CN102303343A

CN102303343A - Comb connection method

Info

Publication number: CN102303343A
Application number: CN201110311579A
Authority: CN
Inventors: 陈基禄; 周月林
Original assignee: WUXI COUNTY FARUI WOODEN PRODUCTS PROFESSIONAL COOPERATION
Current assignee: WUXI COUNTY FARUI WOODEN PRODUCTS PROFESSIONAL COOPERATION
Priority date: 2011-10-14
Filing date: 2011-10-14
Publication date: 2012-01-04

Abstract

The invention relates to a comb connection method. A comb handle and a comb tooth body are combined into a comb through a comb handle connecting face and a comb tooth body connecting face, the comb handle is characterized in that the cross section thereof is parallel to the texture thereof, the comb tooth body is characterized in that the comb teeth thereof is parallel to the texture thereof, and in order to enhance the connection, latex is respectively coated on the comb handle connecting face and the comb tooth body connecting face before combination; the method of the invention can be applied to comb processes, the comb processed and manufactured according to the method of the invention has the characteristic that the comb handle and the texture of the comb tooth body are vertical to the stressed direction, thus increasing the force withstanding ability of combs and prolonging the service life of wooden combs.

Description

The method that comb connects

Technical field

The present invention relates to the method that comb connects, particularly the method that is connected with the broach body by the comb handle.

Background technology

Comb is the instrument of combing hair, be one of indispensable apparatus in people's daily life, so wooden comb enjoys liking of people.At present, the comb handle and the broach of wooden comb is connected as a single entity on the market, and be owing to be subjected to force direction vertical with broach, parallel with the timber striped with the comb of wide grained wood processing after comb gets wet and is used multiple times, and causes the resistance of band broach to reduce and rupture easily.Same, with perpendicular line Wood Processing comb, owing to be subjected to force direction vertical with the comb handle, parallel with the timber striped, cause the resistance of perpendicular line comb handle to reduce and fracture easily.The comb that the method for using comb handle and broach to be connected as a single entity is processed can't be taken into account the easy fracture problem of broach and comb handle simultaneously.With the comb handle of band materials processing comb,, the broach and the comb handle that process are inlayed the resistance that increases broach and comb handle simultaneously with the broach of perpendicular grain material processing comb.At present, not open manufacture craft about comb handle and broach combined comb.Therefore, be badly in need of the method that a kind of comb connects, broach and band materials processing comb handle that perpendicular grain material is processed make up, and prolong the service life of woodwork comb.

Summary of the invention

In view of this,, solve comb broach and comb handle easy fracture problem, adopt following technical scheme in order originally to overcome above defective:

The method that comb connects; To comb handle and broach body and connect into comb through comb handle joint face and broach body joint face; The cross section that said comb handle is said comb handle is parallel with the texture of said comb handle, and the broach that said broach body is said broach body is parallel with the texture of said broach body.

Further, coat latex respectively at said comb handle joint face and broach body joint face before the connection.

Further, said latex contains 38 parts in 6 parts of oxidised maize starch, 0.5 part of sodium acid carbonate, 0.2 part of ammonium persulfate, 1 part of borax, 5 parts of polyvinyl alcohol, 50 parts in NaOH and water.

Further, be cured pressurization after connecting, be specially: in temperature is to handle more than 1.5 hours under the 7-45 ℃ of condition.

Further, to be pressurised in temperature be to handle under 25 ℃ of conditions 1.5 hours in said curing.

Further, release is placed, and is specially: release, placed 24-72 hour then.

Further, said release is placed as release, places then 24 hours.

Beneficial effect of the present invention is: according to the stressing conditions of comb, select the broach of the processing respectively body and comb handle of suitable striped; The comb handle band materials processing of comb makes to be subjected to force direction vertical with the striped of timber, and its comb handle is easy fracture not; The perpendicular grain material processing of the broach body and function of comb; Make broach identical with the grain direction of material during tooth punching, make to be subjected to force direction vertical with the striped of timber, its broach is easy fracture not.Broach with different texture processing makes up with the comb handle then, and broach has stronger resistance simultaneously with the comb handle, has prolonged the service life of comb simultaneously.

Other advantages of the present invention, target and characteristic will be set forth in specification subsequently to a certain extent; And to a certain extent; Based on being conspicuous to those skilled in the art, perhaps can from practice of the present invention, obtain instruction to investigating hereinafter.

Description of drawings

Fig. 1 is a comb constitutional diagram of the present invention.

The specific embodiment

Below will combine embodiment that the present invention is carried out detailed description.The experimental technique of unreceipted actual conditions in the preferred embodiment is usually according to normal condition.

Embodiment 1

Coat the latexes that composition is 6 parts of oxidised maize starch, 0.5 part of sodium acid carbonate, 0.2 part of ammonium persulfate, 1 part of borax, 5 parts of polyvinyl alcohol, 50 parts in NaOH and 38 parts of mixing compositions of water respectively at the joint face of comb handle 2 and the joint face of broach body 1.Then that cross section is parallel with the texture of comb handle comb handle is connected with broach body joint face through comb handle joint face with the parallel broach body of the texture of broach body with the broach of broach body, is combined into comb, shown in accompanying drawing 1.The comb of combination is solidified pressurization, is to handle 1.5 hours under 25 ℃ of conditions in temperature promptly, and release was then placed 24 hours then.

Embodiment 2

Coat the latexes that composition is 6 parts of oxidised maize starch, 0.5 part of sodium acid carbonate, 0.2 part of ammonium persulfate, 1 part of borax, 5 parts of polyvinyl alcohol, 50 parts in NaOH and 38 parts of mixing compositions of water respectively at the joint face of comb handle 2 and the joint face of broach body 1.Then that cross section is parallel with the texture of comb handle comb handle is connected with broach body joint face through comb handle joint face with the parallel broach body of the texture of broach body with the broach of broach body, is combined into comb, shown in accompanying drawing 1.The comb of combination is solidified pressurization, is to handle more than 2 hours under 45 ℃ of conditions in temperature promptly, and release was then placed 72 hours then.

Embodiment 3

Coat the latexes that composition is 6 parts of oxidised maize starch, 0.5 part of sodium acid carbonate, 0.2 part of ammonium persulfate, 1 part of borax, 5 parts of polyvinyl alcohol, 50 parts in NaOH and 38 parts of mixing compositions of water respectively at the joint face of comb handle 2 and the joint face of broach body 1.Then that cross section is parallel with the texture of comb handle comb handle is connected with broach body joint face through comb handle joint face with the parallel broach body of the texture of broach body with the broach of broach body, is combined into comb, shown in accompanying drawing 1.The comb of combination is solidified pressurization, is to handle more than 3 hours under 7 ℃ of conditions in temperature promptly, and release was then placed 36 hours then.

Above embodiment can and comb handle 2 firm combining with broach body 1, and all according to grain direction processing, the comb that processing obtains is not fragile, can prolong the service life of comb.

Explanation is at last; Above embodiment is only unrestricted in order to technical scheme of the present invention to be described; Although through invention has been described with reference to the preferred embodiments of the present invention; But those of ordinary skill in the art is to be understood that; Can make various changes to it in the form and details, and the spirit and scope of the present invention that do not depart from appended claims and limited.

Claims

1. the method that connects of comb; Be characterised in that: will comb handle (2) and connect into comb through comb handle joint face and broach body joint face with broach body (1); Said comb handle (2) is that the cross section of said comb handle is parallel with the texture of said comb handle, and said broach body (1) is that the broach of said broach body is parallel with the texture of said broach body.

2. the method for comb connection is characterised in that: coat latex respectively at said comb handle joint face and broach body joint face before connecting.

3. the method that connects according to claim 2 comb is characterized in that, said latex contains 38 parts in 6 parts of oxidised maize starch, 0.5 part of sodium acid carbonate, 0.2 part of ammonium persulfate, 1 part of borax, 5 parts of polyvinyl alcohol, 50 parts in NaOH and water.

4. the method that connects according to the said comb of claim 3 is characterized in that, is cured pressurization after connecting, and is specially: in temperature is to handle more than 1.5 hours under the 7-45 ℃ of condition.

5. the method that connects according to the said comb of claim 4 is characterized in that, it is to handle 1.5 hours under 25 ℃ of conditions that said curing is pressurised in temperature.

6. the method that connects according to the said comb of claim 4 is characterized in that, solidifies also to comprise that release places after the pressurization, is specially: release, placed 24-72 hour then.

7. the method that connects according to the said comb of claim 6 is characterized in that said release is placed as release, places then 24 hours.