CN102489861A - 一种氧化物弥散强化合金防震屏零件的焊接方法 - Google Patents
一种氧化物弥散强化合金防震屏零件的焊接方法 Download PDFInfo
- Publication number
- CN102489861A CN102489861A CN2011104231711A CN201110423171A CN102489861A CN 102489861 A CN102489861 A CN 102489861A CN 2011104231711 A CN2011104231711 A CN 2011104231711A CN 201110423171 A CN201110423171 A CN 201110423171A CN 102489861 A CN102489861 A CN 102489861A
- Authority
- CN
- China
- Prior art keywords
- welding
- alloy
- oxide
- screen part
- shockproof screen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及合金焊接技术领域，具体涉及一种氧化物弥散强化合金防震屏零件的焊接方法。首先采用砂纸打磨防震屏零件的焊接表面，然后用化学纯级别的丙酮清洗，并在室温下干燥后，在焊缝两端点焊定位，然后焊接，焊接参数为：在焊接表面施加0.13～0.24MPa的压力0.02s，通电焊接0.16s，焊接电流为6600～8000A，焊接电压为209～213V，通流比70%，焊速0.4m/s。本发明焊接方法焊接的氧化物弥散强化合金防震屏焊接面在1100℃下的拉伸强度达到MGH956合金本体拉伸强度的65%以上，满足发动机设计需求；本发明的操作简单，实现了工程化生产，并推广应用到其他军机、民机和燃机，应用前景广泛。
Description
技术领域
本发明涉及合金焊接技术领域，具体涉及一种氧化物弥散强化合金防震屏零件的焊接方法。
背景技术
某新型航空发动机选用MGH956合金板材制备的防震屏零件需要进行连接。由于MGH956合金的强化相Y2O3纳米颗粒与FeCrAl金属基体的冶金不相容性，导致该类材料的焊接性能差，如采用氩弧焊、电子束焊、激光焊等熔化焊方法容易导致Y2O3纳米颗粒聚集成氧化物夹杂，甚至气孔和裂纹；而且由于焊缝中Y2O3纳米颗粒聚集会导致熔化焊接焊缝高温强度显著下降。同样目前较为先进的TLP扩散焊方法也不适用于MGH956合金的焊接，原因是MGH956合金气体含量高，TLP扩散焊间隙大时，容易产生氧化物夹杂、孔洞、未焊合等缺陷。
发明内容
本发明的目的是针对现有技术存在的不足，提供一种氧化物弥散强化合金防震屏零件的焊接方法，焊后性能满足设计需求并实现了工程化生产。
首先采用砂纸打磨防震屏零件的焊接表面，然后用化学纯级别的丙酮清洗，并在室温下干燥后，在焊缝两端点焊定位，然后焊接，焊接参数为：在焊接表面施加0.13～0.24MPa的压力0.02s，通电焊接0.16s，焊接电流为6600～8000A，焊接电压为209～213V，通流比70%，焊速0.4m/s；
所述的氧化物弥散强化合金防震屏的材料为MGH956合金，弥散强化相为Y2O3纳米颗粒，基体为FeCrAl金属；
焊接后焊接面在1100℃下的拉伸强度达到MGH956合金本体拉伸强度的65%以上。
与现用技术相比，本发明的特点及其有益效果是：
1.通过本发明焊接方法焊接的氧化物弥散强化合金防震屏焊接面在1100℃下的拉伸强度达到MGH956合金本体拉伸强度的65%以上，满足发动机设计需求；
2.本发明的焊接方法操作简单，实现了工程化生产，并推广应用到其他军机、民机和燃机，应用前景广泛。
具体实施方式
下面结合实施例对本发明作详细说明，但本发明的保护范围不仅限于下述的实施例：
下述实施例采用的焊接设备的型号是：МШП-150-1-B；
氧化物弥散强化合金防震屏的材料为MGH956合金，弥散强化相为Y2O3纳米颗粒，基体为FeCrAl金属。
实施例1：
首先采用砂纸打磨防震屏焊接表面，然后用化学纯级别的丙酮清洗，并在室温下干燥后，在焊缝两端点焊定位，然后焊接；
焊接参数为：在焊接表面施加0.13MPa的压力0.02s，通电焊接0.16s，焊接电流为6600A，焊接电压为209V，通流比70%，焊速0.4m/s；
焊接的氧化物弥散强化合金防震屏焊接面在1100℃下的拉伸强度达到MGH956合金本体拉伸强度的66%。
实施例2：
首先采用砂纸打磨防震屏焊接表面，然后用化学纯级别的丙酮清洗，并在室温下干燥后，在焊缝两端点焊定位，然后焊接；
焊接参数为：在焊接表面施加0.24MPa的压力0.02s，通电焊接0.16s，焊接电流为8000A，焊接电压为213V，通流比70%，焊速0.4m/s；
焊接的氧化物弥散强化合金防震屏焊接面在1100℃下的拉伸强度达到MGH956合金本体拉伸强度的70%。
实施例3：
首先采用砂纸打磨防震屏焊接表面，然后用化学纯级别的丙酮清洗，并在室温下干燥后，在焊缝两端点焊定位，然后焊接；
焊接参数为：在焊接表面施加0.2MPa的压力0.02s，通电焊接0.16s，焊接电流为7000A，焊接电压为210V，通流比70%，焊速0.4m/s；
焊接的氧化物弥散强化合金防震屏焊接面在1100℃下的拉伸强度达到MGH956合金本体拉伸强度的67%。
Claims (3)
1.一种氧化物弥散强化合金防震屏零件的焊接方法，首先采用砂纸打磨防震屏零件的焊接表面，然后用化学纯级别的丙酮清洗，并在室温下干燥后，在焊缝两端点焊定位，然后焊接，其特征在于焊接参数为：在焊接表面施加0.13～0.24MPa的压力0.02s，通电焊接0.16s，焊接电流为6600～8000A，焊接电压为209～213V，通流比70%，焊速0.4m/s。
2.根据权利要求1所述的一种氧化物弥散强化合金防震屏零件的焊接方法，其特征在于所述的氧化物弥散强化合金防震屏的材料为MGH956合金，弥散强化相为Y2O3纳米颗粒，基体为FeCrAl金属。
3.根据权利要求1所述的一种氧化物弥散强化合金防震屏零件的焊接方法，其特征在于焊接后焊接面在1100℃下的拉伸强度达到MGH956合金本体拉伸强度的65%以上。