CN102212236A - Pressure-resistant and abrasion-resistant wire PVC (Poly Vinyl Chloride) material - Google Patents
Pressure-resistant and abrasion-resistant wire PVC (Poly Vinyl Chloride) material Download PDFInfo
- Publication number
- CN102212236A CN102212236A CN2011100808043A CN201110080804A CN102212236A CN 102212236 A CN102212236 A CN 102212236A CN 2011100808043 A CN2011100808043 A CN 2011100808043A CN 201110080804 A CN201110080804 A CN 201110080804A CN 102212236 A CN102212236 A CN 102212236A
- Authority
- CN
- China
- Prior art keywords
- resistant
- abrasion
- pressure
- parts
- withstand voltage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A pressure-resistant and abrasion-resistant wire PVC (Poly Vinyl Chloride) material provided by the invention mainly relates to the field of polymer materials, particularly to a functional material for electric wires and cables, and more particularly to a pressure-resistant and abrasion-resistant functional material. The pressure-resistant and abrasion-resistant wire PVC (Poly Vinyl Chloride) material comprises the following components in parts by weight: 100 parts of polyvinyl chloride powder, 45-55 parts of diisononyl phthalate, 4.5-5.5 parts of stabilizing agent, 0.5-1 part of lubricant, 16-20 parts of abrasion-resistance agent, 1.5-2.5 parts of flame retardant agent and 1 part of toner powder. A pressure-resistant and abrasion-resistant wire produced by the formula has stronger performances of pressure resistance and abrasion resistance because of compatibly preparing the composite wear-resisting agent with other addition agents.
Description
Technical field
The present invention relates generally to polymeric material field, especially a kind of electric wire function material, particularly withstand voltage wear-resisting functions material.
Background technology
The PVC goods are widely used in various fields with its excellent corrosion resisting performance and shock resistance, but with respect to other materials, the toughness of PVC goods and wear resisting property have existing deficiency, and this makes it be subjected to significant limitation on using.Owing to the high request of safety performance and environmental-protecting performance, make the application of PVC material also be subjected to very big challenge in the electric wire field.As the U.S. UL company household electrical appliance plastic prod has been adopted new standard, its leading indicator of electric wire performance requriements is reached: 1, abrasion resistance reaches 5000 times; 2, withstand voltage properties reach 200 pounds withstand voltage 7 hours; 3, do not break 500 pounds of withstand voltage 5 seconds.
Summary of the invention
The purpose of this invention is to provide a kind of withstand voltage abrasion resistant electrical wire PVC material, its product has stronger withstand voltage wear resisting property on the basis that keeps original performance, and the product safety environmental protection reaches the new standard that U.S. UL company is adopted the household electrical appliance plastic prod fully.
A kind of withstand voltage abrasion resistant electrical wire PVC material of the present invention, its weight part consists of:
Above-mentioned a kind of withstand voltage abrasion resistant electrical wire PVC material, its weight part consists of:
Described stablizer is the prosperous special-purpose calcium zinc stabilizer 301 of PVC wire cable material that reaches Science and Technology Ltd.'s production in Heyuan City, Guangdong Province; Described anti-wear agent is the anti-wear agent T-850 that Dongguan, Guangdong Province letter enrichment worker company limited produces; Described lubricant is the mixture of polyethylene wax or Zerol and polyethylene wax.
The withstand voltage abrasion resistant electrical wire that adopts above-mentioned prescription to make adopts the compatible preparation of complex abrasion-proof agent and other auxiliary agents, has stronger withstand voltage wear resisting property.
Embodiment
The invention will be further described below in conjunction with embodiment.
Embodiment one:
Described stablizer is the prosperous special-purpose calcium zinc stabilizer 301 of PVC wire cable material that reaches Science and Technology Ltd.'s production in Heyuan City, Guangdong Province; Described anti-wear agent is the anti-wear agent T-850 that Dongguan, Guangdong Province letter enrichment worker company limited produces; Described lubricant is the mixture of 1 part of Zerol and 9 parts of polyethylene waxs; The ammonium polyphosphate that fire retardant adopts zunyi, guizhou county prosperous source phosphatization limited liability company to produce.
The withstand voltage abrasion resistant electrical wire that this prescription is made can reach following index after testing:
1, abrasion resistance reaches 6000 times; 2, withstand voltage properties reach 200 pounds withstand voltage 7.6 hours; 3, do not break 500 pounds of withstand voltage 5 seconds.
Embodiment two:
Described stablizer is the prosperous special-purpose calcium zinc stabilizer 301 of PVC wire cable material that reaches Science and Technology Ltd.'s production in Heyuan City, Guangdong Province; Described anti-wear agent is the anti-wear agent T-850 that Dongguan, Guangdong Province letter enrichment worker company limited produces; Described lubricant is a polyethylene wax; The ammonium polyphosphate that fire retardant adopts zunyi, guizhou county prosperous source phosphatization limited liability company to produce.
The withstand voltage abrasion resistant electrical wire that this prescription is made can reach following index after testing:
1, abrasion resistance reaches 5400 times; 2, withstand voltage properties reach 200 pounds withstand voltage 7.8 hours; 3, do not break 500 pounds of withstand voltage 7 seconds.
Embodiment three:
Described stablizer is the prosperous special-purpose calcium zinc stabilizer 301 of PVC wire cable material that reaches Science and Technology Ltd.'s production in Heyuan City, Guangdong Province; Described anti-wear agent is the anti-wear agent T-850 that Dongguan, Guangdong Province letter enrichment worker company limited produces; Described lubricant is a polyethylene wax; The ammonium polyphosphate that fire retardant adopts zunyi, guizhou county prosperous source phosphatization limited liability company to produce.
The withstand voltage abrasion resistant electrical wire that this prescription is made can reach following index after testing:
2, abrasion resistance reaches 5500 times; 2, withstand voltage properties reach 200 pounds withstand voltage 7.7 hours; 3, do not break 500 pounds of withstand voltage 7 seconds.
Claims (2)
1. a withstand voltage abrasion resistant electrical wire PVC expects that its weight part consists of:
2. a kind of withstand voltage abrasion resistant electrical wire PVC material according to claim 1, its weight part consists of: