CN102275314A - 一种增强点阵夹芯板吸能减振功能的方法 - Google Patents

一种增强点阵夹芯板吸能减振功能的方法 Download PDF

Info

Publication number
CN102275314A
CN102275314A CN2011102222525A CN201110222252A CN102275314A CN 102275314 A CN102275314 A CN 102275314A CN 2011102222525 A CN2011102222525 A CN 2011102222525A CN 201110222252 A CN201110222252 A CN 201110222252A CN 102275314 A CN102275314 A CN 102275314A
Authority
CN
China
Prior art keywords
dot
sandwich panel
room temperature
matrix sandwich
silicon rubber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011102222525A
Other languages
English (en)
Inventor
吴林志
殷莎
彭亮
马力
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Harbin Institute of Technology
Original Assignee
Harbin Institute of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Harbin Institute of Technology filed Critical Harbin Institute of Technology
Priority to CN2011102222525A priority Critical patent/CN102275314A/zh
Publication of CN102275314A publication Critical patent/CN102275314A/zh
Pending legal-status Critical Current

Abstract

一种增强点阵夹芯板吸能减振功能的方法，它涉及一种增强夹芯板吸能减振功能的方法。本发明为了解决现有的点阵夹芯结构本身抵抗冲击和抗振动的作用弱的问题。本发明的步骤：步骤一，将点阵夹芯板的一边作为注入口，将点阵夹芯板的其余三边采用密封带进行密封；步骤二，将双组份室温硫化硅橡胶中的基料和固化剂按照重量份数比100∶1至100∶3的比例放入一容器中充分搅拌，再经真空脱泡后直接注入到点阵结构的空隙中；步骤三，将浇灌双组份室温硫化硅橡胶后的点阵夹芯板，在室温下放置12至24小时，待双组份室温硫化硅橡胶硫化后，取下密封带，完成点阵夹芯板吸能减振功能的强化。本发明用于强化点阵夹芯板的吸能减振功能。

Description

一种增强点阵夹芯板吸能减振功能的方法
技术领域
本发明涉及一种点阵夹芯板的制备方法，具体涉及一种增强点阵夹芯板吸能减振功能的方法。
背景技术
点阵夹芯结构是一类轻质高效的结构，由于它优异的力学性能和功能可设计性，越来越显示出其在航空航天、交通、能源等领域的应用前景。但是，因为这种点阵夹芯结构本身抵抗冲击和抗振动的作用弱，所以限制了点阵夹芯板的应用发展。
发明内容
本发明的目的是为了解决现有的点阵夹芯结构本身抵抗冲击和抗振动的作用弱的问题，进而提供一种增强点阵夹芯板吸能减振功能的方法。
本发明的技术方案是：一种增强点阵夹芯板吸能减振功能的方法的具体步骤为：
步骤一，将点阵夹芯板的一边作为注入口，将点阵夹芯板的其余三边采用密封带进行密封；
步骤二，将双组份室温硫化硅橡胶中的基料和固化剂按照重量份数比100∶1至100∶3的比例放入一容器中充分搅拌，再经真空脱泡后直接注入到点阵结构的空隙中；
步骤三，将浇灌双组份室温硫化硅橡胶后的点阵夹芯板，在室温下放置12至24小时，待双组份室温硫化硅橡胶硫化后，取下密封带，完成点阵夹芯板吸能减振功能的强化。
本发明与现有技术相比具有以下效果：本发明将点阵夹芯板的力学性能与双组份室温硫化硅橡胶的阻尼性能相结合，从而制得复合结构，不仅满足了高比刚度、高比强度的结构性能要求，还兼备优良的阻尼减震性能。本发明的增强点阵夹芯板吸能减振功能的方法的制备技术简单，强化了点阵夹芯板的抗冲击及振动性能突出，在航空及航天领域具有广泛的应用前景。
具体实施方式
具体实施方式一：本实施方式的一种增强点阵夹芯板吸能减振功能的方法的具体步骤为：
步骤一，将点阵夹芯板的一边作为注入口，将点阵夹芯板的其余三边采用密封带进行密封；
步骤二，将双组份室温硫化硅橡胶中的基料和固化剂按照重量份数比100∶1至100∶3的比例放入一容器中充分搅拌，再经真空脱泡后直接注入到点阵结构的空隙中；
步骤三，将浇灌双组份室温硫化硅橡胶后的点阵夹芯板，在室温下放置12至24小时，待双组份室温硫化硅橡胶硫化后，取下密封带，完成点阵夹芯板吸能减振功能的强化。
所述双组份室温硫化硅橡胶为外购，其型号为RTV-2(5080)的固加硅橡胶。
具体实施方式二：本实施方式的步骤二中，将双组份室温硫化硅橡胶中的基料和固化剂按照重量份数比100∶2的比例放入一容器中充分搅拌。双组份室温硫化硅橡胶的耐老化和耐候性更好。其它步骤与具体实施方式一相同。
具体实施方式三：本实施方式的步骤三中，将浇灌双组份室温硫化硅橡胶后的点阵夹芯板，在室温下放置12小时。其它步骤与具体实施方式一相同。
具体实施方式四：本实施方式的步骤三中，将浇灌双组份室温硫化硅橡胶后的点阵夹芯板，在室温下放置13小时。其它步骤与具体实施方式一相同。
具体实施方式五：本实施方式的步骤三中，将浇灌双组份室温硫化硅橡胶后的点阵夹芯板，在室温下放置14小时。其它步骤与具体实施方式一相同。
具体实施方式六：本实施方式的步骤三中，将浇灌双组份室温硫化硅橡胶后的点阵夹芯板，在室温下放置15小时。其它步骤与具体实施方式一相同。
具体实施方式七：本实施方式的步骤三中，将浇灌双组份室温硫化硅橡胶后的点阵夹芯板，在室温下放置16小时。其它步骤与具体实施方式一相同。
具体实施方式八：本实施方式的步骤三中，将浇灌双组份室温硫化硅橡胶后的点阵夹芯板，在室温下放置17小时。其它步骤与具体实施方式一相同。
具体实施方式九：本实施方式的步骤三中，将浇灌双组份室温硫化硅橡胶后的点阵夹芯板，在室温下放置18小时。其它步骤与具体实施方式一相同。
具体实施方式十：本实施方式的步骤三中，将浇灌双组份室温硫化硅橡胶后的点阵夹芯板，在室温下放置19小时。其它步骤与具体实施方式一相同。
具体实施方式十一：本实施方式的步骤三中，将浇灌双组份室温硫化硅橡胶后的点阵夹芯板，在室温下放置20小时。其它步骤与具体实施方式一相同。
具体实施方式十二：本实施方式的步骤三中，将浇灌双组份室温硫化硅橡胶后的点阵夹芯板，在室温下放置21小时。其它步骤与具体实施方式一相同。
具体实施方式十三：本实施方式的步骤三中，将浇灌双组份室温硫化硅橡胶后的点阵夹芯板，在室温下放置22小时。其它步骤与具体实施方式一相同。
具体实施方式十四：本实施方式的步骤三中，将浇灌双组份室温硫化硅橡胶后的点阵夹芯板，在室温下放置23小时。其它步骤与具体实施方式一相同。
具体实施方式十五：本实施方式的步骤三中，将浇灌双组份室温硫化硅橡胶后的点阵夹芯板，在室温下放置24小时。其它步骤与具体实施方式一相同。
具体实施方式十六：本实施方式的步骤三中，将浇灌双组份室温硫化硅橡胶后的点阵夹芯板，在室温下放置12至15小时。其它步骤与具体实施方式一相同。
具体实施方式十七：本实施方式的步骤三中，将浇灌双组份室温硫化硅橡胶后的点阵夹芯板，在室温下放置15至20小时。其它步骤与具体实施方式一相同。
具体实施方式十八：本实施方式的步骤三中，将浇灌双组份室温硫化硅橡胶后的点阵夹芯板，在室温下放置20至24小时。其它步骤与具体实施方式一相同。
具体实施方式十九：本实施方式的步骤一中，点阵夹芯板为金字塔型点阵夹芯板或四面体型点阵夹芯板。其它步骤与具体实施方式一至十八相同。
具体实施方式二十：本实施方式的步骤一中，点阵夹芯板为空心圆管金字塔型点阵夹芯板或空心圆管四面体型点阵夹芯板。其它步骤与具体实施方式一至十八相同。

Claims (7)

1.一种增强点阵夹芯板吸能减振功能的方法，其特征在于：增强点阵夹芯板吸能减振功能的方法的具体步骤为：
步骤一，将点阵夹芯板的一边作为注入口，将点阵夹芯板的其余三边采用密封带进行密封；
步骤二，将双组份室温硫化硅橡胶中的基料和固化剂按照重量份数比100∶1至100∶3的比例放入一容器中充分搅拌，再经真空脱泡后直接注入到点阵结构的空隙中；
步骤三，将浇灌双组份室温硫化硅橡胶后的点阵夹芯板，在室温下放置12至24小时，待双组份室温硫化硅橡胶硫化后，取下密封带，完成点阵夹芯板吸能减振功能的强化。
2.根据权利要求1所述的一种增强点阵夹芯板吸能减振功能的方法，其特征在于：步骤二中，将双组份室温硫化硅橡胶中的基料和固化剂按照重量份数比100∶2的比例放入一容器中充分搅拌。
3.根据权利要求1所述的一种增强点阵夹芯板吸能减振功能的方法，其特征在于：步骤三中，将浇灌双组份室温硫化硅橡胶后的点阵夹芯板，在室温下放置12至15小时。
4.根据权利要求1所述的一种增强点阵夹芯板吸能减振功能的方法，其特征在于：步骤三中，将浇灌双组份室温硫化硅橡胶后的点阵夹芯板，在室温下放置15至20小时。
5.根据权利要求1所述的一种增强点阵夹芯板吸能减振功能的方法，其特征在于：步骤三中，将浇灌双组份室温硫化硅橡胶后的点阵夹芯板，在室温下放置20至24小时。
6.根据权利要求1所述的一种增强点阵夹芯板吸能减振功能的方法，其特征在于：步骤一中，点阵夹芯板为金字塔型点阵夹芯板或四面体型点阵夹芯板。
7.根据权利要求1所述的一种增强点阵夹芯板吸能减振功能的方法，其特征在于：步骤一中，点阵夹芯板为空心圆管金字塔型点阵夹芯板或空心圆管四面体型点阵夹芯板。
CN2011102222525A 2011-08-04 2011-08-04 一种增强点阵夹芯板吸能减振功能的方法 Pending CN102275314A (zh)