CN102160977A - Mineral dispersant and preparation method thereof - Google Patents
Mineral dispersant and preparation method thereof Download PDFInfo
- Publication number
- CN102160977A CN102160977A CN2011100473393A CN201110047339A CN102160977A CN 102160977 A CN102160977 A CN 102160977A CN 2011100473393 A CN2011100473393 A CN 2011100473393A CN 201110047339 A CN201110047339 A CN 201110047339A CN 102160977 A CN102160977 A CN 102160977A
- Authority
- CN
- China
- Prior art keywords
- thiazolinyl
- sulfonic acid
- polyethylene glycol
- nertralizer
- glycol oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a mineral dispersant and a preparation method thereof. The mineral dispersant is an aqueous solution of anionic copolymer, wherein the anionic copolymer is formed by four monomers through free radical polymerization, and neutralized into the mineral dispersant through two different alkaline substances. The mineral dispersant producing process is green and environmentally friendly, the product performance is excellent and stable, the product is easily degraded in the natural world, polydispersity index is lower than 2.2; the mineral dispersant can be used for dispersion of minerals, including mineral grinding dispersion required by industry, water treatment scale dispersion, cement additive and the like.
Description
Technical field
The present invention relates to a kind of mineral matter dispersant and preparation method thereof.
Background technology
The occasions such as grinding dispersion of filler all need to use a kind of mineral matter dispersant in the grinding dispersion of the grinding dispersion of papermaking filler, porcelain, cement diminishing, water body antiscale, water paint, so that slurry content height, stable, the good fluidity of system when grind disperseing, when water treatment, can stablize easy scale forming matters such as carbonate in the water body, phosphate, silicate and be microcrystalline state and be suspended in the water body and do not deposit.
This dispersant relies on acrylate homopolymer for a long time in the performance leading role, and the copolymer of various interpolation trace function monomers also has research report or produced in small quantities to sell, but there are in the following problems one or more in they, so that uses limited:
1) for regulating molecular weight, uses sodium hypophosphite or other phosphorus compound in a large number; Cause the applied environment eutrophication, grow algae easily, cause environmental pollution.
2) for regulating molecular weight, use organic solvents such as isopropyl alcohol in a large number,, increased energy consumption and complexity on the one hand as patent CN92101664, WO2002049765 etc.; The time spent volatilizing loss of solvent recovery cover is bigger on the other hand, and is unfavorable to environment; In addition, the organic matter that remains in the dispersant can enter the downstream application system along with dispersant, produces negative influence.
3) for regulating molecular weight, patent CN200610098170 has used mercaptoethanol, and there is the problem of security, stability in mercaptoethanol, so can't promote the use of substantially.
4) active group unreasonable allocation, the not good and afunction of effect.Patent CN20081002010 pointed out once that " best water treatment agent should have strong acid and two kinds of functional groups of weak acid; wherein strong acid functional group is keeping slight ion characteristic (helping dissolving), and the weak acid group then has stronger restriction ability (inhibition crystalline growth) to active site.In addition ,-COOH to the resistance CaCO
3Dirt is effective ,-OH ,-SO
3H is to resistance Ca
3(PO
4)
2Dirt is useful, have only-COOH ,-OH ,-SO
3H three's synergy just can show best scale inhibition effect, just lacks all very desirable anti-incrustation corrosion inhibitor of this scale inhibition and corrosion mitigating effect in the market." patent CN200610098170, CN200780029577, CN200710013677, CN200910115477,200910039140 mentioned products lack strong acid group and cause afunction; can significantly weaken if be used for phosphatic system dispersion effect, be difficult to avoid phosphate and in fact contain the mineral matter system.
5) commercially available grinding dispersant also often occur slurry return sticking, slurry system is unstable, free dispersant is too many in the slurry (has side effects on the one hand, reduced the product utilization rate on the other hand) etc. problem, commercially available water treatment dispersant often occur flocculating deposition, the phenomenon of poor effect when disperseing zinc and phosphate radical.
Summary of the invention
A technical problem to be solved by this invention is: provide and do not adopt phosphorus-containing compound in a kind of production process, strong acid, the weak acid functional group of containing appropriate ratio in the molecular structure, can prevent simultaneously the cohesion of mineral matter polycrystallite, raising system stability, dispersibility, the mineral matter dispersant of the frictional resistance between the reduction crystallite.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of mineral matter dispersant, this mineral matter dispersant is a kind of aqueous solution of anionic copolymer, the amount of the water in the mineral dispersant is the application performance of impact polymer not, the water yield is added in different step, and the application performance of final products is not had influence.
The anionic copolymer general formula of molecular structure is:
Wherein:
m=1-100，n=10-300，?p=1-40，q=1-300；
R1, R2, R3 are that hydrogen, carbon number are the alkyl of 1-6 or contain the alkyl that heteroatomic carbon number is 1-6, and R1, R2, R3 are identical or different;
X=1-6, y=4-16, and x, y are integer;
M1, M2 are the cationic moiety in category-A nertralizer or the category-B nertralizer, and M1, M2 are identical or different;
The molecular weight ranges of anionic copolymer: 1000-20000 gram/mole;
Anionic copolymer contains four kinds of alkenyl monomer, is respectively: thiazolinyl carboxylic acid, thiazolinyl hydroxypropyl sulfonic acid and/or thiazolinyl hydroxypropyl sulfonate, the degree of polymerization are the thiazolinyl polyethylene glycol oxide sulfonic acid of y and/or thiazolinyl polyethylene glycol oxide sulfonate, the thiazolinyl fatty alcohol that the degree of polymerization is y;
Described category-A nertralizer is: the hydroxide of sodium, potassium, lithium, ammonium or contain 1-8 carbon atom and water-soluble nitrogen-containing compound at least a;
Described category-B nertralizer is: at least a in the hydroxide of magnesium, calcium, barium, zinc, aluminium or the oxide.
Another technical problem to be solved by this invention is: the preparation method that a kind of mineral matter dispersant is provided.
For solving second above-mentioned technical problem, the technical solution used in the present invention is: a kind of preparation method of mineral matter dispersant the steps include:
1) preparation of initiator solution: get initator, be configured to the aqueous solution of 10-40%;
2) preparation of thiazolinyl carboxylic acid aqueous solution: take by weighing the thiazolinyl carboxylic acid, add the water that is not more than Total Water in the finished product, stir, cool off down, add the category-A nertralizer that is not more than expection A, category-B nertralizer total amount, add during the nertralizer, temperature of charge is lower than 40 ℃;
3) in the autoclave, the thiazolinyl hydroxypropyl sulfonic acid of input water, metering and/or thiazolinyl hydroxypropyl sulfonate, the degree of polymerization are the thiazolinyl polyethylene glycol oxide sulfonic acid of y and/or thiazolinyl polyethylene glycol oxide sulfonate, the thiazolinyl fatty alcohol that the degree of polymerization is y, airtight autoclave; Behind nitrogen replacement removal air, be warming up to 60-130 ℃, drip initiator solution, thiazolinyl carboxylic acid aqueous solution simultaneously, 30-300 min drips off simultaneously, liberated heat makes material be warming up to polymerization temperature at 5-15min during the dropping: 100-150 ℃, adjusting still temperature is constant in polymerization temperature, after dropping finishes, constant in polymerization temperature 5-120min, be cooled to below 70 ℃, add the category-A nertralizer, be stirred to molten entirely, add the category-B nertralizer again, be stirred to molten entirely;
Described initator is: at least a in hydrogen peroxide, ammonium persulfate, sodium peroxydisulfate, potassium peroxydisulfate, di-tert-butyl peroxide, tert-butyl peroxide, t-amyl peroxy thing, the methyl ethyl ketone peroxide, and consumption is the 1-10% of alkenyl monomer quality;
Described thiazolinyl carboxylic acid is: at least a in methacrylic acid, itaconic acid, the acrylic acid;
The category-B nertralizer accounts for nertralizer total amount 〉=5%; The total mole of nertralizer total amount is not more than the mole total amount of four alkenyl monomer.
Described thiazolinyl carboxylic acid, thiazolinyl hydroxypropyl sulfonic acid and/or thiazolinyl hydroxypropyl sulfonate, the degree of polymerization are that the thiazolinyl polyethylene glycol oxide sulfonic acid of y and/or the thiazolinyl polyethylene glycol oxide sulfonate that the degree of polymerization is y, the mol ratio of thiazolinyl fatty alcohol are: 5-50:1-10:1-10:0.01-1.0.
Described thiazolinyl hydroxypropyl sulfonic acid is: 2-hydroxyl-3-allyloxy-1-propyl sulfonic acid;
Described thiazolinyl hydroxypropyl sulfonate is: at least a in the triethanolamine salt of the alkali salt of the alkali metal salt of 2-hydroxyl-3-allyloxy-1-propyl sulfonic acid, 2-hydroxyl-3-allyloxy-1-propyl sulfonic acid, the ammonium salt of 2-hydroxyl-3-allyloxy-1-propyl sulfonic acid, 2-hydroxyl-3-allyloxy-1-propyl sulfonic acid.
The described degree of polymerization is that the thiazolinyl polyethylene glycol oxide sulfonic acid of y is: pi-allyl polyethylene glycol oxide sulfonic acid;
The described degree of polymerization is that the thiazolinyl polyethylene glycol oxide sulfonate of y is: at least a in pi-allyl polyethylene glycol oxide sulfonic acid ammonium salt, pi-allyl polyethylene glycol oxide sulfonic acid calcium salt, the pi-allyl polyethylene glycol oxide sulfonate sodium.
Described thiazolinyl fatty alcohol is at least a in propenyl, metallyl alcohol, the suitable-3-hexenol.
Described mineral matter is natural or synthetic calcium carbonate, dolomite, kaolin, talcum, gypsum, lime, magnesia, titanium dioxide, satin white, alundum (Al, aluminium hydroxide, silica, mica at least a, or the typical mixture between above-mentioned filler: talcum-calcium carbonate mixture, calcium carbonate-kaolin mixture, calcium carbonate-alundum (Al or aluminium hydroxide.
Beneficial effect of the present invention:
A) the present invention has avoided the defective of simple function group, adopts strong acid, the weak acid functional group of appropriate ratio, makes dispersant can disperse carbonate, phosphate, silicate in the mineral matter etc. simultaneously;
B) the present invention has inserted hydroxyl in long-chain, has effectively prevented the cohesion of mineral matter polycrystallite;
C) the present invention has inserted the polyethylene glycol oxide of sulfonic group end-blocking in long-chain, effectively improved dispersibility, reduced frictional resistance between crystallite, improved system stability, thereby low sticking, stable, the height that help ground slurry contains admittedly;
D) the present invention adopts autoclave, high temperature polymerization, reduce residual monomer effectively, reduced polydispersity coefficient effectively, helped the homogeneity of polymer molecular weight, thereby also help reducing the free dispersant in the grinding system, improve the utilization ratio of dispersant;
E) the present invention meets the green chemical industry theory, does not adopt phosphorus-containing compound in the production process, and does not have any material release, and production equipment need not clean throughout the year;
F) the present invention quotes ehter bond in a large number, makes product be easy to ecological degraded after entering the Nature.
The specific embodiment
The invention will be further described below by specific embodiment, but can not be as limitation of the present invention.
Embodiment 1
1) preparation of initiator solution: take by weighing ammonium persulfate 176kg and be dissolved in the 352kg deionized water.
2) preparation of thiazolinyl carboxylic acid aqueous solution: take by weighing 1000kg acrylic acid and drop in the reactor, add 100kg water, start the freeze cycle water in stirring and the chuck, drip 86kg 32% liquid caustic soda, drip off the back and stir 30min.
3) in the stainless steel autoclave of being furnished with reflux condensing tube, can overlapping with the strap clamp of pressing constant speed syringe pump, liftable temperature, drop into 1200kg water, 2-hydroxyl-3-allyloxy-1-propyl sulfonic acid 560kg, pi-allyl polyethylene glycol oxide (10) sulfonic acid 1360kg, propenyl 14kg, airtight autoclave.Behind nitrogen replacement removal air, be warming up to 95 ℃, adopt two can be with pressure constant speed syringe pump to drip initiator solution, thiazolinyl carboxylic acid aqueous solution simultaneously respectively, being controlled at 180min drips off simultaneously, liberated heat makes material be warming up to 125 ℃ at 10min during the dropping, constant by the adjusting of the heat transfer medium in autoclave chuck still temperature at 120-130 ℃, after dripping end, at 120-130 ℃ of constant temperature 30min, be cooled to 50 ℃ and remain under this temperature, add calcium oxide 78.82kg and be stirred to dissolving, add potassium hydroxide 822.01kg then, be stirred to dissolving.
Embodiment 2
1) preparation of initiator solution: take by weighing potassium peroxydisulfate 122kg and be dissolved in the 244kg deionized water.
2) preparation of thiazolinyl carboxylic acid aqueous solution: take by weighing the 1300kg methacrylic acid and drop in the reactor, add 130kg water, start the freeze cycle water in stirring and the chuck, drip 94kg 32% liquid caustic soda, drip off the back and stir 30min.
3) in the stainless steel autoclave of being furnished with reflux condensing tube, can overlapping with the strap clamp of pressing constant speed syringe pump, liftable temperature, drop into 1200kg water, 2-hydroxyl-3-allyloxy-1-propyl sulfonic acid sodium 350kg, pi-allyl polyethylene glycol oxide (12) sulfonic acid 1400kg, suitable-3-hexenol 12kg, airtight autoclave.Behind nitrogen replacement removal air, be warming up to 95 ℃, adopt two can be with pressure constant speed syringe pump to drip initiator solution, thiazolinyl carboxylic acid aqueous solution simultaneously respectively, being controlled at 120min drips off simultaneously, liberated heat makes material be warming up to 125 ℃ at 10min during the dropping, constant by the adjusting of the heat transfer medium in autoclave chuck still temperature at 120-130 ℃, after dripping end, at 120-130 ℃ of constant temperature 30min, be cooled to 50 ℃ and remain under this temperature, add zinc oxide 115.2kg and be stirred to dissolving, add 32% liquid caustic soda 1610kg then, be stirred to dissolving.
Embodiment 3
1) preparation of initiator solution: take by weighing 50% hydrogen peroxide 404kg and be dissolved in the 202kg deionized water.
2) preparation of thiazolinyl carboxylic acid aqueous solution: take by weighing 1200kg acrylic acid and drop in the reactor, add 120kg water, start the freeze cycle water in stirring and the chuck, drip 95kg 32% liquid caustic soda, drip off the back and stir 30min.
3) in the stainless steel autoclave of being furnished with reflux condensing tube, can overlapping with the strap clamp of pressing constant speed syringe pump, liftable temperature, drop into 1200kg water, 2-hydroxyl-3-allyloxy-1-propyl sulfonic acid 480kg, pi-allyl polyethylene glycol oxide (8) ichthyodin 1200kg, metallyl alcohol 6kg, airtight autoclave.Behind nitrogen replacement removal air, be warming up to 95 ℃, adopt two can be with pressure constant speed syringe pump to drip initiator solution simultaneously respectively, the thiazolinyl carboxylic acid aqueous solution, being controlled at 180min drips off simultaneously, liberated heat makes material be warming up to 120 ℃ at 8min during the dropping, constant by the adjusting of the heat transfer medium in autoclave chuck still temperature at 115-125 ℃, after dripping end, at 115-125 ℃ of constant temperature 30min, be cooled to 50 ℃ and remain under this temperature, add aluminium oxide 106.38kg and be stirred to dissolving, add dimethylethanolamine 1256.87kg then, be stirred to dissolving.
Embodiment 4
1) preparation of initiator solution: take by weighing methyl ethyl ketone peroxide 132kg and be dissolved in the 264kg deionized water.
2) preparation of thiazolinyl carboxylic acid aqueous solution: take by weighing the 1600kg itaconic acid and drop in the reactor, add 3200kg water, start the freeze cycle water in stirring and the chuck, drip 152kg 32% liquid caustic soda, drip off the back and stir 30min.
3) in the stainless steel autoclave of being furnished with reflux condensing tube, can overlapping with the strap clamp of pressing constant speed syringe pump, liftable temperature, drop into 200kg water, 2-hydroxyl-3-allyloxy-1-propyl sulfonic acid 368kg, pi-allyl polyethylene glycol oxide (10) sodium sulfonate 1330kg, propenyl 6kg, airtight autoclave.Behind nitrogen replacement removal air, be warming up to 110 ℃, adopt two can be with pressure constant speed syringe pump to drip initiator solution, thiazolinyl carboxylic acid aqueous solution simultaneously respectively, being controlled at 120min drips off simultaneously, liberated heat makes material be warming up to 115 ℃ at 10min during the dropping, constant by the adjusting of the heat transfer medium in autoclave chuck still temperature at 115-125 ℃, after dripping end, at 115-125 ℃ of constant temperature 30min, be cooled to 50 ℃ and remain under this temperature, add calcium oxide 67.88kg and be stirred to dissolving, feed liquefied ammonia 175.1kg then.
Embodiment 5
1) preparation of initiator solution: take by weighing tert-butyl peroxide 140kg and be dissolved in the 280kg deionized water.
2) preparation of thiazolinyl carboxylic acid aqueous solution: take by weighing the 1600kg itaconic acid and drop in the reactor, add 3200kg water, start the freeze cycle water in stirring and the chuck, drip 152kg 32% liquid caustic soda, drip off the back and stir 30min.
3) in the stainless steel autoclave of being furnished with reflux condensing tube, can overlapping with the strap clamp of pressing constant speed syringe pump, liftable temperature, drop into 200kg water, 2-hydroxyl-3-allyloxy-1-propyl sulfonic acid 420kg, pi-allyl polyethylene glycol oxide (8) ichthyodin 780kg, suitable-3-hexenol 8kg, airtight autoclave.Behind nitrogen replacement removal air, be warming up to 110 ℃, adopt two can be with pressure constant speed syringe pump to drip initiator solution, thiazolinyl carboxylic acid aqueous solution simultaneously respectively, being controlled at 120min drips off simultaneously, liberated heat makes material be warming up to 115 ℃ at 10min during the dropping, constant by the adjusting of the heat transfer medium in autoclave chuck still temperature at 115-125 ℃, after dripping end, at 115-125 ℃ of constant temperature 30min, be cooled to 50 ℃ and remain under this temperature, add calcium hydroxide 86.33kg and be stirred to dissolving, feed liquefied ammonia 206.04kg then.
Embodiment 6
1) preparation of initiator solution: take by weighing sodium peroxydisulfate 116kg and be dissolved in the 232kg deionized water.
2) preparation of thiazolinyl carboxylic acid aqueous solution: take by weighing the 1300kg methacrylic acid and drop in the reactor, add 130kg water, start the freeze cycle water in stirring and the chuck, drip 94kg 32% liquid caustic soda, drip off the back and stir 30min.
3) in the stainless steel autoclave of being furnished with reflux condensing tube, can overlapping with the strap clamp of pressing constant speed syringe pump, liftable temperature, drop into 1200kg water, 2-hydroxyl-3-allyloxy-1-propyl sulfonic acid ammonium 350kg, pi-allyl polyethylene glycol oxide (12) ichthyodin 1250kg, metallyl alcohol 10kg, airtight autoclave.Behind nitrogen replacement removal air, be warming up to 115 ℃, adopt two can be with pressure constant speed syringe pump to drip initiator solution, thiazolinyl carboxylic acid aqueous solution simultaneously respectively, being controlled at 120min drips off simultaneously, liberated heat makes material be warming up to 125 ℃ at 8min during the dropping, constant by the adjusting of the heat transfer medium in autoclave chuck still temperature at 120-130 ℃, after dripping end, at 120-130 ℃ of constant temperature 30min, be cooled to 50 ℃ and remain under this temperature, add magnesia 56.22kg and be stirred to dissolving, add NaOH 507.6kg then, be stirred to dissolving.
Embodiment 7
1) preparation of initiator solution: take by weighing ammonium persulfate 176kg and be dissolved in the 352kg deionized water.
2) preparation of thiazolinyl carboxylic acid aqueous solution: take by weighing 1000kg acrylic acid and drop in the reactor, add 100kg water, start the freeze cycle water in stirring and the chuck, drip 86kg 32% liquid caustic soda, drip off the back and stir 30min.
3) in the stainless steel autoclave of being furnished with reflux condensing tube, can overlapping with the strap clamp of pressing constant speed syringe pump, liftable temperature, drop into 1200kg water, 2-hydroxyl-3-allyloxy-1-propyl sulfonic acid sodium salt 343.71kg, 2-hydroxyl-3-allyloxy-1-propyl sulfonic acid 280kg, pi-allyl polyethylene glycol oxide (10) sulfonic acid ammonium salt 700kg, pi-allyl polyethylene glycol oxide (10) sulfonic acid 680kg, propenyl 14kg, airtight autoclave.Behind nitrogen replacement removal air, be warming up to 95 ℃, adopt two can be with pressure constant speed syringe pump to drip initiator solution, thiazolinyl carboxylic acid aqueous solution simultaneously respectively, being controlled at 180min drips off simultaneously, liberated heat makes material be warming up to 125 ℃ at 10min during the dropping, constant by the adjusting of the heat transfer medium in autoclave chuck still temperature at 120-130 ℃, after dripping end, at 120-130 ℃ of constant temperature 30min, be cooled to 50 ℃ and remain under this temperature, add calcium oxide 78.82kg and be stirred to dissolving, add potassium hydroxide 675.72kg then, be stirred to dissolving.
Claims (6)
1. mineral matter dispersant, it is characterized in that: this mineral matter dispersant is a kind of aqueous solution of anionic copolymer;
The anionic copolymer general formula of molecular structure is:
Wherein:
m=1-100，n=10-300，?p=1-40，q=1-300；
R1, R2, R3 are that hydrogen, carbon number are the alkyl of 1-6 or contain the alkyl that heteroatomic carbon number is 1-6, and R1, R2, R3 are identical or different;
X=1-6, y=4-16, and x, y are integer;
M1, M2 are the cationic moiety in category-A nertralizer or the category-B nertralizer, and M1, M2 are identical or different;
The molecular weight ranges of anionic copolymer: 1000-20000 gram/mole;
Anionic copolymer contains four kinds of alkenyl monomer, is respectively: thiazolinyl carboxylic acid, thiazolinyl hydroxypropyl sulfonic acid and/or thiazolinyl hydroxypropyl sulfonate, the degree of polymerization are the thiazolinyl polyethylene glycol oxide sulfonic acid of y and/or thiazolinyl polyethylene glycol oxide sulfonate, the thiazolinyl fatty alcohol that the degree of polymerization is y;
Described category-A nertralizer is: the hydroxide of sodium, potassium, lithium, ammonium or contain 1-8 carbon atom and water-soluble nitrogen-containing compound at least a;
Described category-B nertralizer is: at least a in the hydroxide of magnesium, calcium, barium, zinc, aluminium or the oxide.
2. the preparation method of a kind of mineral matter dispersant according to claim 1, its preparation process is:
1) preparation of initiator solution: get initator, be configured to the aqueous solution of 10-40%;
2) preparation of thiazolinyl carboxylic acid aqueous solution: take by weighing the thiazolinyl carboxylic acid, add the water that is not more than Total Water in the finished product, stir, cool off down, add the category-A nertralizer that is not more than expection A, category-B nertralizer total amount, add during the nertralizer, temperature of charge is lower than 40 ℃;
3) in the autoclave, the thiazolinyl hydroxypropyl sulfonic acid of input water, metering and/or thiazolinyl hydroxypropyl sulfonate, the degree of polymerization are the thiazolinyl polyethylene glycol oxide sulfonic acid of y and/or thiazolinyl polyethylene glycol oxide sulfonate, the thiazolinyl fatty alcohol that the degree of polymerization is y, airtight autoclave; Behind nitrogen replacement removal air, be warming up to 60-130 ℃, drip initiator solution, thiazolinyl carboxylic acid aqueous solution simultaneously, 30-300 min drips off simultaneously, liberated heat makes material be warming up to polymerization temperature at 5-15min during the dropping: 100-150 ℃, adjusting still temperature is constant in polymerization temperature, after dropping finishes, constant in polymerization temperature 5-120min, be cooled to below 70 ℃, add the category-A nertralizer, be stirred to molten entirely, add the category-B nertralizer again, be stirred to molten entirely;
Described initator is: at least a in hydrogen peroxide, ammonium persulfate, sodium peroxydisulfate, potassium peroxydisulfate, di-tert-butyl peroxide, tert-butyl peroxide, t-amyl peroxy thing, the methyl ethyl ketone peroxide, and consumption is the 1-10% of alkenyl monomer quality;
Described thiazolinyl carboxylic acid is: at least a in methacrylic acid, itaconic acid, the acrylic acid;
The category-B nertralizer accounts for nertralizer total amount 〉=5%; The total mole of nertralizer total amount is not more than the mole total amount of four alkenyl monomer.
3. the preparation method of a kind of mineral matter dispersant according to claim 2 is characterized in that: described thiazolinyl carboxylic acid, thiazolinyl hydroxypropyl sulfonic acid and/or thiazolinyl hydroxypropyl sulfonate, the degree of polymerization are that the thiazolinyl polyethylene glycol oxide sulfonic acid of y and/or the thiazolinyl polyethylene glycol oxide sulfonate that the degree of polymerization is y, the mol ratio of thiazolinyl fatty alcohol are: 5-50:1-10:1-10:0.01-1.0.
4. the preparation method of a kind of mineral matter dispersant according to claim 2 is characterized in that:
Described thiazolinyl hydroxypropyl sulfonic acid is: 2-hydroxyl-3-allyloxy-1-propyl sulfonic acid;
Described thiazolinyl hydroxypropyl sulfonate is: at least a in the triethanolamine salt of the alkali salt of the alkali metal salt of 2-hydroxyl-3-allyloxy-1-propyl sulfonic acid, 2-hydroxyl-3-allyloxy-1-propyl sulfonic acid, the ammonium salt of 2-hydroxyl-3-allyloxy-1-propyl sulfonic acid, 2-hydroxyl-3-allyloxy-1-propyl sulfonic acid.
5. the preparation method of a kind of mineral matter dispersant according to claim 2 is characterized in that:
The described degree of polymerization is that the thiazolinyl polyethylene glycol oxide sulfonic acid of y is: pi-allyl polyethylene glycol oxide sulfonic acid;
The described degree of polymerization is that the thiazolinyl polyethylene glycol oxide sulfonate of y is: at least a in pi-allyl polyethylene glycol oxide sulfonic acid ammonium salt, pi-allyl polyethylene glycol oxide sulfonic acid calcium salt, the pi-allyl polyethylene glycol oxide sulfonate sodium.
6. the preparation method of a kind of mineral matter dispersant according to claim 2 is characterized in that: described thiazolinyl fatty alcohol is at least a in propenyl, metallyl alcohol, the suitable-3-hexenol.