CN102477238A - Water-based varnish - Google Patents
Water-based varnish Download PDFInfo
- Publication number
- CN102477238A CN102477238A CN2010105574521A CN201010557452A CN102477238A CN 102477238 A CN102477238 A CN 102477238A CN 2010105574521 A CN2010105574521 A CN 2010105574521A CN 201010557452 A CN201010557452 A CN 201010557452A CN 102477238 A CN102477238 A CN 102477238A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- gloss oil
- agent
- based gloss
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a material for construction and decoration and in particular relates to water-based varnish. The formula of the water-based varnish is as follows: 15 to 30 parts of water, 10 to 20 parts of acrylic polymers, 12 to 20 parts of titanium dioxide, 3 to 5 parts of barite powders, 5 to 15 parts of ground calcium carbonate, 3 to 5 parts of kaolin, 3 to 5 parts of mica powders, 0.4 to 0.8 parts of wetting and dispersing agents, 0.3 to 0.4 parts of a defoaming agent, 0.3 to 0.6 parts of a leveling agent, 0.5 to 2 parts of a thickener, 0.2 parts of a multifunctional auxiliary agent, 0.8 to 1 part of a film-forming agent, and 0.8 to 2 parts of a disinfectant and anti-mildew agent. The water-based varnish is made from high-quality acrylic polymers, natural mineral powders and multiple auxiliary agents and refined by the advanced production process. The water-based varnish has the characteristics of environmental friendliness, no toxicity, alkali resistance, mildew resistance, primer-coat property, crack resistance, energy saving, flame retardancy, sound insulation, moisture protection, leakage resistance, strong adhesion, high hardness and dry friction resistance.
Description
Technical field:
The present invention relates to a kind of construction and decoration and use material, particularly a kind of water-based gloss oil.
Background technology:
The water-based gloss oil part that in decoration construction, has been absolutely necessary has with other resins consistency is widely arranged, have do soon, characteristics such as no sticking power, high gloss.But existing water-based gloss oil mostly has in smell and the starting material of products material how much have the human harmful substance, so in use usually can be restricted.
Summary of the invention:
A kind of water-based gloss oil that the present invention invents in order to solve the problems of the technologies described above just.The present invention passes through, and technique means realizes: described water-based gloss oil prescription is following: 15～30 parts in water, 10～20 parts of XPAs, 10～20 parts of white titanium pigments, 3～5 parts of stone flours of a huge sum of money, 5～15 parts of water-ground limestones, 3～5 parts of kaolin, 3～5 parts of mica powders, 0.4～0.8 part of wetting dispersing agent, 0.3～0.4 part of skimmer, 0.3～0.6 part of flow agent, 0.5～2 part of thickening material, 0.2 part of multifunctional assistant, 0.8～1 part of film coalescence aid, 0.8～2 part of biocide mildewcide.
Described water is softening water.
Above-mentioned water-based gloss oil production craft step is: with the water accurate measurement; Contain in stainless steel vessel; Place under the high speed dispersor, under 300 rev/mins of stirrings, evenly drop into the solid thickening material in the water to spread the throwing mode; Then wetting dispersing agent, skimmer, multifunctional assistant, film coalescence aid, biocide mildewcide are dropped in the jar one by one, stir and drop into powder white titanium pigment, huge sum of money stone flour, water-ground limestone, kaolin, mica powder after 5 minutes.Dispersion machine speed is transferred to 1600 rev/mins, add a cover, high speed dispersion added XPA in 30～50 minutes, and the back that under 400～500 rev/mins, stirs adds thickening material, and finished product viscosity is transferred to 100KU ± 2, filtered and packaged to get final product.
The present invention selects the fine XPA for use, and natural mineral powder and multiple auxiliary agent adopt advanced production technique to make with extra care and form.This product is except complete preservation water-based gloss oil and other resins consistency widely; Have fast do, characteristics such as no sticking power, high gloss, at the bottom of also having environment-protecting asepsis, alkali resistant, mildew-resistant, consolidating underseal, characteristics such as cracking resistance, energy-conservation, fire-retardant, sound insulation, protection against the tide, leak stopping, strong adhesion, hardness height, anti-metal to-metal contact.
Embodiment:
A kind of water-based gloss oil, its prescription is made up of for 2 parts 25 parts of softening waters, 15 parts of XPAs, 15 parts of white titanium pigments, 4 parts of stone flours of a huge sum of money, 13 parts in lime carbonate, 5 parts of kaolin, 3 parts of mica powders, 0.9 part of wetting dispersing agent, 0.3 part of skimmer, 0.5 part of flow agent, 3.6 parts of thickening materials, 0.2 part of multifunctional assistant, 1.5 parts of film coalescence aid, biocide mildewcide.
The water-based gloss oil production craft step is: with the water accurate measurement; Contain in stainless steel vessel; Place under the high speed dispersor, under 300 rev/mins of stirrings, evenly drop into the solid thickening material in the water to spread the throwing mode; Then wetting dispersing agent, skimmer, multifunctional assistant, film coalescence aid, biocide mildewcide are dropped in the jar one by one, stir and drop into powder white titanium pigment, huge sum of money stone flour, water-ground limestone, kaolin, mica powder after 5 minutes.Dispersion machine speed is transferred to 1600 rev/mins, add a cover, high speed dispersion added XPA in 30～50 minutes, and the back that under 400～500 rev/mins, stirs adds thickening material, and finished product viscosity is transferred to 100KU ± 2, filtered and packaged to get final product.
The detailed introduction that above specification sheets just carries out the present invention for field personnel of the present invention better understand core of the present invention, this paper also should not be construed limitation of the present invention.All similar or close equal replacements also are interpreted as falling in protection scope of the present invention.
Claims (4)
1. a water-based gloss oil is characterized in that described water-based gloss oil prescription is following: 15～30 parts in water, 10～20 parts of XPAs, 10～20 parts of white titanium pigments, 3～5 parts of stone flours of a huge sum of money, 5～15 parts of water-ground limestones, 3～5 parts of kaolin, 3～5 parts of mica powders, 0.4～0.8 part of wetting dispersing agent, 0.3～0.4 part of skimmer, 0.3～0.6 part of flow agent, 0.5～2 part of thickening material, 0.2 part of multifunctional assistant, 0.8～1 part of film coalescence aid, 0.8～2 part of biocide mildewcide.
2. water-based gloss oil according to claim 1 is characterized in that described water-based gloss oil prescription is following: 25 parts in water, 15 parts of XPAs, 15 parts of white titanium pigments, 4 parts of stone flours of a huge sum of money, 13 parts in lime carbonate, 5 parts of kaolin, 3 parts of mica powders, 0.9 part of wetting dispersing agent, 0.3 part of skimmer, 0.5 part of flow agent, 3.6 parts of thickening materials, 0.2 part of multifunctional assistant, 1.5 parts of film coalescence aid, 2 parts of biocide mildewcides.
3. water-based gloss oil according to claim 1 is characterized in that described water is softening water.
4. the production technique of a water-based gloss oil as claimed in claim 1; It is characterized in that said production craft step is: with the water accurate measurement; Contain in stainless steel vessel; Place under the high speed dispersor, under 300 rev/mins of stirrings, evenly drop into the solid thickening material in the water to spread the throwing mode; Then wetting dispersing agent, skimmer, multifunctional assistant, film coalescence aid, biocide mildewcide are dropped in the jar one by one, stir and drop into powder white titanium pigment, huge sum of money stone flour, water-ground limestone, kaolin, mica powder after 5 minutes.Dispersion machine speed is transferred to 1600 rev/mins, add a cover, high speed dispersion added XPA in 30～50 minutes, and the back that under 400～500 rev/mins, stirs adds thickening material, and finished product viscosity is transferred to 100KU ± 2, filtered and packaged to get final product.