CN102531708A - Special white glaze material for ceramic tile inkjet - Google Patents
Special white glaze material for ceramic tile inkjet Download PDFInfo
- Publication number
- CN102531708A CN102531708A CN2012100145961A CN201210014596A CN102531708A CN 102531708 A CN102531708 A CN 102531708A CN 2012100145961 A CN2012100145961 A CN 2012100145961A CN 201210014596 A CN201210014596 A CN 201210014596A CN 102531708 A CN102531708 A CN 102531708A
- Authority
- CN
- China
- Prior art keywords
- ceramic tile
- powder
- glaze
- ttkg
- special
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a special white glaze material for ceramic tile inkjet, which comprises the following raw materials in percentage by mass: 100 percent of TTKG-533 type brightening glaze material, 10 to 12 percent of zirconium silicate powder, 2 to 5 percent of kaolin powder, 3 to 7 percent of alumina powder and 12 to 17 percent of FKK-7005 clinker. A ceramic tile product prepared by using the special white glaze material for ceramic tile inkjet, which is provided by the invention, has excellent quality indexes such as glaze texture, gloss, hardness and the like. Different proportions of the zirconium silicate power and the alumina powder can be added according to different firing conditions so as to achieve the effects required by the products. The special white glaze material for ceramic tile inkjet is widely applied to floor tile products in the field of ceramic inkjet.
Description
Technical field
The present invention relates to the glaze technical field, be specifically related to the special-purpose white enamel
of a kind of ceramic tile ink-jet.
Background technology
The leading ink-jet printing apparatus of releasing in Europe has just been introduced the Chinese pottery manufacturing market, and at the ceramic glaze technological side, traditional employed one-tenth glaze can influence ceramic special-purpose ink in burning till color development later because of the difference of combined compsn in the prescription.
Summary of the invention
The present invention provides a kind of ceramic tile ink-jet special-purpose white enamel, can keep the ink one-tenth glaze glaze of color development the most by force, can make product glazing process operation through standard on production line make product present best color development effect.
The object of the invention is realized through following technical scheme:
The special-purpose white enamel of a kind of ceramic tile ink-jet comprises that the TTKG-533 type increases gorgeous glaze, also comprises zirconium silicate powder, kaolin powder, aluminum oxide powder or FKK-7005 frit.
Preferably, described white enamel comprises that the TTKG-533 type increases gorgeous glaze and zirconium silicate powder, and the mass percent of its component is:
The TTKG-533 type increases gorgeous glaze 100%
Zirconium silicate powder 10-15%.
Preferably, described white enamel comprises that the TTKG-533 type increases gorgeous glaze, zirconium silicate powder, kaolin powder and aluminum oxide powder, and the mass percent of its component is:
The TTKG-533 type increases gorgeous glaze 100%
Zirconium silicate powder 10-15%
Kaolin powder 2-5%
Aluminum oxide powder 3-7%.
Preferably, said white enamel comprises that the TTKG-533 type increases gorgeous glaze and FKK-7005 frit, and the mass percent of its component is:
The TTKG-533 type increases gorgeous glaze 100%
FKK-7005 frit 12-17%.
Preferably, described TTKG-533 increases the special mixed mineral powder that gorgeous glaze is a 150-300 order particle diameter.
Compared with prior art, the advantage of technical scheme of the present invention is:
Increasing gorgeous glaze with the TTKG-533 type of being processed by the mixed mineral powder of 150-300 order particle diameter is main ingredient, and adds following raw material and adjust the needed effect of ceramic tile, and brief introduction is following:
1. high purity silicic acid zirconium powder has the opacity of height; Can adjust ceramic tile surface whiteness 2. aluminum oxide powders and have higher refractory temperature; Can adjust ceramic tile surface gloss 3. kaolin powders and have plasticity-preferably, 4. FKK-7005 frits take place with the minimizing defective and have transparency preferably in the physicals when being used to adjust glazing, can adjust the special-purpose white enamel of sharpness ceramic tile ink-jet of the present invention of ceramic tile surface gloss and color; Can make the value of tile product be able to promote; And because the ink colour developing has directly reduced the usage quantity of ink deeply, cost is minimized, and quality is able to promote; Environmental issue is able to the high-quality development, makes also that simultaneously the tile product competitive power internationally of China improves again.
And the raw material through experiment showed, above-mentioned interpolation is very good for the color development of ceramic ink, and combines the special volumetric expansion data of raw material, different firing conditions is carried out the interpolation of different ratios and uses.
Embodiment
Following enforcement example can make the technician of this specialty more comprehensively understand the present invention, but does not limit the present invention in any way.
Embodiment 1
When the firing temperature of once-firing ceramic tile was the 1190-1220 ℃ of left and right sides, the special-purpose white enamel of a kind of ceramic tile ink-jet of the present invention was counted by weight percentage, and contains following moity: TTKG-533 100%
Zirconium silicate powder 12%
Kaolin powder 3%
Aluminum oxide powder 5%
Embodiment 2
When the firing temperature of once-firing ceramic tile was the 1175-1200 ℃ of left and right sides, the special-purpose white enamel of another kind of ceramic tile ink-jet of the present invention was counted by weight percentage, and contains following moity: TTKG-533 100%
Zirconium silicate powder 12%
Embodiment 3
When the firing temperature of once-firing ceramic tile is about 1175-1200 ℃, and ceramic tile is when being dark glossy surface
The special-purpose white enamel of another ceramic tile ink-jet of the present invention is counted by weight percentage, and contains following moity: TTKG-533 100%
FKK-7005 15%
Saidly increasing the special mixed mineral powder that gorgeous glaze TTKG-533 is a 150-300 order particle diameter, is the one-tenth glaze glaze of good mixing fully.
The foregoing description just is to let the one of ordinary skilled in the art can understand content of the present invention and enforcement according to this in order technical conceive of the present invention and characteristics to be described, to be its objective is, can not limit protection scope of the present invention with this.The variation or the modification of every equivalence that the essence of content has been done according to the present invention all should be encompassed in protection scope of the present invention.
Claims (5)
1. the special-purpose white enamel of ceramic tile ink-jet is characterized in that, comprises that the TTKG-533 type increases gorgeous glaze, also comprises zirconium silicate powder, kaolin powder, aluminum oxide powder or FKK-7005 frit.
2. the special-purpose white enamel of ceramic tile ink-jet according to claim 1 is characterized in that described white enamel comprises that the TTKG-533 type increases gorgeous glaze and zirconium silicate powder, and the mass percent of its component is:
The TTKG-533 type increases gorgeous glaze 100%
Zirconium silicate powder 10-15%.
3. the special-purpose white enamel of ceramic tile ink-jet according to claim 1 is characterized in that described white enamel comprises that the TTKG-533 type increases gorgeous glaze, zirconium silicate powder, kaolin powder and aluminum oxide powder, and the mass percent of its component is:
The TTKG-533 type increases gorgeous glaze 100%
Zirconium silicate powder 10-15%
Kaolin powder 2-5%
Aluminum oxide powder 3-7%.
4. according to the special-purpose white enamel of the described ceramic tile ink-jet of claim 1, it is characterized in that described white enamel comprises that the TTKG-533 type increases gorgeous glaze and FKK-7005 frit, the mass percent of its component is:
The TTKG-533 type increases gorgeous glaze 100%
FKK-7005 frit 12-17%.
5. according to the special-purpose white enamel of any described ceramic tile ink-jet in the claim 1 to 4, it is characterized in that described TTKG-533 increases the mixed mineral powder that gorgeous glaze is a 150-300 order particle diameter.