CN102408605A - Environmentally-friendly sanitary water contact hose and production method thereof - Google Patents
Environmentally-friendly sanitary water contact hose and production method thereof Download PDFInfo
- Publication number
- CN102408605A CN102408605A CN201110251876XA CN201110251876A CN102408605A CN 102408605 A CN102408605 A CN 102408605A CN 201110251876X A CN201110251876X A CN 201110251876XA CN 201110251876 A CN201110251876 A CN 201110251876A CN 102408605 A CN102408605 A CN 102408605A
- Authority
- CN
- China
- Prior art keywords
- touches
- water tube
- hose
- water
- tube hose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to an environmentally-friendly sanitary water contact hose and a production method thereof. The raw material formula of the water contact hose comprises the following components in parts by weight: 100 parts of base resin, 1-5 parts of silane, 0.02-0.04 part of cross-linking catalyst, 0.01-0.2 part of peroxide and 0.1-0.5 part of antioxidant. The water contact hose is prepared by extruding and processing shaping the above raw materials to obtain a pipe, and vulcanizing and cross-linking. The water contact hose has Shore A hardness of 55-95, has good corrosion resistance, cold and heat circulation resistance and aging resistance, and can achieve national sanitation requirement and pass microorganism toxicity test, therefore, the water contact hose is especially suitable for preparation of water contact internal pipes of knitted pipes or sprinkler pipes.
Description
Technical field
The present invention relates to a kind of water tube hose and working method thereof touched; The silane crosslinking polyolefin elastic body that is particularly related to the environmentally-friendly sanitary of a kind of Shao A hardness in 55 ~ 95 scopes touches water tube hose; It can be through the test of mikrobe toxicity; Have more outstanding sanitation performance, be especially suitable for use as the pipe in the water that touches of braided tube, flower sprinkling tube etc.
Background technology
Braided tube that
are traditional or flower sprinkling tube can use terpolymer EP rubber (EPDM) sebific duct or SE (PVC) sebific duct to do usually and touch pipe in the water.These touch, and there is number of drawbacks in pipe in the water; Little etc. if any peculiar smell, loss of properties on aging, use temperature scope, the most important thing is not environmental protection of EPDM or PVC material itself, pvc material self is chloride; And EPDM also can add multiple harmful additive etc. in the course of processing; Ooze out polluted-water easily, the braided tube or the flower sprinkling tube that therefore use these materials to process generally all do not reach sanitary index, are difficult to test through mikrobe toxicity.
silane crosslinking polyolefin elastic body material has attracted more and more people's research and use owing to have good low-temperature resistance, performance such as wear-resisting, ageing-resistant and corrosion-resistant and excellent bending property.There is patent report that the silane crosslinking polyolefin elastic material is used as cable insulation, obtained the flexible insulation cable.Many pieces of patent reports are also arranged about the preparing method's of silicane cross-linking polyolefin composition research and about the research of other physicochemical properties of silane cross-linked polyolefin material and improvement etc., but the report of the toxicity aspect of still unmatchful silane cross-linked polyolefin material and the report of the research in the pipe in the water that touches that is applied to high braided tube of hygienic requirements or flower sprinkling tube at present
Summary of the invention
technical problem to be solved by this invention be overcome braided tube in the prior art or flower sprinkling tube touch that pipe does not reach the defective of hygienic requirements in the water, a kind of water tube hose that touches of environmentally-friendly sanitary is provided.
another object of the present invention provides the above-mentioned working method of touching water tube hose.
the 3rd purpose of the present invention is that the above-mentioned water tube hose that touches is used for touching in the water of braided tube or flower sprinkling tube and manages, and makes the braided tube or the flower sprinkling tube product that have outstanding sanitation performance, can not polluted water.
For solving above technical problem, the present invention takes following technical scheme:
A kind of environmentally-friendly sanitary touch water tube hose, make through vulcanization crosslinking again through extruding machine-shaping, in parts by weight, prepare this composition of raw materials that touches water tube hose and be:
Matrix resin 100
Silane 1 ~ 5
Crosslinking catalyst 0.02 ~ 0.4
Superoxide 0.01 ~ 0.2
Oxidation inhibitor 0.1 ~ 0.5
Wherein, said matrix resin is that polyolefin elastomer and polyvinyl resin are with any part by weight blended mixture;
Said silane is vinyltrimethoxy silane or vinyltriethoxysilane or both combinations;
Said crosslinking catalyst is dibutyl tin laurate or two LAURIC ACID 99 MIN dioctyl tins;
Said superoxide is 2,5-dimethyl--2,5-bis(t-butylperoxy) hexane;
said oxidation inhibitor is four [methylene β-(3, the 5-di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester and combination of 1 ~ 2:1 by weight proportion of diphosphorous acid pentaerythritol stearic acid ester 2.
preferably, in the said matrix resin, by weight, polyolefin elastomer: the ratio of polyvinyl resin is between 0.82 ~ 0.45.
preferably, said polyolefin elastomer is the combination of 0 ~ 2:0 ~ 2:1 by weight proportion of ethylene propylene copolymer, POE and ethylene-butylene copolymer.
preferably, the density of said polyvinyl resin between 0.90 ~ 0.97, melting index<20g/10min.
The working method of touching water tube hose of above-mentioned environmentally-friendly sanitary comprises the steps:
(1), raw material is prepared: the consumption proportion by each component in the composition of raw materials takes by weighing each component;
(2), the preparation of A material: behind the oxidation inhibitor thorough mixing with the superoxide of the silane of the matrix resin of 92% ~ 98% formula ratio, formula ratio, formula ratio, 45% ~ 55% formula ratio; In forcing machine, carry out extruding pelletization; The granulation melt temperature is 110 ~ 220 ℃; The gained plastic pellet is the A material through drying;
(3), the preparation of B material: will remain formula ratio matrix resin, formula ratio crosslinking catalyst and remain the oxidation inhibitor thorough mixing of formula ratio after; In forcing machine, carry out extruding pelletization; The granulation melt temperature is 110 ~ 170 ℃, and the gained plastic pellet is the B material through drying;
(4), extrusion moulding: with step (2) gained A material, step (3) gained B material and an amount of look mother thorough mixing in blender, then compound is added forcing machine and carry out extrusion moulding, process tubing;
(5), vulcanization crosslinking: step (4) gained tubing is vulcanized through the water-bath of vapor bath or 40 ~ 90 ℃, and curing time is 10 ~ 24 hours, accomplishes cross-linking process, promptly gets the said water tube hose that touches.
The water tube hose processing of polishing is further touched with the present invention in
, can be used as to touch that pipe is applied on braided tube or the flower sprinkling tube in the water.
Because the enforcement of above technical scheme, the present invention compared with prior art has following advantage:
the present invention touch water tube hose and have good anti-corrosion, cold-resistant thermal cycling property and ageing-resistant performance, and Shao A hardness has good elasticity and snappiness between 55 ~ 95; Simultaneously, the present invention touches water tube hose and can reach the national health requirement and pass through the test of mikrobe toxicity, therefore is particularly suitable for making the pipe in the water that touches of braided tube or flower sprinkling tube.
Embodiment
are done further detailed explanation below in conjunction with concrete embodiment to the present invention, but are not limited to these embodiment.
Embodiment 1 ~ 8
The composition of raw materials that touches water tube hose of
embodiment 1 ~ 8 is seen table 1.
The composition of raw materials that touches water tube hose of table 1 embodiment 1 ~ 8
Among
above embodiment, employed polyolefin elastomer is the combination of 0 ~ 2:0 ~ 2:1 by weight proportion of ethylene propylene copolymer, POE and ethylene-butylene copolymer; Silane is vinyltrimethoxy silane; Crosslinking catalyst is two LAURIC ACID 99 MIN dioctyl tins; Superoxide is 2,5-dimethyl--2,5-bis(t-butylperoxy) hexane; Oxidation inhibitor is four [methylene β-(3, the 5-di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester and combination of 1 ~ 2:1 by weight proportion of diphosphorous acid pentaerythritol stearic acid ester 2.
Above-mentioned each embodiment all produces as follows and touches water tube hose, and step is:
(1), raw material is prepared: the consumption proportion by each component in the composition of raw materials takes by weighing each component;
(2), the preparation of A material: behind the oxidation inhibitor thorough mixing with the superoxide of the silane of the matrix resin of 92% ~ 98% formula ratio, formula ratio, formula ratio, 45% ~ 55% formula ratio; In forcing machine, carry out extruding pelletization; The granulation melt temperature is 110 ~ 220 ℃; The gained plastic pellet is the A material through fluidized drying;
(3), the preparation of B material: will remain formula ratio matrix resin, formula ratio crosslinking catalyst and remain the oxidation inhibitor thorough mixing of formula ratio after; In forcing machine, carry out extruding pelletization; The granulation melt temperature is 110 ~ 170 ℃, and the gained plastic pellet is the B material through fluidized drying;
(4), extrusion moulding: with step (2) gained A material, step (3) gained B material and an amount of look mother thorough mixing in blender, then compound is added forcing machine and carry out extrusion moulding, process tubing; The look female female product of the nontoxic look of food grade of selecting only plays the toning effect, and consumption accounts for 0 ~ 2% of whole machining process material total amount;
(5), vulcanization crosslinking: step (4) gained tubing is vulcanized through the water-bath of vapor bath or 40 ~ 90 ℃; Curing time is 10 ~ 24 hours; Accomplish cross-linking process, promptly obtain the water tube hose that touches of silane crosslinking polyolefin elastic body material.
Embodiment 9
Among
embodiment 1 ~ 8; Embodiment 3 prepared Shao A hardness of touching water tube hose are between 85 ~ 81; Be fit to make the pipe in the water that touches of flower sprinkling tube or braided tube the most, therefore the water tube hose that touches to embodiment 3 gained carries out the physicochemical property test, and the result is shown in table 2.
Table 2 embodiment 3 gained touch the The performance test results of water tube hose
Embodiment 10
The embodiment 3 prepared water tube hoses that touch are carried out the health detection, and examination criteria is GB/T 17219-1998 " the safety evaluation standard of Drinking Water transmission & distribution wetting system and protective material ", and assay is as shown in table 3:
Table 3 embodiment 3 gained touch the health detected result of water tube hose
Continuous table 3
Mikrobe toxicity test is carried out to the water tube hose that touches of embodiment 3 gained in addition in
, and the result is qualified.
are touched water tube hose with this and were soaked in respectively in methyl alcohol, acetone, hydrochloric acid, sulfuric acid, nitric acid and the sodium hydroxide solution 180 days, and material does not have xanthochromia and crack performance takes place.
can be known by above test result; The water tube hose that touches that silane crosslinking polyolefin elastic body material of the present invention is processed not only has good ageing-resistant, corrosion resistance nature; And have very outstanding sanitation performance, therefore can substitute the pipe use in the water of touching of existing terpolymer EP rubber (EPDM) sebific duct or SE (PVC) sebific duct as braided tube or flower sprinkling tube.
More than the present invention has been done detailed description; Its purpose is to let the personage that is familiar with this art can understand content of the present invention and implements; Can not limit protection scope of the present invention with this; All equivalences of doing according to spirit of the present invention change or modify, and all should be encompassed in protection scope of the present invention
Claims (7)
- An environmentally-friendly sanitary touch water tube hose, it is characterized in that: in parts by weight, the said composition of raw materials that touches water tube hose is:Matrix resin 100Silane 1 ~ 5Crosslinking catalyst 0.02 ~ 0.4Superoxide 0.01 ~ 0.2Oxidation inhibitor 0.1 ~ 0.5Wherein, said matrix resin is that polyolefin elastomer and polyvinyl resin are with any part by weight blended mixture;Said silane is vinyltrimethoxy silane or vinyltriethoxysilane or both combinations;Said crosslinking catalyst is dibutyl tin laurate or two LAURIC ACID 99 MIN dioctyl tins;Said superoxide is 2,5-dimethyl--2,5-bis(t-butylperoxy) hexane;Said oxidation inhibitor is four [methylene β-(3, the 5-di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester and combination of 1 ~ 2:1 by weight proportion of diphosphorous acid pentaerythritol stearic acid ester 2;The said water tube hose that touches is extruded machine-shaping through above-mentioned raw materials, makes through vulcanization crosslinking again.
- 2. the water tube hose that touches according to claim 1 is characterized in that: in the said matrix resin, by weight, polyolefin elastomer: the ratio of polyvinyl resin is between 0.82 ~ 0.45.
- 3. the water tube hose that touches according to claim 1 is characterized in that: said polyolefin elastomer is the combination of 0 ~ 2:0 ~ 2:1 by weight proportion of ethylene propylene copolymer, POE and ethylene-butylene copolymer.
- 4. the water tube hose that touches according to claim 1 is characterized in that: the density of said polyvinyl resin between 0.90 ~ 0.97, melting index<20g/10min.
- 5. the described working method of touching water tube hose of each claim in the claim 1 ~ 4 is characterized in that: comprise the steps:(1), raw material is prepared: the consumption proportion by each component in the composition of raw materials takes by weighing each component;(2), the preparation of A material: behind the oxidation inhibitor thorough mixing with the superoxide of the silane of the matrix resin of 92% ~ 98% formula ratio, formula ratio, formula ratio, 45% ~ 55% formula ratio; In forcing machine, carry out extruding pelletization; The granulation melt temperature is 110 ~ 220 ℃; The gained plastic pellet is the A material through drying;(3), the preparation of B material: will remain formula ratio matrix resin, formula ratio crosslinking catalyst and remain the oxidation inhibitor thorough mixing of formula ratio after; In forcing machine, carry out extruding pelletization; The granulation melt temperature is 110 ~ 170 ℃, and the gained plastic pellet is the B material through drying;(4), extrusion moulding: with step (2) gained A material, step (3) gained B material and an amount of look mother thorough mixing in blender, then compound is added forcing machine and carry out extrusion moulding, process tubing;(5), vulcanization crosslinking: step (4) gained tubing is vulcanized through the water-bath of vapor bath or 40 ~ 90 ℃, and curing time is 10 ~ 24 hours, accomplishes cross-linking process, promptly gets the said water tube hose that touches.
- In the claim 1 ~ 4 the described water tube hose that touches of each claim as touching in the water pipe in the application in braided tube or flower sprinkling tube field.
- 7. what the described working method of claim 5 made touches water tube hose as touching the application of managing in the water in braided tube or flower sprinkling tube field.