CN102367212A - Water mixed high temperature daub - Google Patents
Water mixed high temperature daub Download PDFInfo
- Publication number
- CN102367212A CN102367212A CN2011102645498A CN201110264549A CN102367212A CN 102367212 A CN102367212 A CN 102367212A CN 2011102645498 A CN2011102645498 A CN 2011102645498A CN 201110264549 A CN201110264549 A CN 201110264549A CN 102367212 A CN102367212 A CN 102367212A
- Authority
- CN
- China
- Prior art keywords
- daub
- matrix
- mass ratio
- water mixed
- mixed high
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses water mixed high temperature daub which comprises a matrix and a binder. According to the invention, the mass ratio of the matrix to the binder is 7-8:3; the matrix comprises high-alumina clinker powder, alumina clinker micro powder and bentonite; the binder comprises binding clay, modified starch and sodium tripolyphosphate; the mass ratio of high-alumina clinker powder to alumina clinker micro powder to bentonite is 5:3:1; the mass ratio of binding clay to modified starch to sodium tripolyphosphate is 1:2:5. The technical effects of the invention are as follows: the water mixed high temperature daub has sufficient strength at normal temperature and increasingly greater strength with the rise of temperature of a heated kiln; the advantages of a simple production process and low cost are obtained; colloid is not used as an adhesive; when the daub is used, denseness of the daub is controlled through addition amount of tap water according to a construction method and the situation of the kiln.
Description
Technical field
The present invention relates to a kind of material of construction, specifically is a kind of Water mixed high-temp. daub.
Background technology
Much more very confirmed in production plant by sub-clay denseness, but because user's stove kind and constructional method are different, and also different to the requirement of denseness, tired denseness can not be adjusted, bring inconvenience to the user, use range is limited, and makes troubles to transportation.
Summary of the invention
In order to overcome above-mentioned defective, the invention provides a kind of normal temperature and promptly produce sufficient intensity, the Water mixed high-temp. daub that after heating, also rises with kiln temperature rising intensity.
Technical scheme of the present invention is achieved in that a kind of Water mixed high-temp. daub, is made up of matrix and tackiness agent, and the mass ratio of said matrix and tackiness agent is 7-8:3, and said matrix is made up of high-alumina powder clinker, bauxite clinker micro mist and wilkinite; Said tackiness agent is made up of bonding clay, treated starch and tripoly phosphate sodium STPP.
High-alumina powder clinker, bauxite clinker micro mist and bentonitic mass ratio are 5:3:1 in the said matrix.
The mass ratio of bonding clay, treated starch and tripoly phosphate sodium STPP is 1:2:5 in the said tackiness agent.
Technique effect of the present invention is: the present invention is that a kind of normal temperature promptly produces sufficient intensity; After heating with the rising of kiln temperature; Intensity also increases thereupon; Production technique is simple, cost is low, makes tackiness agent without colloid, controls the denseness of clay during use with the amount of water of tap water according to constructional method and kiln situation.
Embodiment
A kind of Water mixed high-temp. daub is made up of matrix and tackiness agent, and the mass ratio of said matrix and tackiness agent is 8:3, and said matrix is made up of high-alumina powder clinker, bauxite clinker micro mist and wilkinite; Said tackiness agent is made up of bonding clay, treated starch and tripoly phosphate sodium STPP.High-alumina powder clinker, bauxite clinker micro mist and bentonitic mass ratio are 5:3:1 in the said matrix.The mass ratio of bonding clay, treated starch and tripoly phosphate sodium STPP is 1:2:5 in the said tackiness agent.
The above; Be merely the preferable embodiment of the present invention; But protection scope of the present invention is not limited thereto; Any technician who is familiar with the present technique field is equal to replacement or change according to technical scheme of the present invention and inventive concept thereof in the technical scope that the present invention discloses, all should be encompassed within protection scope of the present invention.
Claims (3)
1. a Water mixed high-temp. daub is characterized in that, is made up of matrix and tackiness agent, and the mass ratio of said matrix and tackiness agent is 7-8:3, and said matrix is made up of high-alumina powder clinker, bauxite clinker micro mist and wilkinite;
Said tackiness agent is made up of bonding clay, treated starch and tripoly phosphate sodium STPP.
2. Water mixed high-temp. daub according to claim 1 is characterized in that, high-alumina powder clinker, bauxite clinker micro mist and bentonitic mass ratio are 5:3:1 in the said matrix.
3. Water mixed high-temp. daub according to claim 1 is characterized in that, the mass ratio of bonding clay, treated starch and tripoly phosphate sodium STPP is 1:2:5 in the said tackiness agent.