dichlorobenzoperoxide.Fluidizer and curing compound are familiar with by the technician of PVC floor production industry, and it can select suitable fluidizer and curing compound as required voluntarily.Nano material then is the silicon material.
Through verification experimental verification, as best proportioning, the last flaggy 40 of PVC is made up of 50% PVC material, 40% calcium carbonate, 5% nano material, 5% fluidizer; Flaggy 50 is made up of 40% PVC material, 50% calcium carbonate, 10% curing compound among the PVC; Flaggy 60 is made up of 60% PVC material, 30% calcium carbonate, 5% nano material, 5% fluidizer under the PVC.
Six layer materials of the present invention can obtain supplying the PVC nanometer floor of constructing and using after hot-forming, die-cut sheet forming.

Claims (5)

1. PVC nanometer floor is characterized in that: include among UV surface course (10), PVC wearing layer (20), PVC printing rete (30), the last flaggy of PVC (40), the PVC flaggy (60) under flaggy (50) and the PVC from top to bottom successively; By weight percentage: the last flaggy of PVC (40) is made up of 45%～55% PVC material, 35%～45% calcium carbonate, 4%～6% nano material, 4%～6% fluidizer; Flaggy among the PVC (50) is made up of 35%～45% PVC material, 45%～55% calcium carbonate, 8%～10% curing compound; Flaggy under the PVC (60) is made up of 55%～60% PVC material, 25%～35% calcium carbonate, 4%～6% nano material, 4%～5% fluidizer.
2. PVC nanometer according to claim 1 floor is characterized in that: described fluidizer is phthalate, citric acid ester type, phosphoric acid ester, epoxies, adipate ester class or polyesters compound.
3. PVC nanometer according to claim 1 floor is characterized in that: described curing compound is cumyl peroxide, benzoyl peroxide or 2, the 4-dichlorobenzoperoxide.
4. according to each described PVC nanometer floor in the claim 1 to 3, it is characterized in that: described nano material is the silicon material.
5. PVC nanometer according to claim 4 floor is characterized in that: by weight percentage: the last flaggy of PVC (40) is made up of 50% PVC material, 40% calcium carbonate, 5% nano material, 5% fluidizer; Flaggy among the PVC (50) is made up of 40% PVC material, 50% calcium carbonate, 10% curing compound; Flaggy under the PVC (60) is made up of 60% PVC material, 30% calcium carbonate, 5% nano material, 5% fluidizer.
CN 201210198807 2012-06-12 2012-06-12 PVC (polyvinyl chloride) nano-floor Pending CN102720335A (en)