CN102586946B - High-strength graphene ordered porous fibers and preparation method thereof - Google Patents
High-strength graphene ordered porous fibers and preparation method thereof Download PDFInfo
- Publication number
- CN102586946B CN102586946B CN201210001524.3A CN201210001524A CN102586946B CN 102586946 B CN102586946 B CN 102586946B CN 201210001524 A CN201210001524 A CN 201210001524A CN 102586946 B CN102586946 B CN 102586946B
- Authority
- CN
- China
- Prior art keywords
- graphene
- weight portion
- ordered porous
- graphite
- graphene oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses high-strength graphene ordered porous fibers and a preparation method thereof. The method comprises the following steps of: oxidizing graphite to obtain graphene oxide; dispersing the graphene oxide in water to obtain 1 to 20 mass percent spinning solution liquid crystal sol; continuously extruding a spinning solution at a constant speed from a spinning head capillary to liquid nitrogen, and solidifying; performing freeze drying to obtain graphene oxide ordered porous fibers; and performing chemical reduction to obtain the graphene ordered porous fibers. The obtained graphene ordered porous fibers are low in density, high in porosity, excellent in mechanical properties and high in toughness, can be used for supporting various catalysts and also can be used as light leads.
Description
Technical field
The present invention relates to a kind of porous graphene fiber, relate in particular to a kind of high-strength graphene ordered porous fibers and preparation method thereof.
Background technology
Graphene is a kind of novel two-dimensional nano material, has caused the research boom of academia and industrial quarters since self-discovery.This material has the intensity that known materials is the highest, excellent electric conductivity and thermal conductivity, the highest carrier transport speed, the large tempting characteristics such as specific area.At present, realize and prepare Graphene macroscopic material, comparatively general method is to take native graphite as raw material preparation oxidation oxidation of precursor Graphene, by chemical oxidation-reducing process, realize again a large amount of preparations (Tung, V. C., the et al. Nature Nanotechnol. of Graphene, 2009
4, 25 – 29).Due to a large amount of organo-functional group in its surface, graphene oxide shows good dissolubility in water; Due to its large flakiness ratio (being generally greater than 1000), graphene oxide can show liquid crystal behavior in water, i.e. spontaneous formation ordered structure simultaneously.The Graphene macroscopic material that being found to be of graphene oxide liquid crystal prepared high-sequential provides a simple effective method.Yet, utilize this characteristic of graphene oxide liquid crystal to prepare Graphene Microscopic order material and remain the challenge realizing in Graphene application.
Summary of the invention
The object of the invention is, for the deficiencies in the prior art, provides a kind of high-strength graphene ordered porous fibers and preparation method thereof.The present invention adopts graphite to carry out the ordered porous fiber of Graphene as raw material, and the ordered porous fiber making has low-density, high-tensile strength and high compression-strength, good toughness and electric conductivity.Process costs of the present invention is low, simple to operate.
The object of the invention is to be achieved through the following technical solutions: a kind of preparation method of high-strength graphene ordered porous fibers, comprises the following steps:
(1) graphite raw material of 1 weight portion, 1 ~ 100 weight portion sulfuric acid, 0.5 ~ 5 weight portion potassium peroxydisulfate and 0.5 ~ 5 weight portion phosphorus pentoxide are mixed, at 25 ~ 100 ℃, stirring reaction is 1 ~ 10 hour, after cool to room temperature, with deionized water, dilute, with filter membrane suction filtration, with deionized water washing, to neutral, air dry obtains intercalated graphite for 10 ~ 50 hours;
(2) intercalated graphite of gained in 1 weight portion step 1,1 ~ 100 weight portion sulfuric acid and 0.5 ~ 10 weight portion potassium permanganate are mixed, at-10 ~ 50 ℃, stirring reaction is after 0.1 ~ 10 hour, add deionized water and 0.1 ~ 10 weight portion hydrogen peroxide of 10 ~ 2000 weight portions to stir 0.1 ~ 10 hour, with membrane filtration, with deionized water cyclic washing, to neutral, air dry obtains graphite oxide;
(3) the graphite oxide ene product of gained in 1 weight portion step 2 is dissolved in the water of 5 ~ 100 weight portions, with the ultrasonic processing of 0 ~ 50KHz 0.1 ~ 10 hour, obtains graphene oxide spinning solution colloidal sol;
(4) get the graphene oxide spinning solution colloidal sol of step 3 gained, extruded velocity with 1 ~ 100 mL/h, it by diameter, is the spinning capillary of 50 ~ 500 μ m, colloidal sol is clamp-oned and in liquid nitrogen, stopped 1 ~ 50s and condense, further freeze drying or critical freeze drying 2-40h, finally obtain ordered porous graphene oxide fiber again;
(5) the graphene oxide fiber of gained in step 4 is placed in to reductant and reduces 0.1 ~ 100h, washing is dry, obtains high-strength graphene ordered porous fibers.
The present invention has following technique effect:
1, adopting graphite is that raw material is prepared graphene fiber, raw material sources extensively, be easy to get;
2, the graphene oxide presoma of highly dissoluble and stable graphene oxide liquid crystal gel have been prepared simplely;
3, adopt spinning-cryodesiccated method to prepare the ordered porous fiber of graphene oxide;
4, the ordered porous fiber of graphene oxide making has very low density, high-tensile strength and high compression-strength, fine toughness;
5, the ordered porous fiber of Graphene making has very low density, high-tensile strength and high compression-strength, fine toughness, has excellent electric conductivity simultaneously.
The specific embodiment
The preparation method of high-strength graphene ordered porous fibers of the present invention, comprises the following steps:
1, the graphite raw material of 1 weight portion, 1 ~ 100 weight portion sulfuric acid, 0.5 ~ 5 weight portion potassium peroxydisulfate and 0.5 ~ 5 weight portion phosphorus pentoxide are mixed, at 25 ~ 100 ℃, stirring reaction is 1 ~ 10 hour, after cool to room temperature, with deionized water, dilute, with filter membrane suction filtration, with deionized water washing, to neutral, air dry obtains intercalated graphite for 10 ~ 50 hours.
Graphite is native graphite or pyrolytic graphite, and sulfuric acid is the sulfuric acid that mass concentration is greater than 80%.
2, the intercalated graphite of gained in 1 weight portion step 1,1 ~ 100 weight portion sulfuric acid and 0.5 ~ 10 weight portion potassium permanganate are mixed, at-10 ~ 50 ℃, stirring reaction is after 0.1 ~ 10 hour, add deionized water and 0.1 ~ 10 weight portion hydrogen peroxide of 10 ~ 2000 weight portions to stir 0.1 ~ 10 hour, with membrane filtration, with deionized water cyclic washing, to neutral, air dry obtains graphite oxide.
Sulfuric acid is the sulfuric acid that mass concentration is greater than 80%.
3, the graphite oxide ene product of gained in 1 weight portion step 2 is dissolved in the water of 5 ~ 100 weight portions, with the ultrasonic processing of 0 ~ 50KHz 0.1 ~ 10 hour, obtains graphene oxide spinning solution colloidal sol;
5, get the graphene oxide spinning solution colloidal sol of step 4 gained, extruded velocity with 1 ~ 100 mL/h, it by diameter, is the spinning capillary of 50 ~ 500 μ m, colloidal sol is clamp-oned and in liquid nitrogen, stopped 1 ~ 50s and condense, further freeze drying or critical freeze drying 2-40h, finally obtain the ordered porous fiber of graphene oxide again;
6, the graphene oxide fiber of gained in step 5 is placed in to reductant and reduces 0.1 ~ 100h, washing is dry, obtains high-strength graphene ordered porous fibers.
One or more the mixing of reductant in hydrazine hydrate, sodium borohydride, hydrobromic acid, hydroiodic acid, acetic acid forms.
The ordered porous fiber of high strength graphene oxide that this method obtains, graphene oxide is arranged vertically and is piled into along fiber axially extending bore, and the diameter of fiber is 5-500 micron, and density is 0.02-0.1g/cm
3, TENSILE STRENGTH is 5-10MPa, and compressive strength is 0.5-2MPa, and elongation at break is 0.3-10%.The high-strength graphene ordered porous fibers that this method obtains, graphene oxide is arranged vertically and is piled into along fiber axially extending bore, and density is 0.01-0.1g/cm
3, TENSILE STRENGTH is 5-20MPa, and compressive strength is 1-5MPa, and the diameter of fiber is 5-500 micron, and elongation at break is 1-10%, conductance is greater than 1000S/m.
Below by embodiment, the present invention is specifically described; the present embodiment is only for the present invention is described further; can not be interpreted as limiting the scope of the invention; those skilled in the art makes some nonessential change and adjustment according to the content of foregoing invention, all belongs to protection scope of the present invention.
embodiment 1:
Step (a): add 10g graphite in reaction bulb, 90% sulfuric acid of 10g, 1 g potassium peroxydisulfate and 1 g phosphorus pentoxide, at 80 ℃, stirring reaction is 5 hours, after cool to room temperature, with deionized water dilution, with filter membrane suction filtration, with deionized water cyclic washing filter cake, repeatedly to neutral, air dry obtains intercalated graphite for 10 hours;
Step (b): the intercalated graphite product that adds gained in 5g step (a) in reaction bulb, 80% sulfuric acid of 20g and 2.5g potassium permanganate, at 50 ℃, stirring reaction is after 2 hours, add 30% hydrogen peroxide of 1kg deionized water and 0.5g to stir 10 hours, with membrane filtration, with deionized water cyclic washing filter cake, to neutral, air dry obtains graphite oxide;
Step (c): add the graphite oxide ene product of gained in 1g step (b) in reaction bulb in 10g water, with the ultrasonic processing of 50KHz 1 hour, obtain graphene oxide spinning solution colloidal sol;
Step (d): get the graphene oxide spinning solution colloidal sol of gained in step (c), take the extruded velocity of 30 mL/h by diameter the spinning capillary as 20 μ m, in liquid nitrogen, solidify 1s postlyophilization 3h, obtain the ordered porous fiber of high strength graphene oxide;
Step (e): the ordered porous fiber of graphene oxide of gained in step (d) is placed in to hydrobromic acid, is heated to 80 ℃ of reaction 10h, through washing the dry high-strength graphene ordered porous fibers that obtains reduction.
Through above step, the graphene oxide obtaining has good dissolubility in water, forms stable liquid crystal gel under high concentration.In liquid crystal gel, graphene oxide sheet is layer structure and arranges.The diameter of the ordered porous fiber of graphene oxide of gained is 20 microns, and density is 0.1g/cm
3, TENSILE STRENGTH is 8-10MPa, and compressive strength is 1-2MPa, and elongation at break is 5-10%.High-strength graphene ordered porous fibers, graphene film is arranged vertically and is piled into along fiber axially extending bore, and density is 0.5-0.8g/cm
3, TENSILE STRENGTH is 15-20MPa, and compressive strength is 4-5MPa, and the diameter of fiber is 15-20 micron, and elongation at break is 8-10%, conductance is greater than 1000S/m.
embodiment 2:
Step (a): add 10g graphite in reaction bulb, 90% sulfuric acid of 100 g, 50 g potassium peroxydisulfates and 50 g phosphorus pentoxides, at 80 ℃, stirring reaction is 5 hours, after cool to room temperature, with deionized water dilution, with filter membrane suction filtration, with deionized water cyclic washing filter cake, repeatedly to neutral, air dry obtains intercalated graphite for 10 hours;
Step (b): the intercalated graphite product that adds gained in 5g step (a) in reaction bulb, 90% sulfuric acid of 300g and 50g potassium permanganate, at 50 ℃, stirring reaction is after 2 hours, add 30% hydrogen peroxide of 1kg deionized water and 30g to stir 10 hours, with membrane filtration, with deionized water cyclic washing filter cake, to neutral, air dry obtains graphite oxide;
Step (c): add the graphite oxide ene product of gained in 1g step (b) in reaction bulb in 20g water, with the ultrasonic processing of 50KHz 1 hour, obtain graphene oxide spinning solution colloidal sol;
Step (d): the graphene oxide spinning solution colloidal sol of getting gained in step (c), take the extruded velocity of 20 mL/h by diameter the spinning capillary as 100 μ m, in liquid nitrogen, solidify 1s postlyophilization 10h, obtain the ordered porous fiber of high strength graphene oxide;
Step (e): the ordered porous fiber of graphene oxide of gained in step (d) is placed in to acetic acid and hydrobromic mixed acid, is heated to 80 ℃ of reaction 10h, through washing the dry high-strength graphene ordered porous fibers that obtains reduction.
Through above step, the graphene oxide obtaining has good dissolubility in water, forms stable liquid crystal gel under high concentration.In liquid crystal gel, graphene oxide sheet is layer structure and arranges.The diameter of the ordered porous fiber of graphene oxide of gained is 100 microns, and density is 0.05g/cm
3, TENSILE STRENGTH is 5-8MPa, and compressive strength is 0.5-1MPa, and elongation at break is 5-10%.High-strength graphene ordered porous fibers, graphene film is arranged vertically and is piled into along fiber axially extending bore, and density is 0.03-0.04g/cm
3, TENSILE STRENGTH is 10-15MPa, and compressive strength is 2-4MPa, and the diameter of fiber is 80-100 micron, and elongation at break is 8-10%, conductance is greater than 1000S/m.
Above-described embodiment is used for the present invention that explains, rather than limits the invention, and in the protection domain of spirit of the present invention and claim, any modification and change that the present invention is made, all fall into protection scope of the present invention.
Claims (3)
1. a preparation method for the ordered porous fiber of Graphene, is characterized in that, comprises the following steps:
(1) graphite raw material of 1 weight portion, 1 ~ 100 weight portion sulfuric acid, 0.5 ~ 5 weight portion potassium peroxydisulfate and 0.5 ~ 5 weight portion phosphorus pentoxide are mixed, at 25 ~ 100 ℃, stirring reaction is 1 ~ 10 hour, after cool to room temperature, with deionized water, dilute, with filter membrane suction filtration, with deionized water washing, to neutral, air dry obtains intercalated graphite for 10 ~ 50 hours;
(2) intercalated graphite of gained in 1 weight portion step (1), 1 ~ 100 weight portion sulfuric acid and 0.5 ~ 10 weight portion potassium permanganate are mixed, at-10 ~ 50 ℃, stirring reaction is after 0.1 ~ 10 hour, add deionized water and 0.1 ~ 10 weight portion hydrogen peroxide of 10 ~ 2000 weight portions to stir 0.1 ~ 10 hour, with membrane filtration, with deionized water cyclic washing, to neutral, air dry obtains graphite oxide;
(3) graphite oxide of gained in 1 weight portion step (2) is dissolved in the water of 5 ~ 100 weight portions, with the ultrasonic processing of 50KHz 1 hour, obtains graphene oxide spinning solution colloidal sol;
(4) get the graphene oxide spinning solution colloidal sol of step (3) gained, extruded velocity with 1 ~ 100 mL/h, it by diameter, is the spinning capillary of 50 ~ 500 μ m, colloidal sol is clamp-oned and in liquid nitrogen, stopped 1 ~ 50s and condense, further freeze drying or critical freeze drying 2-40h, finally obtain ordered porous graphene oxide fiber again;
(5) the graphene oxide fiber of gained in step (4) is placed in to reductant and reduces 0.1 ~ 100h, washing is dry, obtain the ordered porous fiber of Graphene, one or more the mixing of described reductant in hydrazine hydrate, sodium borohydride, hydrobromic acid, hydroiodic acid, acetic acid forms.
2. the preparation method of the ordered porous fiber of Graphene according to claim 1, is characterized in that, in described step (1), described graphite is native graphite or pyrolytic graphite.
3. the preparation method of the ordered porous fiber of Graphene according to claim 1, is characterized in that, in described step (1) and step (2), described sulfuric acid is the sulfuric acid that mass concentration is greater than 80%.