Summary of the invention
In view of above-mentioned the deficiencies in the prior art, the object of the present invention is to provide the two component printing ink of a kind of high abrasion, be intended to solve the not good and not good problem of wear resisting property of sticking power on part UV finish paint ground that traditional printing ink exists.
In order to solve the problems of the technologies described above, technical scheme of the present invention is as follows:
The two component printing ink of a kind of high abrasion by weight percentage, comprise following component:
Acrylic resin liquid 85-98;
Defoamer 0.2-6;
Anti-wear agent 0.1-10.
The two component printing ink of described high abrasion, wherein, by weight percentage, the two component printing ink of described high abrasion comprise following component:
Acrylic resin liquid 97.5;
Defoamer 0.5;
Anti-wear agent 2.
The two component printing ink of described high abrasion, wherein, the solids content of described acrylic resin liquid is equal to or greater than 40%, and its acid number is equal to or greater than 1%.
The two component printing ink of described high abrasion, wherein, described defoamer is a silicone antifoam agent.
The two component printing ink of described high abrasion, wherein, anti-wear agent is special modified polyorganosiloxane.
The two component printing ink of described high abrasion wherein, need after described printing ink is made to add isocyanate curing agent, and add-on is 20% of an ink by weight.
The two component printing ink of described high abrasion, wherein, the viscosity of described printing ink is 10000~20000cps under 20 ℃ of room temperatures.
The two component printing ink of a kind of high abrasion by weight percentage, comprise following component:
Acrylic resin liquid 80-95;
Dispersion agent 0.1-3;
Toner 1-20;
Defoamer 0.1-5;
Anti-wear agent 0.1-6.
The two component printing ink of described high abrasion, wherein, by weight percentage, described printing ink comprises following component:
Acrylic resin liquid 86.5;
Dispersion agent 0.5;
Toner 10;
Defoamer 1;
Anti-wear agent 2.
The two component printing ink of described high abrasion, wherein, described dispersion agent is the amino acid ester copolymer solution.
Beneficial effect of the present invention: it has effectively overcome the existing problem of silk-screen pad-transfer printing ink on the existing UV finish paint.Because the two component silk-screen pad-transfer printing inks of high abrasion of the present invention have high-wearing feature, and are not halogen-containing, and owing to contain an amount of auxiliary agent, make it to have good use properties, its sticking power on various UV finish paints is good, and the patience of each side is also quite excellent.
Embodiment
The invention provides the two component printing ink of a kind of high abrasion, clearer, clear and definite for making purpose of the present invention, technical scheme and effect, below the present invention is described in more detail.Should be appreciated that specific embodiment described herein only in order to explanation the present invention, and be not used in qualification the present invention.
The two component printing ink of a kind of high abrasion, by weight percentage, this printing ink comprises following component:
Acrylic resin liquid 85-98;
Defoamer 0.2-6;
Anti-wear agent 0.1-10.
The preferable weight percent of printing ink of the present invention consists of:
Acrylic resin liquid 97.5;
Defoamer 0.5;
Anti-wear agent 2.
Printing ink of the present invention can also add toner and dispersion agent, and by weight percentage, printing ink comprises following component:
Acrylic resin liquid 80-95;
Dispersion agent 0.1-3;
Toner 1-20;
Defoamer 0.1-5;
Anti-wear agent 0.1-6.
Printing ink optimum weight per-cent of the present invention consists of:
Acrylic resin liquid 86.5;
Dispersion agent 0.5;
Toner 10;
Defoamer 1;
Anti-wear agent 2.
Specifically, the solids content of described acrylic resin liquid is equal to or greater than 40%, and its acid number is equal to or greater than 1%.Solvent for use is different Fu Er ketone in the described acrylic resin liquid.
Described defoamer is a silicone antifoam agent, and its effect is to reduce the bubble that is produced in manufacturing and the use.
Described dispersion agent is the amino acid ester copolymer solution, its effect be homodisperse those be difficult to be dissolved in the solid particulate of liquid, also can prevent simultaneously the sedimentation and the cohesion of solid particulate.
Described anti-wear agent is special modified polyorganosiloxane, and it has extremely excellent flow leveling, the sliding sense in excellent surface, wear-resisting and anti scuffing performance.The effect of anti-wear agent is the wear resisting property that increases the China ink layer.
Described toner is the pigment of halogen-containing organic or inorganic not.
Described UV finish paint is the coating that ultraviolet light irradiation solidify to form.
Printing ink of the present invention is under 20 ℃ of room temperatures, and its viscosity is 10000~20000cps, both can be used for silk-screen and also can be used for bat printing.Retroussage effect of the present invention is better, reaches high-wear resistance easily, and sticking power is good on various UV finish paints, and has ethanol-tolerant performance preferably.
Printing ink of the present invention is two component printing ink, needs to add solidifying agent before using, and could use after mixing.Described isocyanate curing agent is the aliphatic isocyanates solidifying agent, and solid content is absolutely.The effect of described solidifying agent is solvent resistance and the scratch-resistant performance that improves the China ink layer.
The following example is that further explanation of the present invention and explanation are not constituted any limitation the present invention.
Embodiment 1
Get 97 parts of acrylic resin liquid (weight), add anti-wear agent 2 parts of (weight) and 1 part of defoamer (weight), wherein anti-wear agent is selected special modified polyorganosiloxane for use, and formed mixture gets product after being uniformly dispersed through 1200 rpms rotating speed high-speed stirring 30-40 minute.
Embodiment 2
Get 89 parts of acrylic resin liquid (weight), add 0.5 part of dispersion agent, anti-wear agent 1 part of (weight) and 10 parts of toners (weight), 600 rpms rotating speed stirring at low speed 15 minutes, cross three-roller six times after stirring, add 0.5 part of defoamer again, stirred 20 minutes with 1200 rpms rotating speed then, get product after being uniformly dispersed.
Embodiment 3
Get 87 parts of acrylic resin liquid (weight), add 0.5 part of dispersion agent, anti-wear agent 2 parts of (weight) and 10 parts of toners (weight), 600 rpms rotating speed stirring at low speed 15 minutes, cross three-roller six times after stirring, add 0.5 part of defoamer again, stirred 20 minutes with 1200 rpms rotating speed then, get product after being uniformly dispersed.
Embodiment 4
Get 86 parts of acrylic resin liquid (weight), add 0.5 part of dispersion agent, anti-wear agent 4 parts of (weight) and 10 parts of toners (weight), 600 rpms rotating speed stirring at low speed 15 minutes, cross three-roller six times after stirring, add 0.5 part of defoamer again, stirred 20 minutes with 1200 rpms rotating speed then, get product after being uniformly dispersed.
Physics and chemistry China ink layer performance behind the two component printing ink adding of the above embodiment gained high abrasion isocyanate curing agent on the UV finish paint is referring to table 1, and wherein the addition of isocyanate curing agent is 20%.
Table 1
? |
Ethanol-tolerant |
RCA/175gf |
Embodiment 1 |
200 times |
150 times |
Embodiment 2 |
150 times |
60 times |
Embodiment 3 |
200 times |
110 times |
Embodiment 4 |
170 times |
140 times |
Should be understood that, for those of ordinary skills, can be improved according to the above description or conversion, and all these improvement and conversion all should belong to the protection domain of claims of the present invention.