CN102673072A - Lace composite fabric and method for producing same - Google Patents
Lace composite fabric and method for producing same Download PDFInfo
- Publication number
- CN102673072A CN102673072A CN2012101899646A CN201210189964A CN102673072A CN 102673072 A CN102673072 A CN 102673072A CN 2012101899646 A CN2012101899646 A CN 2012101899646A CN 201210189964 A CN201210189964 A CN 201210189964A CN 102673072 A CN102673072 A CN 102673072A
- Authority
- CN
- China
- Prior art keywords
- lace
- fabric
- composite material
- adhesive
- production method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a lace composite fabric and a method for producing the same, wherein the method comprises the steps of: a, film laying: a layer of transparent film is laid on a reverse fabric; b, compositing: a layer of adhesive is uniformly coated on the transparent film, the lace is laid on the adhesive layer, and then pressing is carried out; and c, maintaining: the adhered fabric is stood in a room with a certain temperature and humidity to be maintained. The lace can be composited onto any fabric, the composited fabric not only can maintain the characteristics of the original fabric, but also is added with the soft style of the lace, a poly urethane (PU) film which is laid on the reverse fabric is light, thin and air permeable, and can prevent the adhesive from permeating into the reverse fabric, so the whole fabric looks very clean, and the pattern of the lace can be more clearly seen; and the lace composite fabric which is obtained by the method can be used on clothes for four seasons, so the lace market is greatly expanded.
Description
Technical field
The present invention relates to the production field of composite material, refer more particularly to the production field of lace lining.
Background technology
Lace lining fashion is luxurious, natural, graceful and poised gracefulness, is a kind of lining that welcome by the women, but traditional lace lining is frivolous, often only is applicable to the time clothes of spring and summer money, and is not suitable for fashionable dress autumn and winter, and its market is very limited.
Summary of the invention
Technical problem to be solved by this invention is the deficiency to above-mentioned prior art, provide a kind of in the autumn and winter fashionable dress also employable lace composite material and production method thereof.
For solving the problems of the technologies described above, the technical scheme that the present invention takes is: a kind of production method of lace composite material the steps include:
A, overlay film: on the reverse side lining, cover the last layer transparent membrane;
B, compound: on transparent membrane, evenly coat layer of adhesive, lace is covered on the adhesive phase, then pressurization;
C, maintenance: the lining after bonding is statically placed in has the indoor of uniform temperature and humidity and maintain.
As the further improved technical scheme of the present invention, used transparent membrane is the PU film among the step a.
As the further improved technical scheme of the present invention, the thickness of said PU film is 0.3-0.4mm.
As the further improved technical scheme of the present invention, adhesive therefor is the PU adhesive among the step b.
As the further improved technical scheme of the present invention, temperature described in the step c is 90-100 ℃, and said humidity is 90-100%.
As the further improved technical scheme of the present invention, temperature described in the step c is 100 ℃, and said humidity is 100%.
As the further improved technical scheme of the present invention, service time is 72-120 hour among the step c.
As the further improved technical scheme of the present invention, service time is 120 hours among the step c.
And the lace composite material that obtains according to top any one method.
The present invention can be compound to lace on any lining; Lining after compound can keep the characteristic of original lining, has increased the soft and graceful style of lace again, and the PU film that on the reverse side lining, covers is frivolous; Ventilative; Can prevent adhesive permeation to the reverse side lining, make whole cloth cover look very clean, can let clear manifesting of decorative pattern of lace; The lace composite material that obtains with this method is according to the difference of its reverse side lining, can load onto suitablely at Garments capable of wearing in four seasons, expanded lace market greatly.
Description of drawings
Fig. 1 is a lace composite material structural representation of the present invention.
The specific embodiment
Embodiment 1
Select for use woolen material as the reverse side lining in the present embodiment, covering the PU film on the woolen material, the thickness of PU film is 0.4mm; On the PU film, evenly be coated with one deck PU adhesive; PU film and PU adhesive are all purchased many positive Chemical Industry Science Co., Ltd from Guangzhou, then lace are covered on the adhesive, to whole lining pressurization; The pressure size has no special requirements, and places the indoor maintenance of 100 ℃ and 100% humidity to get final product in 120 hours then.Lace composite material after compound comprises reverse side precoat 1, rete 2, adhesive layer 3 and lace layer 4.
Tension force around when lace being adhered on the reverse side lining should be consistent; Otherwise the meeting of the cloth cover after compound out-of-flatness, PU film of selecting for use and PU adhesive fastness have excellent water tolerance and gas permeability more than 4 grades; Anti-yellow function is arranged, otherwise the lining comfortableness after compound can descend.
The PU film can be fixed on the reverse side lining when whole lining is pressurizeed as thin as a wafer firmly.
Lace composite material of the present invention is used further to follow-up technology after after maintenance, preferably doing the processing of cutting edge.Lace composite material of the present invention can wash after maintenance, can not dry-clean during washing, and available water and washing agent clean, and water temperature must not surpass 40 ℃, and lining can not tan by the sun under the sun for a long time.
Lace lining on the inventive method is can also be on reverse side lining both sides all compound forms the sandwich structure of lace-reverse side lining-lace.
Claims (9)
1. the production method of a lace composite material is characterized in that the steps include:
A, overlay film: on the reverse side lining, cover the last layer transparent membrane;
B, compound: on transparent membrane, evenly coat layer of adhesive, lace is covered on the adhesive phase, then pressurization;
C, maintenance: the lining after bonding is statically placed in has the indoor of uniform temperature and humidity and maintain.
2. the production method of lace composite material according to claim 1 is characterized in that: used transparent membrane is the PU film among the step a.
3. the production method of lace composite material according to claim 2 is characterized in that: the thickness of said PU film is 0.3-0.4mm.
4. the production method of lace composite material according to claim 1 is characterized in that: adhesive therefor is the PU adhesive among the step b.
5. the production method of lace composite material according to claim 1 is characterized in that: temperature described in the step c is 90-100 ℃, and said humidity is 90-100%.
6. the production method of lace composite material according to claim 5 is characterized in that: temperature described in the step c is 100 ℃, and said humidity is 100%.
7. the production method of lace composite material according to claim 1 is characterized in that: service time is 72-120 hour among the step c.
8. the production method of lace composite material according to claim 7 is characterized in that: service time is 120 hours among the step c.
9. according to any lace composite material that obtains in the claim 1 to 8.