CN102367332A - Method for manufacturing polarized lens for increasing buoy definition - Google Patents
Method for manufacturing polarized lens for increasing buoy definition Download PDFInfo
- Publication number
- CN102367332A CN102367332A CN201010589741XA CN201010589741A CN102367332A CN 102367332 A CN102367332 A CN 102367332A CN 201010589741X A CN201010589741X A CN 201010589741XA CN 201010589741 A CN201010589741 A CN 201010589741A CN 102367332 A CN102367332 A CN 102367332A
- Authority
- CN
- China
- Prior art keywords
- eyeglass
- cleaning
- liquid medicine
- toner
- polarized lenses
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a TAC (triacetyl cellulose) polarized lens for increasing the buoy definition which is the contrast ratio among red, green and yellow, and a manufacturing method thereof. A coloring agent comprises red toner, a white liquid medicine, a yellow liquid medicine and a black liquid medicine, wherein the red toner is a high efficiency emulsification stabilizing agent, and is a special coloring toner for the TAC polarized lens, and the liquid medicines are special coloring liquid medicines for the TAC polarized lens. The method for manufacturing the lens comprises the following steps: 1, cleaning the lens; 2, removing a membrane and cleaning; 3, removing oil from the membrane removed lens, drying, and detecting; 4, cleaning, putting the lens in a coloring agent to plate a color, and examining; and 5, drying, reinforcing, and drying again. The method of the invention has the following beneficial effects: a defect that a common polarized lens which only filters light cannot increase the contrast of assigned light is substantially improved after the common polarized lens is colored by the mixed dye according to a ratio shown in the specification, and especially the contrast ratio of common colors of buoys is improved, so the sensitivity and the reaction capability of naked eyes on subtle changes of the buoys are increased.
Description
Technical field
The present invention relates to a kind of method of manufacture that can be used to increase the polarized lenses of buoy sharpness, improved the clear degree that increases of the type polarized lenses well.
Background technology
Go fishing on the water surface in the sun, light during by water-reflected part produced dazzle by polarization.The negative role of dazzle--highlight, weaken colorimetric purity; It is unclear that contour of object is thickened, and makes glasses tired, uncomfortable.During fishing buoy color commonly used be red, yellow, green, black alternately, multicoloured buoy is difficult to differentiate sound more on the water surface that gleams of light are reflecting on waves in the river, the polaroid utilization is processed according to the polarization theory of light, has the specific function of imitating the elimination dazzle.The color of common polaroid is basically by grey, green, the brown composition, though can filter dazzle, reduction degree and intensification contrast gradient for color especially manifest for the requirement that increases the color sharpness in the buoy and just seem helpless.
Through spectrometer analysis, the particular color that increases clear eyeglass optionally sops up the light wave of some specific wavelengths, to strengthen the visual effect of the color on visible light, promptly strengthens the contrast of color such as redness and yellow in the buoy; The sharpness of increase buoy color that can maximum ratio,
Summary of the invention
The objective of the invention is to reach in the fishing process, deepen versicolor contrast gradient and boldness in the buoy.Improve the sensitivity response ability that naked eyes change buoy.
The present invention is achieved in that a kind of polarized lenses that can increase red, green, yellow contrast gradient, and the eyeglass staining agent is made up of red toner and white, yellow, black three kinds of liquid medicine.Wherein: red toner is a kind of emulsion stabilizer efficiently, is TAC polarized lenses special dyeing toner.Described liquid medicine is TAC polarized lenses special dyeing liquid medicine.Described TAC polarized lenses is triacetate fiber fat (Triacetyl cellulose) polarized lenses,
The manufacturing step of polarized lenses of the present invention is following:
(1) cleaning eyeglass;
(2) membrane removal and cleaning;
(3) demoulding eyeglass deoils, dries and detects;
(4) put into staining agent plating look and check after the cleaning;
(5) oven dry, reinforcement, oven dry once more.
Useful result of the present invention is: after the mixing colouring agent dyeing through this kind proportioning; Having improved common polarized lenses greatly only filters; But can't increase the defective of specifying the light contrast gradient; Especially increased the contrast gradient of color commonly used in the buoy, made naked eyes increase sensitivity response ability the slight change of buoy.
Embodiment
The present invention is a kind of polarized lenses that can increase red, green, yellow contrast gradient, and the staining agent of eyeglass is made up of red toner and white, yellow, black three kinds of liquid medicine.Wherein: the weight ratio of red toner, baiyao water, xanthate water, black powder water is 5: 38: 18: 17.Described red toner is a kind of emulsion stabilizer efficiently: XG 550, chemical formula: C15H1106 with amino acetanilide diazotization, with the acetyl H acid coupling, saltouts and gets, and is TAC polarized lenses special dyeing toner, can buy in the dyestuff market.Described liquid medicine is TAC polarized lenses special dyeing liquid medicine, and wherein baiyao water is the phenylcarbinol aqueous solution, and mass concentration is 95%; Yellow syrup is the p-diaminodiphenyl azo aqueous solution, and mass concentration is 80%; Black liquid medicine is the toluylene aqueous solution, and mass concentration is 85%.Described TAC polarized lenses is triacetate fiber fat (Triacetyl cellulose) polarized lenses.
Method of manufacture of the present invention is specially:
(1), at first put into cleaning box to the polarisation white eyeglass that shears specification, with conventional mobile filter cleaning water under the temperature of 0-30 degree, mobile cleaning 2 hours.
(2), by taking out the porilized lens base that has cleaned the band protective membrane in the cleaning box; Change in full-automatic " Poly comes the membrane removal machine "; Remove the upper and lower two membranes on the polarized lenses by artificial semi-automation, put into mobile filter cleaning case once more, clean 0.5 hour at normal temperatures.
(3), put into the demoulding and the eyeglass that cleaned the aqueous solution of mass concentration 5% sodium hydroxide; In 40 degree temperature, cleaned 6 minutes, remove the greasy dirt on the eyeglass, put into baking oven then; Temperature with 60 degree was dried by the fire 2 hours; The check of entering testing procedures, it is no abnormal, smooth to reach lens surface through check, surface contact angle 14 degree.
(4), the good after eyeglass of check of baking, with conventional mobile filter cleaning liquid cleaning, it is poor to put into the plating look that mixes up dyestuff then once more.Plating look groove need be allocated dyestuff in advance: add clear water 80KG earlier; Be warmed to about 85 ± 5 ℃, in the whipping process that does not stop, add staining agent then, at first add red toner 500 grams and stir; Add black powder water 1700ml after about 1 hour; Add xanthate water 1800ml after half a hour, after 2 hours, add baiyao water 3800ml, restir mixed up dyestuff in 4 hours.After eyeglass is put into plating look groove, can not stir, liquid medicine can slowly be penetrated into the eyeglass the inside.The dyeing duration is 2 fens kinds, plates look, and then gets into testing procedures, will reach the apparent no toner accumulation of eyeglass, good evenness, surface contact angle 40 degree through check.
The eyeglass that will plate once more (5), at last behind the look is put into baking oven, dries by the fire 3 hours with the temperature of 60 degree.Put into the good eyeglass of baking and strengthen on the stiffened machine, carry out upper and lower reinforcement, the stiffened solution ratio: concentration is 18 kilograms of 100% triacetate fiber fat (TAC) polarized lenses reinforced solutions, and it is even that 1.6 kilograms of absolute ethyl alcohols carry out agitation and dilution.Enhanced time is 30 minutes, and then puts into baking oven, dries by the fire 4 hours with the temperature of 80 degree, takes out and promptly produces required polarized lenses.
Embodiment:
Get the polarisation white eyeglass that shears specification from fixed temperature and humidity eyeglass storehouse, put into cleaning box to the polarisation white eyeglass that shears specification, under the temperature of 0-30 degree, clean 2 hours with conventional mobile filter cleaning liquid.In by cleaning box, take out the porilized lens base that has cleaned the band protective membrane; Change in full-automatic " Poly comes the membrane removal machine "; Remove the upper and lower two membranes on the polarized lenses by artificial semi-automation, put into mobile filter cleaning case once more, clean 0.5 hour at normal temperatures.Cleaning the eyeglass of demoulding, put into the aqueous solution that contains 5% sodium hydroxide, in 40 degree temperature, cleaned 6 minutes, remove the greasy dirt on the eyeglass, put into baking oven then, dried by the fire 2 hours with the temperature of 60 degree.The good eyeglass of baking, with conventional mobile filter cleaning liquid cleaning, it is poor to put into the plating look that mixes up dyestuff then once more; Plating look groove need be allocated dyestuff in advance: add clear water 80KG earlier, be warmed to about 85 ± 5 ℃, add red toner 500 grams then and stir; Add black powder water 1700ml after about 1 hour; Add xanthate water 1800ml after half a hour, after 2 hours, add baiyao water 3800ml, restir mixed up dyestuff in 4 hours; Eyeglass can not stir after putting into plating look groove, and liquid medicine can slowly be penetrated into the eyeglass the inside.The dyeing duration is 2 fens kinds, plates look, can plate out the color of approval.And then put into baking oven, dried by the fire 3 hours with the temperature of 60 degree.Put into the good eyeglass of baking and strengthen on the stiffened machine, carry out upper and lower reinforcement, and then put into baking oven 80 and spend, dried by the fire 4 hours, take out and to reach the effect of oneself wanting.Dyeing back transmittance: 2#; UV400: through; Red transmitance: 60.13%; Yellow transmitance: 43.42%; Green transmitance: 24.75%; The apparent no toner of eyeglass is piled up, good evenness, stiffened hardness 3.5H.
Claims (5)
1. staining agent that can increase the polarized lenses of red, green, yellow contrast gradient; Form by red toner and white, yellow, black three kinds of liquid medicine; Wherein: red toner is a kind of emulsion stabilizer efficiently; Be TAC polarized lenses special dyeing toner, described liquid medicine is TAC polarized lenses special dyeing liquid medicine.
2. staining agent according to claim 1, wherein: the weight ratio of red toner, baiyao water, xanthate water, black powder water is 5: 38: 18: 17.Described red toner is a kind of emulsion stabilizer efficiently: XG 550, and chemical formula: C15H1106 with amino acetanilide diazotization, with the acetyl H acid coupling, saltouts and gets, and is TAC polarized lenses special dyeing toner, can buy in the dyestuff market; Described liquid medicine is TAC polarized lenses special dyeing liquid medicine, and wherein baiyao water is the phenylcarbinol aqueous solution, and mass concentration is 95%; Yellow syrup is the p-diaminodiphenyl azo aqueous solution, and mass concentration is 80%; Black liquid medicine is the toluylene aqueous solution, and mass concentration is 85%.
3. method of manufacture that can increase the polarized lenses of red, green, yellow contrast gradient, its manufacturing step is following:
(1) cleaning eyeglass; (2) membrane removal and cleaning; (3) demoulding eyeglass deoils, dries and detects; (4) put into staining agent plating look and check after the cleaning; (5) oven dry, reinforcement, oven dry once more.
4. method of manufacture according to claim 3 is specially:
(1), at first put into cleaning box to the polarisation white eyeglass that shears specification, with conventional mobile filter cleaning water under the temperature of 0-30 degree, mobile cleaning 2 hours;
(2), by taking out the porilized lens base that has cleaned the band protective membrane in the cleaning box; Change in full-automatic " Poly comes the membrane removal machine "; Remove the upper and lower two membranes on the polarized lenses by artificial semi-automation, put into mobile filter cleaning case once more, clean 0.5 hour at normal temperatures;
(3), put into the demoulding and the eyeglass that cleaned the aqueous solution of mass concentration 5% sodium hydroxide; In 40 degree temperature, cleaned 6 minutes, remove the greasy dirt on the eyeglass, put into baking oven then; Temperature with 60 degree was dried by the fire 2 hours; The check of entering testing procedures, it is no abnormal, smooth to reach lens surface through check, surface contact angle 14 degree;
(4), the good after eyeglass of check of baking, with conventional mobile filter cleaning liquid cleaning, it is poor to put into the plating look that mixes up dyestuff then once more.Plating look groove need be allocated dyestuff in advance: add clear water 80KG earlier; Be warmed to about 85 ± 5 ℃, in the whipping process that does not stop, add staining agent then, at first add red toner 500 grams and stir; Add black powder water 1700ml after about 1 hour; Add xanthate water 1800ml after half a hour, after 2 hours, add baiyao water 3800ml, restir mixed up dyestuff in 4 hours.After eyeglass is put into plating look groove, can not stir, liquid medicine can slowly be penetrated into the eyeglass the inside.The dyeing duration is 2 fens kinds, plates look, and then gets into testing procedures, will reach the apparent no toner accumulation of eyeglass, good evenness, surface contact angle 40 degree through check;
The eyeglass that will plate once more (5), at last behind the look is put into baking oven, dries by the fire 3 hours with the temperature of 60 degree.Put into the good eyeglass of baking on the reinforcement stiffened machine; Carry out upper and lower reinforcement, the stiffened solution ratio: concentration is 18 kilograms of 100% triacetate fiber fat (TAC) polarized lenses reinforced solutions, and it is even that 1.6 kilograms of absolute ethyl alcohols carry out agitation and dilution; Enhanced time is 30 minutes; And then put into baking oven, and dried by the fire 4 hours with the temperature of 80 degree, take out and promptly produce required polarized lenses.
5. according to claim 3,4 described method of manufacture, transmittance: 2# behind the eyeglass plating look behind the plating look; UV400: through; Red transmitance: 60.13%; Yellow transmitance: 43.42%; Green transmitance: 24.75%; The apparent no toner of eyeglass is piled up, good evenness, stiffened hardness 3.5H.