CN102251197A - 一种高碳铬轴承钢及其制造方法 - Google Patents
一种高碳铬轴承钢及其制造方法 Download PDFInfo
- Publication number
- CN102251197A CN102251197A CN2010101798932A CN201010179893A CN102251197A CN 102251197 A CN102251197 A CN 102251197A CN 2010101798932 A CN2010101798932 A CN 2010101798932A CN 201010179893 A CN201010179893 A CN 201010179893A CN 102251197 A CN102251197 A CN 102251197A
- Authority
- CN
- China
- Prior art keywords
- steel
- carbon
- molten steel
- chromium bearing
- bearing steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
实施例1 | 实施例2 | 实施例3 | 实施例4 | 对比例1 | 对比例2(GCr15) | 对比例3(GCr15SiMn) | |
C | 1.15 | 0.95 | 0.91 | 1.00 | 0.90 | 0.99 | 1.00 |
Mn | 1.61 | 1.65 | 1.80 | 1.61 | 1.45 | 0.31 | 1.01 |
Si | 0.70 | 0.44 | 0.58 | 0.64 | 0.55 | 0.21 | 0.61 |
Cr | 1.51 | 1.80 | 1.58 | 1.70 | 1.45 | 1.48 | 1.48 |
Al | 0.021 | 0.030 | 0.038 | 0.030 | 0.004 | / | / |
Ti | 0.0015 | 0.0030 | 0.0028 | 0.001 | 0.003 | / | / |
0 | 0.0004 | 0.0005 | 0.0006 | 0.0006 | 0.001 | / | / |
Cu | 0.12 | 0.11 | 0.11 | 0.08 | / | / | / |
Ni | 0.06 | 0.07 | 0.06 | 0.04 | / | / | / |
Mo | 0.04 | 0.05 | 0.02 | 0.03 | / | / | / |
N | 0.0067 | 0.0063 | 0.0046 | 0.0040 | / | / | / |
Sn | 0.010 | 0.008 | 0.006 | 0.002 | / | / | / |
Sb | 0.003 | 0.003 | 0.004 | 0.002 | / | / | / |
As | 0.010 | 0.009 | 0.013 | 0.004 | / | / | / |
S | 0.008 | 0.010 | 0.018 | 0.015 | 0.002 | 0.009 | 0.004 |
P | 0.010 | 0.008 | 0.013 | 0.004 | 0.004 | 0.007 | 0.009 |
Claims (8)