CN102466595A - Method for testing influence of resin addition amounts on leakage stoppage effect of super-absorbent resin - Google Patents
Method for testing influence of resin addition amounts on leakage stoppage effect of super-absorbent resin Download PDFInfo
- Publication number
- CN102466595A CN102466595A CN2010105586675A CN201010558667A CN102466595A CN 102466595 A CN102466595 A CN 102466595A CN 2010105586675 A CN2010105586675 A CN 2010105586675A CN 201010558667 A CN201010558667 A CN 201010558667A CN 102466595 A CN102466595 A CN 102466595A
- Authority
- CN
- China
- Prior art keywords
- super
- moisture absorbing
- resin
- strong moisture
- absorbing resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for testing the influence of the resin addition amounts on a leakage stoppage effect of super-absorbent resin. The method for testing the influence of the resin addition amount on the leakage stoppage effect of the super-absorbent resin comprises the following steps of: selecting a super-absorbent resin sample; respectively injecting the super-absorbent rein sample into rock cores with same rack core sand grain diameter with different resin addition amounts; recording leakage stoppage times and leakage amounts, and then testing loading capacities; and analyzing the influence of resin addition amounts on the leakage stoppage effect of the super-absorbent rein according to the tested leakage stoppage times, leakage amounts and loading capacities, and further determining the optimal resin addition amount. The method disclosed by the invention can be used for testing the influence of different resin addition amounts on the leakage stoppage effect of the super-absorbent resin, has the advantages of high testing precision and simple test samples and provides a theoretical basis for application of the super-absorbent resin to leakage stoppage.
Description
Technical field
The present invention relates to a kind of method of testing the resin dosage to the influence of super-strong moisture absorbing resin plugging effect.
Background technology
Drilling fluid leakage is a kind of common down hole problem in the drilling operation.That leakage can occur in is shallow, in and deep formation, also can in the geochronic stratum of difference, take place, and all possibly occur in the stratum of all kinds of lithology.The leakage that has is that mud pit level slowly descends, and then having into of having do not have, in case miss; Not only incur loss through delay the drilling operation time, prolong drilling period, the loss drilling fluid; The infringement hydrocarbon zone is disturbed geological logging work, but also possibly caused a series of complex situations and accidents such as well slough, bit freezing, blowout; Even cause well to be scrapped, cause great economic loss.Therefore, in drilling operation, should avoid the generation of leakage as far as possible.
According to statistics, whole world leakage incidence accounts for 25 20 percent to percent of total well number, and the annual fund that expends because of leakage is up to several hundred million units in the global petroleum industry.All there is the leakage problem to some extent in the most of oil fields of China, and the most outstanding is that Chuan Dong is regional with south, river, and annual leak stopping is consuming time to account for 5～8% of the gross drilling time.Also to consume a large amount of drilling fluids and lost circulation material simultaneously, drilling cost is risen significantly.As area, east, a river year loss mud amount is 8000～13000m a few years ago
3, year about 200 wells of generation leakage, 14～35 rig moons of lost time, year is directly consumed 400～6,000,000 yuan.
The leakage problem is drilling well work long-term existence and fails the technical barrier of fine solution that leakage stopping technology is the important topic that drilling engineering circle studies for a long period of time.Leakage stopping technology has had bigger development in recent years, and each oil field has all summed up the leak-stopping technique technology of suitable this area characteristics both at home and abroad, and the kind of lost circulation material is on the increase, and the leak stopping success ratio is also improving constantly.
However, because the each department formation lithology changes hole, crack, solution cavity developmental state difference; The reason of leakage is complicated, the leakage type is different; Restraining factors are more, and the specific aim of leakage stopping technology is stronger, are difficult to so far carry out leakproof and leak stopping with a general pattern.It is even more serious particularly to bore fissured formation leakage problem.According to incompletely statistics, the reserves of state's internal fissure property bad ground account for 50% of total reserves, but grow because of formation fracture, hole, and the leakage problem is difficult to solve, the loss that causes and serious.Therefore, the pernicious leakage problem of crack property bad ground has become the emphasis that drilling well circle is paid close attention to.
About the research of super-strong moisture absorbing resin, external starting is morning, and what wherein effect was maximum is the U.S. and Japan, secondly is Germany and French.And decades in evening are wanted in domestic relative research, but in the last few years, relevant technology emerges in an endless stream, and each side all is being devoted to research whole-heartedly.
1961, north research institute of United States Department of Agriculture began from starch-grafted vinyl cyanide, and super-strong moisture absorbing resin is studied, and this type of research subsequently is more and more deep, and successfully developed super-strong moisture absorbing resin to the seventies end of the sixties.After this, number of research projects has been carried out to the aspects such as kind, manufacturing approach, performance and application of super-strong moisture absorbing property resin in countries in the world such as Germany, France, has obtained achievement.Begin the eighties to occur producing the water absorptivity material through chemical reaction with other natural compound derivatives.
The expansion of and applied research synthetic along with super absorbent resin, the also corresponding development of its forming processing technology.Absorbent composites produced in the eighties in 20th century, because it can improve many performances such as intensity of hydrogel after the brine tolerance, absorption speed, suction of super-strong moisture absorbing property resin, so development rapidly.To the beginning of the nineties, advance by leaps and bounds especially.In recent years the blend of water-absorbing resins has begun one's study.These provide wide prospect more for the development super absorbent resin.
The dominant company of world production super absorbent resin in 1985 has only 13 families, to nineteen ninety-five foreign study and the company of production reach nearly 50 families unexpectedly.Japan is maximum in the world super-strong moisture absorbing resin production and research state.Cooperate with other countries such as the U.S., Germany again subsequently, the super-strong moisture absorbing resin technology is rapid growth constantly.
For the super-strong moisture absorbing resin Study on Theory, the 1950's, the suction theory of Flory was established theoretical foundation for the development of absorbent polymer.After the sixties, super-strong moisture absorbing property resin began to go into operation, along with its fast development, People more and more need to feel the further instructive theory of further investigation super-strong moisture absorbing property resin.The end of the seventies, various countries began to pay attention to its research in succession.State such as Japan and the United States particularly, more fruitful theoretical research has been carried out in aspects such as, hydrating structure theoretical in suction and macromolecule hydrogel, and new development has been arranged.
The super-strong moisture absorbing resin water absorptivity is strong, can absorb the water of tens to several thousand times of own vols, and the ability biodegradation is widely used, and considers it also is a good selection from the global environment factor.Transport fluid suppresses water absorbent polymer and expands, and with water filling behind mixture pump such as the drop ply, makes its expansion, thus the shutoff weak zone, and particularly to serious fractured leakage situation, this technology is in aboveground successful Application.Abroad on the super-strong moisture absorbing resin leakage stopping technology, start to walk early, achievement is many, and the correlation technique instance is also a lot.
Super-strong moisture absorbing resin is popularized in the petroleum industry field gradually, and the research that relevant oilfield chemistry is used hydroscopic high-molecular resin has also caused oilfielder's attention.Particularly in the oil gas field probing, be used as the chemical plugging material, chemical plugging is a kind of important techniques measure in the oil gas field drilling process.Development since the eighties has obtained good achievement.At present, the on-the-spot lost circulation additive of the hydroscopic high-molecular resin class of Application and Development has SYZ, PAT and TP-9010 type brand, JPD imbibition polymkeric substance, WS-1 type GEL USED FOR PLUGGING WELL LOST CIRCULATION, WEA-1 delayed expansion particle lost circulation additive.
In addition, super-strong moisture absorbing resin can be made encapsulant in the defeated construction of oil gas field ground line; In probing, make additive for drilling fluid, can be used as the lubricant of drill bit and the gel of drilling fluid; Application in other professional domains of oilfield chemistry because of its performance is remarkable, like tertiary oil recovery, is made gel in oil gas field waste water treatment aqueous fracturing fluid, the acid fracturing liquid, the hardening agent of well control fluid etc.
In a word, the development of super-strong moisture absorbing resin is also just in nearly decades.No matter, perhaps, all obtained huge development from the situation of processing and application and theoretical research from the kind and the quantity of product.Because performance that hydroscopic high-molecular resin is peculiar and considerable application prospect; Develop extremely rapid over 30 years; By general application performance, function, to the high-level exploitation development of intelligent multi-function material, its application has been penetrated into all trades and professions of national economy.Particularly be a new applied research direction in oilfield chemistry, have a good application prospect.
Summary of the invention
The objective of the invention is to overcome the shortcoming and defect of above-mentioned prior art; A kind of method of testing the resin dosage to the influence of super-strong moisture absorbing resin plugging effect is provided; This method of testing can be measured the influence of different resins dosage to the super-strong moisture absorbing resin plugging effect fast; Measuring accuracy is high, and testing procedure is simple, for super-strong moisture absorbing resin is applied to leak stopping theoretical foundation is provided.
The object of the invention is realized through following technical proposals: a kind of method of testing the resin dosage to the influence of super-strong moisture absorbing resin plugging effect may further comprise the steps:
(a) it is subsequent use to produce the super-strong moisture absorbing resin sample;
(b) choose a certain amount of super-strong moisture absorbing resin sample;
(c), respectively the super-strong moisture absorbing resin sample is mixed the rock core that lost circulation additive injects identical rock core sand grains diameter with the well slurry with different resin dosages;
(d) record shutoff time and wastage, treat that it does not leak after, leave standstill a period of time, record bearing capacity then;
(e) according to the shutoff time, wastage and the bearing capacity that record, analyze of the influence of different resins dosage, and then determine best resin dosage the super-strong moisture absorbing resin plugging effect.
In the said step (b), the particle diameter of the super-strong moisture absorbing resin sample of choosing is greater than 40 orders.
In the said step (c), the diameter of rock core sand grains is respectively 10～6 orders.
In the said step (d), time of repose is 30 minutes.
In the said step (c), injection pressure 1.0MPa.
In the said step (c), the super-strong moisture absorbing resin sample quality of adding accounts for the super-strong moisture absorbing resin sample and mixes 0.3%, 0.5% or 0.8% of lost circulation additive gross mass with the well slurry.
In sum, the invention has the beneficial effects as follows: can measure the influence of different resins dosage to the super-strong moisture absorbing resin plugging effect fast, measuring accuracy is high, and testing procedure is simple, for super-strong moisture absorbing resin is applied to leak stopping theoretical foundation is provided.
Embodiment
Below in conjunction with embodiment, the present invention is done further detailed description, but embodiment of the present invention is not limited only to this.
Embodiment:
A kind of method of testing the resin dosage that the present invention relates to the influence of super-strong moisture absorbing resin plugging effect, its concrete steps are following:
(a) it is subsequent use to produce the super-strong moisture absorbing resin sample;
(b) choose a certain amount of super-strong moisture absorbing resin sample;
(c), respectively the super-strong moisture absorbing resin sample is mixed the rock core that lost circulation additive injects identical rock core sand grains diameter with the well slurry with different resin dosages;
(d) record shutoff time and wastage, treat that it does not leak after, leave standstill a period of time, record bearing capacity then;
(e) according to the shutoff time, wastage and the bearing capacity that record, analyze of the influence of different resins dosage, and then determine best resin dosage the super-strong moisture absorbing resin plugging effect.
In the said step (b), the particle diameter of the super-strong moisture absorbing resin sample of choosing is greater than 40 orders.
In the said step (c), the diameter of rock core sand grains is respectively 10～6 orders.
In the said step (d), time of repose is 30 minutes.
In the said step (c), injection pressure 1.0MPa.
In the said step (c), the super-strong moisture absorbing resin sample quality of adding accounts for the super-strong moisture absorbing resin sample and mixes 0.3%, 0.5% or 0.8% of lost circulation additive gross mass with the well slurry.It is as shown in table 1 to record the result through said method
The plugging effect of the super-strong moisture absorbing resin under the table 1 different resins dosage
Can find out from table 1: the plugging effect difference under several kinds of dosages is little, all can form shutoff in a short period of time, blocks promptly and does not leak.Super-strong moisture absorbing resin is in the property of drilling fluid influence experiment in front; It is little to the influence of drilling fluid key property to draw different dosage super-strong moisture absorbing resins; Viscosity and shear force increase with dosage, too greatly then will certainly influence its flowability, are unfavorable for wellbore construction; Bring difficulty to pumping, so we choose below 0.5% and are advisable.
Above-mentioned method of testing can be measured the influence of different resins dosage to the super-strong moisture absorbing resin plugging effect fast, and measuring accuracy is high, and testing procedure is simple, for super-strong moisture absorbing resin is applied to leak stopping theoretical foundation is provided.
The above only is preferred embodiment of the present invention, is not the present invention is done any pro forma restriction, and every foundation technical spirit of the present invention, any simple modification, equivalent variations to above embodiment did all fall within protection scope of the present invention.
Claims (6)
1. a method of testing the resin dosage to the influence of super-strong moisture absorbing resin plugging effect is characterized in that, may further comprise the steps:
(a) it is subsequent use to produce the super-strong moisture absorbing resin sample;
(b) choose a certain amount of super-strong moisture absorbing resin sample;
(c), respectively the super-strong moisture absorbing resin sample is mixed the rock core that lost circulation additive injects identical rock core sand grains diameter with the well slurry with different resin dosages;
(d) record shutoff time and wastage, treat that it does not leak after, leave standstill a period of time, record bearing capacity then;
(e) according to the shutoff time, wastage and the bearing capacity that record, analyze of the influence of different resins dosage, and then determine best resin dosage the super-strong moisture absorbing resin plugging effect.
2. a kind of method of testing the resin dosage to the influence of super-strong moisture absorbing resin plugging effect according to claim 1 is characterized in that in the said step (b), the particle diameter of the super-strong moisture absorbing resin sample of choosing is greater than 40 orders.
3. a kind of method of testing the resin dosage to the influence of super-strong moisture absorbing resin plugging effect according to claim 1 is characterized in that in the said step (c), the diameter of rock core sand grains is respectively 10～6 orders.
4. a kind of method of testing the resin dosage to the influence of super-strong moisture absorbing resin plugging effect according to claim 1 is characterized in that in the said step (d), time of repose is 30 minutes.
5. a kind of method of testing the resin dosage to the influence of super-strong moisture absorbing resin plugging effect according to claim 1 is characterized in that, in the said step (c), and injection pressure 1.0MPa.
6. a kind of method of testing the resin dosage according to claim 1 to the influence of super-strong moisture absorbing resin plugging effect; It is characterized in that; In the said step (c), the super-strong moisture absorbing resin sample quality of adding accounts for the super-strong moisture absorbing resin sample and mixes 0.3%, 0.5% or 0.8% of lost circulation additive gross mass with the well slurry.