CN102260423A - Alcohol-soluble phosphate high temperature resistant long-acting anti-corrosive paint and preparation method thereof - Google Patents
Alcohol-soluble phosphate high temperature resistant long-acting anti-corrosive paint and preparation method thereof Download PDFInfo
- Publication number
- CN102260423A CN102260423A CN 201110199797 CN201110199797A CN102260423A CN 102260423 A CN102260423 A CN 102260423A CN 201110199797 CN201110199797 CN 201110199797 CN 201110199797 A CN201110199797 A CN 201110199797A CN 102260423 A CN102260423 A CN 102260423A
- Authority
- CN
- China
- Prior art keywords
- component
- proportioning
- paint
- high temperature
- temperature resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an alcohol-soluble phosphate high temperature resistant long-acting anti-corrosive paint and a preparation method thereof. The alcohol-soluble phosphate high temperature resistant long-acting anti-corrosive paint is characterized in that: a priming paint and a finish paint are integrated; and the paint comprises a component A and a component B, wherein the component A contains phosphoric acid, aluminum hydroxide, magnesium oxide, absolute alcohol and ethyl lactate; and the component B contains ethyl lactate, absolute alcohol, polyvinyl butyral, a calcium zinc stabilizer, copper oxide, enamel black, a hyper dispersant, fumed silica and a fluorine modified acrylic acid levelling agent. The prepared product resists high temperature of 1,000DEG C for a long term, and has good self-drying property, physical and mechanical properties and conductivity, excellent welding and cutting properties, salt mist resistance of more than 1,000 hours, and long-term acid and alkali corrosion resistance.
Description
Technical field
The present invention relates to a kind of coating, high temperature resistant, the long-lasting protection coatings of phosphoric acid salt that particularly a kind of pure dissolubility, environmental protection, performance are given prominence to.
Background technology
Fire resistant anticorrosive paint generally is meant more than 200 ℃, the paint film nondiscoloration, do not come off, the coating that still can keep suitable physical and mechanical properties, good acid-proof alkaline, high-temperature resistant coating kind commonly used is more in the market, be generally organosilicon heat-resistant coating and inorganic heat-resisting coating, heat-resistant anticorrosive erosion coating is widely used in chimney, high temperature steam pipeline, heat exchanger, High Temperature Furnaces Heating Apparatus, petroleum cracking equipment and engine etc.
Silicone based heat-resistant anticorrosive erosion coating, heat-resisting 200～300 ℃ of silicone resin varnish; With the silicone resin is base-material, adds aluminum paste, heat-resistant filler, frit coatings formulated, can be from doing, and heat resisting temperature can reach 300～600 ℃, but acid and alkali-resistance not; Silicone based heat-resistant anticorrosive erosion coating have better heat-resisting, water tolerance, electrical insulating property and favorable mechanical performance, but hardness is low, and flame resistivity is relatively poor, the cost height.
Mineral-type heat-resistant anticorrosive erosion coating heat resisting temperature can reach 400～1000 ℃, even higher.Mineral-type heat resisting coating flame resistivity is good, hardness is high, but paint film property is more crisp, and is strict to the processing requirements of ground.The performance of a few class heat resisting coatings commonly used relatively sees Table 1.
A few class heat resisting coating performances that table 1 is commonly used compare
Organosilicon heat-resistant anticorrosive erosion solvent based coating generally exists environmental pollution big, operates defectives such as harmful.Tetraethyl silicate heat-resistant anticorrosive erosion coating (pure dissolubility) can only be made zinc-rich paint, and paint film is crisp, can not make glossiness paint film, not defective such as acid and alkali-resistance.Silicate heat resisting coating (water-soluble), silicon-dioxide silicon sol heat resisting coating paint film are crisp, defectives such as poor adhesive force.Phosphate Heat Resistant Coatings (water-soluble) needs oven dry, and paint film is crisp, not defective such as resistance to acids and bases.
Summary of the invention
Goal of the invention of the present invention is in order to overcome the defective of product described in the background technology, and a kind of have excellent physical mechanical property, excellent antiseptic property, environment-protecting asepsis, pure soluble phosphoric acid salt high temperature resistant long acting anti-corrosive paint applied widely are provided.
Second goal of the invention of the present invention is for a kind of rational practicable preparation method is provided in the soluble phosphoric acid salt high temperature resistant long acting anti-corrosive paint described in first goal of the invention.
First goal of the invention of the present invention is achieved by the following technical solution.A kind of pure soluble phosphoric acid salt high temperature resistant long acting anti-corrosive paint, its priming paint and finish paint unite two into one, and comprise A component and the B component that can carry out mixing match;
Wherein each moiety of A component with and the per-cent of weight be: phosphoric acid 50%～70%, aluminium hydroxide 3%～10%, magnesium oxide 1%～5%, ethyl lactate 8%～20%, raw spirit 10%～30%;
Wherein each moiety of B component with and the per-cent of weight be: ethyl lactate 5%～10%, raw spirit 15%～30%, polyvinyl butyral acetal 3%～5%, calcium zinc stabilizer 1%～5%, cupric oxide 50%～70%, pottery black 3%～10%, high-carbon black pigment 1%～2%, hyper-dispersant 0.1%～0.5%, aerosil 0.2%～0.5%, fluorin modified crylic acid flow agent 0.1%～0.5%.
A component and B component mix by proportioning during use, and the proportioning of its weight is A:B=0.5～1:1.
Second goal of the invention of the present invention is achieved by the following technical solution.A kind of preparation method of pure soluble phosphoric acid salt high temperature resistant long acting anti-corrosive paint comprises being prepared as follows step:
I), preparation A component: (1) at first drops into phosphoric acid by proportioning, stirs with 500 ~ 800r/min speed, slowly drops into aluminium hydroxide, magnesium oxide by proportioning while stirring then.⑵ after fed intake and finish, about 30 minutes of high speed dispersion required to disperse more than the rotating speed 1200r/min.⑶ heat up, stir, and temperature rises to 155～158 ℃, and solution is complete to stop heating when transparent.⑷ stir, the logical cooling water temperature of chuck, when temperature is reduced to below 70 ℃, drops into ethyl lactate, anhydrous industrial alcohol in regular turn by proportioning while stirring.⑸ inspection by sampling, criterion of acceptability is: " be coated with-4 viscosity/25 ℃, 100～150s; Solids content 50%～55% ", can after 180 order filtering nets filter then.
II), preparation B component: (1) at first drops into ethyl lactate in regular turn by proportioning, and raw spirit stirs with 500 ~ 800r/min speed, slowly drops into polyvinyl butyral acetal by proportioning while stirring then.⑵ after fed intake and finish, about 30～60 minutes of high speed dispersion required to disperse to dissolve fully until PVB more than the rotating speed 1200r/min.With 500 ~ 800r/min speed stir down by proportioning drop in regular turn slowly that calcium zinc stabilizer, cupric oxide, pottery are black, high-carbon black pigment, hyper-dispersant and aerosil.⑷ after fed intake and finish, about 30 minutes of high speed dispersion required to disperse more than the rotating speed 1200r/min.⑸ the pre-dispersed laggard sand mill of high speed grinds, and mesh-of-grind requires to be not more than 40 microns, squeezes in the paint cylinder after mesh-of-grind is up to standard.⑹ drop into fluorin modified crylic acid flow agent, stir about 15 minutes by proportioning.⑺ after inspection by sampling, standard reach index in the table 8, filter can through 180 order filtering nets.
When III) using with A component and B component in the ratio proportioning of A:B=0.5～1:1 and stir, spray then.
Beneficial effect of the present invention is as follows:
1. excellent physical and mechanical performance the technology of the present invention product alcohol soluble phosphoric acid salt high temperature resistant long acting anti-corrosive paint can form the same coating of similar enamel behind crosslinking curing, and coating is hard and have characteristics such as snappiness, wear resistance, electroconductibility, shock-resistance preferably.
2. the coating of You Yi chemical-resistant and antiseptic property alcohol soluble phosphoric acid salt high temperature resistant long acting anti-corrosive paint has excellent chemical-resistant, the long period of soaking of chemical such as the acid of height, alkali, salt, various oil product, aliphatic hydrocarbon.
3. environmental protection and nontoxicity alcohol soluble phosphoric acid salt high temperature resistant long acting anti-corrosive paint adopts alcoholic solvent as thinner in the construction application process, and is harmless to the workmen.
Embodiment
Illustrate as follows to of the present invention further describing:
A kind of pure soluble phosphoric acid salt high temperature resistant long acting anti-corrosive paint, its priming paint and finish paint unite two into one, and comprise A component and the B component that can carry out mixing match;
Example 1:A set of dispense is than table (table 2)
The B set of dispense is than table (table 3)
Example 2:A set of dispense is than table (table 4)
The B set of dispense is than table (table 5)
Example 3:
The A set of dispense is than table (table 6)
The B set of dispense is than table (table 7)
Above-mentioned preparation method comprises the following steps:
A), preparation A component: (1) at first drops into phosphoric acid, so that (500 ~ 800r/min) speed stir, and slowly drop into aluminium hydroxide, magnesium oxide then while stirring.⑵ after feed intake and finish, about 30 minutes of high speed dispersion (more than the 1200r/min).⑶ heat up, stir, and temperature rises to 155～158 ℃, stops heating.⑷ stir cooling, when temperature is reduced to below 70 ℃, drops into ethyl lactate, anhydrous industrial alcohol while stirring in regular turn.
⑸ inspection by sampling, qualified after-filtration (180 order) can.
B), preparation B component: (1) drops into ethyl lactate at first in regular turn, and raw spirit is so that (500 ~ 800r/min) speed stir, and slowly drop into polyvinyl butyral acetal then while stirring.⑵ after fed intake and finish, about 30～60 minutes of high speed dispersion (more than the 1200r/min) was dissolved fully until PVB.⑶ so that (500 ~ 800r/min) speed stir and to drop into slowly down that calcium zinc stabilizer, cupric oxide, pottery are black, high-carbon black pigment, hyper-dispersant and aerosil.⑷ after feed intake and finish, about 30 minutes of high speed dispersion.⑸ the pre-dispersed laggard sand mill of high speed grinds, and squeezes in the paint cylinder after mesh-of-grind is qualified.⑹ drop into flow agent, stir about 15 minutes.⑺ inspection by sampling, qualified after-filtration (180 order) can.
C), before the construction A component and B component are sprayed in the ratio proportioning of A:B=0.5～1:1 and the back that stirs.
The technology of the present invention product performance and technical indicator see the following form 8.
Table 8 the technology of the present invention product performance technical indicator
Annotate: HG/T3668-2000 " zinc rich primer " coating and pigment standard compilation coating products universal lacquer volume 2007 editions, China Standard Press
GB/T 1728--1978(1989) " paint film, putty membrane assay method time of drying " coating and pigment standard compilation coating test method general use volume is 2007 editions, China Standard Press
GB/T 1732--1993 " paint film shock-resistance assay method " coating and pigment standard compilation coating test method general use volume 2007 editions, China Standard Press
GB/T 1720--1979(1989) " paint film adhesion assay method " coating and pigment standard compilation coating test method general use volume is 2007 editions, China Standard Press
GB/T 1735-1979(1989) " paint film thermotolerance assay method " coating and pigment standard compilation coating test method general use volume 2007 editions, China Standard Press
GB/T3048.2-2007 " electric wire electrical performance test method "
GB/T6747-2008 " shop primer peculiar to vessel " www.bzjsw.com
GB/T1771-1991 " mensuration of the anti-neutral salt spray performance of paint and varnish " coating and pigment standard compilation coating test method general use volume 2007 editions, China Standard Press
GB/T1763-1993 " paint film chemical reagent resistance assay method " coating and pigment standard compilation coating test method general use volume 2007 editions, China Standard Press
GB/T1733--1993 " paint film water tolerance assay method " coating and pigment standard compilation coating test method general use volume 2007 editions, China Standard Press
GB/T 6739-2006 " paint and varnish pencil method is measured hardness of paint film " coating and pigment standard compilation coating test method general use volume 2007 editions, China Standard Press
GB/T 9754-1988 " paint and varnish is the mensuration of 20 °, 60 ° and 85 ° specular glosss of the colored paint paint film of containing metal pigment not " coating and pigment standard compilation coating test method general use volume 2007 editions, China Standard Press
As can be seen from Table 10, this invention product has following characteristics:
1. excellent physical and mechanical performance the technology of the present invention product alcohol soluble phosphoric acid salt high temperature resistant long acting anti-corrosive paint can form the same coating of similar enamel behind crosslinking curing, and coating is hard and have characteristics such as snappiness, wear resistance, electroconductibility, shock-resistance preferably.
2. the coating of You Yi chemical-resistant and antiseptic property alcohol soluble phosphoric acid salt high temperature resistant long acting anti-corrosive paint has excellent chemical-resistant, the long period of soaking of chemical such as the acid of height, alkali, salt, various oil product, aliphatic hydrocarbon.
3. environmental protection and nontoxicity alcohol soluble phosphoric acid salt high temperature resistant long acting anti-corrosive paint adopts alcoholic solvent as thinner in the construction application process, and is harmless to the workmen.
8. the technology of the present invention product removes and can be applicable to traditional boiler, automobile skeleton, engine, vapor pipe, also can be applicable to the corrosion-proof coating under high temperature service acid and alkali-resistance and the chemical plant indoor and outdoor hot environment, has widened Application Areas.
Claims (3)
1. pure soluble phosphoric acid salt high temperature resistant long acting anti-corrosive paint, its priming paint and finish paint unite two into one, and comprise A component and the B component that can carry out mixing match, and the proportioning of the weight of A component and B component is A:B=0.5～1:1;
Each moiety that it is characterized in that A component wherein with and the per-cent of weight be: phosphoric acid 50%～70%, aluminium hydroxide 3%～10%, magnesium oxide 1%～5%, ethyl lactate 8%～20%, raw spirit 10%～30%;
Wherein each moiety of B component with and the per-cent of weight be: ethyl lactate 5%～10%, raw spirit 15%～30%, polyvinyl butyral acetal 3%～5%, calcium zinc stabilizer 1%～5%, cupric oxide 50%～70%, pottery black 3%～10%, high-carbon black pigment 1%～2%, hyper-dispersant 0.1%～0.5%, aerosil 0.2%～0.5%, fluorin modified crylic acid flow agent 0.1%～0.5%.
2. pure soluble phosphoric acid salt high temperature resistant long acting anti-corrosive paint as claimed in claim 1, described A component and B component mix by proportioning when it is characterized in that using, and the proportioning of its weight is A:B=0.5～1:1.
3. the preparation method of the pure soluble phosphoric acid salt high temperature resistant long acting anti-corrosive paint described in the claim 1 is characterized in that its preparation method comprises the following steps:
I), preparation A component: (1) at first drops into phosphoric acid by proportioning, stirs with 500 ~ 800r/min speed, slowly drops into aluminium hydroxide, magnesium oxide by proportioning while stirring then; (2) feed intake finish after, about 30 minutes of high speed dispersion require to be disperseed more than the rotating speed 1200r/min; (3) heat up, stir, temperature rises to 155～158 ℃, and solution is complete to stop heating when transparent; (4) stirring, the logical cooling water temperature of chuck when temperature is reduced to below 70 ℃, drop into ethyl lactate, anhydrous industrial alcohol by proportioning while stirring in regular turn; (5) inspection by sampling, qualified after 180 order filtering nets filter the back can;
II), preparation B component: (1) at first drops into ethyl lactate in regular turn by proportioning, and raw spirit stirs with 500 ~ 800r/min speed, slowly drops into polyvinyl butyral acetal by proportioning while stirring then; (2) feed intake finish after, about 30～60 minutes of high speed dispersion require to disperse to dissolve fully until PVB more than the rotating speed 1200r/min; (3) with 500 ~ 800r/min speed stir down by proportioning drop in regular turn slowly that calcium zinc stabilizer, cupric oxide, pottery are black, high-carbon black pigment, hyper-dispersant and aerosil; (4) feed intake finish after, about 30 minutes of high speed dispersion require to be disperseed more than the rotating speed 1200r/min; (5) the pre-dispersed laggard sand mill of high speed grinds, and mesh-of-grind requires to be not more than 40 microns, squeezes in the paint cylinder after mesh-of-grind is up to standard; (6) drop into fluorin modified crylic acid flow agent, stir about 15 minutes by proportioning; (7) filter can through 180 order filtering nets;
When III) using with A component and B component in the ratio proportioning of A:B=0.5～1:1 and stir, spray then.