CN102617056A - Gelled material based on slag, preparation method and application of gelled material - Google Patents
Gelled material based on slag, preparation method and application of gelled material Download PDFInfo
- Publication number
- CN102617056A CN102617056A CN2012100828662A CN201210082866A CN102617056A CN 102617056 A CN102617056 A CN 102617056A CN 2012100828662 A CN2012100828662 A CN 2012100828662A CN 201210082866 A CN201210082866 A CN 201210082866A CN 102617056 A CN102617056 A CN 102617056A
- Authority
- CN
- China
- Prior art keywords
- slag
- parts
- gelling material
- preparation
- rhombspar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a gelled material based on slag, a preparation method and application of the gelled material. The gelled material provided by the invention comprises the following raw materials in parts by weight: 10-20 parts of dolomite, 1-5 parts of excitant and 80-90 parts of the slag. Compared with the prior art, the gelled material provided by the invention has the advantages that the slag with the most parts is adopted, the waste is utilized, and the resource is saved; the pollutant emission in a production process is close to zero, and the environment is protected; and the compression resistant strength performance and the flexural strength performance are superior to those of the prior art, the cost is lower, and the economic benefit is larger.
Description
Technical field
The present invention relates to a kind of material of construction, particularly, relate to a kind of gelling material, and its preparation method and application.
Background technology
The present domestic novel environment friendly gelling material that is applied to building materials field; Comparatively single (as: people such as Sun Baoyun utilizes blast furnace slag that the Laigang produces to replace cement with 30% volume to employed industrial residue in the raw material; Intensity has reached the requirement that label is 325 ordinary Portland cement); Can not realize the resource utilization of solid waste such as multiple industrial residue simultaneously, and not put on a large scale in the actual buildings build; Even a spot of case history is arranged, also be that some industrial solid wastes are used as concrete little volume additive, do not have to realize solid waste as starting material real the time, and production process approaches zero pollutant emission.
Patented claim CN201010163504.7 discloses a kind of desulfurated plaster-high-calcium fly ash geopolymer gelled material; It is characterized in that: the raw material of this geopolymer gelled material comprises high-calcium fly ass, thermal treatment desulfurated plaster and composite chemical admixture, and wherein: to be desulfurated plaster get at temperature lower calcination 0.5h~1.5h of 600 ℃~800 ℃ the thermal treatment desulfurated plaster; The composite chemical admixture is formulated by sodium hydroxide and liquid sodium silicate, the modulus M (SiO of composite chemical admixture
2)/n (Na
2O) be 1.5~2.0; Quantity relative ratio relationship between these three kinds of raw materials is: the mass ratio of high-calcium fly ass and thermal treatment desulfurated plaster is 9: 1~8: 2; The quality of the Na2O that is introduced by the composite chemical admixture is 10%~15% of high-calcium fly ass and a thermal treatment desulfurated plaster quality sum.These technology materials are more, dealing with complicated, and cost is higher, and the gelling material ultimate compression strength that makes is also lower.
Be the deficiency that existing gelling material all exists some aspect, this influences the development and the popularization of gelling material.
Summary of the invention
In order to solve prior art problems, it is a kind of based on scoriaceous gelling material that the present invention provides.
Another object of the present invention is to provide said preparation method based on scoriaceous gelling material.
It is said based on the application of scoriaceous gelling material at building field that a purpose more of the present invention is to provide.
Provided by the invention based on scoriaceous gelling material, comprise the raw material of following weight part: 10~20 parts of rhombspars, 80~90 parts in 1~5 part of exciting agent and slag.
Provided by the invention based on scoriaceous gelling material, preferably, comprise the raw material of following weight part: 13~15 parts of rhombspars, 83~86 parts in 1~2 part of exciting agent and slag.
Provided by the invention based on scoriaceous gelling material, more preferably, comprise the raw material of following weight part: 14 parts of rhombspars, 84 parts in 2 parts of exciting agents and slag.
Wherein, said exciting agent is selected from: Na
2CO
3, among KCl, NaCl and NaOH etc. one or more.
Preparing method based on scoriaceous gelling material provided by the invention is after each raw material is ground to fine particle, to mix in proportion, in stirrer, stirs, and promptly gets.
Among the above-mentioned preparation method:
Before rhombspar is ground, can earlier it be calcined.
It is wherein, said that rhombspar is carried out the incinerating temperature is 800~1000 ℃.Preferred 900 ℃.
The fineness of said former abrasive lapping is respectively: rhombspar 3000~6000cm
2/ g, exciting agent 3000~6000cm
2/ g and slag 5000~7000cm
2/ g.
The time of said raw material stirring is 25~35s.Preferred 30s.
The rotating speed of stirrer is 250~350r/min during said raw material stirring.Preferred 300r/min.
Material provided by the invention can be applied to building field.
Gelling material provided by the invention, the high compressive strength of 28d can reach 37.5MPa, and high breaking strength reaches 5.8MPa, and its pi of strength is superior to 325 cement (28d ultimate compression strength is 32.5MPa, and folding strength is 5.5MPa).And prepare gelling material with this industrial solid wastes of slag, production process approaches zero pollutant emission.As the alternative article of material of construction cement, the pollution of Cement industry is reduced significantly, until whole eliminations, realize the resource utilization of a large amount of solid waste.
In a word, the present invention compared with prior art adopts the slag of more content, can realize the resource utilization of solid waste such as multiple industrial residue simultaneously, utilization of waste material; Do not use concrete, lime etc., economize on resources; Production process approaches zero pollutant emission, the protection environment; Resistance to compression, resisting strength property to be superior to prior art, and cost is lower, economic benefit is bigger.
Embodiment
Following examples are used to explain the present invention, but are not used for limiting scope of the present invention.
Exciting agent used in the present invention all is solid, can buy from market.Slag and rhombspar are the conventional materials in this area.
Percentage ratio of the present invention " % " all refers to weight percent.
Embodiment 1
Gelling material: rhombspar 14%, exciting agent Na
2CO
30.5%, KCl 0.5% and NaCl1%, slag 84%.
The preparation method: rhombspar, exciting agent after slag, the 900 ℃ of calcinings are added shredder respectively, and (fineness is respectively: rhombspar 4000cm to be milled to fine particle
2/ g, exciting agent 4000cm
2/ g and slag 6000cm
2/ g), each component is added mixing machine according to above-mentioned weight, stir (churning time 30s, stirring velocity 300r/min) promptly gets gelling material.
The gelling material that makes is applied to the construction that the room is used in the construction site temporarily, reaches 37.5MPa through its 28d ultimate compression strength of national building materials test center test verification, folding strength reaches 5.8MPa.
Embodiment 2
Gelling material: rhombspar 15%, exciting agent Na
2CO
30.5% with NaCl 0.5%, slag 84%.
The preparation method: rhombspar, exciting agent after slag, the 800 ℃ of calcinings are added shredder respectively, and (fineness is respectively: rhombspar 6000cm to be milled to fine particle
2/ g, exciting agent 3000cm
2/ g and slag 5000cm
2/ g), each component is added mixing machine according to above-mentioned weight, stir (churning time 25s, stirring velocity 250r/min) promptly gets gelling material (ultimate compression strength reaches 35.0MPa, and folding strength reaches 5.5MPa).
Embodiment 3
Gelling material: rhombspar 15%, exciting agent NaCl 2%, slag 83%.
The preparation method: rhombspar, exciting agent after slag, the 800 ℃ of calcinings are added shredder respectively, and (fineness is respectively: rhombspar 3000cm to be milled to fine particle
2/ g, exciting agent 6000cm
2/ g and slag 7000cm
2/ g), each component is added mixing machine according to above-mentioned weight, stir (churning time 25s, stirring velocity 300r/min) promptly gets gelling material (ultimate compression strength reaches 36.0MPa, and folding strength reaches 5.6MPa).
Embodiment 4
Gelling material: rhombspar 13%, exciting agent Na
2CO
30.5%, NaCl 1% and NaOH0.5%, slag 85%.
The preparation method: rhombspar, exciting agent after slag, the 1000 ℃ of calcinings are added shredder respectively, and (fineness is respectively: rhombspar 4000cm to be milled to fine particle
2/ g, exciting agent 5000cm
2/ g and slag 6000cm
2/ g), each component is added mixing machine according to above-mentioned weight, stir (churning time 35s, stirring velocity 350r/min) promptly gets gelling material (ultimate compression strength reaches 35.5MPa, and folding strength reaches 5.6MPa).
Embodiment 5
Gelling material: rhombspar 13%, exciting agent NaCl 1%, slag 86%.
The preparation method: rhombspar, exciting agent after slag, the 900 ℃ of calcinings are added shredder respectively, and (fineness is respectively: rhombspar 5000cm to be milled to fine particle
2/ g, exciting agent 4000cm
2/ g and slag 6000cm
2/ g), each component is added mixing machine according to above-mentioned weight, stirring, (churning time 30s, stirring velocity 300r/min promptly get gelling material (ultimate compression strength reaches 35.0MPa, and folding strength reaches 5.5MPa).
Claims (10)
1. one kind based on scoriaceous gelling material, it is characterized in that, comprises the raw material of following weight part: 10~20 parts of rhombspars, 1~5 part of exciting agent and 80~90 parts in slag.
2. gelling material according to claim 1 is characterized in that, comprises the raw material of following weight part: 13~15 parts of rhombspars, 83~86 parts in 1~2 part of exciting agent and slag.
3. gelling material according to claim 1 and 2 is characterized in that, comprises the raw material of following weight part: 14 parts of rhombspars, 84 parts in 2 parts of exciting agents and slag.
4. according to any described gelling material of claim 1~3, it is characterized in that said exciting agent is selected from: Na
2CO
3, among KCl, NaCl and the NaOH one or more.
5. the preparation method of any described gelling material of claim 1~4 is characterized in that, is after each raw material is ground to fine particle, to mix in proportion, in stirrer, stirs, and promptly gets.
6. the preparation method of gelling material according to claim 5 is characterized in that, before rhombspar is ground, earlier it is calcined; It is 800~1000 ℃ that rhombspar is carried out the incinerating temperature.
7. the preparation method of gelling material according to claim 5 is characterized in that, the fineness of said former abrasive lapping is respectively: rhombspar 3000~6000cm
2/ g, exciting agent 3000~6000cm
2/ g and slag 5000~7000cm
2/ g.
8. the preparation method of gelling material according to claim 5 is characterized in that, the time of said raw material stirring is 25~35s.
9. the preparation method of gelling material according to claim 5 is characterized in that, the rotating speed of said stirrer is 250~350r/min.
10. any described gelling material of claim 1~4 is in the application of building field.