CN102691061A - 一种热轧球墨铸铁轧辊扁头激光熔覆制造工艺 - Google Patents

一种热轧球墨铸铁轧辊扁头激光熔覆制造工艺 Download PDF

Info

Publication number
CN102691061A
CN102691061A CN2012101904593A CN201210190459A CN102691061A CN 102691061 A CN102691061 A CN 102691061A CN 2012101904593 A CN2012101904593 A CN 2012101904593A CN 201210190459 A CN201210190459 A CN 201210190459A CN 102691061 A CN102691061 A CN 102691061A
Authority
CN
China
Prior art keywords
homalocephalus
powder
flat head
laser
cladding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012101904593A
Other languages
English (en)
Inventor
张金涛
刘文斌
陈海涛
张宝辉
杨佳才
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing Dalu Tianrui Laser Engineering Technology Co Ltd
Original Assignee
Beijing Dalu Tianrui Laser Engineering Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beijing Dalu Tianrui Laser Engineering Technology Co Ltd filed Critical Beijing Dalu Tianrui Laser Engineering Technology Co Ltd
Priority to CN2012101904593A priority Critical patent/CN102691061A/zh
Publication of CN102691061A publication Critical patent/CN102691061A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种热轧球墨铸铁轧辊扁头激光熔覆制造工艺，去除轧辊扁头的油污和锈蚀，机加工去除扁头扁表面的疲劳层，使得熔覆在一个相对平的表面进行；将调好粉量的钴基熔覆合金粉末用送粉器预置到扁头表面，用CO2激光器快速扫描预置好的粉末，形成与基体成冶金结合的底层表面覆层，然后扁头表面实现快速冷却；其他覆层采用铁基粉末，根据扁头磨损程度，选择总覆层的厚度与层数；将熔覆好的轧辊扁头机加工到图纸尺寸，并对成品进行超声波探伤。本发明一种热轧球墨铸铁轧辊扁头激光熔覆制造工艺，对产品的表面修复后使部件强度得到保障，修复费用较重置价格要低很多，而且缩短了维修时间，解决了部件快速抢修难题，实现企业设备连续可靠运行。

Description

一种热轧球墨铸铁轧辊扁头激光熔覆制造工艺
技术领域
本发明涉及一种热轧球墨铸铁轧辊扁头激光熔覆制造工艺，属于设备维护工艺领域。
背景技术
在生产实践中，转动的部件由于长期磨损导致无法满足正常生产的要求，需要进行修复，但是传统的堆焊等修复方法对一些特殊的部件修复无法达到要求，需要新的部件修复方法。
发明内容
本发明要解决的技术问题是克服现有的缺陷，提供了一种热轧球墨铸铁轧辊扁头激光熔覆制造工艺。可以缩短设备维修时间，同时保证设备维修质量，提高设备运转的效率。
为了解决上述技术问题，本发明提供了如下的技术方案：
一种热轧球墨铸铁轧辊扁头激光熔覆制造工艺，采用汽油、酒精等溶剂去除轧辊扁头的油污和锈蚀，机加工去除扁头扁表面的疲劳层。去除扁表面的疲劳层时，去除尺寸要与轧辊扁头磨损的最低点一致，使得熔覆在一个相对平的表面进行，便于均匀预置熔覆粉末。
将调好粉量的钴基熔覆合金粉末用送粉器预置到扁头表面，用CO2激光器快速扫描预置好的粉末，激光熔池快速熔化粉末与扁头基体表面薄层，形成与基体成冶金结合的底层表面覆层，然后扁头表面实现快速冷却。
其他覆层采用铁基粉末，通过送粉器预置扁头表面，用CO2激光器快速扫描预置好的粉末，激光熔池快速熔化粉末与扁头结合，形成多层覆层，然后扁头表面实现快速冷却；每层覆层的熔覆厚度为1.2mm。根据扁头磨损程度，选择总覆层的厚度与层数；
将熔覆好的轧辊扁头机加工到图纸尺寸，并对成品进行超声波探伤。
进一步的，激光器采用DL-HL-5000型CO2激光器。
进一步的，工艺参数：激光功率3.5-4.5kw，用离焦量为300mm的铜镜聚焦圆形光斑，其光斑直径为3mm，搭接量为1-1.6mm,扫描速度V=400-1200mm/min。
本发明一种热轧球墨铸铁轧辊扁头激光熔覆制造工艺，对产品的表面修复后的部件强度得到保障，其修复费用较重置价格要低很多，而且缩短了维修时间，解决了部件快速抢修难题，实现企业设备连续可靠运行。
具体实施方式
  一种热轧球墨铸铁轧辊扁头激光熔覆制造工艺，采用汽油、酒精等溶剂去除轧辊扁头的油污和锈蚀，机加工去除扁头扁表面的疲劳层。去除扁表面的疲劳层时，去除尺寸要与轧辊扁头磨损的最低点一致，使得熔覆在一个相对平的表面进行。
将调好粉量的钴基熔覆合金粉末用送粉器预置到扁头表面，采用DL-HL-5000型CO2激光器快速扫描预置好的粉末，激光熔池快速熔化粉末与扁头基体表面薄层，形成与基体成冶金结合的底层表面覆层，然后扁头表面实现快速冷却。使钴基熔覆合金粉末与轧辊本身基材能更好的结合，抑制裂纹产生。
其他覆层采用铁基粉末，通过送粉器预置扁头表面，采用DL-HL-5000型CO2激光器快速扫描预置好的粉末，激光熔池快速熔化粉末与扁头结合，形成多层覆层，然后扁头表面实现快速冷却；每层覆层的熔覆厚度为1.2mm。
覆层工艺参数：激光功率3.5-4.5kw，用离焦量为300mm的铜镜聚焦圆形光斑，其光斑直径为3mm，搭接量为1-1.6mm,扫描速度V=400-1200mm/min。
由于扁头有不同程度的磨损，因此根据扁头磨损程度，选择总覆层的厚度与层数。
将熔覆好的轧辊扁头机加工到图纸尺寸，并对成品进行超声波探伤。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (5)

1.一种热轧球墨铸铁轧辊扁头激光熔覆制造工艺，其特征在于：去除轧辊扁头的油污和锈蚀，机加工去除扁头扁表面的疲劳层，去除尺寸要与轧辊扁头磨损的最低点一致，使得熔覆在一个相对平的表面进行；
将调好粉量的钴基熔覆合金粉末用送粉器预置到扁头表面，用CO2激光器快速扫描预置好的粉末，激光熔池快速熔化粉末与扁头基体表面薄层，形成与基体成冶金结合的底层表面覆层，然后扁头表面实现快速冷却；
其他覆层采用铁基粉末，通过送粉器预置扁头表面，用CO2激光器快速扫描预置好的粉末，激光熔池快速熔化粉末与扁头结合，形成多层覆层，然后扁头表面实现快速冷却；根据扁头磨损程度，选择总覆层的厚度与层数；
将熔覆好的轧辊扁头机加工到图纸尺寸，并对成品进行超声波探伤。
2.根据权利要求1所述的一种热轧球墨铸铁轧辊扁头激光熔覆制造工艺，其特征在于：去除轧辊扁头的油污和锈蚀采用汽油、酒精等溶剂。
3.根据权利要求1所述的一种热轧球墨铸铁轧辊扁头激光熔覆制造工艺，其特征在于：激光器采用DL-HL-5000型CO2激光器。
4.根据权利要求1所述的一种热轧球墨铸铁轧辊扁头激光熔覆制造工艺，其特征在于：工艺参数：激光功率3.5-4.5kw，用离焦量为300mm的铜镜聚焦圆形光斑，其光斑直径为3mm，搭接量为1-1.6mm,扫描速度V=400-1200mm/min。
5.根据权利要求1所述的一种热轧球墨铸铁轧辊扁头激光熔覆制造工艺，其特征在于：每层覆层的熔覆厚度为1.2mm。
CN2012101904593A 2012-06-11 2012-06-11 一种热轧球墨铸铁轧辊扁头激光熔覆制造工艺 Pending CN102691061A (zh)