CN102329141A - Silicon-carbide composite corundum mullite brick - Google Patents
Silicon-carbide composite corundum mullite brick Download PDFInfo
- Publication number
- CN102329141A CN102329141A CN201110206877A CN201110206877A CN102329141A CN 102329141 A CN102329141 A CN 102329141A CN 201110206877 A CN201110206877 A CN 201110206877A CN 201110206877 A CN201110206877 A CN 201110206877A CN 102329141 A CN102329141 A CN 102329141A
- Authority
- CN
- China
- Prior art keywords
- granularity
- corundum
- mullite
- parts
- silicon carbide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a silicon-carbide composite corundum mullite brick, which is manufactured through the following raw materials in parts by weight: 60-90 parts of natural calcined mullite with the particle size of 4-0mm, 5-20 parts of corundum powder with the particle size of 120-320 meshes, 5-25 parts of silicon carbide with the particle size of 120-320 meshes, 5-10 parts of clay powder with the particle size of 120-200 meshes and 3-5 parts of water. According to the invention, with the natural calcined mullite as the main raw material and the added silicon carbide and the corundum powder, the silicon-carbide composite corundum mullite brick is formed through high pressure and sintered at a high temperature, is used in a bosh and a furnace crucible of a small and medium-sized blast furnace, can resist the high temperature of 1700-1800 DEG C, and has the advantages of same performance compared with that of the traditional corundum mullite brick, low price, high cost-performance ratio and good economic benefit.
Description
Technical field
The present invention relates to a kind of silicon carbide compound corundum-mullite brick and preparation method thereof.
Background technology
Corundum brick is meant that the content of aluminum oxide is greater than 90%; With the corundum is the fire resistive material product of principal crystalline phase; Have very high cold crushing strength and high loading softening begins temperature, and good chemical stability, acidity or slag basic, metal and glass metal etc. all there are stronger resistivity; Be widely used in various high temperature furnace lining such as cracking, receiver, metallurgy industry, and the kiln furnitures of petrochemical complex and chemical fertilizer industry, but the cost of corundum brick is high.
Summary of the invention
The technical problem that the present invention will solve is that the cost of corundum brick is high, and a kind of silicon carbide compound corundum-mullite brick and preparation method thereof is provided.
Technical scheme of the present invention is: a kind of silicon carbide compound corundum-mullite brick, and it is to be processed by the raw material of following parts by weight:
Granularity is the natural fused mullite 60-90 of 4-0 mm
Granularity is 120-320 purpose lapis amiridis 5-20
Granularity is 120-320 purpose silit 5-25
Granularity is 120-200 purpose clay powder 5-10
Water 3-5.
Silicon carbide compound corundum-mullite brick, preferably process by the raw material of following parts by weight:
Granularity is the natural fused mullite 70-80 of 4-0 mm
Granularity is 120-320 purpose lapis amiridis 10-15
Granularity is 120-320 purpose silit 10-20
Granularity is 120-200 purpose clay powder 6-8
Water 4-5.
Silicon carbide compound corundum-mullite brick, optimum is processed by the raw material of following parts by weight:
Granularity is the natural fused mullite 75 of 4-0 mm
Granularity is a 120-320 purpose lapis amiridis 12
Granularity is a 120-320 purpose silit 15
Granularity is a 120-200 purpose clay powder 7
Water 4.
The preparation method of silicon carbide compound corundum-mullite brick: after raw materials mix, under 1600-1650 ℃ temperature, sintering 12-14 hour.
The invention has the beneficial effects as follows: the present invention is main with natural fused mullite raw material, has added silit and lapis amiridis, high-pressure molding; High temperature sintering uses at the bosh of medium and small blast furnace and cupola well, high temperature that can anti-1700-1800 ℃; Compare with the traditional corundum mullite brick, performance is suitable, and price is low; Cost performance is high, and is good in economic efficiency.
Embodiment
Embodiment 1
A kind of silicon carbide compound corundum-mullite brick, it is to be processed by following raw material: granularity is that natural fused mullite 90 kg, the granularity of 4-0 mm is that 120 purpose lapis amiridiss, 20 kg, granularity are that 320 purpose silit, 25 kg, granularity are 200 purpose clay powders, 10 kg, water 5 kg.
The preparation method of silicon carbide compound corundum-mullite brick: after raw materials mix, under 1600 ℃ temperature, sintering 12 hours.
Embodiment 2
A kind of silicon carbide compound corundum-mullite brick, it is to be processed by following raw material: granularity is that natural fused mullite 60 kg, the granularity of 4-0 mm is that 160 purpose lapis amiridiss, 5 kg, granularity are that 180 purpose silit, 5 kg, granularity are 120 purpose clay powders, 5 kg, water 3 kg.
The preparation method of silicon carbide compound corundum-mullite brick: after raw materials mix, under 1650 ℃ temperature, sintering 14 hours.
Embodiment 3
Silicon carbide compound corundum-mullite brick, it is processed by following raw material: granularity is that natural fused mullite 80 kg, the granularity of 4-0 mm is that 300 purpose lapis amiridiss, 15 kg, granularity are that 320 purpose silit, 20 kg, granularity are 180 purpose clay powders, 8 kg, water 5 kg.
The preparation method of silicon carbide compound corundum-mullite brick: after raw materials mix, under 1600 ℃ temperature, sintering 13 hours.
Embodiment 4
Silicon carbide compound corundum-mullite brick, it is processed by following raw material: granularity is that natural fused mullite 70 kg, the granularity of 4-0 mm is that 240 purpose lapis amiridiss, 10 kg, granularity are that 280 purpose silit, 10 kg, granularity are 180 purpose clay powders, 6 kg, water 4 kg.
The preparation method of silicon carbide compound corundum-mullite brick: after raw materials mix, under 1650 ℃ temperature, sintering 12 hours.
Embodiment 5
Silicon carbide compound corundum-mullite brick, it is processed by following raw material: granularity is that natural fused mullite 75 kg, the granularity of 4-0 mm is that 120-320 purpose lapis amiridis 12 kg, granularity are that 120-320 purpose silit 15 kg, granularity are 120-200 purpose clay powder 7 kg, water 4 kg.
The preparation method of silicon carbide compound corundum-mullite brick: after raw materials mix, under 1650 ℃ temperature, sintering 12 hours.
Claims (4)
1. a silicon carbide compound corundum-mullite brick is characterized in that, it is to be processed by the raw material of following parts by weight:
Granularity is the natural fused mullite 60-90 of 4-0 mm
Granularity is 120-320 purpose lapis amiridis 5-20
Granularity is 120-320 purpose silit 5-25
Granularity is 120-200 purpose clay powder 5-10
Water 3-5.
2. silicon carbide compound corundum-mullite brick according to claim 1 is characterized in that, it is to be processed by the raw material of following parts by weight:
Granularity is the natural fused mullite 70-80 of 4-0 mm
Granularity is 120-320 purpose lapis amiridis 10-15
Granularity is 120-320 purpose silit 10-20
Granularity is 120-200 purpose clay powder 6-8
Water 4-5.
3. silicon carbide compound corundum-mullite brick according to claim 2 is characterized in that, it is to be processed by the raw material of following parts by weight:
Granularity is the natural fused mullite 75 of 4-0 mm
Granularity is a 120-320 purpose lapis amiridis 12
Granularity is a 120-320 purpose silit 15
Granularity is a 120-200 purpose clay powder 7
Water 4.
4. like the preparation method of claim 1 or 2 or 3 described silicon carbide compound corundum-mullite bricks, it is characterized in that: after raw materials mix, under 1600-1650 ℃ temperature, sintering 12-14 hour.