CN102700349A - Decorative gilding and preparation process of decorative gilding - Google Patents
Decorative gilding and preparation process of decorative gilding Download PDFInfo
- Publication number
- CN102700349A CN102700349A CN2012101509772A CN201210150977A CN102700349A CN 102700349 A CN102700349 A CN 102700349A CN 2012101509772 A CN2012101509772 A CN 2012101509772A CN 201210150977 A CN201210150977 A CN 201210150977A CN 102700349 A CN102700349 A CN 102700349A
- Authority
- CN
- China
- Prior art keywords
- gilding
- layer
- decorative
- coated
- peel ply
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of industrial gilding, in particular to decorative gilding and a preparation process of the decorative gilding. The decorative gilding provided by the invention comprises a polyester (PET) bottom layer, a peeling layer, a coloring layer, an aluminum coating and a base color layer. In the process method for preparing the gilding, the decorative gilding is obtained by industrial production; during mounting, the gilding can be used after the PET bottom layer is peeled off through the peeling layer; and the problems of high cost and high requirements of the traditional gilding on the technology are avoided. Otherwise, the metal color is guaranteed to be consistent by the arrangement of the coloring layer, the aluminum coating and the base color layer; the appearance effect is excellent; the coated coloring layer can also be used for avoiding the problem of surface oxidation and blackening caused by sweat and the like.
Description
Technical field:
The present invention relates to industrial gilding technical field, relate in particular to a kind of decoration gilding and preparation technology thereof.
Background technology:
Gilding is a kind of ancient skill, is the rarity of Chinese nation's folk tradition technology, and is widely used in the decoration and the various packaging product of imperial palace noble or figure of buddha temple, and splendid or honorable to show it, in the society, the scope of application is more and more wider in modern times.Generally, gilding uses the proof gold sheet to prolong pressure usually and forms, and needs highly skilled special technician to accomplish, and output is little; Produce limitedly, true yellow gold forms, and is with high costs; In addition, thin gilding receives sweat stain or other pollutions easily in installation or use; Oxidation blackout phenomenon takes place in surface easily, causes the gilding finish to differ, and has a strong impact on appearance.
Summary of the invention:
The object of the invention is exactly that existence processing to the gilding of prior art is difficult for, costs an arm and a leg, surface problem such as oxidation blackout and the deficiency that exists and a kind of a kind of decoration gilding and preparation technology thereof who overcomes the above problems is provided easily.
To achieve these goals, the technical scheme of the present invention's employing is:
A kind of decoration gilding comprises by the level of following order and forming: PET bottom, peel ply, dyed layer, aluminium coated, background color layer.
Aforesaid a kind of its preparation technology who decorates gilding comprises following preparation technology:
(1), at a coated cellulose resin peel ply of PET bottom;
(2), coated with polyurethane coloring resin layer on the coating peel ply of step 1;
(3), vacuum plating aluminium lamination on the dyed layer of step 2;
(4), coated with polyurethane resin background color layer on the aluminium coated of step 3.
Beneficial effect of the present invention is: a kind of decoration gilding of the present invention comprises PET bottom, peel ply, dyed layer, aluminium coated, background color layer; And the process of making gilding of the present invention; Process through suitability for industrialized production, can tear the PET bottom through peel ply during installation and use at once, also can peel off PET bottom and peel ply through stripping machine; And be cut into the big or small gilding of certain specification, and carry out the circulation sale field; Gilding of the present invention and process thereof are avoided the problem that requirement high, cost expensive of traditional gilding to technology; In addition; Through dyed layer, aluminium coated, background color layer are set; The assurance metallic luster is consistent, and appearance is good, and the dyed layer that is coated with can also avoid sweat stain etc. to cause the problem of surface oxidation blackening to produce.
Figure of description:
Fig. 1 is a gilding structural representation of the present invention
The specific embodiment:
Below in conjunction with embodiment the present invention is further described:
A kind of decoration gilding, as shown in Figure 1, comprise by the level of following order and forming: PET bottom 1, peel ply 2, dyed layer 3, aluminium coated 4, background color layer 5.
A kind of its preparation technology who decorates gilding of the present invention comprises following preparation technology:
(1), at a coated cellulose resin peel ply of PET bottom;
(2), coated with polyurethane coloring resin layer on the coating peel ply of step 1;
(3), vacuum plating aluminium lamination on the dyed layer of step 2;
(4), coated with polyurethane resin background color layer on the aluminium coated of step 3.
Certainly, the above only is preferred embodiment of the present invention, so all equivalences of doing according to the described structure of patent claim of the present invention, characteristic and principle change or modify, includes in patent claim of the present invention.
Claims (2)
1. decorate gilding for one kind, it is characterized in that, comprise by the level of following order and forming: PET bottom, peel ply, dyed layer, aluminium coated, background color layer.
2. a kind of its preparation technology who decorates gilding as claimed in claim 1 is characterized in that, comprises following preparation technology:
(1), at a coated cellulose resin peel ply of PET bottom;
(2), coated with polyurethane coloring resin layer on the coating peel ply of step 1;
(3), vacuum plating aluminium lamination on the dyed layer of step 2;
(4), coated with polyurethane resin background color layer on the aluminium coated of step 3.