CN102504642A - Unsaturated polyester putty for automobile sheetmetal - Google Patents
Unsaturated polyester putty for automobile sheetmetal Download PDFInfo
- Publication number
- CN102504642A CN102504642A CN201110385169XA CN201110385169A CN102504642A CN 102504642 A CN102504642 A CN 102504642A CN 201110385169X A CN201110385169X A CN 201110385169XA CN 201110385169 A CN201110385169 A CN 201110385169A CN 102504642 A CN102504642 A CN 102504642A
- Authority
- CN
- China
- Prior art keywords
- parts
- unsaturated polyester
- automobile
- atom ash
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses unsaturated polyester putty for automobile sheetmetal. Main agent of the unsaturated polyester putty comprises, by weight, 100 parts of unsaturated polyester resin, 5-7 parts of methyl hydroxyethyl toluidine, 1-2 parts of styrene, 0.8-1.2 part of polytetrafluoroethylene wax, 0.5-1 part of hydroquinone, 1-2 parts of gaseous SiO2, 4-6 parts of titanium dioxide, 1-2 parts of hollow glass beads, 5-8 parts of pulvistalci and 5-6 parts of expansion ultrafine powder. Initiator of the unsaturated polyester putty comprises, by weight, 60-70 parts of benzoyl peroxide, 25-35 parts of dibutyl phthalate, and 2-8 parts of silicon dioxide.
Description
Technical field
The present invention relates to the chemistry painting industry field, particularly a kind of plates of automobile is with the atom ash.
Background technology
The atom ash is equipped with color stuffing, toughner, promotor etc. by unsaturated polyester resin and makes with the solidifying agent packing.Can regulate curing speed through hardener dose, be mainly used in the preceding filleting of application and fill and lead up, be a kind of of putty.Be with other synthetic resins putty differences: 100% participates in solidifying, and arbitrarily moulding is once filled up the above coating of 10mm and do not had contraction; Normal temperature quick-drying, easy polishing; Good with the sticking power of metal, intensity is high, and is fine and smooth, smooth, smooth, has certain antirust ability, not priming and well supporting with all kinds of coating.The atom ash is to develop a kind of faster pointing material over nearly 20 years in the world.Today of science and technology develop rapidly, the rhythm of people work and life is more and more faster, and is following also increasingly high to the requirement of working efficiency, and automobile that has just driven repairman shop into is just want at once it is fixed and driven away.So just require the plates of automobile repairing trades to increase work efficiency, accelerate speed of application, bring many adverse consequencess thus, as caused some by the atom ash that a vehicle body embedding in the near future that repairs is coated with foaming is arranged, the generation of phenomenon such as come off.But lay the blame on its occurrence cause with regard to aforesaid this situation and mainly contain 2 points; Be because operator's misoperation causes on the one hand; On the other hand, also be most important reason, be performances such as existing atom ash fast does, blade coating, polishing can't be fully up to expectations.These performances are limited by the component and the producing and manufacturing technique of traditional atom ash, so must determine the bad of its performance.
Therefore, be necessary to develop a kind of new atom ash, to be adapted to the demand that the plates of automobile repairing trades are increased work efficiency.
Summary of the invention
To the deficiency of prior art, one of the object of the invention is to provide a kind of plates of automobile with the atom ash.
For realizing above-mentioned purpose, the technical scheme that the present invention adopts is following:
A kind of plates of automobile is with the atom ash, and the host of said atom ash is made up of following component in weight part: 100 parts of unsaturated polyester resins, dimethyl hydroxyethyl Tolylamine 5-7 part; Vinylbenzene 1-2 part; Tetrafluoroethylene wax 0.8-1.2 part, Resorcinol 0.5-1 part, gas phase SiO
21-2 part, white titanium pigment 4-6 part, hollow glass micropearl 1-2 part, talcum powder 5-8 part, expansion micro mist 5-6 part, initiator by following composition by weight forming: Lucidol 60-70 part, Witcizer 300 25-35 part, silicon-dioxide 2-8 part.
Preferably, the host of said atom ash is made up of following component in weight part: 100 parts of unsaturated polyester resins, 6 parts of dimethyl hydroxyethyl Tolylamine, 1.5 parts of vinylbenzene, 1 part in tetrafluoroethylene wax, 0.8 part of Resorcinol, gas phase SiO
21.5 part, 5 parts of white titanium pigments, 1.5 parts of hollow glass micropearls, 6.5 parts of talcum powder, 5.5 parts of expansion micro mists, initiator by following composition by weight forming: 65 parts of Lucidols, 30 parts of Witcizer 300s, 5 parts of silicon-dioxide.
Beneficial effect of the present invention is:
1) the atom ash of the present invention after fixing of filming is fast, and it is little influenced by temperature and humidity, applies can polish after 25 minutes.
2) atom ash light specific gravity of the present invention, under the equal in quality, being coated with and scraping area is more than 1.8 times of common ash.
3) do not contain any heavy metal element in the atom ash of the present invention, the feature of environmental protection is good; Promotor is that varies is formed, and toxicity is low; On various metal substrates surface good adhesive is arranged all.Workability is superior, and each item physical and chemical index is high.
Embodiment
Embodiment one
A kind of plates of automobile is with the atom ash, and the host of said atom ash is made up of following component in weight part: 100 parts of unsaturated polyester resins, 5 parts of dimethyl hydroxyethyl Tolylamine, 2 parts of vinylbenzene, 0.8 part in tetrafluoroethylene wax, 1 part of Resorcinol, gas phase SiO
21 part, 6 parts of white titanium pigments, 1 part of hollow glass micropearl, 8 parts of talcum powder, 5 parts of expansion micro mists, initiator by following composition by weight forming: 70 parts of Lucidols, 25 parts of Witcizer 300s, 8 parts of silicon-dioxide.
Embodiment two
A kind of plates of automobile is with the atom ash, and the host of said atom ash is made up of following component in weight part: 100 parts of unsaturated polyester resins, 7 parts of dimethyl hydroxyethyl Tolylamine, 1 part of vinylbenzene, 1.2 parts in tetrafluoroethylene wax, 0.5 part of Resorcinol, gas phase SiO
22 parts, 4 parts of white titanium pigments, 2 parts of hollow glass micropearls, 5 parts of talcum powder, 6 parts of expansion micro mists, initiator by following composition by weight forming: 60 parts of Lucidols, 35 parts of Witcizer 300s, 2 parts of silicon-dioxide.
Embodiment three
A kind of plates of automobile is with the atom ash, and the host of said atom ash is made up of following component in weight part: 100 parts of unsaturated polyester resins, 6 parts of dimethyl hydroxyethyl Tolylamine, 1.5 parts of vinylbenzene, 1 part in tetrafluoroethylene wax, 0.8 part of Resorcinol, gas phase SiO
21.5 part, 5 parts of white titanium pigments, 1.5 parts of hollow glass micropearls, 6.5 parts of talcum powder, 5.5 parts of expansion micro mists, initiator by following composition by weight forming: 65 parts of Lucidols, 30 parts of Witcizer 300s, 5 parts of silicon-dioxide.
Applicant's statement; The present invention explains detailed process equipment of the present invention and technical process through the foregoing description; But the present invention is not limited to above-mentioned detailed process equipment and technical process, does not mean that promptly the present invention must rely on above-mentioned detailed process equipment and technical process could be implemented.The person of ordinary skill in the field should understand, and to any improvement of the present invention, to the interpolation of the equivalence replacement of each raw material of product of the present invention and ancillary component, the selection of concrete mode etc., all drops within protection scope of the present invention and the open scope.
Claims (2)
1. a plates of automobile is characterized in that with the atom ash, and the host of said atom ash is made up of following component in weight part: 100 parts of unsaturated polyester resins; Dimethyl hydroxyethyl Tolylamine 5-7 part, vinylbenzene 1-2 part, tetrafluoroethylene wax 0.8-1.2 part; Resorcinol 0.5-1 part, gas phase SiO
21-2 part, white titanium pigment 4-6 part, hollow glass micropearl 1-2 part, talcum powder 5-8 part, expansion micro mist 5-6 part, initiator by following composition by weight forming: Lucidol 60-70 part, Witcizer 300 25-35 part, silicon-dioxide 2-8 part.
2. a kind of plates of automobile as claimed in claim 1 is with the atom ash; It is characterized in that the host of said atom ash is made up of following component in weight part: 100 parts of unsaturated polyester resins, 6 parts of dimethyl hydroxyethyl Tolylamine; 1.5 parts of vinylbenzene; 1 part in tetrafluoroethylene wax, 0.8 part of Resorcinol, gas phase SiO
21.5 part, 5 parts of white titanium pigments, 1.5 parts of hollow glass micropearls, 6.5 parts of talcum powder, 5.5 parts of expansion micro mists, initiator by following composition by weight forming: 65 parts of Lucidols, 30 parts of Witcizer 300s, 5 parts of silicon-dioxide.