CN102703836A - 一种低温用无缝钢管的制造方法 - Google Patents
一种低温用无缝钢管的制造方法 Download PDFInfo
- Publication number
- CN102703836A CN102703836A CN2012101601919A CN201210160191A CN102703836A CN 102703836 A CN102703836 A CN 102703836A CN 2012101601919 A CN2012101601919 A CN 2012101601919A CN 201210160191 A CN201210160191 A CN 201210160191A CN 102703836 A CN102703836 A CN 102703836A
- Authority
- CN
- China
- Prior art keywords
- percent
- tempering
- low temperature
- temperature
- steel tube
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及无缝钢管领域,特别涉及一种低温用无缝钢管的制造方法,其特征在于,采用双联法熔炼,其化学成分组成按重量百分比如下:C0.14-0.19%、Si0.20-0.50%、Mn 1.00-1.60%、P≤0.02%、S≤0.01%、Ni1.0-1.7%、Cr0.50-0.80%、Mo 0.20-0.70%、V≤0.10%、Cu≤0.10%、Nb≤0.05%,其余为Fe;该钢管的调质包括淬火和回火,淬火温度为900-940℃,淬火后水冷;回火温度为540-620℃,回火后空冷。与现有技术相比,本发明的优点是:1)890MPa高强度,尤其具有-40℃的低温冲击性能;2)满足起重机臂架的综合性能。
Description
技术领域
本发明涉及890MPa高强低温用无缝钢管领域,特别涉及一种低温用无缝钢管的制造方法。
背景技术
目前,我国大型液压履带式起重机臂架用无缝钢管均从国外引进,尤以德国和日本的性能最好,但这两个国家对此类钢管的生产保密性较强,而国内HSM890强度级别的低温用无缝钢管主要设计理念是靠添加W元素提高钢的低温性能,但因不能保证-40℃的低温冲击性能,一直未被起重机制造企业认可。
为了降低起重机生产企业的生产成本,缩短订货周期,急需一种高强度低温性能优异的新钢种,填补我国低温领域钢种空白,为钢铁企业创造更大的经济效益。
发明内容
本发明的目的是提供一种低温用无缝钢管的制造方法,克服现有技术的不足,采用双联法降低钢中P、S有害元素含量,添加Ni元素,以提高钢管的低温韧性,保证较高的可焊性,满足起重机臂架的综合性能要求。
为解决上述技术问题,本发明的技术方案是:
一种低温用无缝钢管的制造方法,采用双联法熔炼,其化学成分组成按重量百分比如下:
C 0.14-0.19%、Si 0.20-0.50%、Mn 1.00-1.60%、P≤0.02%、S≤0.01%、Ni 1.0-1.7%、Cr 0.50-0.80%、Mo 0.20-0.70%、V≤0.10%、Cu≤0.10%、Nb≤0.05%,其余为Fe;
所述一种低温用无缝钢管的调质方法,包括淬火和回火,其淬火温度为900-940℃,淬火后水冷;其回火温度为540-620℃,回火后空冷。
与现有技术相比,本发明的有益效果是:
1)采用双联法降低钢中P、S有害元素含量,添加Ni元素,以提高钢的低温韧性,具有较高的可焊性,在保证890MPa高强度下,尤其具有-40℃以上的低温冲击性能;
2)配合合理的调质方法,提高钢的淬透性,降低钢的韧脆转变温度和解理断裂倾向,满足起重机臂架的综合性能要求;
3)除起重机臂架外,也可应用于其他结构用管,具有减轻结构件的自重,提高工程的安全性,降低生产企业的生产成本,缩短订货周期的诸多优点。
具体实施方式
下面结合具体实施例对本发明作进一步说明:
本发明的一种低温用无缝钢管的制造方法,采用转炉双联法熔炼,保证钢水纯净度,其化学成分组成在下述范围内都能满足大型液压履带式起重机臂架的性能要求,其具体化学成分按重量百分比如下:
C 0.14-0.19%、Si 0.20-0.50%、Mn 1.00-1.60%、P≤0.02%、S≤0.01%、Ni 1.0-1.7%、Cr 0.50-0.80%、Mo 0.20-0.70%、V≤0.10%、Cu≤0.10%、Nb≤0.05%,其余为Fe。
本发明低温用无缝钢管的调质方法可按钢管壁厚不同,选择不同制度:具体可按壁厚5-12mm范围和壁厚12-25mm范围为分两种。
实施例1
本发明Φ83规格的一种低温用无缝钢管,采用以下调质方法:淬火温度900~940℃,水冷,保温时间36分钟;回火温度540~620℃,保温时间60分钟,空冷。
工业试生产性能检验结果: 见表1。
表1
实施例2
本发明Φ127规格的一种低温用无缝钢管,采用以下调质方法:淬火温度900~940℃,水冷,保温时间72分钟;回火温度540~620℃,保温时间120分钟,空冷。
工业试生产性能检验结果: 见表2。
表2
Claims (1)
1.一种低温用无缝钢管的制造方法,其特征在于,采用双联法熔炼,其化学成分组成按重量百分比如下:
C 0.14-0.19%、Si 0.20-0.50%、Mn 1.00-1.60%、P≤0.02%、S≤0.01%、Ni 1.0-1.7%、Cr 0.50-0.80%、Mo 0.20-0.70%、V≤0.10%、Cu≤0.10%、Nb≤0.05%,其余为Fe;
所述一种低温用无缝钢管的调质方法,包括淬火和回火,其淬火温度为900-940℃,淬火后水冷;其回火温度为540-620℃,回火后空冷。