CN102618143A - Heavy-duty anticorrosion coating - Google Patents
Heavy-duty anticorrosion coating Download PDFInfo
- Publication number
- CN102618143A CN102618143A CN2012100140722A CN201210014072A CN102618143A CN 102618143 A CN102618143 A CN 102618143A CN 2012100140722 A CN2012100140722 A CN 2012100140722A CN 201210014072 A CN201210014072 A CN 201210014072A CN 102618143 A CN102618143 A CN 102618143A
- Authority
- CN
- China
- Prior art keywords
- parts
- heavy
- epoxy resin
- epoxy
- duty coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a heavy-duty anticorrosion coating. Raw materials of the coating comprise, by weight, 20-35 parts of an epoxy resin 618, 20-35 parts of an epoxy resin 828, 5-15 parts of butyl glycidyl ether, 1-5 parts of a tertiary amine curing accelerator, 1-5 parts of a polysiloxane, 8 parts of a polyamide, and 12 parts of a modified araliphatic amine epoxy curing agent. A method for preparing the coating comprises the following steps: mixing the epoxy resin 618 with the epoxy resin 828, adding a specific filler, an assistant and the curing agent to form the heavy-duty anticorrosion coating which does not contain an organic solvent, has a high solid content, has no solvents to volatile, and has no damages to constructors during construction. The coating which can be sprayed and brushed can form a film at normal temperature, and can be very conveniently constructed, so the environmental pollution is effectively reduced; and a coat of the coating has the advantages of strong adhesion and wear resistance, excellent anticorrosion performance, and very ideal water, salt spray, acid and alkali resistances.
Description
Technical field
The present invention relates to paint field, be specifically related to a kind of heavy-duty coating.
Background technology
Metal and concrete facilities such as all are far away, coastal waters boats and ships, naval vessel submarine, oceanographic engineering, drilling unit, port and pier, water conservancy projects, landification equipment and bridge construction; Be in for a long time under water or in 100% the wet environment; Its surface corrosion, attaching organism and filthy corrosion phenomenon are very serious, and the maintenance interval of oceangoing vessel generally all is once every two years.In actual condition, many metals that are difficult under water move are equipped and the concrete facility, have to let alone burn into and pollute.
And traditional heavy-duty coating, it is low to exist solids content, and solvent is high; Film forming is thin, and sticking power is low, and surface treatment is strict; Construction technology is complicated, technical barrier such as the dew point restriction is arranged, environmental pollution is serious and the life-span is short, especially during coating to carrying out strict rust cleaning in the metallic surface; Require simultaneously by the application surface drying, these all are the difficult problems that traditional heavy-duty coating is faced with for a long time.
For above-mentioned reasons, antiseptic projects such as China's oceanographic engineering and shipping industry and petroleum and petrochemical industry, because of surface treatment and application do not reach standard, reasons such as coating property difference, annual nearly trillion the corrosion financial loss that all will produce.At present; The anticorrosion industry in China ocean presses for a kind of ecological, environmental protective, solvent-free, solids content 100%, nontoxicity, the restriction of no dew point and has high arris conservation rate; Can be under water, in the severe environment of 100% humid zone rust, the long-acting heavy-duty coating that metal and concrete surface are directly constructed.
Summary of the invention
The invention reside in provides a kind of organic solvent that do not contain, and antiseptic property is good, have stronger sticking power and wear resisting property, the heavy-duty coating of being convenient to construct.
Technical scheme of the present invention is following:
A kind of heavy-duty coating, its raw material consists of:
618 20～35 parts of epoxy resin;
828 20～35 parts of epoxy resin;
5～15 parts of epoxy propane butyl ethers;
1～5 part of tertiary amine curing catalyst;
1～5 part of ZGK 5;
8 parts of polymeric amide;
12 parts of modification virtue fat amine epoxy curing agents;
Said umber is weight part.
As improvement, the raw material of heavy-duty coating consists of:
618 25～35 parts of epoxy resin;
828 15～30 parts of epoxy resin;
5～10 parts of epoxy propane butyl ethers;
1～5 part of tertiary amine curing catalyst;
1～5 part of ZGK 5;
1～3 part of clorafin;
1～3 part in poly carboxylic acid sodium;
8 parts of polymeric amide;
10 parts of modification virtue fat amine epoxy curing agents;
2 parts of phenolic aldehyde amine epoxy resin;
Said umber is weight part.
As improvement, the viscosity of said tertiary amine curing catalyst is 50-65mPa.s; The amine value of polymeric amide is 200-220 mgk0H/g; The viscosity of modification virtue fat amine epoxy curing agent is 300～600 mPa.s, and the amine value is 315～345 mgk0H/g.
As improvement, the raw material of described heavy-duty coating is formed and is also comprised
20～30 parts of antirust, anti-corrosive color stuffings;
5～20 parts of tinting pigments.
Wherein, the antirust, anti-corrosive color stuffing is selected from the mixture of one or more arbitrary proportions in the following material: zn phosphate, iron mica, aluminium triphosphate, permanent white, ST antirusting powder, talcum powder.
Wherein, tinting pigment is selected from the mixture of one or more arbitrary proportions in the following material: iron oxide red powder, white titanium pigment, carbon black.
As improvement, the mean particle size of antirust, anti-corrosive color stuffing is not less than 1000 orders.
The protective system that adopts above-mentioned raw materials to produce does not add organic solvent, and solid content is high, and solvent-free volatilization is safe from harm to the workmen during construction; This coating not only can spray but also can brush, film forming at normal temperatures, and it is very convenient to construct, and an application of wet film can reach more than the 1200 μ m, reduces construction application road number, has both shortened the duration, has reduced environmental pollution again effectively; This paint coatings has stronger sticking power, wear resisting property and excellent antiseptic property, and no matter water-fast, salt spray resistance still is that acid-proof alkaline is all very good.
The preparation method of heavy-duty coating of the present invention is conventional preparation method, and concrete steps are:
Earlier a certain proportion of epoxy resin 618, epoxy resin 828, epoxy propane butyl ether are packed in the stirred vessel, employed stirred vessel be conventional stirred vessel, and keeping rotating speed is that 1200r/min stirs, make its abundant miscible after; Add antirust color stuffing, tinting pigment; Keeping rotating speed is that 2500r/min continues to stir 0.5h; To stir resulting material joins three-roll grinder (three-roll grinder is that Changzhou east essence reaches machine works and produces; Model is S150) be ground to the fineness of regulation, add a certain amount of tertiary amine curing catalyst, ZGK 5 and other auxiliary agents again and carry out obtaining finished product after the miscible processing.
Embodiment
The following special preferred embodiment of lifting elaborates to the present invention.
The raw material that following examples adopt is:
Epoxy resin 618, epoxy resin 828 are produced by Sanmu Group Co., Ltd., Jiangsu;
Polymeric amide: its amine value is 200-220 mgk0H/g;
Phenolic aldehyde amine epoxy resin adopts Sanmu Group Co., Ltd., Jiangsu to produce, and model is T-31;
The tertiary amine curing catalyst adopts Junjiang Science and Technology Co Ltd, Shanghai to produce curing catalyst TR-30, and its viscosity is 50-65mPa.s;
Modification virtue fat amine epoxy curing agent is produced by Junjiang Science and Technology Co Ltd, Shanghai, and model is D9050, and its viscosity is 300～600 mPa.s, and the amine value is 315～345 mgk0H/g.
The antirust, anti-corrosive color stuffing: mean particle size is 1000 orders.
Embodiment 1
Following umber is weight part.
The raw material of heavy-duty coating consists of:
618 25 parts of epoxy resin
35 parts of epoxy resin E-52
10 parts of epoxy propane butyl ethers
20 parts of zn phosphates
7 parts in iron oxide red powder
2 parts of ZGK 5
1 part of tertiary amine curing catalyst
8 parts of polymeric amide
12 parts of modification virtue fat amine epoxy curing agents.
Embodiment 2
The raw material of heavy-duty coating consists of:
618 20 parts of epoxy resin
30 parts of epoxy resin E-52
15 parts of epoxy propane butyl ethers
25 parts of iron micas
5 parts of white titanium pigments
1 part of ZGK 5
4 parts of tertiary amine curing catalysts
8 parts of polymeric amide
12 parts of modification virtue fat amine epoxy curing agents.
Embodiment 3
The raw material of heavy-duty coating consists of:
618 35 parts of epoxy resin
828 20 parts of epoxy resin
5 parts of epoxy propane butyl ethers
12 parts of zn phosphates
18 parts of aluminium triphosphates
6 parts of carbon blacks
2 parts of ZGK 5
2 parts of tertiary amine curing catalysts
8 parts of polymeric amide
12 parts of modification virtue fat amine epoxy curing agents.
Embodiment 4
The raw material of heavy-duty coating consists of:
618 24 parts of epoxy resin
828 20 parts of epoxy resin
5 parts of epoxy propane butyl ethers
23 parts in permanent white
10 parts of white titanium pigments
10 parts of carbon blacks
5 parts of ZGK 5
3 parts of tertiary amine curing catalysts
8 parts of polymeric amide
12 parts of modification virtue fat amine epoxy curing agents.
Embodiment 5
The raw material of heavy-duty coating consists of:
618 21 parts of epoxy resin
828 23 parts of epoxy resin
10 parts of epoxy propane butyl ethers
5 parts of iron micas
12 parts of ST antirusting powders
3 parts of talcum powder
10 parts in iron oxide red powder
8 parts of carbon blacks
3 parts of tertiary amine curing catalysts
5 parts of ZGK 5
8 parts of polymeric amide
12 parts of modification virtue fat amine epoxy curing agents.
Embodiment 6
The raw material of heavy-duty coating consists of:
618 25 parts of epoxy resin
828 30 parts of epoxy resin
8 parts of epoxy propane butyl ethers
10 parts of aluminium triphosphates
8 parts in permanent white
7 parts of talcum powder
5 parts in iron oxide red powder
1 part of tertiary amine curing catalyst
2 parts of ZGK 5
3 parts of clorafins
1 part in poly carboxylic acid sodium
8 parts of polymeric amide
10 parts of modification virtue fat amine epoxy curing agents
2 parts of phenolic aldehyde amine epoxy resin.
Embodiment 7
The raw material of heavy-duty coating consists of:
618 28 parts of epoxy resin
828 15 parts of epoxy resin
10 parts of epoxy propane butyl ethers
20 parts in permanent white
4 parts in iron oxide red powder
6 parts of white titanium pigments
10 parts of carbon blacks
2 parts of tertiary amine curing catalysts
1 part of ZGK 5
1 part of clorafin
3 parts in poly carboxylic acid sodium
8 parts of polymeric amide
10 parts of modification virtue fat amine epoxy curing agents
2 parts of phenolic aldehyde amine epoxy resin.
Embodiment 8
The raw material of heavy-duty coating consists of:
618 35 parts of epoxy resin
828 17 parts of epoxy resin
5 parts of epoxy propane butyl ethers
10 parts of zn phosphates
10 parts of aluminium triphosphates
10 parts of ST antirusting powders
5 parts in iron oxide red powder
1 part of tertiary amine curing catalyst
5 parts of ZGK 5
1 part of clorafin
1 part in poly carboxylic acid sodium
8 parts of polymeric amide
10 parts of modification virtue fat amine epoxy curing agents
2 parts of phenolic aldehyde amine epoxy resin.
Embodiment 9
The raw material of heavy-duty coating consists of:
618 30 parts of epoxy resin
828 25 parts of epoxy resin
5 parts of epoxy propane butyl ethers
22 parts of iron micas
10 parts of carbon blacks
5 parts of tertiary amine curing catalysts
1 part of ZGK 5
1 part of clorafin
1 part in poly carboxylic acid sodium
8 parts of polymeric amide
10 parts of modification virtue fat amine epoxy curing agents
2 parts of phenolic aldehyde amine epoxy resin.
Utilize following instrument that the performance of the coating of the foregoing description system is measured,
The big trier factory that reaches in Hegman grind gage (QXD-100 type) Tianjin
Coating adhesion test instrument (QFZ type) Tianjin Dong Wenya material-testing machine ltd
Coating impact instrument (QCJ type) Tianjin Dong Wenya material-testing machine ltd
Accurate salt-fog test machine (HG-60 type) Suzhou Heng Gang Electronics Co., Ltd.
Paint film compliance test apparatus (QTX type) Tianjin Dong Wenya material-testing machine ltd
The auspicious plant and instrument of pull-out test appearance (PosiTsetAT type) Shanghai labor ltd.
The detected performance test data of the foregoing description are as shown in table 1,
Table 1
The case of practical implementation described in the present invention is merely preferable case study on implementation of the present invention, is not to be used for limiting practical range of the present invention.The equivalence of promptly doing according to the content of claim of the present invention changes and modifies, all should be as technological category of the present invention.
Claims (8)
1. heavy-duty coating is characterized in that raw material consists of:
618 20～35 parts of epoxy resin;
828 20～35 parts of epoxy resin;
5～15 parts of epoxy propane butyl ethers;
1～5 part of tertiary amine curing catalyst;
1～5 part of ZGK 5;
8 parts of polymeric amide;
12 parts of modification virtue fat amine epoxy curing agents;
Above-mentioned umber is weight part.
2. heavy-duty coating according to claim 1 is characterized in that raw material consists of:
618 25～35 parts of epoxy resin;
828 15～30 parts of epoxy resin;
5～10 parts of epoxy propane butyl ethers;
1～5 part of tertiary amine curing catalyst;
1～5 part of ZGK 5;
1～3 part of clorafin;
1～3 part in poly carboxylic acid sodium;
8 parts of polymeric amide;
10 parts of modification virtue fat amine epoxy curing agents;
2 parts of phenolic aldehyde amine epoxy resin;
Said umber is weight part.
3. heavy-duty coating according to claim 1 and 2, the viscosity that it is characterized in that said tertiary amine curing catalyst is 50-65mPa.s; The amine value of polymeric amide is 200-220 mgk0H/g; The viscosity of modification virtue fat amine epoxy curing agent is 300～600 mPa.s, and the amine value is 315～345 mgk0H/g.
4. heavy-duty coating according to claim 1 is characterized in that the raw material composition of said heavy-duty coating also comprises
20～30 parts of antirust, anti-corrosive color stuffings;
5～20 parts of tinting pigments.
5. heavy-duty coating according to claim 4, the viscosity that it is characterized in that said tertiary amine curing catalyst is 50-65mPa.s; The amine value of polymeric amide is 200-220 mgk0H/g; The viscosity of modification virtue fat amine epoxy curing agent is 300～600 mPa.s, and the amine value is 315～345 mgk0H/g.
6. heavy-duty coating according to claim 4 is characterized in that one or more arbitrary proportions that said antirust, anti-corrosive color stuffing is selected from zn phosphate, iron mica, aluminium triphosphate, permanent white, ST antirusting powder, the talcum powder mix.
7. heavy-duty coating according to claim 4 is characterized in that one or more arbitrary proportions in said tinting pigment chosen from Fe rouge and powder, white titanium pigment, the carbon black mix.
8. heavy-duty coating according to claim 4 is characterized in that the mean particle size of antirust, anti-corrosive color stuffing is not less than 1000 orders.