A kind of new automobile quench liquid
Technical field
The present invention relates to the quench liquid technology, relate in particular to a kind of new automobile quench liquid.
Background technology
What early stage automobile cooling was used to reduce freezing point is salt, but salts substances is prone to cause rust, easy crystalline deposit.Also have one type to adopt alcohols, comprise methyl alcohol, ethanol, but there is potential safety hazard in this type of material lower boiling, inflammable.
Existing automobile cooling comprises compound and organic type.Contain materials such as amine to environment and human body harmful, nitrate salt, organic acid salt chromic salt in compound; The silicate that lacks the stable protective membrane of quick formation one deck in the organic type can not in time play protective effect to water tank and cooling system internal surface.
Water in the existing simultaneously automobile cooling contains calcium, mg ion, and the life-time service of water makes and causes local heat radiation bad attached to the winterization system surface by calcium ions and magnesium ions formation of deposits dirt, destroys winterization system, causes a series of consequences such as system's seepage.
Summary of the invention
The objective of the invention is to overcome the defective of prior art and provide a kind of resistance to corrosion strong, prevent that incrustation scale from producing, and prevents that water tank is overheated, the environment-friendly novel automobile cooling of low freezing point.
The objective of the invention is to realize like this:
A kind of new automobile quench liquid of the present invention is mixed by the each component of following mass percent:
Above-mentioned a kind of new automobile quench liquid, wherein, said alcohols mixture is the mixture of being made up of terepthaloyl moietie and USP Kosher, wherein the mass ratio of terepthaloyl moietie and USP Kosher is 65: 35-80: 20.
Above-mentioned a kind of new automobile quench liquid, wherein, said pigment is at least a in blue, rose-red and light yellow of acid lake blue, weak acid.
Above-mentioned a kind of new automobile quench liquid, wherein, said surfactant additive is a metasilicate.
Above-mentioned a kind of new automobile quench liquid, wherein, said surfactant additive is a Starso.
Above-mentioned a kind of new automobile quench liquid, wherein, said inhibiter is monobasic or binary organic acid.
Above-mentioned a kind of new automobile quench liquid, wherein, said inhibiter is sad.
Above-mentioned a kind of new automobile quench liquid, wherein, said pH regulator agent is a borax.
Above-mentioned a kind of new automobile quench liquid, wherein, said skimmer is a silicone emulsion.
The present invention compares with existing automobile cooling, has following beneficial effect:
1. automobile cooling of the present invention adopts deionized water, efficiently solves the system's leakage problems that causes because of calcium ions and magnesium ions formation of deposits dirt;
2. two kinds of high boiling alcohols of the present invention's employing reach optimum proportion; Wherein USP Kosher is by biological extraction, environmentally safe; And combine compound and the advantage organic acid salt quench liquid; The resist that metasilicate in the automobile cooling of the present invention can form can prevent the burn into cavitation erosion and the fouling of internal surface, and the formation of this resist is very quick.Possessed the low consumption rate of monobasic or binary organic acid simultaneously, prolonged work-ing life.
Embodiment
To combine embodiment that the present invention is described further below.
Embodiment 1
The component of above-mentioned each mass percent is mixed, make automobile cooling of the present invention, this automobile cooling is following through detecting each item index:
Can see that from above-mentioned corrosion test result automobile cooling of the present invention can effectively prevent the burn into cavitation erosion and the fouling on surface, owing to adopted deionized water, efficiently solves the system's leakage problems that causes because of calcium ions and magnesium ions formation of deposits dirt in addition.
Embodiment 2
The component of above-mentioned each mass percent is mixed, make automobile cooling of the present invention, this automobile cooling is following through detecting each item index:
Can see that from above-mentioned corrosion test result automobile cooling of the present invention can effectively prevent the burn into cavitation erosion and the fouling on surface, owing to adopted deionized water, efficiently solves the system's leakage problems that causes because of calcium ions and magnesium ions formation of deposits dirt in addition.
Embodiment 3
The component of above-mentioned each mass percent is mixed, make automobile cooling of the present invention, this automobile cooling is following through detecting each item index:
Can see that from above-mentioned corrosion test result automobile cooling of the present invention can effectively prevent the burn into cavitation erosion and the fouling on surface, owing to adopted deionized water, efficiently solves the system's leakage problems that causes because of calcium ions and magnesium ions formation of deposits dirt in addition.
Above embodiment only supplies to explain the present invention's usefulness; But not limitation of the present invention; The technician in relevant technologies field under the situation that does not break away from the spirit and scope of the present invention, can also make various conversion or modification; Therefore all technical schemes that are equal to also should belong to category of the present invention, should be limited each claim.