CN102373782A - Floor synthesized by double-layer plant fiber and plastic - Google Patents
Floor synthesized by double-layer plant fiber and plastic Download PDFInfo
- Publication number
- CN102373782A CN102373782A CN201010248322XA CN201010248322A CN102373782A CN 102373782 A CN102373782 A CN 102373782A CN 201010248322X A CN201010248322X A CN 201010248322XA CN 201010248322 A CN201010248322 A CN 201010248322A CN 102373782 A CN102373782 A CN 102373782A
- Authority
- CN
- China
- Prior art keywords
- parts
- double
- floor
- plastic
- auxiliary material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to a PVC (polyvinyl chloride) floor and particularly relates to a floor synthesized by double-layer plant fiber and plastic. The floor synthesized by double-layer plant fiber and plastic is characterized by being formed by a double-layer structure, wherein the auxiliary material forms a surface layer, and the main material forms a bottom layer; the main material comprises the following components in parts by weight: 100-120 parts of PVC resin, 100-200 parts of wood fiber, 8-10 parts of dimethyl bis-isooctyl thioglycolate, 25-30 parts of dioctyl phthalate, 11-15 parts of ethoxylate aliphatic alkylamine and 10 parts of paraffin; and the auxiliary material comprises the following components in parts by weight: 100-120 parts of PVC resin, 10-12 parts of MBS resin, 3-5 parts of zinc stearate, 4-6 parts of dibutyl phthalate, 5-8 parts of tribasic lead sulfate and 2-4 parts of di-tert-butyl hydroquinone. The floor provided by the invention has the advantages of environment friendliness, low cost, high tenacity, good thermal performance and the like.
Description
Technical field
The invention belongs to the PVC floor, the floor that particularly double-deck string and plastics are synthetic.
Background technology
Along with the high speed development of science and technology, the Application and Development of new material will become one of emphasis of 21 century China's technical development.In recent years, along with the enhancing of environmental consciousness in the global range and national governments strengthen the safeguard measure to natural environment, make the scientific research personnel have to develop towards material and this direction of environment coordination to the design of material.The natural polymer string more and more causes people's attention as the potential advantages of reinforcing material.See with regard to raw-material utilization and final processing aspect, derive from year growing plants fiber and no matter still all can not cause injurious effects environment as the reinforcing material of thermosetting plastics as the reinforcing material of thermoplastic; The string reinforcing material is compared with conventional plastic filler such as glass fiber French chalk; Have the high and low cost of specific strength, density low (all lower), high tenacity than all inorfils, good thermal property, draw ratio is big, specific area is big, under specific process conditions, also can form advantage such as biodegradation it and the formed composite product of thermoplastic blend have light weight, inexpensive, processability good, the advantages such as little, renewable and degradable to the production equipment wearing and tearing; This is that other any materials are incomparable, thereby has broad application prospects in a lot of fields.The present invention provides a kind of novel double-layer string and plastics synthetic floor, has environmental protection, low cost, high tenacity, good advantages such as thermal property.
Summary of the invention
Goal of the invention
The present invention provides a kind of double-deck string and plastics synthetic floor, environmental protection, low cost, high tenacity, good thermal property.
Technical scheme
The floor that a kind of double-deck string and plastics are synthetic is characterized in that being made up of double-decker, and auxiliary material is formed the top layer, and major ingredient constitutes bottom; By weight,
The major ingredient prescription is: Corvic 100-120 part, wood fiber 100-200 part, dimethyl dimercapto 2-ethyl hexyl ethanoate tin 8-10 part, phthalic acid two hot vinegar 25-30 parts, the alkylamine 11-15 of ethoxylated fat family part, 10 parts in paraffin;
The prescription of auxiliary material is: Corvic 100-120 part, MBS resin 10-12 part, zinc stearate 3-5 part, dibutyl phthalate 4-6 part, lead sulfate tribasic 5-8 part, di-tert-butyl hydroquinone's resin 2-4 part.
The preparation technology on the floor that a kind of double-deck string and plastics are synthetic:
A, batch mixing mix above-mentioned prescription;
B, mixing: on two roller plastics processing mills that the PVC plasticizing is even; Temperature is about 140-160;
C, extrude: extrude by foamed plastic extruder and co-extrusion machine pressure after the mixing completion of major ingredient and auxiliary material, wherein about temperature 140-160, pressure 180-200kg/cm
2
D, synthetic double-deck processing typing, warp cooling traction again;
E, finished product.
Beneficial effect
1, the present invention adopts string to replace traditional filler such as kaolin etc.; Because string has natural toughness; Make that the moral floor that generates has excellent toughness and intensity, utilize string and plastic processing production floor simultaneously, utilize the product of PVC/ fiber composite that preferable performance is arranged; Like environmental protection, low cost, high tenacity, good thermal property, can satisfy the quality requirement of certified products.
2, the present invention adopts double-decker, and surface structure adopts the bigger prescription of intensity, has and resistance to wears, characteristics such as resistance to compression.
The specific embodiment
Embodiment 1
A kind of double-decker antistatic polyvinyl chloride plastic floor is characterized in that being made up of double-decker, and auxiliary material is formed the top layer, and major ingredient constitutes bottom; By weight,
The major ingredient prescription is: Corvic 100kg, wood fiber 100kg, dimethyl dimercapto 2-ethyl hexyl ethanoate tin 8kg, phthalic acid two hot vinegar 25kg, the alkylamine 11kg of ethoxylated fat family, paraffin 10kg;
The prescription of auxiliary material is: Corvic 100kg, MBS resin 10kg, zinc stearate 3kg, dibutyl phthalate 4kg, lead sulfate tribasic 5kg, di-tert-butyl hydroquinone's resin 2kg.
The preparation technology on the floor that a kind of double-deck string and plastics are synthetic:
A, batch mixing mix above-mentioned prescription;
B, mixing: on two roller plastics processing mills that the PVC plasticizing is even; Temperature is about 140-160;
C, extrude: extrude by foamed plastic extruder and co-extrusion machine pressure after the mixing completion of major ingredient and auxiliary material, wherein about temperature 140-160, pressure 180-200kg/cm
2
D, synthetic double-deck processing typing, warp cooling traction again;
E, finished product.
Embodiment 2
A kind of double-decker antistatic polyvinyl chloride plastic floor is characterized in that being made up of double-decker, and auxiliary material is formed the top layer, and major ingredient constitutes bottom; By weight,
The major ingredient prescription is:: Corvic 120kg, wood fiber 200kg, dimethyl dimercapto 2-ethyl hexyl ethanoate tin 10kg, phthalic acid two hot vinegar 30kg, the alkylamine 15kg of ethoxylated fat family, paraffin 10kg.
The prescription of auxiliary material is: Corvic 120kg, MBS resin 12kg, zinc stearate 5kg, dibutyl phthalate 6kg, lead sulfate tribasic 8kg, di-tert-butyl hydroquinone's resin 4kg.
The preparation technology on the floor that a kind of double-deck string and plastics are synthetic:
A, batch mixing mix above-mentioned prescription;
B, mixing: on two roller plastics processing mills that the PVC plasticizing is even; Temperature is about 140-160;
C, extrude: extrude by foamed plastic extruder and co-extrusion machine pressure after the mixing completion of major ingredient and auxiliary material, wherein about temperature 140-160, pressure 180-200kg/cm
2
D, synthetic double-deck processing typing, warp cooling traction again;
E, finished product.
Claims (1)
1. the synthetic floor of double-deck string and plastics is characterized in that being made up of double-decker, and auxiliary material is formed the top layer, and major ingredient constitutes bottom; By weight,
The major ingredient prescription is: Corvic 100-120 part, wood fiber 100-200 part, dimethyl dimercapto 2-ethyl hexyl ethanoate tin 8-10 part, phthalic acid two hot vinegar 25-30 parts, the alkylamine 11-15 of ethoxylated fat family part, 10 parts in paraffin;
The prescription of auxiliary material is: Corvic 100-120 part, MBS resin 10-12 part, zinc stearate 3-5 part, dibutyl phthalate 4-6 part, lead sulfate tribasic 5-8 part, di-tert-butyl hydroquinone's resin 2-4 part.