CN102363711A - Automobile rubber protecting agent and manufacturing method thereof - Google Patents
Automobile rubber protecting agent and manufacturing method thereof Download PDFInfo
- Publication number
- CN102363711A CN102363711A CN201010588628XA CN201010588628A CN102363711A CN 102363711 A CN102363711 A CN 102363711A CN 201010588628X A CN201010588628X A CN 201010588628XA CN 201010588628 A CN201010588628 A CN 201010588628A CN 102363711 A CN102363711 A CN 102363711A
- Authority
- CN
- China
- Prior art keywords
- rubber
- automobile rubber
- automobile
- protective material
- rubber protective
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an automobile rubber protecting agent and a manufacturing method thereof. The automobile rubber protecting agent comprises the following components, by mass, 50-80% of a C8-13 aryl-free alkane, 1-10% of silicone oil, 1-10% of a silicone resin, 0.1-1% of a wetting agent, 0.05-1% of an antioxidant, 0.1-0.5% of a light stabilizer, and 20-40% of a deodorized liquefied petroleum gas. The manufacturing method comprises the following steps: 1, adding silicone oil, the silicone resin, the wetting agent, the antioxidant and an ultraviolet ray absorbent to a solvent; 2, uniformly stirring, pittng an obtained solution into an aerosol can after the complete dissolving, and 3, finally charging the deodorized liquefied petroleum gas into the aerosol can to obtain the automobile rubber protecting agent of the invention. The automobile rubber protecting agent of the invention allows the erosion of oxygen, ozone, light, heat, acid rain and the like to rubber members to be obstructed, the rubber hardening and aging to be prevented, the service time of the rubber members to be prolonged, and oil stains adhered to the rubber surface to be cleaned, so the rubber surface looks like new.
Description
Technical field
The present invention relates to a kind of maintaining agent for automobiles, relate to a kind of aerosol-type automobile rubber protective material specifically.
Background technology
Rubber part on the automobile is more relatively, and major part is to be used for sealing vehicle window and damping part, has the function of waterproof on the one hand, has sound insulation, damping, buffering function on the other hand.Along with the vehicle prolongation of duration of service; These rubber parts sclerosis that can be gradually and aging even break in case above-mentioned phenomenon occurs, just can cause poor sealing; Not only can not keep off the rain, reduce vehicle riding comfort by wind resistance, but also can cause working hour expense and Master Cost when keeping in repair higher.Although along with development of technology; Automobile has lifting by a relatively large margin with the rubber parts quality, but abominable in view of the Chinese automobile environment for use, often is parked in outdoor; Stand the roasting solarization of the hot sun; The erosion of acid rain, automobile rubber spare all can have damage in various degree after using for some time, and is therefore necessary to the maintenance of automobile rubber spare.
Cause that ageing of rubber mainly contains the factor of several aspects: oxygen, ozone, heat, light, mechanical stress, acid rain etc.Oxygen, ozone can react with radical in the rubber molecule, make molecular rupture, cause the change of rubber performance; Heat energy causes the cracking of rubber or crosslinked, quickens the aging of rubber; What in the light wave rubber is played destruction mainly is the higher ultraviolet ray of energy; The ultraviolet ray except can directly cause the rubber molecule chain break and crosslinked; Rubber produces radical because of absorbing luminous energy, causes and the promote the oxidation chain reaction process, and this its middle-ultraviolet lamp plays a part heating; Sulfuric acid, nitric acid in the acid rain have corrosive nature to rubber, shorten the work-ing life of rubber.
Summary of the invention
The object of the present invention is to provide the protectant method of manufacture of a kind of automobile rubber; Be mainly used in the automobile door and window sealing member; Rubber parts such as automobile shock parts make automobile rubber spare avoid the erosion of oxygen, ozone, light, heat, acid rain, protect rubber lastingly; Stop the rubber sclerosis with aging, prolong rubber parts duration of service.
The technical scheme that the present invention adopted is:
To ageing of rubber mechanism,, thereby reach the aged effect of maintaining or delaying automobile rubber spare from the destruction of these factors of many aspects blocking-up to rubber parts.Dimethyl silicone oil, silicone resin have excellent hydrophobic property, can completely cut off acid rain, and silicone resin has certain film-forming properties, can protect rubber parts lastingly; UV light absorber can absorb the damaging ultraviolet ray of rubber; Oxidation inhibitor then can be resisted the erosion to rubber of airborne oxygen, ozone.
Automobile rubber protective material of the present invention comprises following component: solvent, dimethyl silicone oil, silicone resin, wetting agent, UV light absorber, oxidation inhibitor, deodorization LPG liquefied petroleum gas.The mass percent of each component is following:
Solvent 50-80%
Dimethyl silicone oil 1-10%
Silicone resin 1-10%
Wetting agent 0.1-1%
Oxidation inhibitor 0.05-1%
UV light absorber 0.1-0.5%
Deodorization LPG liquefied petroleum gas 20-40%
Described solvent can be that C8-C13 does not have the aralkyl hydrocarbon, and C8-C13 does not have fragrant straight-chain paraffin, isomerization alkanes or naphthenic hydrocarbon.
Described dimethyl-silicon oil viscosity be 100-20000 (25 ℃, mm
2/ s).
Described silicone resin can be one or more in amino silicone, high light silicone resin, the fluorine silicon resin.
Described wetting agent is polyether-modified polysiloxane-based wetting agent.
Described oxidation inhibitor can be one or more in Hinered phenols antioxidant or the aromatic amine oxidation inhibitor.
Described UV light absorber is that UV531 or UV770 or both are used.
Automobile rubber protective material of the present invention has following characteristics:
1. make automobile rubber spare avoid the erosion of oxygen, ozone, light, heat, acid rain etc., protect rubber lastingly, stop the rubber sclerosis, prolong rubber parts duration of service with aging.
2. can clean attached to the greasy dirt on the rubber parts, use back light as new.
3. this automobile rubber protective material is aerosol-type, and is easy to use, only needs a spray gently, just can be effective, time saving and energy saving, and do not hinder lacquer painting.
The practical implementation method:
For better implement the present invention, lift following instance explanation, but embodiment not a limitation of the present invention at present.
Instance 1
A kind of automobile rubber protective material, each constituent mass per-cent is following:
Solvent 55%
Dimethyl silicone oil 8%
Silicone resin 5%
Wetting agent 0.5%
Oxidation inhibitor 0.2%
UV light absorber 0.3%
Deodorization LPG liquefied petroleum gas 31%
The practical implementation method is: with stirring in dimethyl silicone oil, silicone resin, wetting agent, oxidation inhibitor, the UV light absorber adding solvent, pack into after treating to dissolve fully in the aerosol jar, charge into the deodorization LPG liquefied petroleum gas again, promptly get product of the present invention.
Instance 2
A kind of automobile rubber protective material, each constituent mass per-cent is following:
Solvent 55%
Dimethyl silicone oil 6%
Silicone resin 6%
Wetting agent 0.3%
Oxidation inhibitor 0.3%
UV light absorber 0.2%
Deodorization LPG liquefied petroleum gas 32.2%
The practical implementation method is: with stirring in dimethyl silicone oil, silicone resin, wetting agent, oxidation inhibitor, the UV light absorber adding solvent, pack into after treating to dissolve fully in the aerosol jar, charge into the deodorization LPG liquefied petroleum gas again, promptly get product of the present invention.
Instance 3
A kind of automobile rubber protective material, each constituent mass per-cent is following:
Solvent 60%
Silicone oil 7%
Silicone resin 3%
Wetting agent 0.4%
Oxidation inhibitor 0.2%
UV light absorber 0.1%
Deodorization LPG liquefied petroleum gas 29.3%
The practical implementation method is: with stirring in dimethyl silicone oil, silicone resin, wetting agent, oxidation inhibitor, the UV light absorber adding solvent, pack into after treating to dissolve fully in the aerosol jar, charge into the deodorization LPG liquefied petroleum gas again, promptly get product of the present invention.
Claims (7)
1. an automobile rubber protective material is characterized in that it comprises no aralkyl hydrocarbon solvent 50-80%, dimethyl silicone oil 1-10%, silicone resin 1-10%, wetting agent 0.1-1%, oxidation inhibitor 0.05-1%, UV light absorber 0.1-0.5%, the deodorization LPG liquefied petroleum gas 20-40% of following component (mass percent): C8-C13.
2. automobile rubber protective material according to claim 1 is characterized in that solvent can be that C8-C13 does not have fragrant straight-chain paraffin, isomerization alkanes or naphthenic hydrocarbon.
3. automobile rubber protective material according to claim 1, it is characterized in that the dimethyl-silicon oil viscosity be 100-20000 (25 ℃, mm
2/ s).
4. automobile rubber protective material according to claim 1 is characterized in that silicone resin can be one or more in amino silicone, high light silicone resin, the fluorine silicon resin.
5. automobile rubber protective material according to claim 1 is characterized in that wetting agent is polyether-modified polysiloxane-based wetting agent.
6. automobile rubber protective material according to claim 1 is characterized in that oxidation inhibitor can be one or more in Hinered phenols antioxidant or the aromatic amine oxidation inhibitor.
7. automobile rubber protective material according to claim 1 is characterized in that UV light absorber is that UV531 or UV770 or both are used.