CN102443335A - Epoxy flooring coating for computer machine room - Google Patents
Epoxy flooring coating for computer machine room Download PDFInfo
- Publication number
- CN102443335A CN102443335A CN2010105002043A CN201010500204A CN102443335A CN 102443335 A CN102443335 A CN 102443335A CN 2010105002043 A CN2010105002043 A CN 2010105002043A CN 201010500204 A CN201010500204 A CN 201010500204A CN 102443335 A CN102443335 A CN 102443335A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- restir
- filler
- flooring coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an epoxy flooring coating for a computer machine room, which belongs to the chemical field. The epoxy flooring coating comprises the following ingredients by weight part ratio: 80 parts of 828epoxy resin, 12 parts of butyl glycidylether, 0.3 parts of dispersant, 0.7 parts of antifoaming agent, 0.5 parts of levelling agent, 0.6 parts of scratch resistance agent, 100 parts of filling material, 3 parts of iron oxide red and 10 parts of curing agent; the preparation method comprises the processes of adding, uniformly stirring and mixing, wherein the construction thickness of flooring is 2.0-5.0 mm; the epoxy flooring coating has the advantages of simple formula, convenient construction, no toxicity, environmental protection, and strong antistatic effect.
Description
Technical field
The present invention relates to a kind of coating, specifically is a kind of Computer Facilities epoxy flooring coating, belongs to chemical field.
Background technology
Terrace paint is one of coating variety that increased rapidly along with the development of construction industry in recent years as novel material of construction, is widely used in the application of terraces such as factory, hospital, school, office and large-scale public place.Terrace paint is various in style at present; Epoxy flooring coating has excellent chemical resistance, smooth bright and clean because of paint film; Ornamental strong; Traction advantages of higher and become terrace paint kind with fastest developing speed, its main type has solvent-free gravity flow flat pattern, high solid solvent-borne type, conduction type, colored mortar type and aqueous epoxy floor coating etc.That the modern industry terrace requires is dustproof, antiseepage, anti-corrosion, resistance to compression, washable etc.; Epoxy flooring coating has better physical mechanical property and excellent chemical resistance because of filming; And smooth bright and clean, ornamental strong, can satisfy the requirement of modern industry terrace, so be widely used.But current market demand is maximum is easy construction, cost performance is high, wear resisting property is good, the terrace paint of long service life.
Summary of the invention
To the deficiency that above-mentioned prior art exists, the present invention a kind of environmental protection is provided, eliminate static, be applicable to the epoxy flooring coating of Computer Facilities.
Be to realize above-mentioned purpose, the present invention realizes through following technical scheme: a kind of Computer Facilities epoxy flooring coating, and the proportioning of filling a prescription by weight is made up of following component:
The title ratio of weight and number
828 epoxy resin 80
Butylglycidyl ether 12
Dispersion agent 0.3
Skimmer 0.7
Flow agent 0.5
Scratching resistant 0.6
Filler 100
Red iron oxide 3
Solidifying agent 10
Dispersion agent is 963 (Henkel Corp.), and skimmer is AMH2 (Henkel Corp.), and flow agent is that F60 (Henkel Corp.) and scratching resistant are S4 (Henkel Corp.); Filler is 60% silica sand (300 order), 10% white titanium pigment, 20% permanent white and 10% alumina powder; Solidifying agent is the low molecular polyamides solidifying agent.
Preparing method's process step is: stir → reinforced restir → reinforced again restir
1) elder generation's adding 828 epoxy resin, butylglycidyl ether, dispersion agent in container stirs;
2) under condition of stirring, add half the filler, stirred 30 minutes, and then added skimmer, flow agent, scratching resistant stirring 40 minutes;
3) continuation remaining filler of adding and red iron oxide stir and get final product.
Floor construction thickness is 2.0～5.0mm.
The invention has the beneficial effects as follows that prescription is simple, easy construction, asepsis environment-protecting, antistatic effect is strong.
Embodiment
Embodiment 1
A kind of Computer Facilities epoxy flooring coating, the proportioning of filling a prescription by weight is made up of following component:
The title ratio of weight and number
828 epoxy resin 80
Butylglycidyl ether 12
Dispersion agent 0.3
Skimmer 0.7
Flow agent 0.5
Scratching resistant 0.6
Filler 100
Red iron oxide 3
Solidifying agent 10
Dispersion agent is 963 (Henkel Corp.), and skimmer is AMH2 (Henkel Corp.), and flow agent is that F60 (Henkel Corp.) and scratching resistant are S4 (Henkel Corp.); Filler is 60% silica sand (300 order), 10% white titanium pigment, 20% permanent white and 10% alumina powder; Solidifying agent is the low molecular polyamides solidifying agent.
Preparing method's process step is:
1) elder generation's adding 828 epoxy resin, butylglycidyl ether, dispersion agent in container stirs;
2) under condition of stirring, add half the filler, stirred 30 minutes, and then added skimmer, flow agent, scratching resistant stirring 40 minutes;
3) continuation remaining filler of adding and red iron oxide stir and get final product.
Floor construction thickness is 2.0～5.0mm.
Claims (3)
1. Computer Facilities epoxy flooring coating, the proportioning that it is characterized in that filling a prescription by weight is made up of following component:
The title ratio of weight and number
828 epoxy resin 80
Butylglycidyl ether 12
Dispersion agent 0.3
Skimmer 0.7
Flow agent 0.5
Scratching resistant 0.6
Filler 100
Red iron oxide 3
Solidifying agent 10
Described dispersion agent is 963 (Henkel Corp.), and skimmer is AMH2 (Henkel Corp.), and flow agent is that F60 (Henkel Corp.) and scratching resistant are S4 (Henkel Corp.);
Described filler is 60% silica sand (300 order), 10% white titanium pigment, 20% permanent white and 10% alumina powder;
Described solidifying agent is the low molecular polyamides solidifying agent.
2. the making method of an a kind of Computer Facilities epoxy flooring coating as claimed in claim 1 is characterized in that process step is: stir → reinforced restir → reinforced again restir;
Described stirring is meant and in container, adds 828 epoxy resin, butylglycidyl ether, dispersion agent earlier, stirs;
Described reinforced restir is to have pointed to add half the filler in the coating uniformly, stirs after 30 minutes, adds skimmer, flow agent, scratching resistant restir then 40 minutes;
Described reinforced again restir is meant that continuing to add remaining filler and red iron oxide stirs and get final product.
3. according to the said a kind of Computer Facilities epoxy flooring coating of claim 1, it is characterized in that floor construction thickness is 2.0～5.0mm.