CN102584119A - 一种钨晶地坪原料组合物 - Google Patents
一种钨晶地坪原料组合物 Download PDFInfo
- Publication number
- CN102584119A CN102584119A CN2012100073304A CN201210007330A CN102584119A CN 102584119 A CN102584119 A CN 102584119A CN 2012100073304 A CN2012100073304 A CN 2012100073304A CN 201210007330 A CN201210007330 A CN 201210007330A CN 102584119 A CN102584119 A CN 102584119A
- Authority
- CN
- China
- Prior art keywords
- terrace
- tungsten
- brilliant
- parts
- feedstock composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供了一种钨晶地坪原料组合物。该地坪原料组合物按重量份数计:钨合金骨料50~60份、水泥30~40份、色粉0.5~1.5份、减水剂3~5份、硅灰0.3~1份。其中钨合金骨料为冶炼钨过程中的废渣,废渣通过粉碎,可得到粒径级配的钨合金骨料;减水剂为聚羧酸盐减水剂;硅灰主要成分为玻璃态二氧化硅,颗粒粒径在800~1250目。该钨晶地坪原料组合物通过两次撒播施工,所形成的钨晶地坪厚度在5~8㎜,具有良好的耐磨性能和抗冲击性能。
Description
技术领域
本发明涉及一种地坪原料组合物,适用于各种新浇筑的混凝土地面。
技术背景
地坪主要用于工业厂房、停车场、商业卖场、物流仓库等地面,要求具有一定的强度、硬度和耐磨性,同时还要良好的防尘、防潮和防水性能。混凝土地面通常存在毛细孔,表面不致密,地面耐磨、抗冲击性能较差,在使用过程中地面易损坏、起灰。多数混凝土地面在使用一年左右就开始起尘,为了保护地面,多采用地面涂料涂刷受损地表面,然而地面涂料使用一段时间后,由于地面强度不高、耐磨系数低,易导致脱落,因而每年都要进行反复涂层,浪费了人力、物力和财力。为了改善地坪的使用性能,相继有人将金属氧化物骨料或金属骨料应用于水泥基地坪中,这些骨料主要有石英砂、金刚砂、钢纤维、金属合金、矿渣等,从而较大提高了地坪的耐磨性能和抗冲击性能。
发明内容
本发明是针对混凝土地面不耐磨,抗冲击性差、易起尘等不足,提出一种混凝土地面处理方法,目的在于提供一种施工方便、成本低,具有表面坚硬、耐磨抗压、不起尘和耐用的钨晶地坪。
本发明的有益效果是钨晶地坪可有效阻止混凝土地表面易受损起尘,与混凝土地面一起施工,工期短,无需另外施工砂浆找平层。
本发明所述的钨晶地坪原料组合物由钨合金骨料、水泥和其他助剂组成,按重量份数计,所述组分的组成如下:
钨合金骨料 50~60份
水泥 30~40份
色粉 0.5~1.5份
聚羧酸盐减水剂 3~5份
硅灰 0.3~1份
本发明的钨合金骨料为冶炼钨过程中的废渣,废渣含有钨、铁、锰等元素,这些金属元素在冶炼过程中与碳结合,形成了熔点高,硬度大的碳化物。该废渣通过粉碎,可得到粒径级配的钨合金骨料,应用于地坪中表现出良好的耐磨性能和抗冲击性能。本发明采用的减水剂为聚羧酸盐减水剂,具有良好的减水、增塑、保坍及较低的收缩性能,可提高混凝土的标号、缩短施工工期,改善混凝土的耐久性。组分中采用的硅灰颗粒粒径在800~1250目,其主要成分为玻璃态二氧化硅,掺入混凝土中,能进一步提高地坪的强度及抗冲耐磨性能。 由于硅灰可以充填到水泥颗粒中间的空隙中,能降低水化浆体中的孔隙尺寸,改善孔隙尺寸分布,使地坪强度提高,渗透性降低,使混凝土密实。同时硅灰的二次水化作用,新的生成物堵塞混凝土中渗透通道,可减少有危害物质对地坪的传递,较大程度地避免了可溶性的氢氧化钙和钙矾石的生成,抗渗能力强。本发明采用的色粉可采用地坪通用的无机颜料,着色均匀、稳定。
通过原料的复配所制得的钨晶地坪原料组合物为粉体状,开袋即可使用。该钨晶地坪原料组合物在即将初凝的混凝土表面上,通过泌水、一次撒播钨晶地坪原料组合物、打磨、二次撒播钨晶地坪原料组合物、打磨、抹光、涂抹养护剂等工序,即可得到与混凝土基础形成一个整体,具有高致密性的耐磨地面。
具体实施方式
实施例1:
本发明所述的钨晶地坪原料组合物由钨合金骨料、水泥和助剂组成,按重量份数计,所述组分组成如下:
钨合金骨料 52份
水泥 33份
色粉 1份
聚羧酸盐减水剂 3份
硅灰 0.8份
以上钨晶地坪原料组合物为粉体状,在即将初凝的混凝土表面上,通过泌水、一次撒播钨晶地坪组合物、打磨、二次撒播钨晶地坪原料组合物、打磨、抹光、涂抹养护剂等工序,即可得到高性能耐磨地面,厚度一般在5~8毫米,与混凝土形式一个整体,所形成的钨晶地坪莫氏硬度达到:8;耐磨性:(GBTl2988-91)磨坑长度21.1mm;抗压强度:(GB/l77-85)91.5N/mm。
实施例2:
本发明所述的钨晶地坪原料组合物由钨合金骨料、水泥和助剂组成,按重量份数计,所述组分组成如下:
钨合金骨料 58份
水泥 36份
色粉 1份
聚羧酸盐减水剂 4份
硅灰 1份
以上钨晶地坪原料组合物为粉体状,在即将初凝的混凝土表面上,通过泌水、一次撒播钨晶地坪组合物、打磨、二次撒播钨晶地坪原料组合物、打磨、抹光、涂抹养护剂等工序,即可得到高性能耐磨地面,厚度一般在5~8毫米,与混凝土形式一个整体,所形成的钨晶地坪莫氏硬度达到:9;耐磨性: (GBTl2988-91)磨坑长度20.3mm;抗压强度:(GB/l77-85)92.3N/mm。
Claims (3)
1. 一种钨晶地坪原料组合物,其特征在于钨晶地坪原料组合物按重量份数计:钨合金骨料 50~60份、水泥30~40份、色粉0.5~1.5份、减水剂3~5份、硅灰0.3~1份。
2.根据权利要求1所述的一种钨晶地坪原料组合物,其特征在于:
(1)所述的钨合金骨料为冶炼钨过程中的废渣,废渣通过粉碎,可得到粒径级配的钨合金骨料,应用于地坪中表现出良好的耐磨性能和抗冲击性能;
(2)所述的减水剂为聚羧酸盐减水剂;
(3)所述的硅灰颗粒粒径在800~1250目,主要成分为玻璃态二氧化硅,掺入混凝土中,能进一步提高地坪的强度及抗冲耐磨性能。
3.一种钨晶地坪原料组合物,其特征在于:所述的钨晶地坪原料组合物通过两次撒播,所形成的钨晶地坪厚度在5~8㎜。