CN102520477A - 耐高温150℃紧包光纤及其制备工艺 - Google Patents
耐高温150℃紧包光纤及其制备工艺 Download PDFInfo
- Publication number
- CN102520477A CN102520477A CN2012100033646A CN201210003364A CN102520477A CN 102520477 A CN102520477 A CN 102520477A CN 2012100033646 A CN2012100033646 A CN 2012100033646A CN 201210003364 A CN201210003364 A CN 201210003364A CN 102520477 A CN102520477 A CN 102520477A
- Authority
- CN
- China
- Prior art keywords
- high temperature
- hard
- pressed bale
- etfe
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明是耐高温150℃紧包光纤及其制备工艺,其特征是纤芯的外围是采用紫外固化丙烯酸酯涂覆的涂覆层;涂覆层的外围是采用乙烯四氟乙烯共聚物的紧包外层;其制备工艺,光纤纤芯分单模和多模,单模结构9/125μm,多模结构50/125μm或62.5/125μm;涂覆层采用紫外固化丙烯酸酯涂覆,涂覆层外径为250μm;紧包层是采用高温挤塑机单层、双层薄壁挤出高温乙烯四氟乙烯共聚物ETFE,优点:耐高低温-65℃~+150℃,紧包内层、紧包外层耐高温150℃。高强度、耐弯曲、抗冲击、耐老化、长寿命、耐腐蚀、阻燃等特性,可在恶劣的环境下提供高可靠服务,适用于航空航天、电子、机载特殊环境条件下的高速信号传输。
Description
技术领域
本发明涉及的是耐高温150℃紧包光纤及其制备工艺,产品具有耐高低温-65℃~+150℃、高强度、耐弯曲、抗冲击、耐老化、长寿命、耐腐蚀、阻燃等特性,可在恶劣的环境下提供高可靠服务,适用于航空航天、电子、机载特殊环境条件下的高速信号传输。
背景技术
目前,常见的民用光纤领域,国内生产的厂家已经很多,技术水平也很成熟。但在军用领域光纤的应用还处在初期发展阶段。主要原因是军用光纤要求较高,不但要求良好的环境和力学性能,如耐高低温、高强度、抗冲击、耐弯曲、长寿命等特殊要求。所以,军用光纤、光缆选用的材料和制造工艺与常规民品有很大区别。耐高温150℃紧包光纤正是考虑军品的应用要求,充分考虑其适用性和安全性,充分考虑高低温、高强度、耐弯曲、抗冲击、耐老化、长寿命、耐腐蚀、阻燃等特殊使用环境要求。
发明内容
本发明提出的是一种耐高温150℃紧包光纤及其制备工艺,其目的旨在克服现有技术所存在的上述缺陷,具有耐高、低温,高强度、高阻燃,光学性能稳定等特点。
本发明的技术解决方案:其特征是纤芯的外围是采用紫外固化丙烯酸酯涂覆的涂覆层;涂覆层的外围是采用乙烯四氟乙烯共聚物ETFE的紧包外层;其制备工艺,光纤纤芯分单模和多模,单模结构9/125μm,多模结构50/125μm或62.5/125μm;涂覆层采用紫外固化丙烯酸酯涂覆,涂覆层外径为250μm;紧包外层是采用高温挤塑机单层薄壁挤出的高温乙烯四氟乙烯共聚物ETFE,用紫外固化丙烯酸酯涂覆的涂覆层耐温等级是-65℃~+150℃;采用高温挤塑机单层薄壁挤出的高温乙烯四氟乙烯共聚物ETFE的紧包外层耐高温150℃。
本发明的优点:1)耐高温:涂覆层采用特殊紫外固化丙烯酸酯涂覆,紧包护层采用乙烯四氟乙烯共聚物ETFE,长期最高工作温度能达到+150℃。2)耐低温:涂覆层采用特殊紫外固化丙烯酸酯涂覆,紧包护层采用乙烯四氟乙烯共聚物ETFE,使紧包光纤可以在―65℃下正常敷设安装,可以解决一般材料由于低温敷设易造成硬化、脆裂等问题,从而满足低温环境的使用要求。3)高强度:紧包护层采用乙烯四氟乙烯共聚物ETFE,提高了紧包光纤的机械性能,跟常温普通紧包光纤相比抗拉力大大提高。
4)高阻燃、耐老化、长寿命、耐腐蚀:采用乙烯四氟乙烯共聚物ETFE紧包护层,此种材料具有很高的阻燃性能、耐老化、长寿命和耐腐蚀性能。
5)稳定性:采用乙烯四氟乙烯共聚物ETFE紧包护层,与纤芯有较好的附着力,结构圆整稳定,光学性能稳定。
附图说明
附图1是ф600μm紧包光纤结构示意图。
附图2是ф900μm紧包光纤结构示意图。
图中的1是纤芯;2是涂覆层;3是紧包内层;4是紧包外层。
具体实施方式
对照附图1,其特征是纤芯1的外围是采用紫外固化丙烯酸酯涂覆的涂覆层2;涂覆层2的外围是采用乙烯四氟乙烯共聚物ETFE的紧包外层4;
其制备工艺,光纤纤芯分单模和多模,典型的规格有:单模结构9/125μm,多模结构50/125μm或62.5/125μm;涂覆层采用紫外固化丙烯酸酯涂覆,涂覆层外径为250μm;紧包外层4是采用高温挤塑机单层薄壁挤出的高温乙烯四氟乙烯共聚物ETFE。用特殊紫外固化丙烯酸酯涂覆的涂覆层2耐温等级是-65℃~+150℃;采用高温挤塑机单层薄壁挤出的高温乙烯四氟乙烯共聚物ETFE的紧包外层4耐高温150℃。
对照附图2,其特征是纤芯1的外围是采用紫外固化丙烯酸酯涂覆的涂覆层2;涂覆层2的外围是采用乙烯四氟乙烯共聚物ETFE的紧包内层3;紧包内层3的外围是采用乙烯四氟乙烯共聚物ETFE的紧包外层4;
其制备工艺,光纤纤芯分单模和多模,典型的规格有:单模结构9/125μm,多模结构50/125μm或62.5/125μm;涂覆层采用紫外固化丙烯酸酯涂覆,涂覆层外径为250μm;紧包内层、紧包外层是采用高温挤塑机双层薄壁挤出的高温乙烯四氟乙烯共聚物ETFE。用特殊紫外固化丙烯酸酯涂覆的涂覆层2耐温等级是-65℃~+150℃;采用高温挤塑机双层薄壁挤出的高温乙烯四氟乙烯共聚物ETFE的紧包内层、紧包外层耐高温150℃。
光纤线芯涂覆层采用特殊紫外固化丙烯酸酯涂覆,比普通光纤线芯提高了耐热性能,耐温达到150℃;紧包护层采用乙烯四氟乙烯共聚物ETFE,采用单层薄壁挤出和双层薄壁挤出两种结构,提高了紧包光纤的耐高低温性能-65℃~+150℃,采用乙烯四氟乙烯共聚物ETFE护层,机械性能和耐环境性能也大大提高。
用涂覆设备涂覆特殊紫外固化丙烯酸酯。用高温光纤挤出机设备制造紧包内层。用高温光纤挤出机设备制造紧包外层。
Claims (2)
1.耐高温150℃紧包光纤,其特征是纤芯的外围是采用紫外固化丙烯酸酯涂覆的涂覆层;涂覆层的外围是采用乙烯四氟乙烯共聚物(ETFE)的紧包外层;其制备工艺,光纤纤芯分单模和多模,单模结构9/125μm,多模结构50/125μm或62.5/125μm;涂覆层采用紫外固化丙烯酸酯涂覆,涂覆层外径为250μm;紧包外层是采用高温挤塑机单层薄壁挤出的高温乙烯四氟乙烯共聚物(ETFE),用紫外固化丙烯酸酯涂覆的涂覆层耐温等级是-65℃~+150℃;采用高温挤塑机单层薄壁挤出的高温乙烯四氟乙烯共聚物(ETFE)的紧包外层耐高温150℃。
2.根据权利要求1所述的耐高温150℃紧包光纤,其特征是采用紫外固化丙烯酸酯涂覆的涂覆层的外围是采用乙烯四氟乙烯共聚物(ETFE)的紧包内层;紧包内层的外围是采用乙烯四氟乙烯共聚物(ETFE)的紧包外层;紧包内层、紧包外层是采用高温挤塑机双层薄壁挤出的高温乙烯四氟乙烯共聚物(ETFE),采用高温挤塑机双层薄壁挤出的高温乙烯四氟乙烯共聚物(ETFE)的紧包内层、紧包外层耐高温150℃。