CN102583350B - Preparation method of graphene material - Google Patents
Preparation method of graphene material Download PDFInfo
- Publication number
- CN102583350B CN102583350B CN2012100467880A CN201210046788A CN102583350B CN 102583350 B CN102583350 B CN 102583350B CN 2012100467880 A CN2012100467880 A CN 2012100467880A CN 201210046788 A CN201210046788 A CN 201210046788A CN 102583350 B CN102583350 B CN 102583350B
- Authority
- CN
- China
- Prior art keywords
- graphene
- graphite
- preparation
- gear
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a preparation method of a graphene material. The preparation method comprises the following steps of: dissolving powdered graphite into an organic solvent or water to form a suspension; placing the suspension in a container equipped with a gear group, wherein the gear operates at a low speed; taking out slurry for ultrasonic treatment, carrying out high-speed centrifuging so that graphite particles and graphite sheets which are not stripped and torn are precipitated at the bottom of a centrifuging tube through centrifugal action, and a solution on the upper layer comprises a single layer of graphene and multiple layers of graphene; and finally, concentrating and separating the solution on the upper layer to obtain the graphene powder or a stable graphene solution. According to the invention, continuous rotating and stirring of a graphite suspension are carried out by utilizing the gear group, the continuous meshing and tearing of the graphite sheet are carried out through gear teeth, thereby overcoming the disadvantages of multiple defects and low yield in a conventional mechanical method and preparing the graphene in high efficiency and high quality.
Description
Technical field
The present invention relates to a kind of preparation method of grapheme material, belong to the novel nano-material field.
Background technology
The Graphene of Two-dimensional Carbon atomic crystal has good electricity leads and thermal conductivity and other Their Exotic Properties, and how preparing quickly and efficiently the Graphene of better quality and can conveniently applying is the emphasis direction that people explore this new function material.
Initial Graphene is torn and is found to exist from graphite block body by adhesive tape, constantly extends a lot of preparation methods.Comprise mechanically peel method, thermal expansion graphite method, chemical Vapor deposition process etc.But the method that exists at present also has shortcoming separately.For example, the adhesive tape method of Tearing needs repeatedly just can prepare the Graphene of trace, and the Graphene of processing on adhesive tape is cumbersome; Ball milled is because the shock of ball can will be introduced more defect in the Graphene two-dimensional surface; The time that chemical method etc. need to be grown is prepared, and chemical method needs number of chemical reagent.
Gear uses usually used as a kind of gearing, and in rotation, motion-work wheel and driven wheel ceaselessly mesh, and ceaselessly has frictional tear between wheel tooth.The mechanical means of Graphene can be torn out two-dimentional atomic crystal layer exactly effectively., for above characteristics, gear can be rotated as a kind of method that effectively prepares high-quality Graphene.
Summary of the invention
The preparation method who the purpose of this invention is to provide a kind of grapheme material, the method, in conjunction with performance, the characteristics of Graphene, propose to utilize gear-driven engagement,, in conjunction with supersound process and high speed centrifugation, prepare Graphene.
The present invention adopts following technical scheme:
The preparation method of grapheme material is characterized in that comprising the following steps:
(1) powdered graphite is dissolved in organic solvent or water, forms suspension, then put into the container that gear unit is installed, gear, in low speed 1-800 rev/min rotation, rotates 0.5-30 hour, takes out slurry;
(2) step (1) slurry is carried out supersound process 0.5-2 hour, then high speed centrifugation, centrifugal rotational speed is at 1000-4000 rev/min, centrifugal more than 5 minutes, make the unstripped graphite granule of tearing and graphite flake be deposited in the centrifuge tube bottom by centrifugation, and upper solution is single-layer graphene and multi-layer graphene solution;
(3) upper solution after centrifugal in step (2) is concentrated, separating treatment, can obtain graphene powder or graphene solution.
The preparation method of described grapheme material is characterized in that: described Graphite Powder 99 is artificial synthetic graphite powder, natural graphite powder, high temperature pyrolysis Graphite Powder 99.
The preparation method of described grapheme material is characterized in that: described organic solvent is alcohol, acetone, dimethyl formamide, phenyl aldehyde.
The preparation method of described grapheme material is characterized in that: described gear unit is comprised of the gear of two or more quantity.
Beneficial effect of the present invention:
The present invention utilizes gear unit to gyrate and stirs simultaneously graphite suspension, by wheel tooth, ceaselessly meshes, and ceaselessly tears graphite flake, has overcome the conventional mechanical method and has introduced the shortcoming that defect is many, yield poorly, and can prepare efficiently, in high quality Graphene.
Description of drawings
Fig. 1 is gear unit schematic diagram used in the present invention.
Fig. 2 is the Graphene transmission electron microscope TEM photo that the present invention prepares.
Embodiment
Embodiment: Graphite Powder 99 and phenyl aldehyde are formed suspension according to the solubility of 2mg/ml, put into the container that gear unit is installed, gear rotational speed 50 right side of turning left, rotated 5 hours, takes out slurry, supersound process 0.5 hour, carry out high speed centrifugation, centrifugal rotational speed 4000 turns, 5 minutes, make the unstripped graphite granule of tearing and graphite flake be deposited in centrifuge tube or concentrator bowl bottom by centrifugation, and upper solution is single-layer graphene and multi-layer graphene solution.Graphene in the upper solution that obtains is carried out transmission electron microscope scanning, and Fig. 2 is the Graphene transmission electron microscope TEM photo of preparation.Fig. 1 is gear unit schematic diagram used in the present invention.
Claims (4)
1. the preparation method of a grapheme material is characterized in that comprising the following steps:
(1) powdered graphite is dissolved in organic solvent or water, forms suspension, then put into the container that gear unit is installed, gear, in low speed 1-800 rev/min rotation, rotates 0.5-30 hour, takes out slurry;
(2) step (1) slurry is carried out supersound process 0.5-2 hour, then high speed centrifugation, centrifugal rotational speed is at 1000-4000 rev/min, centrifugal more than 5 minutes, make the unstripped graphite granule of tearing and graphite flake be deposited in the centrifuge tube bottom by centrifugation, and upper solution is single-layer graphene and multi-layer graphene solution;
(3) upper solution after centrifugal in step (2) is concentrated, separating treatment, can obtain graphene powder or graphene solution.
2. the preparation method of grapheme material according to claim 1, it is characterized in that: described Graphite Powder 99 is artificial synthetic graphite powder, natural graphite powder, high temperature pyrolysis Graphite Powder 99.
3. the preparation method of grapheme material according to claim 1, it is characterized in that: described organic solvent is alcohol, acetone, dimethyl formamide, phenyl aldehyde.
4. the preparation method of grapheme material according to claim 1, it is characterized in that: described gear unit is comprised of the gear of two or more quantity.