CN102162023A - Uniform post-treatment method for steel aluminum 9 graphite solid-liquid phase composite board - Google Patents
Uniform post-treatment method for steel aluminum 9 graphite solid-liquid phase composite board Download PDFInfo
- Publication number
- CN102162023A CN102162023A CN 201010613893 CN201010613893A CN102162023A CN 102162023 A CN102162023 A CN 102162023A CN 201010613893 CN201010613893 CN 201010613893 CN 201010613893 A CN201010613893 A CN 201010613893A CN 102162023 A CN102162023 A CN 102162023A
- Authority
- CN
- China
- Prior art keywords
- phase composite
- steel
- graphite
- graphite solid
- liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a uniform post-treatment method for a steel aluminum 9 graphite solid-liquid phase composite board, and belongs to the field of the research of room temperature rolling post-treatment of interfacial shear strength of steel aluminum 9 graphite solid-liquid phase composite boards. The two-pass rolling treatment that the total reduction ratio is 1.6 percent and the proportion of pass reduction ratios of a first pass and a second pass is (1:3)-(1:1) is performed on the steel aluminum 9 graphite solid-liquid phase composite board formed by a 08A1 steel plate with the thickness of 1.2mm and an aluminum 9 graphite cladding layer with the thickness of 2.5mm on a precision rolling mill at room temperature. The difference value of transverse interfacial shear strength of the composite board can be reduced to be less than 1.9MPa.
Description
Technical field
The present invention relates to a kind of rolling post-treating method of interface shear strength room temperature of steel aluminium 9 graphite solid-liquid-phase composite plates.
Background technology
Publication number: CN1710114A, denomination of invention: on " a kind of post-treating method of steel-back aluminium-base solid-liquid-phase composite plate ", set forth the rolling post-treating method of room temperature of steel-back aluminium-base solid-liquid-phase composite plate, promptly, at room temperature, on finishing rolling mill, to steel-back aluminium-base solid-liquid-phase composite plate, be rolled aftertreatment, utilize the difference of aluminium base coating that rolling processing produces and steel backing deflection to remedy the difference of aluminium base coating and steel backing shrinkage in the composite solidification process of cooling, and then reduce composition board interface additional stress, the composition board interface shear strength is improved.This method technology is simple, composition board interface shear strength value improves bigger, but, because this method is carrying out there is aluminium base coating deflection non-uniform phenomenon when one-pass roller is handled, therefore cause the uneven distribution of composition board interface shear strength usually, can be in composition board interface shear strength difference transversely up to 3～5MPa.
Steel aluminium 9 graphite solid-liquid-phase composite plates are the solid-liquid-phase composite plates that are made of thick 08Al steel plate of 1.2mm and the thick aluminium 9 graphite coating of 2.5mm, when adopting the CN1710114A patented method to be rolled aftertreatment, at ideal draft comparatively is under 1.6% condition, because aluminium 9 graphite coating are at composition board deflection skewness transversely, cause the difference between the composition board interface shear strength transversely can be up to 3MPa.
For steel aluminium 9 graphite solid-liquid-phase composite plates, the difference of transverse interface shearing resistance is more little, and work reliability is high more, and range of application is wide more, so the difference of steel aluminium 9 graphite solid-liquid-phase composite plate transverse interface shearing resistances is the smaller the better.
Summary of the invention
Technical problem to be solved by this invention is, overcome the deficiency of the existing steel aluminium rolling post-treating methods of 9 graphite solid-liquid-phase composite plate room temperatures " transverse interface shearing resistance difference is big ", a kind of post-treating method that can improve steel aluminium 9 graphite solid-liquid-phase composite plate transverse interface shearing resistance distributing homogeneities is provided, further dwindles the difference of composition board transverse interface shearing resistance.
The technical solution adopted for the present invention to solve the technical problems is: to steel aluminium 9 graphite solid-liquid-phase composite plates, at room temperature, on finishing rolling mill, carry out total draft and be percentage pass reduction ratio 1.6%, first passage and second passage and be 1: 3～1: 1 the rolling processing of two passages.
The invention has the beneficial effects as follows: for the rolling processing of composition board room temperature, because roller is jumped, the existence of the unequal factor of matrix, transversely produce nonaffine deformation inevitably in composition board, the difference that causes composition board transverse interface shearing resistance, and draft is big more, distortion transversely is inhomogeneous more, and the difference of composition board transverse interface shearing resistance is big more.If nonaffine deformation transversely with the rolling generation of single pass heavy reduction rate, decompose in the middle of the little draft distortion of multi-pass, then one-pass roller can be handled the big-difference of the transverse deformation amount that produces, be decomposed into the little difference of the transverse deformation amount of multi-pass, and the optimum combination by each percentage pass reduction, can also further coordinate the difference of transverse deformation amount.The present invention utilizes the optimum combination of the percentage pass reduction of first passage and second passage further to reduce and coordinated the difference of the transverse deformation amount of the rolling processing of room temperature, thereby has reached the purpose that reduces composition board transverse interface shearing resistance difference.Utilize the present invention, steel aluminium 9 graphite solid-liquid-phase composite plates are carried out the rolling processing of room temperature, composition board transverse interface shearing resistance difference can be reduced in the 1.9MPa, reduce by 37% at least than adopting the CN1710114A patented method to carry out the 3MPa that the rolling processing of room temperature obtains.
Embodiment
A kind of even post-treating method of steel aluminium 9 graphite solid-liquid-phase composite plates, at room temperature, on finishing rolling mill, to the steel aluminium 9 graphite solid-liquid-phase composite plates that constitute by thick 08Al steel plate of 1.2mm and the thick aluminium 9 graphite coating of 2.5mm, carry out two passages, total draft is 1.6% rolling aftertreatment, the big-difference of the aluminium 9 graphite coating transverse deformation amounts that the rolling aftertreatment of single pass heavy reduction rate is produced, decomposition and coordination are the little difference of the aluminium 9 graphite coating transverse deformation amounts of the rolling aftertreatment generation of the little draft of two passages, thereby further reduced composition board transverse interface shearing resistance difference, improved the distributing homogeneity of steel aluminium 9 graphite solid-liquid-phase composite plate interface shear strengths.
Embodiment one, to steel aluminium 9 graphite solid-liquid-phase composite plates, the percentage pass reduction ratio of carrying out first passage and second passage is 1: 3 the rolling aftertreatment of two passage room temperatures, is 1.9MPa in composition board interface shear strength difference transversely.
Embodiment two, to steel aluminium 9 graphite solid-liquid-phase composite plates, the percentage pass reduction ratio of carrying out first passage and second passage is 1: 2.5 the rolling aftertreatment of two passage room temperatures, is 1.8MPa in composition board interface shear strength difference transversely.
Embodiment three, to steel aluminium 9 graphite solid-liquid-phase composite plates, the percentage pass reduction ratio of carrying out first passage and second passage is 1: 2 the rolling aftertreatment of two passage room temperatures, is 1.6MPa in composition board interface shear strength difference transversely.
Embodiment four, to steel aluminium 9 graphite solid-liquid-phase composite plates, the percentage pass reduction ratio of carrying out first passage and second passage is 1: 1.5 the rolling aftertreatment of two passage room temperatures, is 1.7MPa in composition board interface shear strength difference transversely.
Embodiment five, to steel aluminium 9 graphite solid-liquid-phase composite plates, the percentage pass reduction ratio of carrying out first passage and second passage is 1: 1 the rolling aftertreatment of two passage room temperatures, is 1.8MPa in composition board interface shear strength difference transversely.
As seen, to the steel aluminium 9 graphite solid-liquid-phase composite plates that constitute by thick 08Al steel plate of 1.2mm and the thick aluminium 9 graphite coating of 2.5mm, the percentage pass reduction ratio of carrying out total draft and be 1.6%, first passage and second passage is 1: 3～1: 1 the rolling aftertreatment of two passage room temperatures, and composition board interface shear strength difference transversely is reduced in the 1.9MPa.
Claims (1)
1. the even post-treating method of steel aluminium 9 graphite solid-liquid-phase composite plates, at room temperature, on finishing rolling mill, the steel aluminium 9 graphite solid-liquid-phase composite plates that are made of thick 08Al steel plate of 1.2mm and the thick aluminium 9 graphite coating of 2.5mm are rolled aftertreatment, it is characterized in that, to steel aluminium 9 graphite solid-liquid-phase composite plates, carry out total draft and be percentage pass reduction ratio 1.6%, first passage and second passage and be 1: 3～1: 1 the rolling processing of two passages.