CN102266191A - Three-dimensional printed curtain capable of releasing negative ions and preparation technology of printing slurry thereof - Google Patents
Three-dimensional printed curtain capable of releasing negative ions and preparation technology of printing slurry thereof Download PDFInfo
- Publication number
- CN102266191A CN102266191A CN2010101981444A CN201010198144A CN102266191A CN 102266191 A CN102266191 A CN 102266191A CN 2010101981444 A CN2010101981444 A CN 2010101981444A CN 201010198144 A CN201010198144 A CN 201010198144A CN 102266191 A CN102266191 A CN 102266191A
- Authority
- CN
- China
- Prior art keywords
- mass parts
- curtain
- epvc
- negative ions
- heat stabilizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention prepares a three-dimensional printed curtain capable of releasing negative ions and describes a preparation process of printing slurry and the printed curtain. EPVC (emulsion polyvinyl chloride) is taken as a carrier, jaconet, ninon, flannel, cotton linen fabric and polyester fabric are taken as base materials, and the resin three-dimensional printing technology is adopted for fixing a gull rock negative ion additive on the curtain, so that the curtain has the effect of releasing the negative ions; and the process is convenient and fast, a pattern is rich in three-dimensional sense and effect of realeasing the negative ions is significant.
Description
Technical field:
The invention belongs to fields such as detergents and cosmetic, material preparation, fine chemistry industry, exquisite technology, curtain decorative.
Background technology
Just there has been window in China since ancient times, had window just the someone expect having thing that window is given being covered, so curtain has just been arranged. at first people do not have cloth not have paper yet, they work as curtain with leaf. people cloth had been arranged afterwards, silk has just been arranged, Cai Lun invention has afterwards improved after the papermaking technology again, so most of common people family can have paper to work as curtain. in China kirigami has just been arranged, kirigami on the curtain is just developed and has been handed down by broad-rimmed bamboo hat. today, curtain with we the space and deposit, style thousand becomes, and pattern ten thousand is changed, function and usage also refine to any usefulness the place.Along with the rapid progress of science and technology, people have given curtain multiple function, mainly contain 1, absorbing sound and lowering noise, and 2, uvioresistant, 3, utilize light, 4, dust suction, 5, the maximum ornament 6 of metope, protection privacy.
And the report of the curtain of relevant at present release anion also seldom.The objective of the invention is to sea-gull stone anionic additive is applied in the curtain, make curtain when possessing above-mentioned functions, also have the unique function that discharges anion.
Negative aeroion is called " air vitamin " or " long-living element ", and the anion number of keeping health of people is at 600/cm3, anion have certain health care functions and can play certain deodorizing, inhale flavor, sterilization, dedusting, the function that purifies air.Sea-gull stone anionic additive is made up of the material that opal, tourmaline, mineral fossil, auxiliary agent etc. can discharge anion, has the function that discharges anion.
Summary of the invention
With EPVC is carrier, by the technology of resin stereo stamp, sea-gull stone anionic additive is anchored on the curtain, and then makes curtain possess the effect that discharges anion, and the method is convenient and swift, and flower shape is rich in third dimension, and the effect that discharges anion is remarkable.Discharge anion 3 D stereo stamp curtain, its concentrator is made up of following prescription: the EPVC:100 mass parts; Sea-gull stone anionic additive: 0.5～8 mass parts; Plasticizer: 50～70 mass parts; Swelling agent: 0～8 mass parts; Filler: 0～30 mass parts; Heat stabilizer: 1.0～3.0 mass parts; Lubricant: 0～2 mass parts.
Plasticizer is dioctyl phthalate, dibutyl phthalate or has with EPVC good compatibility, plasticizer that viscosity stability is good are arranged.Heat stabilizer is can suppress factors such as light, heat to produce aging and material that increase its stability, increase the service life to solid flower shape, as liquid zinc barium heat stabilizer, liquid calcium zinc heat stabilizer.Blowing agent is the material that Celogen Az or other are applicable to the EPVC foaming, and decomposition temperature is less than 180 ℃.
Curtain base material: jaconet, nylon taffeta.Flannelette, diablement fort, woven dacron.
Embodiment
Embodiment 1: 60 mass parts plasticizer, 2 mass parts heat stabilizers, 7 quality blowing agents are fully mixed and join in the mixer, 100 mass parts that measure are stuck with paste the resin adding or joined in the mixer in batches, more than the stirring at low speed 60min, will print the static placement of slurry more than the 10h.Determine to want the position of stamp and purified treatment is carried out on the dacron surface, it is surperficial and put it in the baking oven bake 10min～15min in 170 ℃～175 ℃ scopes that the slurry that has prepared is printed on the terylene curtain.Can prepare the release anion number by above-mentioned technology is 500/cm
3Following 3 D stereo stamp terylene curtain.
Embodiment 2: with 4 mass parts sea-gull stone anionic additives, 60 mass parts plasticizer, 2 mass parts heat stabilizers, 7 quality blowing agents fully mix and join in the mixer, 100 mass parts that measure are stuck with paste the resin adding or joined in the mixer in batches, more than the stirring at low speed 60min, will print the static placement of slurry more than the 10h.Determine to want the position of stamp and purified treatment is carried out on the dacron surface, it is surperficial and put it in the baking oven bake 10min～15min in 170 ℃～175 ℃ scopes that the slurry that has prepared is printed on the terylene curtain.Can prepare the release anion number by above-mentioned technology is 600/cm
3Above 3 D stereo stamp terylene curtain.
Embodiment 3: with 6 mass parts sea-gull stone anionic additives, 65 mass parts plasticizer, 2 mass parts heat stabilizers fully mix and join in the mixer, 100 mass parts that measure are stuck with paste the resin adding or joined in the mixer in batches, more than the stirring at low speed 60min, will print the static placement of slurry more than the 10h.Determine to want the position of stamp and purified treatment is carried out on the dacron surface, it is surperficial and put it in the baking oven bake 10min～15min in 170 ℃～175 ℃ scopes that the slurry that has prepared is printed on the terylene curtain.Can prepare the release anion number by above-mentioned technology is 600/cm
3Above 3 D stereo stamp terylene curtain.
Embodiment 4: with 8 mass parts sea-gull stone anionic additives, 65 mass parts plasticizer, 2 mass parts heat stabilizers, 8 quality blowing agents fully mix and join in the mixer, 100 mass parts that measure are stuck with paste the resin adding or joined in the mixer in batches, more than the stirring at low speed 60min, will print the static placement of slurry more than the 10h.Determine to want the position of stamp and purified treatment is carried out on the dacron surface, it is surperficial and put it in the baking oven bake 10min～15min in 170 ℃～175 ℃ scopes that the slurry that has prepared is printed on the terylene curtain.Can prepare the release anion number by above-mentioned technology is 600/cm
3Above 3 D stereo stamp terylene curtain.
Claims (5)
1. discharge anion 3 D stereo stamp curtain, its concentrator is made up of following prescription: the EPVC:100 mass parts; Sea-gull stone anionic additive: 0.5～8 mass parts; Plasticizer: 50～70 mass parts; Swelling agent: 0～8 mass parts; Filler: 0～30 mass parts; Heat stabilizer: 1.0～3.0 mass parts; Lubricant: 0～2 mass parts.
2. according to claims 1 described curtain, its material can be jaconet, nylon taffeta, flannelette, diablement fort, woven dacron, terylene Compound Fabric.
3. form by the material that opal, tourmaline, mineral fossil, auxiliary agent etc. can discharge anion according to claims 1 described sea-gull stone anionic additive.
4. be dioctyl phthalate, dibutyl phthalate according to claims 1 described plasticizer or have with EPVC good compatibility, plasticizer that viscosity stability is good are arranged.Heat stabilizer is can suppress factors such as light, heat to produce aging and material that increase its stability, increase the service life to solid flower shape, as liquid zinc barium heat stabilizer, liquid calcium zinc heat stabilizer.Blowing agent is the material that Celogen Az or other are applicable to the EPVC foaming, and decomposition temperature is less than 180 ℃.
5. in the combination material, have extraordinary dispersiveness according to claims 2 described sea-gull stone anionic additive super fines, in process, do not have any defective workmanship.