CN102180548A - Reverse osmosis scale inhibition and dispersion agent and preparation method thereof - Google Patents
Reverse osmosis scale inhibition and dispersion agent and preparation method thereof Download PDFInfo
- Publication number
- CN102180548A CN102180548A CN 201110060436 CN201110060436A CN102180548A CN 102180548 A CN102180548 A CN 102180548A CN 201110060436 CN201110060436 CN 201110060436 CN 201110060436 A CN201110060436 A CN 201110060436A CN 102180548 A CN102180548 A CN 102180548A
- Authority
- CN
- China
- Prior art keywords
- reverse osmosis
- dispersion agent
- preparation
- scale inhibition
- percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of water treatment, and in particular relates to a reverse osmosis scale inhibition and dispersion agent and a preparation method thereof. The reverse osmosis scale inhibition and dispersion agent is prepared by compounding the following materials in percentage by weight: 10 to 30 percent of 2-phosphono-1,2,4-tricarboxylic acid butane, 10 to 20 percent of amino tris(methylene phosphonic acid), 20 to 40 percent of sulfonate copolymer, 2 to 5 percent of polyaspartic acid and the balance of deionized water. The preparation method comprises the following steps of: adding the deionized water into a reaction kettle, adding the 2-phosphono-1,2,4-tricarboxylic acid butane, the amino tris(methylene phosphonic acid), the sulfonate copolymer and the polyaspartic acid, and stirring at normal temperature for 55 to 65 minutes. The components have high compatibility, complementarity and synergy, the reverse osmosis scale inhibition and dispersion agent replaces an imported product, the operating cost of a reverse osmosis device is reduced, the normal operation of the reverse osmosis device is ensured, and the preparation method is simple, and easy to implement.
Description
Technical field
The invention belongs to water-treatment technology field, be specifically related to a kind of reverse osmosis dirt dispersion agent and preparation method thereof.
Background technology
Scale inhibitors is mainly used in reverse osmosis (RO) water treatment system, owing to contain more Ca in the water
2+, Mg
2+, Na
+, K
+, SO
4 2-, Cl
-, HCO
3 -, NO
3 -Plasma, when reverse osmosis unit removed ion in anhydrating, the water concentrated (generally at 3~4 times) of the dense water side of reverse osmosis because of big multiple is arranged was so have CaCO
3, CaSO
4, BaSO
4, Mg (OH)
2, Fe
2O
3, Ca
3(PO
4)
2Separate out with clay particle etc., be deposited on the film surface, stop water to see through film.Its consequence, the lighter influences the operation of reverse osmosis system, and weight person can't move reverse osmosis system.
The Scale inhibitors that China's reverse osmosis unit (RO) uses at present is by external import, most of usefulness be that the U.S. clear power company or Bei Di company produce, use the running cost height, based on this, my company has carried out a series ofly studying repeatedly and testing to reverse osmosis antisludging agent, finally developed and mass-produced the Scale inhibitors that can be applied to reverse osmosis unit (RO) and functional, price is than low 2.5 times of at present external equivalents price.
Summary of the invention
Technical problem to be solved by this invention is the deficiency that exists at prior art, and a kind of reverse osmosis dirt dispersion agent is provided, and has reduced the running cost of reverse osmosis unit; The present invention provides simple preparation method simultaneously.
Reverse osmosis dirt dispersion agent of the present invention is characterized in that forming by the material of following weight percent is composite:
Described co-polymer of sulfonate is the commercially available prod, forms solid content 〉=30.0% by vinylformic acid, hydroxypropyl acrylate and 2-acrylamido-2-methyl isophthalic acid-propanesulfonic acid copolymerization.
Described 2-phosphonate group-1,2,4-butane tricarboxylate (PBTAC) is the commercially available prod, liquid, active constituent (in PBTC) mass content 〉=50.0%.
Described Amino Trimethylene Phosphonic Acid (ATMP) is the commercially available prod, liquid, active constituent (in ATMP) mass content 〉=50.0%.
Described poly aspartic acid is the commercially available prod, white solid, mass content 〉=98.5%.
The preparation method of reverse osmosis dirt dispersion agent:
Add deionized water in reactor after, add 2-phosphonate group-1,2 again, 4-butane tricarboxylate, Amino Trimethylene Phosphonic Acid, co-polymer of sulfonate and poly aspartic acid, normal temperature stir down and made in 55~65 minutes.
The present invention is a kind of compound drug, and each component has good compatibleness, complementarity and synergetic property: 2-phosphonate group-1,2, the 4-butane tricarboxylate is to CaCO
3, CaSO
4And Mg (OH)
2Has good scale inhibition dissemination; Poly aspartic acid is to BaSO
4, SrSO
4, Mg (OH)
2, Fe
2O
3, Mn
2O
3With clay particle good dispersion and scale inhibition function are arranged, simultaneously organic ion is also had good dissemination; Co-polymer of sulfonate is to CaCO
3, Ca
3(PO
4)
2, Zn (OH)
2, Fe
2O
3And suspended particles have good dispersing and antisludging effect in the water.And each component has good complexing action to positively charged ion in the water, energy and Ca
2+, Mg
2+, Ba
2+, Fe
2+, Fe
3+, Mn
2+Deng positively charged ion generation complex reaction.
Compared with prior art, beneficial effect of the present invention is as follows:
Each component of the present invention has good compatibleness, complementarity and synergetic property, and existing good scale effect can disperse CaCO again
3, CaSO
4, BaSO
4, Fe
2O
3, Mg (OH)
2, Mn
2O
3, Ca
3(PO
4)
2With settlings such as clay particles, can also good complexing action be arranged with positively charged ion in the water.The present invention has replaced imported product, has reduced the running cost of reverse osmosis unit, guaranteed that reverse osmosis system normally moves, and the preparation method is simple, and is easy to implement.
Embodiment
Below in conjunction with embodiment the present invention is described further.
Embodiment 1
A kind of reverse osmosis dirt dispersion agent forms by the material of following weight percent is composite:
The preparation method: add deionized water in reactor after, add 2-phosphonate group-1,2 again, 4-butane tricarboxylate, Amino Trimethylene Phosphonic Acid, co-polymer of sulfonate and poly aspartic acid, normal temperature stir down and made in 60 minutes.
Embodiment 2
A kind of reverse osmosis dirt dispersion agent forms by the material of following weight percent is composite:
The preparation method: add deionized water in reactor after, add 2-phosphonate group-1,2 again, 4-butane tricarboxylate, Amino Trimethylene Phosphonic Acid, co-polymer of sulfonate and poly aspartic acid, normal temperature stir down and made in 60 minutes.
Embodiment 3
A kind of reverse osmosis dirt dispersion agent forms by the material of following weight percent is composite:
The preparation method: add deionized water in reactor after, add 2-phosphonate group-1,2 again, 4-butane tricarboxylate, Amino Trimethylene Phosphonic Acid, co-polymer of sulfonate and poly aspartic acid, normal temperature stir down and made in 60 minutes.
Embodiment 4
A kind of reverse osmosis dirt dispersion agent forms by the material of following weight percent is composite:
The preparation method: add deionized water in reactor after, add 2-phosphonate group-1,2 again, 4-butane tricarboxylate, Amino Trimethylene Phosphonic Acid, co-polymer of sulfonate and poly aspartic acid, normal temperature stir down and made in 60 minutes.
Industrial application example 1
Yinchuan power plant of Energetix Group Ltd. have quadruplet per hour water production rate be 100m
3The reverse osmosis membrane that the reverse osmosis unit of/h adopts is the polyamide composite film that U.S. Tao Shi company produces, the film device producing water ratio is 75%, ratio of desalinization 〉=96%, the pretreated Huanghe water of former hydromining, former is the dirt dispersion agent 0100 that certain company of foreign country produces with reverse osmosis antisludging agent, through moving approximately more than a year, one section pressure reduction 0.40MPa, two sections pressure reduction reach the 0.45MPa water pressure and increase, power consumption increases, water production rate descends more, at the beginning of 2010 4 months, my company has carried out matting to its quadruplet reverse osmosis equipment, and operator are trained, and then adds I the dirt dispersion agent RO-LS100 of company's production and moves to 2011.3.2, operating performance is better, and every of water production rate is all at 98~103m
3In/h the scope, desalination rate 〉=98%, one section pressure reduction all<0.25MPa, two sections pressure reduction all<0.2Mpa.
Industrial application example 2
There is the reverse osmosis equipment that will put into operation two end of the year in 2003 Qilu Petrochemical transformation of the way unit power houses, the reverse osmosis antisludging agent MDC150 that uses U.S. Bei Di company to produce before former, former hydromining mixes use with part Huanghe water and part underground water, enterprise is in order to reduce cost, use the dirt dispersion agent RO-LS100 to 2011.3.2 that my company produces instead in August, 2007, operating performance is better, and producing water ratio reaches 75%, and water production rate is at 98~102m
3/ h, desalination rate>98%, the water inlet electricity is led at 600us/cm, go out water power and lead at 9~10us/cm, one section pressure reduction all<0.23Mpa, two sections pressure reduction all<0.19Mpa.
Claims (2)
1. reverse osmosis dirt dispersion agent is characterized in that forming by the material of following weight percent is composite:
2. the preparation method of the described reverse osmosis dirt dispersion agent of claim 1, it is characterized in that: after in reactor, adding deionized water, add 2-phosphonate group-1 again, 2,4-butane tricarboxylate, Amino Trimethylene Phosphonic Acid, co-polymer of sulfonate and poly aspartic acid, normal temperature stir down and made in 55~65 minutes.