CN102345374A - Double-layer high-filling rigid polyvinyl chloride floor - Google Patents
Double-layer high-filling rigid polyvinyl chloride floor Download PDFInfo
- Publication number
- CN102345374A CN102345374A CN2010102447721A CN201010244772A CN102345374A CN 102345374 A CN102345374 A CN 102345374A CN 2010102447721 A CN2010102447721 A CN 2010102447721A CN 201010244772 A CN201010244772 A CN 201010244772A CN 102345374 A CN102345374 A CN 102345374A
- Authority
- CN
- China
- Prior art keywords
- parts
- double
- floor
- polyvinyl chloride
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to a polyvinyl chloride (PVC) floor, and in particular relates to a double-layer high-filling rigid polyvinyl chloride floor. The double-layer high-filling rigid polyvinyl chloride floor is characterized by consisting of a double-layer structure, wherein a surface layer consists of auxiliary materials; a bottom layer consists of main materials; the main materials comprise the following components in part by weight: 100 to 120 parts of polyvinyl chloride resin, 8 to 10 parts of dimethyl dithiol tin acetic acid enthyl hexyl, 200 to 250 parts of calcium carbonate, 200 to 250 parts of expanded perlite, 25 to 30 parts of phthalic acid diphenyl octyl phosphate, 10 parts of paraffin and 20 to 25 parts of activated charcoal (AC) foaming agent; and the auxiliary materials comprise the following components in part by weight: 100 to 120 parts of polyvinyl chloride resin, 10 to 20 parts of methacrylate butadiene styrene (MBS) resin, 3 to 5 parts of zinc stearate, 4 to 6 parts of phthalic acid butyl phthalate, 5 to 8 parts of tribasic lead sulfate and 2 to 4 parts of di-tert-butylhydroquinone resin. Various properties such as impact strength and the like of the floor can meet using requirements; and the floor is well accepted by passengers, drivers and sellers.
Description
Technical field
The invention belongs to the PVC floor, the particularly double-deck high hard pvc flooring of filling.
Background technology
The floor belongs to PVC hollow profile shapes to high filling RPVC (being called for short R one PVC), is to be primary raw material with polyvinyl chloride resin, adds heat stabilizer, impact modifier, sliding agent and filler, extrudes through batch mixes to form.Its width is respectively 55mm and 110mm.It is a kind of suitable with strength of wood, and more attractive in appearance, wear-resisting, moistureproof, mothproof, fire prevention and be prone to clean to mould substitute materials for wood.R one Pvc floor is installed on automobile, and each car can be saved Zm, and timber, thereby produce R one Pvc floor is exploitation second forest reserves, the offspring that benefits future generations, increase economic benefit and satisfy the major issue of market demand.In recent years, R one PVC floor was widely used in electric car, automobile and building.
The present invention provides a kind of new type double floor height to fill hard pvc flooring, satisfies the demand of growing R one PVC.
Summary of the invention
Goal of the invention
The present invention provides a kind of new type double floor height to fill hard pvc flooring, satisfies the demand of growing R one PVC.
Technical scheme
A kind of double-deck high hard pvc flooring of filling is characterized in that being made up of double-decker, and auxiliary material is formed the top layer, and major ingredient constitutes bottom; By weight wherein,
The prescription of major ingredient is: Corvic 100-120 part, dimethyl dimercapto 2-ethyl hexyl ethanoate tin 8-10 part, calcium carbonate 200-250 part, expanded perlite 200-250 part, dioctyl phthalate 25-30 part, 10 parts in paraffin, AC blowing agent 20-25 part.
The prescription of auxiliary material is: Corvic 100-120 part, MBS resin 10-12 part, zinc stearate 3-5 part, dibutyl phthalate 4-6 part, lead sulfate tribasic 5-8 part, di-tert-butyl hydroquinone's resin 2-4 part.
A kind of double-deck high preparation technology who fills hard pvc flooring:
A, batch mixing mix above-mentioned prescription;
B, mixing: on two roller plastics processing mills that the PVC plasticizing is even; Temperature is about 140-160;
C, extrude: extrude by foamed plastic extruder and co-extrusion machine pressure after the mixing completion of major ingredient and auxiliary material, wherein about temperature 140-160, pressure 180-200kg/cm
2
D, synthetic double-deck processing typing, warp cooling traction again;
E, finished product.
Beneficial effect
1, the various performances such as impact strength on this floor all can satisfy instructions for use, receive the passenger deeply and drive, the personnel of selling welcome.Usually, must water flushing compartment after motor bus, electric car are stopped transport every day, past floor compartment is wood materials, and timber is unable to undergo aqueous corrosion, whenever at a distance from 1 year even will upgrade once half a year.This PVC plastic floor is excellent always after adopting this PVC floor.
2, the present invention adopts double-decker, and surface structure adopts the bigger prescription of intensity, has and resistance to wears, characteristics such as resistance to compression.
The specific embodiment
Embodiment 1
A kind of double-deck high hard pvc flooring of filling is characterized in that being made up of double-decker, and auxiliary material is formed the top layer, and major ingredient constitutes bottom; By weight wherein,
The prescription of major ingredient is: Corvic 100kg, dimethyl dimercapto 2-ethyl hexyl ethanoate tin 8kg, calcium carbonate 200kg, expanded perlite 200kg, dioctyl phthalate 25kg, paraffin 10kg, AC blowing agent 20kg.
The prescription of auxiliary material is: Corvic 100kg, MBS resin 10kg, zinc stearate 3kg, dibutyl phthalate 4kg, lead sulfate tribasic 5kg, di-tert-butyl hydroquinone's resin 2kg.
A kind of double-deck high preparation technology who fills hard pvc flooring:
A, batch mixing mix above-mentioned prescription;
B, mixing: on two roller plastics processing mills that the PVC plasticizing is even; Temperature is about 140-160;
C, extrude: extrude by foamed plastic extruder and co-extrusion machine pressure after the mixing completion of major ingredient and auxiliary material, wherein about temperature 140-160, pressure 180-200kg/cm
2
D, synthetic double-deck processing typing, warp cooling traction again;
E, finished product.
Embodiment 2
A kind of double-deck high hard pvc flooring of filling is characterized in that being made up of double-decker, and auxiliary material is formed the top layer, and major ingredient constitutes bottom; By weight wherein,
The prescription of major ingredient is: Corvic 120kg, dimethyl dimercapto 2-ethyl hexyl ethanoate tin 10kg, calcium carbonate 250kg, expanded perlite 250kg, dioctyl phthalate 30kg, paraffin 10kg, AC blowing agent 25kg.
The prescription of auxiliary material is: Corvic 120kg, MBS resin 12kg, zinc stearate 5kg, dibutyl phthalate 6kg, lead sulfate tribasic 8kg, di-tert-butyl hydroquinone's resin 4kg.
A kind of double-deck high preparation technology who fills hard pvc flooring:
A, batch mixing mix above-mentioned prescription;
B, mixing: on two roller plastics processing mills that the PVC plasticizing is even; Temperature is about 140-160;
C, extrude: extrude by foamed plastic extruder and co-extrusion machine pressure after the mixing completion of major ingredient and auxiliary material, wherein about temperature 140-160, pressure 180-200kg/cm
2
D, synthetic double-deck processing typing, warp cooling traction again;
E, finished product.
Claims (1)
1. the double-deck high hard pvc flooring of filling is characterized in that being made up of double-decker, and auxiliary material is formed the top layer, and major ingredient constitutes bottom; By weight wherein,
The prescription of major ingredient is: Corvic 100-120 part, dimethyl dimercapto 2-ethyl hexyl ethanoate tin 8-10 part, calcium carbonate 200-250 part, expanded perlite 200-250 part, dioctyl phthalate 25-30 part, 10 parts in paraffin, AC blowing agent 20-25 part;
The prescription of auxiliary material is: Corvic 100-120 part, MBS resin 10-12 part, zinc stearate 3-5 part, dibutyl phthalate 4-6 part, lead sulfate tribasic 5-8 part, di-tert-butyl hydroquinone's resin 2-4 part.