CN102531203A - Corrosion inhibitor for boiler acid washing and production method thereof - Google Patents
Corrosion inhibitor for boiler acid washing and production method thereof Download PDFInfo
- Publication number
- CN102531203A CN102531203A CN201210024719XA CN201210024719A CN102531203A CN 102531203 A CN102531203 A CN 102531203A CN 201210024719X A CN201210024719X A CN 201210024719XA CN 201210024719 A CN201210024719 A CN 201210024719A CN 102531203 A CN102531203 A CN 102531203A
- Authority
- CN
- China
- Prior art keywords
- water
- boiler
- inhibiter
- corrosion inhibitor
- acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a corrosion inhibitor for boiler acid washing and a production method thereof, wherein the corrosion inhibitor for boiler acid washing consists of the following components according to mass percent: 3-6% of citric acid, 5-10% of N, N-double-phosphine acyl methyl aspartic acid, 0.5-1.5% of dodecyl betaine, 0.1-0.3% of thiourea, 0.5-2.5% of methylene phosphonic acid, 0.5-2.5% of 2-phosphonate-1, 2, 4-tricarboxylic acid butane, 0.5-1.5% of tdlyltriazole, 0.5-1.5% of N-alkylamino-2-perfluoroalkyl imidazoline quaternary ammonium salt, 0.5-1.5% of sodium alginate, 1-3% of sodium chromate, 0.5-1.5% of zinc chloride and the balance of water. The corrosion inhibitor for boiler acid washing has a good corrosion inhibition effect and good applicability, the static corrosion speed is lower than 0.2g/m<2> h, a test block is bright after the cleaning, harmful film is not left, and the dirty dissolving capability is strong.
Description
Technical field
The present invention relates to a kind of inhibiter and preparation method thereof, relate in particular to a kind of boiler acid pickling with inhibiter and preparation method thereof.
Background technology
Human development and progress is to be the basis with natural resources and human environment of depending on for existence.China's Freshwater resources rich occupies the 5th in the world.But per capita resources occupies the 18 in the world.Therefore water resources is not rich.Along with China's Increase of population and rapid economy development, limited water resource is shortage more.The water resource pollution of China also is very serious.See that from national situation urban water shortage is serious at present, has caused serious economy loss and social environment problem.The lack of water city distributes and is spread to the whole nation gradually by North China, northeast, the Northwest and the coastal eastern region of concentrating at present.
Therefore water saving, administer sewage and develop the effect that new water source has no less important.The most important thing is process water in the town water.The consumption of water coolant ranks first in the process water.Therefore practicing thrift water coolant becomes primary target.The main method of practicing thrift water coolant is to take recirculated cooling water and improve cycles of concentration.But the harmful ion composition behind the employing recirculated cooling water in the water increases, and from cooling tower, brings a large amount of dissolved oxygens, dust and bacterium again into, and water quality is degenerated, so that brings problems such as burn into fouling, bacterium algae and foundry loam to cooling water system.Greatly developing Water Treatment Chemicals plays an important role to water saving, improvement sewage.Water conditioner be in process water, domestic water, the wastewater treatment process the chemical agent that must use.Use through these chemical agents makes water reach the certain quality requirement.The main effect of water conditioner is the formation of control incrustation scale, mud, reduces foam, reduces the corrosion of the material that contact with water, removes suspended solids and toxic substance in anhydrating, and deodorization and discoloration softens and stabilizing water quality etc.Therefore, water conditioner can be divided into four types of main medicaments.Be inhibiter, Scale inhibitors, sterilant and flocculation agent.China's water conditioner just draws attention after introducing the large chemical fertilizer device seventies and progressively grows up.After this developed a series of water conditioner.
In recent years, boiler acid pickling use inhibiter is a kind of special corrosion agent of being badly in need of in the present boiler matting.Yet existing boiler acid pickling is stable inadequately with the inhibiter performance, and the quality guaranteed period is short, and has than the strong and stimulating smell.
Summary of the invention
In order to solve the above-mentioned deficiency that prior art exists, one of technical problem to be solved by this invention provides a kind of boiler acid pickling and uses inhibiter.
Two of technical problem to be solved by this invention provides the preparation method of above-mentioned boiler acid pickling with inhibiter.
Technical scheme of the present invention is achieved in that
A kind of boiler acid pickling is used inhibiter, is made up of by mass percentage following component:
Hydrocerol A 3-6%;
N, the two (phosphonomethyl) aspartic acid 5-10% of N-;
Empgen BB 0.5-1.5%;
Thiocarbamide 0.1-0.3%;
Diethylene triamine pentamethylene phosphonic 0.5-2.5%;
2-phosphonate group-1,2,4-butane tricarboxylate 0.5-2.5%;
TTA 0.5-1.5%;
N-alkylamino-2-perfluoroalkyl imidazoline quaternary ammonium salt 0.5-1.5%;
Sodium alginate 0.5-1.5%;
Sodium chromate-51Cr 1-3%;
Zinc chloride 0.5-1.5%;
Surplus is a water.
The present invention also provides the preparation method of above-mentioned boiler acid pickling with inhibiter; Heat water to 40-60 ℃, empgen BB is dissolved in the water, again with thiocarbamide, diethylene triamine pentamethylene phosphonic, 2-phosphonate group-1; 2; 4-butane tricarboxylate, TTA, N-alkylamino-2-perfluoroalkyl imidazoline quaternary ammonium salt, sodium alginate, Sodium chromate-51Cr and zinc chloride add stirring, add Hydrocerol A and N at last, the two (phosphonomethyl) aspartic acids of N-; Mix, can make boiler acid pickling of the present invention and use inhibiter.
Boiler acid pickling of the present invention is with the method for use of inhibiter, can for:
Connect the boiler cleaning system, the debugging feedwater is depressed into boiler water filling to the drum low-water level that meets the requirements, and isolates and the cleaning system without interaction, is warming up to about 80 ℃, adds boiler acid pickling of the present invention and uses inhibiter, keeps circulating under this temperature, and the time was controlled at 2-4 hour.
With respect to prior art, beneficial effect of the present invention is embodied as:
(1) the used most polymer raw materials of the present invention are the biodegradable product, belong to environmental friendly product, and chemical property is stable, toxicity is low.
(2) corrosion mitigating effect and suitability are good, add can play corrosion inhibition on a small quantity, and static corrosion speed is lower than 0.2 gram/rice
2Hour, can't produce the needle-like spot corrosion or enlarge and deepen primary corrosion spot; Clean back test piece light, the residual harmful film does not have obvious copper facing phenomenon; It is strong to dissolve dirty ability, can in 85 ℃, not decompose fast, go bad anti-long-term storage; Waste liquid is ordorless, and toxicity is low, allow compliance with emission standards.
(3) be suitable for steel and comprise common boiler steel, soft steel, steel alloy, drum steel such as 20A, 20g, SA299, BHW35, BHW38 etc. also are suitable for the pickling of red copper in hydrochloric acid and Hydrocerol A simultaneously.
Embodiment
Embodiment 1
Raw material is prepared:
Take by weighing 100 kilograms of raw materials, wherein:
3 kilograms of Hydrocerol As;
N, 10 kilograms of the two (phosphonomethyl) aspartic acids of N-;
0.5 kilogram of empgen BB;
0.3 kilogram of thiocarbamide;
0.5 kilogram of diethylene triamine pentamethylene phosphonic;
2-phosphonate group-1,2,2.5 kilograms of 4-butane tricarboxylates;
0.5 kilogram of TTA;
1.5 kilograms of N-alkylaminos-2-perfluoroalkyl imidazoline quaternary ammonium salt;
0.5 kilogram of sodium alginate;
3 kilograms of Sodium chromate-51Crs;
0.5 kilogram of zinc chloride.
Surplus is a water.
Be water and dialkyl group trimethyl-glycine, thiocarbamide, diethylene triamine pentamethylene phosphonic, 2-phosphonate group-1; 2; 4-butane tricarboxylate, TTA, N-alkylamino-2-perfluoroalkyl imidazoline quaternary ammonium salt, sodium alginate, Sodium chromate-51Cr, zinc chloride, Hydrocerol A and N, the gross weight of the two (phosphonomethyl) aspartic acids of N-is 100 kilograms.
Heat water to 40-60 ℃, empgen BB is dissolved in the water, again with thiocarbamide, diethylene triamine pentamethylene phosphonic, 2-phosphonate group-1; 2; 4-butane tricarboxylate, TTA, N-alkylamino-2-perfluoroalkyl imidazoline quaternary ammonium salt, sodium alginate, Sodium chromate-51Cr and zinc chloride add stirring, add Hydrocerol A and N at last, the two (phosphonomethyl) aspartic acids of N-; Mix, can make boiler acid pickling of the present invention and use inhibiter.
Boiler acid pickling of the present invention is with the method for use of inhibiter, can for:
Connect the boiler cleaning system, the debugging feedwater is depressed into boiler water filling to the drum low-water level that meets the requirements, and isolates and the cleaning system without interaction, is warming up to about 80 ℃, adds boiler acid pickling of the present invention and uses inhibiter, keeps circulating under this temperature, and the time was controlled at 2-4 hour.
Through test, static corrosion speed 0.18 gram/rice in the boiler steel
2Hour, can't produce the needle-like spot corrosion or enlarge and deepen primary corrosion spot; Clean back test piece light, the residual harmful film does not have obvious copper facing phenomenon; It is strong to dissolve dirty ability, can in 85 ℃, not decompose fast, go bad anti-long-term storage; Waste liquid is ordorless, and toxicity is low, allow compliance with emission standards.
Carried out the static-state scale inhibition test according to State Standard of the People's Republic of China GB/T16632-2008 " the mensuration tosca method of water treatment scale performance ".
Test result: static-state scale inhibition test resistance lime carbonate rate 96.5%.
Embodiment 2
Raw material is prepared:
Take by weighing 100 kilograms of raw materials, wherein:
6 kilograms of Hydrocerol As;
N, 5 kilograms of the two (phosphonomethyl) aspartic acids of N-;
1.5 kilograms of empgen BBs;
0.1 kilogram of thiocarbamide;
2.5 kilograms of diethylene triamine pentamethylene phosphonics;
2-phosphonate group-1,2,0.5 kilogram of 4-butane tricarboxylate;
1.5 kilograms of TTAs;
0.5 kilogram of N-alkylamino-2-perfluoroalkyl imidazoline quaternary ammonium salt;
1.5 kilograms of sodium alginates;
1 kilogram of Sodium chromate-51Cr;
1.5 kilograms of zinc chloride.
Surplus is a water.
Be water and dialkyl group trimethyl-glycine, thiocarbamide, diethylene triamine pentamethylene phosphonic, 2-phosphonate group-1; 2; 4-butane tricarboxylate, TTA, N-alkylamino-2-perfluoroalkyl imidazoline quaternary ammonium salt, sodium alginate, Sodium chromate-51Cr, zinc chloride, Hydrocerol A and N, the gross weight of the two (phosphonomethyl) aspartic acids of N-is 100 kilograms.
Heat water to 40-60 ℃, empgen BB is dissolved in the water, again with thiocarbamide, diethylene triamine pentamethylene phosphonic, 2-phosphonate group-1; 2; 4-butane tricarboxylate, TTA, N-alkylamino-2-perfluoroalkyl imidazoline quaternary ammonium salt, sodium alginate, Sodium chromate-51Cr and zinc chloride add stirring, add Hydrocerol A and N at last, the two (phosphonomethyl) aspartic acids of N-; Mix, can make boiler acid pickling of the present invention and use inhibiter.
Obviously, directly above-mentioned each raw material simply stirring is mixed, also can make boiler acid pickling of the present invention and use inhibiter.
Boiler acid pickling of the present invention is with the method for use of inhibiter, can for:
Connect the boiler cleaning system, the debugging feedwater is depressed into boiler water filling to the drum low-water level that meets the requirements, and isolates and the cleaning system without interaction, is warming up to about 80 ℃, adds boiler acid pickling of the present invention and uses inhibiter, keeps circulating under this temperature, and the time was controlled at 2-4 hour.
Through test, static corrosion speed 0.16 gram/rice in the BHW35 drum steel
2Hour, can't produce the needle-like spot corrosion or enlarge and deepen primary corrosion spot; Clean back test piece light, the residual harmful film does not have obvious copper facing phenomenon; It is strong to dissolve dirty ability, can in 85 ℃, not decompose fast, go bad anti-long-term storage; Waste liquid is ordorless, and toxicity is low, allow compliance with emission standards.
Carried out the static-state scale inhibition test according to State Standard of the People's Republic of China GB/T16632-2008 " the mensuration tosca method of water treatment scale performance ".
Test result: static-state scale inhibition test resistance lime carbonate rate 97.2%.
Claims (2)
1. a boiler acid pickling is used inhibiter, it is characterized in that, is made up of by mass percentage following component:
Hydrocerol A 3-6%;
N, the two (phosphonomethyl) aspartic acid 5-10% of N-;
Empgen BB 0.5-1.5%;
Thiocarbamide 0.1-0.3%;
Diethylene triamine pentamethylene phosphonic 0.5-2.5%;
2-phosphonate group-1,2,4-butane tricarboxylate 0.5-2.5%;
TTA 0.5-1.5%;
N-alkylamino-2-perfluoroalkyl imidazoline quaternary ammonium salt 0.5-1.5%;
Sodium alginate 0.5-1.5%;
Sodium chromate-51Cr 1-3%;
Zinc chloride 0.5-1.5%;
Surplus is a water.
2. eco-friendly boiler acid pickling as claimed in claim 1 is characterized in that with the preparation method of inhibiter:
Heat water to 40-60 ℃, empgen BB is dissolved in the water, again with thiocarbamide, diethylene triamine pentamethylene phosphonic, 2-phosphonate group-1; 2; 4-butane tricarboxylate, TTA, N-alkylamino-2-perfluoroalkyl imidazoline quaternary ammonium salt, sodium alginate, Sodium chromate-51Cr and zinc chloride add stirring, add Hydrocerol A and N at last, the two (phosphonomethyl) aspartic acids of N-; Mix, can make boiler acid pickling of the present invention and use inhibiter.