CN102344682A - Modified nylon 66 material for valve seat sealing ring - Google Patents
Modified nylon 66 material for valve seat sealing ring Download PDFInfo
- Publication number
- CN102344682A CN102344682A CN2011102947055A CN201110294705A CN102344682A CN 102344682 A CN102344682 A CN 102344682A CN 2011102947055 A CN2011102947055 A CN 2011102947055A CN 201110294705 A CN201110294705 A CN 201110294705A CN 102344682 A CN102344682 A CN 102344682A
- Authority
- CN
- China
- Prior art keywords
- nylon
- content
- modification
- valve seat
- materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a modified nylon 66 material for a valve seat sealing ring. The modified nylon 66 material comprises the following components in percentage by mass: 63.5-65.2% of nylon 66, 14.2-15.8% of polytetrafluoroethylene, 9.2-10.7% of aluminum bronze powder, 9.3-11% of Grafoil graphite and 0.44-0.55% of other additives, wherein the modified nylon 66 material comprises the following additive components in percentage by mass: 0.12-0.17% of maleic anhydride grafted polypropylene, 0.18-0.21% of glass fiber and 0.14-0.17% of carbon fiber. The valve seat sealing ring manufactured from the modified nylon 66 material has strength enhancement performance, toughness enhancement performance, rub resistance, weather resistance, self lubrication and high tensile property, and has obvious advantages as compared with the traditional sealing ring.
Description
Technical field
The present invention relates to the valve base sealing loop material, relate in particular to a kind of modification of nylon 66 materials that are used for valve seat insert.
Background technology
Current energy industry development is rapid, and the exploitation of oil, Sweet natural gas equal energy source and transmission need be used the valve of a large amount of pipelines and control pipeline.Mostly in awful weather, topography and geomorphology extreme difference, the rare area of human footmarks, physical environment and weather are extremely abominable in the new place of production of oil, Sweet natural gas equal energy source, and be very high to the performance quality requirement of energy transport pipeline.And ducted medium often contains foreign material even sandstone arranged, and the design of giving pipeline valve proposes a very big difficult problem with using, and sealing-ring is as requisite significant components in the pipeline valve, and its performance quality has determined the behaviour in service and the life-span of valve.
In the present stage pipeline valve many with tetrafluoroethylene as valve seat insert.Though tetrafluoroethylene has excellent sealing performance, its mechanical property is bad, and tensile strength, ultimate compression strength are not high, and resilience is poor.Also useful both at home and abroad nylon 66; Perhaps with the sealing-ring as pipeline valve such as nylon 66 filled glass fibers, nylon 66 filled polytetrafluoroethylenes, nylon 66 filling carbon fibres; But above-mentioned materials can not have the premium properties of each component simultaneously; The over-all properties of sealing-ring is bad, still has very big raising space.
Summary of the invention
The objective of the invention is to overcome the deficiency of prior art, a kind of modification of nylon that is used for valve seat insert 66 materials that have enhancing, toughness reinforcing, rub resistance, weather-proof, self-lubricating, high tensile property simultaneously are provided.
Modification of nylon 66 materials that are used for valve seat insert in the component of mass percentage content modification of nylon 66 materials are: nylon 66 content are 63.5%～65.2%, polytetrafluoroethylene content is 14.2%～15.8%, the xantal powder content is 9.2%～10.7%, the Grafoil content of graphite is 9.3%～11%, other additive level is 0.44%～0.55%.
The mass percent that described other components of additives accounts for modification of nylon 66 materials is: maleic anhydride inoculated polypropylene content is 0.12%～0.17%, content of glass fiber is 0.18%～0.21%, carbon fibre content is 0.14%～0.17%.
Modification of nylon 66 valve seat inserts provided by the invention; Adopting nylon 66 is main raw material(s); Improved the comprehensive mechanical property of sealing-ring; Tetrafluoroethylene can improve the weathering resistance and the wear resistance of sealing-ring as the weighting material of modification of nylon 66; Grafoil graphite can improve the weathering resistance of sealing-ring; And playing self-lubricating function, the use of maleic anhydride inoculated polypropylene, carbon fibre and glass fibre can improve toughness, intensity, the tensile property of sealing-ring.Modification of nylon 66 valve seat inserts provided by the invention have enhancing, toughness reinforcing, rub resistance, weather-proof, self-lubricating, high tensile property simultaneously, have compared significant advantage with the conventional seals circle.
Embodiment
Modification of nylon 66 materials that are used for valve seat insert in the component of mass percentage content modification of nylon 66 materials are: nylon 66 content are 63.5%～65.2%, polytetrafluoroethylene content is 14.2%～15.8%, the xantal powder content is 9.2%～10.7%, the Grafoil content of graphite is 9.3%～11%, other additive level is 0.44%～0.55%.The mass percent that described other components of additives accounts for modification of nylon 66 materials is: maleic anhydride inoculated polypropylene content is 0.12%～0.17%, content of glass fiber is 0.18%～0.21%, carbon fibre content is 0.14%～0.17%.
In these modification of nylon 66 material synthesis; At first add 63.5%～65.2% nylon 66; And be heated to 320 ℃ of fusings; Add 14.2%～15.8% tetrafluoroethylene and 9.3%～11% Grafoil graphite then simultaneously; Add other additive of 0.44%～0.55% after stirring; Comprise 0.12%～0.17% maleic anhydride inoculated polypropylene, 0.18%～0.21% glass fibre and 0.14%～0.17% carbon fibre; Add 9.2%～10.7% xantal powder at last; Stir; This process continues heating, and mixture temperature remains on 320 ℃.With the spiral press injector fused modification of nylon 66 extruded in plastic are advanced the sealing-ring forming mould, sealing-ring is taken out in the pressurize moulding after the water-cooled.The valve seat insert that utilizes this technology and modification of nylon 66 materials to process; Tensile strength is 110～120MPa; Slip resistance is 68～72MPa; Compressive strength can reach 155～163MPa; Flexural strength can reach 168～175MPa, and wear resisting property, compression recovery performance are excellent, and flame retardant resistance, abrasion resistance are fabulous; Have self-lubricating function, can adapt to-60～80 ℃ Working environment.
Compared to domestic traditional sealing-ring; The present invention adopts modification of nylon 66 to be main raw material(s); Tetrafluoroethylene is auxiliary packing material; Compared to external nylon 66 sealing-rings; The modification of nylon 66 that the present invention adopts serves as simultaneously as weighting material with tetrafluoroethylene, xantal powder, Grafoil graphite and other additive, but not single weighting material.
Nylon 66 is typical hard and tough polyamide polymers, because good toughness, deformability is strong, is the excellent materials as sealing-ring therefore, and wear resisting property is excellent, and comprehensive mechanical property is better than general-purpose plastics such as tetrafluoroethylene.
The tetrafluoroethylene mechanical property is bad, and tensile strength, ultimate compression strength are not high, and resilience is poor, can reduce sealing-ring use properties and life-span as sealing ring material separately.But tetrafluoroethylene has excellent sealing performance, high temperature resistant, low temperature resistant and wear resisting property, reduces the content of tetrafluoroethylene, uses as weighting material, can improve the over-all properties of sealing-ring.The filling aluminum bronze powder can reduce frictional coefficient, improve the ultimate compression strength of material, makes sealing-ring have self-lubricating function simultaneously, and Grafoil graphite can improve weather-proof, the resistance to elevated temperatures of sealing-ring, simultaneously as lubricant, reduces wearing and tearing.
The adding of maleic anhydride inoculated polypropylene has significant toughening effect to nylon 66, and carbon fibre and glass fibre can improve intensity, tensile property and the resistance to elevated temperatures of sealing-ring as toughener.
Embodiment 1:
Modification of nylon 66 materials that are used for valve seat insert in the component of mass percentage content modification of nylon 66 materials are: nylon 66 content are 64.5%, polytetrafluoroethylene content is 15%, xantal powder content 10%, Grafoil content of graphite are 10%, other additive level is 0.5%.The mass percent that described other components of additives accounts for modification of nylon 66 materials is: maleic anhydride inoculated polypropylene content is 0.15%, content of glass fiber is 0.2%, carbon fibre content is 0.15%.
In these modification of nylon 66 material synthesis; At first add 64.5% nylon 66; And be heated to 320 ℃ of fusings; Add 15% tetrafluoroethylene and 10% Grafoil graphite then simultaneously, other additive of 0.5% is added in the back that stirs, and comprises 0.15% maleic anhydride inoculated polypropylene, 0.2% glass fibre and 0.15% carbon fibre; Add 10% xantal powder at last; Stir, this process continues heating, and mixture temperature remains on 320 ℃.With the spiral press injector fused modification of nylon 66 extruded in plastic are advanced the sealing-ring forming mould, sealing-ring is taken out in the pressurize moulding after the water-cooled.The valve seat insert that utilizes this technology and modification of nylon 66 materials to process; Tensile strength is 112～118MPa; Slip resistance is 68～70MPa; Compressive strength can reach 157～163MPa; Flexural strength can reach 168～172MPa, and wear resisting property, compression recovery performance are excellent, and flame retardant resistance, abrasion resistance are fabulous; Have self-lubricating function, can adapt to-65～78 ℃ Working environment.
Embodiment 2:
Modification of nylon 66 materials that are used for valve seat insert in the component of mass percentage content modification of nylon 66 materials are: nylon 66 content are 65.1%, polytetrafluoroethylene content is 14.4%, xantal powder content 10.2%, Grafoil content of graphite are 9.8%, other additive level is 0.5%.The mass percent that described other components of additives accounts for modification of nylon 66 materials is: maleic anhydride inoculated polypropylene content is 0.13%, content of glass fiber is 0.21%, carbon fibre content is 0.16%.
In these modification of nylon 66 material synthesis; At first add 65.1% nylon 66; And be heated to 320 ℃ of fusings; Add 14.4% tetrafluoroethylene and 9.8% Grafoil graphite then simultaneously, other additive of 0.5% is added in the back that stirs, and comprises 0.13% maleic anhydride inoculated polypropylene, 0.21% glass fibre and 0.16% carbon fibre; Add 10.2% xantal powder at last; Stir, this process continues heating, and mixture temperature remains on 320 ℃.With the spiral press injector fused modification of nylon 66 extruded in plastic are advanced the sealing-ring forming mould, sealing-ring is taken out in the pressurize moulding after the water-cooled.The valve seat insert that utilizes this technology and modification of nylon 66 materials to process; Tensile strength is 114～117MPa; Slip resistance is 68～70MPa; Compressive strength can reach 158～163MPa; Flexural strength can reach 167～171MPa, and wear resisting property, compression recovery performance are excellent, and flame retardant resistance, abrasion resistance are fabulous; Have self-lubricating function, can adapt to-65～80 ℃ Working environment.
Embodiment 3:
Modification of nylon 66 materials that are used for valve seat insert in the component of mass percentage content modification of nylon 66 materials are: nylon 66 content are 64.2%, polytetrafluoroethylene content is 15.5%, xantal powder content 9.7%, Grafoil content of graphite are 10.1%, other additive level is 0.5%.The mass percent that described other components of additives accounts for modification of nylon 66 materials is: maleic anhydride inoculated polypropylene content is 0.16%, content of glass fiber is 0.19%, carbon fibre content is 0.15%.
In these modification of nylon 66 material synthesis; At first add 64.2% nylon 66; And be heated to 320 ℃ of fusings; Add 15.5% tetrafluoroethylene and 10.1% Grafoil graphite then simultaneously, other additive of 0.5% is added in the back that stirs, and comprises 0.16% maleic anhydride inoculated polypropylene, 0.19% glass fibre and 0.15% carbon fibre; Add 9.7% xantal powder at last; Stir, this process continues heating, and mixture temperature remains on 320 ℃.With the spiral press injector fused modification of nylon 66 extruded in plastic are advanced the sealing-ring forming mould, sealing-ring is taken out in the pressurize moulding after the water-cooled.The valve seat insert that utilizes this technology and modification of nylon 66 materials to process; Tensile strength is 112～118MPa; Slip resistance is 68～72MPa; Compressive strength can reach 157～163MPa; Flexural strength can reach 169～174MPa, and wear resisting property, compression recovery performance are excellent, and flame retardant resistance, abrasion resistance are fabulous; Have self-lubricating function, can adapt to-60～75 ℃ Working environment.
Claims (2)
1. modification of nylon 66 materials that are used for valve seat insert is characterized in that in the component of mass percentage content modification of nylon 66 materials being: nylon 66 content are 63.5%～65.2%, polytetrafluoroethylene content is 14.2%～15.8%, the xantal powder content is 9.2%～10.7%, the Grafoil content of graphite is 9.3%～11%, other additive level is 0.44%～0.55%.
2. a kind of modification of nylon 66 materials that are used for valve seat insert according to claim 1 is characterized in that the mass percent that described other components of additives accounts for modification of nylon 66 materials is: maleic anhydride inoculated polypropylene content is 0.12%～0.17%, content of glass fiber is 0.18%～0.21%, carbon fibre content is 0.14%～0.17%.