CN102303999A - 接力式离子转换控释肥料的制备方法 - Google Patents

接力式离子转换控释肥料的制备方法 Download PDF

Info

Publication number
CN102303999A
CN102303999A CN201110238627A CN201110238627A CN102303999A CN 102303999 A CN102303999 A CN 102303999A CN 201110238627 A CN201110238627 A CN 201110238627A CN 201110238627 A CN201110238627 A CN 201110238627A CN 102303999 A CN102303999 A CN 102303999A
Authority
CN
China
Prior art keywords
reaction kettle
fertilizer
mixing ratio
uniformly stirring
weight mixing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201110238627A
Other languages
English (en)
Inventor
吴庆树
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tianjin Shiyide Fertilizer Co Ltd
Original Assignee
Tianjin Shiyide Fertilizer Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tianjin Shiyide Fertilizer Co Ltd filed Critical Tianjin Shiyide Fertilizer Co Ltd
Priority to CN201110238627A priority Critical patent/CN102303999A/zh
Publication of CN102303999A publication Critical patent/CN102303999A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种接力式离子转换控释肥料的制备方法,其制备方法的步骤为:(1)按重量配比向反应釜内加水及聚丙烯胺,搅拌均匀;(2)将反应釜降温到80℃,然后按重量配比加入玉米淀粉,均匀搅拌;(3)将反应釜升温至95℃,按重量配比添加松香,搅拌均匀;(4)向反应釜内按重量配比加入液体石蜡,搅拌均匀,保持搅拌及温度1小时;(5)将反应釜降温至80℃,然后按重量配比添加膨润土,搅拌均匀,即可出料。本方法所制肥料克服了国内外所广泛使用的速效化肥普遍存在的利用率低、环境污染严重的问题,肥料效果好,环境污染小,经济效益高,制作简单容易,成本低廉,养分利用率达到65%。

Description

接力式离子转换控释肥料的制备方法
技术领域
本发明属于化肥领域,涉及浓缩化肥,尤其是一种接力式离子转换控释肥料的制备方法。
背景技术
化肥在农业生产中占有重要地位,是农业生产中最大的物质投资,约占其全部生产性支出的50%左右。农业实践表明,肥料性质与土壤环境条件的综合影响使肥料利用率低是化肥使用中普遍存在的问题。目前国外化肥利用率约为50-55%,我国化肥利用率约为35%,养分通常经冲淋、分解、水溶性磷转化成难溶的构溶性磷等流失。化肥的利用率太低会造成超量施肥,使土壤的物理性质不断恶化,这样会影响农作物的产量和质量的提高。因此,采用包膜化肥用于提高化肥利用率和降低环境污染成为一种趋势。
离子转换控释技术,是将高分子纤维脂离子添加在肥料中,使其直接参与肥料中的离子转换,调节肥料在土壤中的水解速度,从而达到控制释放的目的。当肥料施入土壤后,高分子纤维脂离子可通过土壤的湿度自动调整膨胀系数,利用膨胀系数调整肥料颗粒的微细孔的吸、阻水能力控制养分释放速度。养分释放的时间周期是根据不同的高分子纤维脂离子的组合和比例,控制肥料颗粒在不同阶段的时间释放,达到接力释放的目的。接力释放包括前期释放、中期释放及后期释放,与农作物吸收养分的规律相一致,能够使肥料在硝化过程中养分释放速率始终保持平稳状态,有效提高了养分的利用率。
通过检索,虽发现相关文献多篇,但均与本专利申请有较大的不同。
发明内容
本发明的目的在于克服现有技术的不足之处,提供一种肥料效果好、环境污染小、经济效益高的接力式离子转换控释肥料的制备方法。
本发明的目的是通过以下技术方案实现的:
一种接力式离子转换控释肥料的制备方法,其制备方法的步骤为:
(1)按重量配比向反应釜内加水及聚丙烯胺,将反应釜加热到90℃,加热时间40分钟,搅拌均匀;
(2)将反应釜降温到80℃,然后按重量配比加入玉米淀粉,加完后,保温0.5小时,均匀搅拌;
(3)将反应釜升温至95℃,按重量配比添加松香,保温50分钟,搅拌均匀;
(4)向反应釜内按重量配比添加液体石蜡,搅拌均匀,保持搅拌及温度1小时;
(5)将反应釜降温至80℃,然后按重量配比添加膨润土,搅拌均匀,即可出料。
而且,所述各物质及其重量百分比范围分别为:
聚丙酰胺  4%-6%;
玉米淀粉  8%-12%;
松香      4%-6%;
液体石蜡  4%-6%;
膨润土    4%-6%;
其余加水至100%。
本发明的优点和积极效果是:
1、本方法所制肥料克服了国内外所广泛使用的速效化肥普遍存在的利用率低、环境污染严重的问题,肥料效果好,环境污染小,经济效益高,制作简单容易,成本低廉,养分利用率达到65%。
2、本方法所制肥料使高分子纤维脂在肥料中产生离子转换过程,从而实现肥料养分在不同时期接力式释放。
3、本方法所制肥料通过控制肥料的不同释放时间的三个反应釜,在计量泵的控制下,将三种物料间断地输入到一个转鼓内,利用时间差和鼓内设置区域装置,同时生产出具有三种不同释放时间的空使肥料,整个工艺设计科学。
具体实施方式
以下结合具体实施方法来进一步说明本发明;需要强调的是:对于本领域普通技术人员来说,可以根据上述说明加以改进或变换,而所有这些改进和变换都应属于本发明所附权利要求的保护范围。
实施例1:
一种接力式离子转换控释肥料的制备方法,其原料构成及其重量百分比分别为:
聚丙酰胺  5%;
玉米淀粉  10%;
松香      5%;
液体石蜡  5%;
膨润土    5%;
水        70%。
制备方法的步骤为:
(1)按重量配比向反应釜内加水及聚丙烯胺,将反应釜加热到90℃,加热时间40分钟,搅拌均匀;
(2)将反应釜降温到80℃,然后按重量配比加入玉米淀粉,加完后,保温0.5小时,均匀搅拌;
(3)将反应釜升温至95℃,按重量配比添加松香,保温50分钟,搅拌均匀;
(4)向反应釜内按重量配比加入液体石蜡,搅拌均匀,保持搅拌及温度1小时;
(5)将反应釜降温至80℃,然后按重量配比添加膨润土,搅拌均匀,即可出料。
上述得到的肥料,经过实验,养分利用率65%左右,远远大于现有的速效肥料33%的养分利用率。
实施例2:
一种接力式离子转换控释肥料的制备方法,其原料构成及其重量百分比分别为:
聚丙酰胺  6%;
玉米淀粉  8%;
松香      4%;
液体石蜡  6%;
膨润土    4%;
水        72%。
其制备方法的步骤及内容同于实施例1。
实施例3:
一种接力式离子转换控释肥料的制备方法,其原料构成及其重量百分比范围分别为:
聚丙酰胺  4%;
玉米淀粉  12%;
松香      6%;
液体石蜡  4%;
膨润土    6%;
水        68%。
其制备方法的步骤及内容同于实施例1。

Claims (2)

1.一种接力式离子转换控释肥料的制备方法,其特征在于:其制备方法的步骤为:
(1)按重量配比向反应釜内加水及聚丙烯胺,将反应釜加热到90℃,加热时间40分钟,搅拌均匀;
(2)将反应釜降温到80℃,然后按重量配比加入玉米淀粉,加完后,保温0.5小时,均匀搅拌;
(3)将反应釜升温至95℃,按重量配比添加松香,保温50分钟,搅拌均匀;
(4)向反应釜内按重量配比加入液体石蜡,搅拌均匀,保持搅拌及温度1小时;
(5)将反应釜降温至80℃,然后按重量配比添加膨润土,搅拌均匀,即可出料。
2.根据权利要求1所述的接力式离子转换控释肥料的制备方法,其特征在于:所述各物质及其重量百分比范围分别为:
聚丙酰胺  4%-6%;
玉米淀粉  8%-12%;
松香      4%-6%;
液体石蜡  4%-6%;
膨润土    4%-6%;
其余加水至100%。
CN201110238627A 2011-08-19 2011-08-19 接力式离子转换控释肥料的制备方法 Pending CN102303999A (zh)