CN102269679A - Method for measuring wear resistance of inner lining paper for cigarettes - Google Patents
Method for measuring wear resistance of inner lining paper for cigarettes Download PDFInfo
- Publication number
- CN102269679A CN102269679A CN 201110168340 CN201110168340A CN102269679A CN 102269679 A CN102269679 A CN 102269679A CN 201110168340 CN201110168340 CN 201110168340 CN 201110168340 A CN201110168340 A CN 201110168340A CN 102269679 A CN102269679 A CN 102269679A
- Authority
- CN
- China
- Prior art keywords
- sample
- friction
- lining paper
- paper
- chromatism
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a method for measuring wear resistance of inner lining paper for cigarettes. The method comprises the following steps: randomly marking measurement points on a sample to be measured, and using an integrating sphere type spectrophotometer to measure the original color difference value of each measurement point before wear; and after rubbing the front surface of the sample to be measured and white paper 40 times on an ink friction instrument, measuring the color difference value after wear, wherein the difference between the two color difference values is a quantitative evaluation index for determining the wear resistance of the inner lining paper for the cigarettes; and the smaller the difference is, the better the wear resistance is. By adopting the method, the wear resistance of the inner lining paper for the cigarettes can be conveniently and quickly measured. The machine friction in the process of putting the sample on the machine can be simulated and the quantitative analysis can be performed on the wear resistance of the sample. The measurement result is accurate and reliable, and objective and scientific evaluation and measurement can be performed on the wear resistance of the sample. The method has practical significance for ensuring the quality and the using effects of the inner lining paper for the cigarettes.
Description
Technical field
The invention belongs to cigarette supplementary physical and chemical inspection technical field, be specifically related to a kind of method of measuring the tobacco lining paper anti-wear performance.
Background technology
Tobacco lining paper is the paper that is lining in soft box of cigarette or hard box internal layer, and cigarette is played certain protection against the tide, damp proof effect, prevents that cigarette from going mouldy and fragrance loss.The quality of wearing quality directly influences its result of use on the packaging.The tobacco lining paper that wears no resistance in packaging process since the friction of machine can cause in the lining paper surface spent by mill, or the packing quality problems such as bad that are shaped, the degree of uniformity of wearing quality also directly has influence on the forming effect of packing, the place that wearing quality is good is shaped smooth, the place that the wears no resistance easy feeler that is shaped, not only can cause hidden danger of quality, also can influence the appearance of packing.But, also do not have at present comparatively the assay method of science that the tobacco lining paper anti-wear performance is estimated.Be to guarantee inherence, the external quality of cigarette product, set up a kind of standard, objective and scientific methods and come the anti-wear performance of tobacco lining paper is measured and evaluation has great importance.
Summary of the invention
The objective of the invention is at the deficiencies in the prior art, a kind of assay method of tobacco lining paper wearing quality is provided, so that the anti-wear performance of tobacco lining paper is carried out the evaluation of objective science.
Purpose of the present invention is achieved by the following technical programs.
The assay method of tobacco lining paper wearing quality may further comprise the steps:
(1) tobacco lining paper is cut into the testing sample of 13.0mm * 5.0mm;
(2) on each sample, demarcate 10 measuring points at random,, obtain mean value, be the preceding original value of chromatism of mill with the aberration of each measuring point on the integrating sphere type spectrophotometric determination sample;
(3) narrow two side faces is stained with Double-face gummed paper respectively on two sides narrow on the printing ink friction instrument friction table top and abrading block face;
(4) get a clean blank sheet of paper and adhere on the wear resistant instrument friction table top,, promptly prop up the opposite face simultaneously that contacts and adhere to outwardly on the abrading block, start printing ink friction instrument, the test sample front is rubbed mutually with blank sheet of paper with cigarette with the test sample front;
(5) after the friction 40 times, the sample on the abrading block is taken off, measure the value of chromatism after the friction of each measuring point, obtain mean value, i.e. mill back value of chromatism;
(6) deduct the preceding original value of chromatism of mill to grind the back value of chromatism, the aberration difference before and after obtaining rubbing, this difference is the quantitative evaluation index of tobacco lining paper anti-wear performance, and the difference bright anti-wear performance of novel more is good more.
The present invention has the following advantages: this method can conveniently be measured the tobacco lining paper anti-wear performance.Can simulate the machine friction of going up in the machine process, the anti-wear performance of sample is made quantitative test.Its measurement result can be carried out the evaluation and the judgement of objective science to the sample wearing quality accurately and reliably.Quality and the result of use that guarantees tobacco lining paper had realistic meaning.
Embodiment
The present invention is described in further detail below by embodiment, but embodiment is not the qualification to the technology of the present invention feature.
Embodiment 1
One, definition:
Anti-wear performance: refer to the tobacco lining paper surface interaction energy of the friction force performance of bearing outside.This method is to represent with the variation of value of chromatism, and promptly tobacco lining paper is through certain pressure, and after the friction of speed and number of times, its friction back value of chromatism deducts the resulting difference of value of chromatism before the friction.The more little anti-wear performance of difference is good more, otherwise then poor more.
Two, reference to standard
The mensuration of GB/T 7975 paper and cardboard color (diffuse reflection method)
The standard atmosphere condition that GB/T 10739 paper, cardboard and paper pulp sample are handled and tested
Three, determining instrument
3.1. integrating sphere type spectrophotometer, model are SP64, U.S. X-Rite, and Incorporated Ai Seli incorporated company produces.
3.2. printing ink frictiograph, model are 10-18-01-0002, U.S. TESTING MACHINES company produces.Abrading block adopts 2 pounds (0.96 kilogram); Test speed: 85 times/minute; Cycle index: 40 times.
Four, condition determination
Temperature: 23 ± 1 ℃; Relative humidity: 50 ± 2%.
Five, assay method
In whole mensuration process, the testing sample surface cleaning be should guarantee, hand or other article contact measurement position forbidden.
5.1. prepare tobacco lining paper sample to be measured, sample is cut into about 13.0mm * 5.0mm.
5.2. on each sample, demarcate 10 measuring points at random, with the aberration of each measuring point of SP64 series integrating sphere type spectrophotometric determination sample, obtain mean value, be the preceding original value of chromatism of mill, note is made A
1
5.3. narrow two side faces is stained with Double-face gummed paper on two sides narrow on the printing ink friction instrument friction table top and abrading block face.
5.4. get a clean blank sheet of paper, adhere on the wear resistant instrument friction table top, the sample outside is adhered on the abrading block outwardly, start printing ink friction instrument and carry out outer externally friction.
, after 40 times the sample on the abrading block is taken off 5.5. rub, measure each measuring point friction back value of chromatism, obtain mean value, promptly mill back value of chromatism is remembered and is A
2
5.6 mill back value of chromatism deducts the preceding original value of chromatism of friction, the aberration difference before and after obtaining rubbing, and note is made A
0, this difference is the quantitative evaluation index of tobacco lining paper anti-wear performance, and the difference bright anti-wear performance of novel more is good more.
Six, the calculating of measurement result and expression:
A
0?=?A
2?—?A
1
In the formula: A
0Aberration difference before and after the-friction
A
2Value of chromatism after the-friction
A
1-original value of chromatism
Use this assay method to 3 tobacco lining paper samples anti-wear performance carried out practical measurement, resulting data are shown in table 1～3.
Table 1 sample 1
#The anti-wear performance test result
Table 2 sample 2
#The anti-wear performance test result
Table 3 sample 3
#The anti-wear performance test result
Claims (1)
1. the assay method of a tobacco lining paper wearing quality may further comprise the steps:
(1) tobacco lining paper is cut into the testing sample of 13.0mm * 5.0mm;
(2) on each sample, demarcate 10 measuring points at random,, obtain mean value, be the preceding original value of chromatism of mill with the aberration of each measuring point on the integrating sphere type spectrophotometric determination sample;
(3) narrow two side faces is stained with Double-face gummed paper respectively on two sides narrow on the printing ink friction instrument friction table top and abrading block face;
(4) get a clean blank sheet of paper and adhere on the wear resistant instrument friction table top,, promptly prop up the opposite face simultaneously that contacts and adhere to outwardly on the abrading block, start printing ink friction instrument, the test sample front is rubbed mutually with blank sheet of paper with cigarette with the test sample front;
(5) after the friction 40 times, the sample on the abrading block is taken off, measure the value of chromatism after the friction of each measuring point, obtain mean value, i.e. mill back value of chromatism;
(6) deduct the preceding original value of chromatism of mill to grind the back value of chromatism, the aberration difference before and after obtaining rubbing, this difference is the quantitative evaluation index of tobacco lining paper anti-wear performance, and the difference bright anti-wear performance of novel more is good more.