CN102516905A - Adhesive for batteries and preparation method for adhesive - Google Patents
Adhesive for batteries and preparation method for adhesive Download PDFInfo
- Publication number
- CN102516905A CN102516905A CN201110386395XA CN201110386395A CN102516905A CN 102516905 A CN102516905 A CN 102516905A CN 201110386395X A CN201110386395X A CN 201110386395XA CN 201110386395 A CN201110386395 A CN 201110386395A CN 102516905 A CN102516905 A CN 102516905A
- Authority
- CN
- China
- Prior art keywords
- agent
- group
- sticks
- glue
- battery according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an adhesive for batteries. The adhesive is prepared from the following materials in percentage by weight: 84 to 95 percent of acrylic ester, 4 to 15 percent of acrylic monomer, 0.1 to 5 percent of water absorbent and 10 to 50 percent of chain initiator. A preparation method for the adhesive for the batteries comprises the following steps of: adding 84 to 95 percent of acrylic ester, 4 to 15 percent of acrylic monomer and 10 to 50 percent of chain initiator into a container, and mixing; heating to the temperature of between 75 and 85 DEG C, continuously stirring in the container, reacting for 4.5 to 5.5 hours, then dripping 40 to 180 grams of 1,6-ethylene glycol diacrylate, and continuously stirring for 1.5 to 2.5 hours; stopping heating, continuously stirring and cooling to room temperature; and finally, adding 0.1 to 5 percent of water absorbent, stirring uniformly, and thus obtaining an adhesive sticker. Compared with similar products in the prior art, the adhesive has the advantages of absorbing water and preventing moisture from entering the batteries.
Description
Technical field
The present invention relates to a kind of battery and stick with glue agent and preparation method thereof.
Background technology
At present, the kernel of lithium cell and nickel metal hydride battery generally is metal (lithium or a ni-mh etc.), and metal electrode that MOX is processed and relevant ionogen are formed, and are used to protect this metal electrode at battery kernel external parcel one deck plastic housing.A large amount of tackiness agent that use bond fixing in the processing cell process.General tackiness agent may be used to lithium cell and nickel metal hydride battery.But the battery of prior art sticks with glue the function that agent does not possess the water entering inside battery that prevents trace in the environment; Then As time goes on; The steam of trace can constantly get into inside battery through the junction of lithium cell and nickel-hydrogen battery outer shell in the environment, and especially at the southern area of humidity, the water that gets into inside battery is more; The water that gets in the battery can cause great damage to battery material, thereby causes shorten the work-ing life of battery.U.S. Patent application US6680148 and one Chinese patent application CN00117141.0 all disclose and have been applied to lithium ion cell electrode agglutinating tackiness agent, but do not have suction and prevent that moisture from getting into the inside battery function.Therefore the battery of prior art sticks with glue agent and does not have suction and prevent that moisture from getting into the inside battery function.
Summary of the invention
The present invention is to provide a kind of and have suction and prevent that the battery of moisture entering inside battery function from sticking with glue agent for solving above technical problem.
For realizing the object of the invention, the used technical scheme of the present invention is: provide a kind of battery to stick with glue agent, it is processed by the material of following components in weight percent:
Propenoate 84%~95%, Acrylic Acid Monomer 4%~15%, water-retaining agent 0.1%~5%, chain initiator 1 ‰~5 ‰.
Described propenoate is Isooctyl acrylate monomer, methyl acrylate, Bing Xisuandingzhi or NSC 20949.
Described water-retaining agent is acetal or ketal.
The structural formula of described acetal or ketal is:
R
1, R
2Group be Wasserstoffatoms, methyl, ethyl, propyl group, butyl or different in group; R
3, R
4Group is methyl, ethyl, propyl group, sec.-propyl or butyl group; R
5Be methylene group.
Compared with prior art; The present invention is owing to added water-retaining agent, and the water-retaining agent of utilization can absorb quantitative moisture, and willing characteristics; Acetal or ketal and the trace or and the trace the reacted product of water be corresponding alcohol, aldehydes or ketones; And alcohol, the aldehydes or ketones of the trace that generates can be used as organism is dissolved in becomes tackiness agent in the tackiness agent a part, thereby have increased the bounding force of tackiness agent, and can people, mobile phone and notebook computer and environment not caused damage; Can effectively stop the steam of trace in the environment to get into inside battery from the battery case junction, thereby can greatly prolong the work-ing life of the battery of mobile phone or notebook computer.
The present invention will solve another technical problem: provide the simple battery of a kind of ME to stick with glue the preparation method of agent, it may further comprise the steps:
At first in container, add propenoate 84%~95%, Acrylic Acid Monomer 4%~15% and chain initiator 1 ‰~5 ‰, and mix; Postheating to 75~85 ℃, and, drip 1 of 40~180g behind reaction 4.5~5.5h to constantly stirring in the container, the 6-glycol diacrylate continues to stir 1.5~2.5h; Then stop heating, continue stirring and be cooled to room temperature; Add water-retaining agent 0.1%~5% at last, stir, process non-setting adhesive and get final product.
Described propenoate is Isooctyl acrylate monomer, methyl acrylate, Bing Xisuandingzhi or NSC 20949.
Described water-retaining agent is acetal or ketal.
The structural formula of described acetal or ketal is:
R
1, R
2Group is for being Wasserstoffatoms, methyl, ethyl, propyl group, butyl or isopropyl group; R
3, R
4Group is methyl, ethyl, propyl group, sec.-propyl or butyl group; R
5Be methylene group.
Compared with prior art, the present invention does not have special devices owing to do not have special preparation condition in the whole process yet, and preparation technology is simpler, and efficient is higher; Simultaneously in the preparation process, dripped 1; The 6-glycol diacrylate as water-retaining agent and water catalyst for reaction, and just adds water-retaining agent after being cooled to room temperature; So water-retaining agent can not lose efficacy because of the water that polyreaction produces in advance; Guarantee product when bonding battery, the water-retaining agent in the product still can absorb moisture, thereby guarantees the stability in use of product.
Embodiment
Below in conjunction with the explanation of practical implementation instance, but the invention is not restricted to following practical implementation instance.
Embodiment 1
A kind of battery sticks with glue the preparation method of agent, and it may further comprise the steps:
At first in container, add propenoate 84% (this example is a methyl acrylate), Acrylic Acid Monomer 12% and chain initiator 1 ‰ (this example is two azo isobutyl cyanogen), and mix; Postheating to 75 ℃, and, drip 1 of 40g behind the reaction 5.5h to constantly stirring in the container, the 6-glycol diacrylate continues to stir 2.5h; Then stop heating, continue stirring and be cooled to room temperature; Add water-retaining agent 4% (this example is the methylal dimethanol) at last, stir, process non-setting adhesive and get final product.
Embodiment 2
A kind of battery sticks with glue the preparation method of agent, and it may further comprise the steps:
At first in container, add propenoate 89% (this example is an Isooctyl acrylate monomer), Acrylic Acid Monomer 9% and chain initiator 3 ‰ (this example is 2,2-dimethoxy-2 phenyl acetophenone), and mix; Postheating to 80 ℃, and, drip 1 of 100g behind the reaction 5h to constantly stirring in the container, the 6-glycol diacrylate continues to stir 2h; Then stop heating, continue stirring and be cooled to room temperature; Add water-retaining agent 2% (this example is an acetone dimethyl acetal) at last, stir, process non-setting adhesive and get final product.
Embodiment 3
A kind of battery sticks with glue the preparation method of agent, and it may further comprise the steps:
At first in container, add propenoate 88% (this example is an Isooctyl acrylate monomer), Acrylic Acid Monomer 10% and chain initiator 2 ‰ (this example is 2,2-dimethoxy-2 phenyl acetophenone), and mix; Postheating to 80 ℃, and, drip 1 of 60g behind the reaction 5h to constantly stirring in the container, the 6-glycol diacrylate continues to stir 2h; Then stop heating, continue stirring and be cooled to room temperature; Add water-retaining agent 2% (this example is the acetone diethyl acetal) at last, stir, process non-setting adhesive and get final product.
Embodiment 4
A kind of battery sticks with glue the preparation method of agent, and it may further comprise the steps:
At first in container, add propenoate 95% (this example is a NSC 20949), Acrylic Acid Monomer 4% and chain initiator 5 ‰ (this example is 2,2-dimethoxy-2 phenyl acetophenone), and mix; Postheating to 85 ℃, and, drip 1 of 180g behind the reaction 4.5h to constantly stirring in the container, the 6-glycol diacrylate continues to stir 1.5h; Then stop heating, continue stirring and be cooled to room temperature; Add water-retaining agent 1% (this example is acetal) at last, stir, process non-setting adhesive and get final product.
Above embodiment is merely preferred embodiment of the present invention; The present invention is not limited only to above embodiment and also allows other structural changes; As: propenoate is a Bing Xisuandingzhi; And meet other acetals or ketal of acetal or ketal general formula or the like, and allly in rights to independence claimed range of the present invention, change, all belong to protection domain of the present invention.
Claims (10)
1. a battery sticks with glue agent, it is characterized in that: it is processed by the material of following components in weight percent:
Propenoate 84%~95%, Acrylic Acid Monomer 4%~15%, water-retaining agent 0.1%~5%, chain initiator 1 ‰~5 ‰.
2. battery according to claim 1 sticks with glue agent, it is characterized in that: described propenoate is Isooctyl acrylate monomer, methyl acrylate, Bing Xisuandingzhi or NSC 20949.
3. battery according to claim 1 sticks with glue agent, it is characterized in that: described water-retaining agent is acetal or ketal.
4. battery according to claim 3 sticks with glue agent, it is characterized in that: the structural formula of described acetal or ketal is:
R
1, R
2Group is Wasserstoffatoms, methyl, ethyl, propyl group, butyl or isopropyl group; R
3, R
4Group is methyl, ethyl, propyl group, sec.-propyl or butyl group; R
5Be methylene group.
5. battery according to claim 1 sticks with glue agent, it is characterized in that: described chain initiator is two azo isobutyl cyanogen or 2,2-dimethoxy-2 phenyl acetophenone.
6. a battery sticks with glue the preparation method of agent, and it is characterized in that: it may further comprise the steps:
At first in container, add propenoate 84%~95%, Acrylic Acid Monomer 4%~15% and chain initiator 1 ‰~5 ‰, and mix; Postheating to 75~85 ℃, and, drip 1 of 40~180g behind reaction 4.5~5.5h to constantly stirring in the container, the 6-glycol diacrylate continues to stir 1.5~2.5h; Then stop heating, continue stirring and be cooled to room temperature; Add water-retaining agent 0.1%~5% at last, stir, process non-setting adhesive and get final product.
7. battery according to claim 6 sticks with glue the preparation method of agent, it is characterized in that: described propenoate is Isooctyl acrylate monomer, methyl acrylate, Bing Xisuandingzhi or NSC 20949.
8. battery according to claim 6 sticks with glue the preparation method of agent, it is characterized in that: described water-retaining agent is acetal or ketal.
9. battery according to claim 6 sticks with glue the preparation method of agent, it is characterized in that: the structural formula of described acetal or ketal is:
R
1, R
2Group is Wasserstoffatoms, methyl, ethyl, propyl group, butyl or isopropyl group; R
3, R
4Group is methyl, ethyl, propyl group, sec.-propyl or butyl group; R
5Be methylene group.
10. battery according to claim 6 sticks with glue the preparation method of agent, it is characterized in that: described chain initiator is two azo isobutyl cyanogen or 2,2-dimethoxy-2 phenyl acetophenone.