CN102634283A - Additive capable of quickly drying paint, and preparation method thereof - Google Patents
Additive capable of quickly drying paint, and preparation method thereof Download PDFInfo
- Publication number
- CN102634283A CN102634283A CN2011101673965A CN201110167396A CN102634283A CN 102634283 A CN102634283 A CN 102634283A CN 2011101673965 A CN2011101673965 A CN 2011101673965A CN 201110167396 A CN201110167396 A CN 201110167396A CN 102634283 A CN102634283 A CN 102634283A
- Authority
- CN
- China
- Prior art keywords
- solvent
- paint
- quick
- siccative
- additive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an additive capable of quickly drying paint, and a preparation method of the additive. The additive comprises the components in parts by weight: 10-20 parts of drier and 80-100 parts of solvent; the preparation method of the additive comprises the steps of: putting a certain amount of solvent into a dispersion container; stirring and leading the solvent to be evenly dispersed; then, putting the drier into the obtained solution, and continuously stirring for 10-30 minutes; detecting the solid content of the drier in the dispersion container, and adjusting the solid content to the preset value by the solvent; after that, continuously stirring for 10-30 minutes; and filtering to obtain the additive capable of quickly drying the paint. Compared with the prior art, the additive can obviously accelerate the drying speed of double-component automobile refinishing coating, and the drying time is shortened to 2 hours from 5 hours under the natural conditions, so that the time is saved, the efficiency is improved, and the cost is saved; furthermore, the invention also can be used for double-component paint in other industries.
Description
Technical field
The present invention relates to a kind of oil paint additive and preparation method thereof, especially relate to a kind of quick-drying additive of paint and preparation method thereof that makes.
Background technology
Since the reform and opening-up, along with rapid development of economy, China's automobile industry has had develop rapidly, has become the big automobile production of the first in the world state at present.Along with automobile pollution is increasing, also increasingly high to the demand and the technical requirements of car refinishing paint.At present under field conditions (factors); Coat with lacquer the hand of delivering to customer from having sprayed; At least needing both wasted the time of user vehicle more than 5 hours, had increased Auto repair shop and automobile production producer cost again; Restrict the development of domestic automobile repairman shop and automobile production producer greatly, reduced the comprehensive competitive power of enterprise.
Summary of the invention
The object of the invention is exactly for the defective that overcomes above-mentioned prior art existence to be provided a kind of time of having saved, and has improved efficient, practices thrift making of cost and paints quick-drying additive and preparation method thereof.
The object of the invention can be realized through following technical scheme:
A kind of quick-drying additive of paint that makes is characterized in that this additive comprises following component and weight part content:
Siccative 10～20;
Solvent 80～100.
The weight part of described siccative is preferred 10～15, the weight part of solvent preferred 85～93.
The weight part of described siccative more preferably 12～13, the weight part of solvent more preferably 88～90.
Described siccative is selected from one or more in isocaprylic acid zinc, zirconium iso-octoate, the dibutyl tin laurate.
Described solvent is selected from one or both in N-BUTYL ACETATE or the 1-Methoxy-2-propyl acetate.
A kind of preparation method who makes the quick-drying additive of paint is characterized in that this method may further comprise the steps:
(1) get the raw materials ready according to following component and weight part content:
Siccative 10～20,
Solvent 80～100;
(2) certain amount of solvent is dropped in the dispersion cup, controlled temperature is 20～30 ℃, and stirring velocity is that 100～200rpm stirring makes solvent dispersion even;
(3) keep stirring that siccative is dropped in the dispersion cup, the control stirring velocity is 100～200rpm, continues to stir 10～30min;
(4) solid content of siccative in the detection dispersion cup utilizes solvent that solid content is adjusted to set(ting)value, continues then to stir 10～30min, promptly obtains making the quick-drying additive of paint after the filtration.
The set(ting)value of described solid content is 1.5～2wt%.
The set(ting)value of described solid content is 1.8wt%.
Compared with prior art, the present invention has the following advantages:
(1) this additive is very obvious for the rate of drying that improves two component car refinishing paints, under field conditions (factors), can shorten to 2 hours with 5 hours;
(2) save the time, improved efficient, practiced thrift cost;
(3) car repair factory and auto producer competitive strength have been improved;
(4) this additive belongs to the general purpose grade product, also applicable in the dual-component coating in the other industry.
Embodiment
Below in conjunction with specific embodiment the present invention is elaborated.
Embodiment 1
A kind of preparation method who makes the quick-drying additive of paint, this method may further comprise the steps:
(1) get the raw materials ready according to following component and content: siccative 10kg, solvent 80kg, wherein siccative is an isocaprylic acid zinc, solvent is a N-BUTYL ACETATE;
(2) certain amount of solvent is dropped in the dispersion cup, controlled temperature is 20 ℃, and stirring velocity is that the 100rpm stirring makes solvent dispersion even;
(3) keep stirring that siccative is dropped in the dispersion cup, the control stirring velocity is 100rpm, continues to stir 10min;
(4) solid content of siccative in the detection dispersion cup utilizes solvent that solid content is adjusted to set(ting)value 1.5wt%, continues then to stir 10min, promptly obtains making the quick-drying additive of paint after the filtration.
Embodiment 2
A kind of preparation method who makes the quick-drying additive of paint, this method may further comprise the steps:
(1) get the raw materials ready according to following component and content: siccative 11kg, solvent 85kg, wherein siccative is the mixture of zirconium iso-octoate and dibutyl tin laurate, solvent is a N-BUTYL ACETATE;
(2) certain amount of solvent is dropped in the dispersion cup, controlled temperature is 25 ℃, and stirring velocity is that the 150rpm stirring makes solvent dispersion even;
(3) keep stirring that siccative is dropped in the dispersion cup, the control stirring velocity is 120rpm, continues to stir 15min;
(4) solid content of siccative in the detection dispersion cup utilizes solvent that solid content is adjusted to set(ting)value 1.8wt%, continues then to stir 15min, promptly obtains making the quick-drying additive of paint after the filtration.
Embodiment 3
A kind of preparation method who makes the quick-drying additive of paint, this method may further comprise the steps:
(1) get the raw materials ready according to following component and content: siccative 15kg, solvent 93kg, wherein siccative is the mixture of isocaprylic acid zinc and dibutyl tin laurate, solvent is a 1-Methoxy-2-propyl acetate;
(2) certain amount of solvent is dropped in the dispersion cup, controlled temperature is 30 ℃, and stirring velocity is that the 200rpm stirring makes solvent dispersion even;
(3) keep stirring that siccative is dropped in the dispersion cup, the control stirring velocity is 200rpm, continues to stir 30min;
(4) solid content of siccative in the detection dispersion cup utilizes solvent that solid content is adjusted to set(ting)value 1.8wt%, continues then to stir 30min, promptly obtains making the quick-drying additive of paint after the filtration.
Embodiment 4
A kind of preparation method who makes the quick-drying additive of paint, this method may further comprise the steps:
(1) get the raw materials ready according to following component and content: siccative 12kg, solvent 90kg, wherein siccative is a dibutyl tin laurate, solvent is the mixture of N-BUTYL ACETATE and 1-Methoxy-2-propyl acetate;
(2) certain amount of solvent is dropped in the dispersion cup, controlled temperature is 30 ℃, and stirring velocity is that the 150rpm stirring makes solvent dispersion even;
(3) keep stirring that siccative is dropped in the dispersion cup, the control stirring velocity is 180rpm, continues to stir 20min;
(4) solid content of siccative in the detection dispersion cup utilizes solvent that solid content is adjusted to set(ting)value 1.6wt%, continues then to stir 25min, promptly obtains making the quick-drying additive of paint after the filtration.
Embodiment 5
A kind of preparation method who makes the quick-drying additive of paint, this method may further comprise the steps:
(1) get the raw materials ready according to following component and content: siccative 13kg, solvent 88kg, wherein siccative is a zirconium iso-octoate, solvent is the mixture of N-BUTYL ACETATE and 1-Methoxy-2-propyl acetate;
(2) certain amount of solvent is dropped in the dispersion cup, controlled temperature is 30 ℃, and stirring velocity is that the 160rpm stirring makes solvent dispersion even;
(3) keep stirring that siccative is dropped in the dispersion cup, the control stirring velocity is 150rpm, continues to stir 20min;
(4) solid content of siccative in the detection dispersion cup utilizes solvent that solid content is adjusted to set(ting)value 2wt%, continues then to stir 25min, promptly obtains making the quick-drying additive of paint after the filtration.
Embodiment 6
A kind of preparation method who makes the quick-drying additive of paint, this method may further comprise the steps:
(1) get the raw materials ready according to following component and content: siccative 20kg, solvent 100kg, wherein siccative is a zirconium iso-octoate, solvent is the mixture of N-BUTYL ACETATE and 1-Methoxy-2-propyl acetate;
(2) certain amount of solvent is dropped in the dispersion cup, controlled temperature is 30 ℃, and stirring velocity is that the 160rpm stirring makes solvent dispersion even;
(3) keep stirring that siccative is dropped in the dispersion cup, the control stirring velocity is 150rpm, continues to stir 20min;
(4) solid content of siccative in the detection dispersion cup utilizes solvent that solid content is adjusted to set(ting)value 2wt%, continues then to stir 30min, promptly obtains making the quick-drying additive of paint after the filtration.
Claims (8)
1. one kind makes the quick-drying additive of paint, it is characterized in that this additive comprises following component and weight part content:
Siccative 10～20;
Solvent 80～100.
2. a kind of quick-drying additive of paint that makes according to claim 1 is characterized in that the weight part of described siccative is preferred 10～15, the weight part of solvent preferred 85～93.
3. a kind of quick-drying additive of paint that makes according to claim 1 is characterized in that, the weight part of described siccative more preferably 12～13, the weight part of solvent more preferably 88～90.
4. a kind of quick-drying additive of paint that makes according to claim 1 is characterized in that described siccative is selected from one or more in isocaprylic acid zinc, zirconium iso-octoate, the dibutyl tin laurate.
5. a kind of quick-drying additive of paint that makes according to claim 1 is characterized in that described solvent is selected from one or both in N-BUTYL ACETATE or the 1-Methoxy-2-propyl acetate.
One kind as claimed in claim 1 make paint quick-drying additive the preparation method, it is characterized in that this method may further comprise the steps:
(1) get the raw materials ready according to following component and weight part content:
Siccative 10～20,
Solvent 80～100;
(2) certain amount of solvent is dropped in the dispersion cup, controlled temperature is 20～30 ℃, and stirring velocity is that 100～200rpm stirring makes solvent dispersion even;
(3) keep stirring that siccative is dropped in the dispersion cup, the control stirring velocity is 100～200rpm, continues to stir 10～30min;
(4) solid content of siccative in the detection dispersion cup utilizes solvent that solid content is adjusted to set(ting)value, continues then to stir 10～30min, promptly obtains making the quick-drying additive of paint after the filtration.
7. a kind of preparation method who makes the quick-drying additive of paint according to claim 6 is characterized in that the set(ting)value of described solid content is 1.5～2wt%.
8. a kind of preparation method who makes the quick-drying additive of paint according to claim 6 is characterized in that the set(ting)value of described solid content is 1.8wt%.