CN102268176A - Method for preparing PET (Polyethylene Terephthalate) acarus expelling high polymer material - Google Patents
Method for preparing PET (Polyethylene Terephthalate) acarus expelling high polymer material Download PDFInfo
- Publication number
- CN102268176A CN102268176A CN2011102437866A CN201110243786A CN102268176A CN 102268176 A CN102268176 A CN 102268176A CN 2011102437866 A CN2011102437866 A CN 2011102437866A CN 201110243786 A CN201110243786 A CN 201110243786A CN 102268176 A CN102268176 A CN 102268176A
- Authority
- CN
- China
- Prior art keywords
- pet
- mite
- oligopolymer
- poly
- grafting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for preparing a PET (Polyethylene Terephthalate) acarus expelling high polymer material. The method comprises the following steps of: (1) grafting an ammonia low polymer (such as a low polymer of hexanediamine) with PET, and grafting with a guanidine salt (polyhexamethylene panoctine, hydrochloric acid polyhexamethylene guanidine and the like) to obtain antibacterial master batch; (2) dehumidifying the prepared antibacterial master batch; (3) weighing raw materials according to a formula, and uniformly stirring; and (4) granulating by using a double screw extruder to control the feeding speed for preventing the raw materials from being degraded. The method has the advantages that: the PET acarus expelling high polymer material prepared with the method has an efficient broad-spectrum antimicrobial and antivirus effect, a durable effect, high performance, excellent quality and reasonable price, is extremely safe to human bodies, and is easy to prepare.
Description
Technical field
The present invention relates to polymeric material field, the become preparation method of mite macromolecular material of particularly a kind of PET.
Background technology
The mite macromolecular material that becomes can suppress and kills microorganisms such as the dirt mite that adheres to, gamasid, trombiculid, demodicid mite, has good anti-microbial effect, is widely used in fields such as room, sanitary ware, daily necessities, communal facility, clothes, industrial filter material.But no matter be to be that representative is adopted the material of organic anti-bacterial or is the inorganic nano antibacterial material of representative with Japan with America and Europe, the mite macromolecular material that becomes that comes out by its preparation technology and flow preparation, all more or less there is the antiseptic-germicide stripping, jeopardize human body safety and antibacterial effect and be difficult to defectives such as lasting, can't satisfy the user demand of combating microorganisms material.
Summary of the invention
In order to overcome above-mentioned defective, the present invention proposes a class does not have stripping, the preparation method of mite macromolecular material that becomes of the PET with the viral effect of the antibiotic anti-reality of high-efficiency broad spectrum.
The present invention for the technical scheme that solves its technical problem and adopt is:
The become preparation method of mite macromolecular material of a kind of PET, it may further comprise the steps:
(1) at first uses Ammonia the oligopolymer oligopolymer and the PET grafting of diamines, prepare antibacterial matrices with poly-six inferior Guanoctines of guanidinesalt or the poly-hexamethyl guanidine grafting of hydrochloric acid again;
(2) antibacterial matrices to preparation carries out dehumidification treatments;
(3) take by weighing raw material by prescription, stir;
(4) utilize dual-screw-stem machine to go out granulation.
The further improvement of the technical program is: described raw material is made up of following components in weight percent:
Polyethylene terephthalate: 92.9~96.3%;
Antioxidant: 0.1~0.3%; Nucleator: 0.3~1%;
Lubricant: 0.3~0.8%; Antiseptic-germicide: 3~5%;
Oxidation inhibitor is selected four [β-(3 for use, 5-di-t-butyl-4-phenyl) propionic acid] pentaerythritol ester, three [2.4-di-tert-butyl-phenyl] phosphorous acid ester, 1,3,5-three (the 4-tertiary butyl-3-hydroxyl-2, the 6-dimethyl benzyl)-1,3,5-triazine-2,4,6-(1H, 3H, 5H)-triketone, 2, wherein one or both of two-three grades of butyl of 6--4-sylvan;
Nucleator is to select the macromolecular compound polyester, and polyoxyethylene glycol is a kind of in the polyolefine;
Lubricant is selected one or both in polyethylene low-molecular-weight wax, oxidic polyethylene, the stearate for use;
Antiseptic-germicide is with the oligopolymer of Ammonia oligopolymer diamines and poly-six inferior Guanoctines of guanidinesalt or the poly-a kind of high molecular polymer of hexamethyl guanidine grafted on polyethylene terephthalate of hydrochloric acid.
The further improvement of the technical program is: the processing parameter of described dual-screw-stem machine is as follows:
Temperature: 220~230 ℃
Die head: 250 ℃
Main frame current control: 90~110A
Melt pressure: 1~2mpa
Melt temperature: 200~210 ℃
Engine speed: 400~2430RPM
Rotating speed feeds intake: 5~10RPM
Vacuum pressure: 0.6~0.8 mpa.
The invention has the beneficial effects as follows: the PET mite macromolecular material that becomes has the effect of the antibiotic anti-real virus of high-efficiency broad spectrum, and effect is lasting, and excellent property has very safely to human body, and be easy to processing, and is inexpensive.
Embodiment
In order to deepen the understanding of the present invention, the invention will be further described below in conjunction with embodiment and accompanying drawing, and this embodiment only is used to explain the present invention, does not constitute the qualification to protection domain of the present invention.
Embodiment:
Wherein: be that the PET of the 100kg mite macromolecular material that becomes is row with the weight part.
Embodiment one: the become preparation method of mite macromolecular material of a kind of PET, and it may further comprise the steps:
(1) at first uses Ammonia the oligopolymer oligopolymer and the PET grafting of diamines, prepare antibacterial matrices with the poly-six inferior Guanoctine grafting of guanidinesalt again;
(2) antibacterial matrices to preparation carries out dehumidification treatments;
(3) take by weighing raw material by prescription, stir;
(4) utilize dual-screw-stem machine to go out granulation;
Get polyethylene terephthalate (PET): 92.9kg; Antioxidant: 0.3kg; Nucleator: 1kg; Lubricant: 0.8kg; Antiseptic-germicide: 5kg, getting raw material stirring is even, and the manufacturing parameter with dual-screw-stem machine is set at then: temperature: 220 ℃; Die head: 250 ℃; Main frame current control: 90A; Melt pressure: 1mpa; Melt temperature: 200 ℃; Engine speed: 400RPM; Rotating speed feeds intake: 5RPM; Vacuum pressure: 0.6 mpa; Utilize dual-screw-stem machine to go out granulation at last.
Embodiment two:
The become preparation method of mite macromolecular material of a kind of PET, it may further comprise the steps:
(1) at first uses Ammonia the oligopolymer oligopolymer and the PET grafting of diamines, prepare antibacterial matrices with the poly-six inferior Guanoctine grafting of guanidinesalt again;
(2) antibacterial matrices to preparation carries out dehumidification treatments;
(3) take by weighing raw material by prescription, stir;
(4) utilize dual-screw-stem machine to go out granulation;
Get polyethylene terephthalate (PET): 96.3kg; Antioxidant: 0.1kg; Nucleator: 0.3kg; Lubricant: 0.3kg; Antiseptic-germicide: 3kg, getting raw material stirring is even, and the manufacturing parameter with dual-screw-stem machine is set at then: temperature: 225 ℃; Die head: 250 ℃; Main frame current control: 100A; Melt pressure: 1.5mpa
Melt temperature: 205 ℃; Engine speed: 1000RPM; Rotating speed feeds intake: 8RPM; Vacuum pressure: 0.7 mpa; Utilize dual-screw-stem machine to go out granulation at last.
Embodiment three:
The become preparation method of mite macromolecular material of a kind of PET, it may further comprise the steps:
(1) at first uses Ammonia the oligopolymer oligopolymer and the PET grafting of diamines, prepare antibacterial matrices with the poly-six inferior Guanoctine grafting of guanidinesalt again;
(2) antibacterial matrices to preparation carries out dehumidification treatments;
(3) take by weighing raw material by prescription, stir;
(4) utilize dual-screw-stem machine to go out granulation;
Get polyethylene terephthalate (PET): 93.5kg; Antioxidant: 0.2kg; Nucleator: 0.8kg; Lubricant: 0.5kg; Antiseptic-germicide: 5kg, getting raw material stirring is even, and the manufacturing parameter with dual-screw-stem machine is set at then: temperature: 230 ℃; Die head: 250 ℃; Main frame current control: 110A; Melt pressure: 2mpa; Melt temperature: 210 ℃; Engine speed: 2430RPM; Rotating speed feeds intake: 10RPM; Vacuum pressure: 0.8 mpa; Utilize dual-screw-stem machine to go out granulation at last.
Through above-mentioned test, obtain following test-results:
1: PET interest mite material of the present invention does not descend the firmly combination of antibiotic group and matrix resin through the yarn fabric that the wire drawing weaving makes through washing its anti-microbial property repeatedly;
2: excellent anti-mite performance has very high scattering ratio to dirt mite, gamasid, trombiculid, demodicid mite on the textiles;
3: the become mite test of test print, the mite rate that becomes reaches 81.1%;
Kill 99% bacterium in 4: 10 minutes, bacterial concentration is 10
5CFU/ml;
5: the anti-microbial property wide spectrum, after testing to intestinal bacteria, streptococcus aureus, Pseudomonas aeruginosa, Bacillus subtilus, pneumococcus, saccharomyces sake, black-koji mould, Candida albicans, common cold virus etc. have killing effect.
The invention has the advantages that: the PET for preparing by this method mite macromolecular material that becomes has the effect of the antibiotic anti-real virus of high-efficiency broad spectrum, and effect is lasting, and excellent property has very safely to human body, and be easy to processing, and is inexpensive.
Claims (3)
1. the PET preparation method of mite macromolecular material that becomes, it is characterized in that: it may further comprise the steps:
(1) at first uses Ammonia the oligopolymer oligopolymer and the PET grafting of diamines, prepare antibacterial matrices with poly-six inferior Guanoctines of guanidinesalt or the poly-hexamethyl guanidine grafting of hydrochloric acid again;
(2) antibacterial matrices to preparation carries out dehumidification treatments;
(3) take by weighing raw material by prescription, stir;
(4) utilize dual-screw-stem machine to go out granulation.
2. the become preparation method of mite macromolecular material of PET according to claim 1, it is characterized in that: described raw material is made up of following components in weight percent:
Polyethylene terephthalate: 92.9~96.3%;
Antioxidant: 0.1~0.3%; Nucleator: 0.3~1%;
Lubricant: 0.3~0.8%; Antiseptic-germicide: 3~5%;
Oxidation inhibitor is selected four [β-(3 for use, 5-di-t-butyl-4-phenyl) propionic acid] pentaerythritol ester, three [2.4-di-tert-butyl-phenyl] phosphorous acid ester, 1,3,5-three (the 4-tertiary butyl-3-hydroxyl-2, the 6-dimethyl benzyl)-1,3,5-triazine-2,4,6-(1H, 3H, 5H)-triketone, 2, wherein one or both of two-three grades of butyl of 6--4-sylvan;
Nucleator is to select the macromolecular compound polyester, and polyoxyethylene glycol is a kind of in the polyolefine;
Lubricant is selected one or both in polyethylene low-molecular-weight wax, oxidic polyethylene, the stearate for use;
Antiseptic-germicide is with the oligopolymer of Ammonia oligopolymer diamines and poly-six inferior Guanoctines of guanidinesalt or the poly-a kind of high molecular polymer of hexamethyl guanidine grafted on polyethylene terephthalate of hydrochloric acid.
3. the become preparation method of mite macromolecular material of PET according to claim 1, it is characterized in that: the processing parameter of described dual-screw-stem machine is as follows:
Temperature: 220~230 ℃
Die head: 250 ℃
Main frame current control: 90~110A
Melt pressure: 1~2mpa
Melt temperature: 200~210 ℃
Engine speed: 400~2430RPM
Rotating speed feeds intake: 5~10RPM
Vacuum pressure: 0.6~0.8 mpa.