CN102332344A - 一种铝合金电缆的热处理方法 - Google Patents
一种铝合金电缆的热处理方法 Download PDFInfo
- Publication number
- CN102332344A CN102332344A CN201110216835A CN201110216835A CN102332344A CN 102332344 A CN102332344 A CN 102332344A CN 201110216835 A CN201110216835 A CN 201110216835A CN 201110216835 A CN201110216835 A CN 201110216835A CN 102332344 A CN102332344 A CN 102332344A
- Authority
- CN
- China
- Prior art keywords
- cable
- thermal treatment
- treatment method
- aluminum alloy
- rare earth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种铝合金电缆的热处理方法,所述电缆材料的组合物按重量百分比的组分为:稀土0.3-0.7%,Si 0.1-0.3%,Mg 0.7-0.8%,Fe 0.3-0.5%,Ni 0.01-0.35%,Zr 0.05-0.1%,余量为铝和不可避免的杂质。该电缆由于加入了稀土元素和Zr,同时在温度为550-650℃,时间为2-4h下热处理,提高了电缆的导电性能、弯曲性能、抗蠕变性能和耐腐蚀性能,保证电缆在长时间过载和过热时的连接热稳定性。
Description
技术领域
本发明涉及一种电缆,具体是涉及一种铝合金电缆的热处理方法。
背景技术
1968年,美国南方电缆公司发明了铝合金电缆,铝合金电缆在美国和加拿大等地区已经有40多年的应用历史,是先进的、成熟的产品。铝合金电缆在美国和加拿大地区广泛应用于机场、军事基地、办公室、住宅、酒店、超市、院校、体育场、医院、工业厂房等场所,由于铝合金电缆特有的性能特点,在几十年的应用过程中,得到了北美地区建筑设计师和电气设计师在安全性能和便捷敷设方面的一致肯定和推荐,铝合金带连锁铠装电缆作为一种新型的、安全可靠的电缆在很多应用领域代替了铜电缆。这种电缆的性能和延伸性能非常好,且非常安全。除此之外它还易于安装,安装这种电缆的简单程度超过其他任何电缆,很多美国电气工程师都希望铝合金电力电缆能够应用于建筑项目中去。
在输电领域,铝质轻、价廉且导电性较好、比强度高,耐磨顺性好,因而在电工领域占优势地位。在架空输电线路,尤其是超高压线路和大跨越线路上,铝合金电缆一直是架空输电电缆线的主体材料。其中,Al-Mg-Si合金具优良的物理性能和机械性能,美国、日本等国已经将此电缆应用于高压输电线路,如广泛采用的6201、6101。该合金的强度高,耐冲性好,缺口敏感性好,具有较好的热塑性,可以高速挤压成结构复杂的各种型材,易于加工,同时耐腐蚀,导电性良好,在输电领域得到广泛的应用。
目前已经开发出了多种铝合金电缆线,但仍然不能满足复杂的自然条件,雨雪冰冻以及远距离跨海架设的需要,仍需进一步改善其性能。而在国内、生产工艺、产品的性能、大跨越高空输电技术与国外相比,还存在一定的差距,随着我国电力需要的不断增长,对电缆提出了更高的要求,因此发展高强度,高导电率的电缆具有很强的现实意义。
发明内容
针对现有技术的不足,本发明的目的之一在于提供一种高强度,导电性更高的电缆,寻找一种更加合适的稀土元素加入其中,有效的改善合金的组织结构,增强其强度和导电率。
本发明的优点在于采用合金化提高了强度和使用寿命,同时采用550-650℃,2-4h的退火热处理工艺,使得晶格缺陷降低,提高合金导电率,有利于均匀化。
本发明所制备的一种铝合金电缆,按质量百分比由以下成分组成:
稀土 0.3-0.7%
Si 0.1-0.3%
Mg 0.7-0.8%
Fe 0.3-0.5%
Ni 0.01-0.35%
Zr 0.05-0.1%
余量为铝和不可避免的杂质;
还包括Ag 0.02-0.05%和Zn 0.015-0.003%;
热处理温度为550-650℃,时间为2-4h。
具体实施方式
实施例一
La 0.4%
Si 0.1%
Mg 0.7%
Fe 0.4%
Ni 0.01%
Zr 0.05%
余量为铝和不可避免的杂质;
热处理温度为550℃,时间为4h。
经检查其导电率为70%IACS,抗拉强度为240MPa,伸长率为15%。
实施例二
Y 0.5%
Si 0.2%
Mg 0.75%
Fe 0.5%
Ni 0.02%
Zr 0.1%
余量为铝和不可避免的杂质
热处理温度为650℃,时间为2h。
经检查其导电率为73%IACS,抗拉强度为250MPa,伸长率为13%。
实施例三
La 0.2%
Y 0.25%
Si 0.1%
Mg 0.7%
Fe 0.4%
Ni 0.03%
Zr 0.08%
余量为铝和不可避免的杂质
热处理温度为600℃,时间为3h。。
经检查其导电率为80%IACS,抗拉强度为260MPa,伸长率为11.5%。
实施例四
La 0.1%
Y 0.4%
Si 0.1%
Mg 0.8%
Fe 0.5%
Ni 0.35%
Ag 0.02
Zn 0.003%
Zr 0.06%
余量为铝和不可避免的杂质
热处理温度为580℃,时间为3.5h。
经检查其导电率为80%IACS,抗拉强度为273MPa,伸长率为11%。
申请人声明,本发明通过上述实施例来说明本发明的详细组成和工艺流程,但本发明并不局限于上述详细组成和工艺流程,即不意味着本发明必须依赖上述详细组成和工艺流程才能实施。所属技术领域的技术人员应该明了,对本发明的任何改进,对本发明产品各原料的等效替换及辅助成分的添加、具体方式的选择等,均落在本发明的保护范围和公开范围之内。
Claims (3)
1.一种铝合金电缆的热处理方法,所述电缆材料的组合物按重量百分比的组分为:
稀土 0.3-0.7%
Si 0.1-0.3%
Mg 0.7-0.8%
Fe 0.3-0.5%
Ni 0.01-0.35%
Zr 0.05-0.1%
余量为铝和不可避免的杂质,其特征在于:所述的热处理温度为550-650℃,时间为2-4h。
2.根据权利要求1所述的方法,其特征还在于:所述稀土为镧、钇的一种,或者是两者的组合。
3.根据权利要求1所述的一种方法,其特征还在于包括Ag 0.02-0.05%和Zn 0.015-0.003%。