CN102154732A - 一种服装用电磁波屏蔽纤维 - Google Patents
一种服装用电磁波屏蔽纤维 Download PDFInfo
- Publication number
- CN102154732A CN102154732A CN2011100741062A CN201110074106A CN102154732A CN 102154732 A CN102154732 A CN 102154732A CN 2011100741062 A CN2011100741062 A CN 2011100741062A CN 201110074106 A CN201110074106 A CN 201110074106A CN 102154732 A CN102154732 A CN 102154732A
- Authority
- CN
- China
- Prior art keywords
- fiber
- electromagnetic wave
- powder
- wave shielding
- fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种服装用电磁波屏蔽纤维，包括聚丙烯晴纤维，所述聚丙烯晴纤维的表面包裹有铜结晶层，所述电磁波屏蔽纤维的组成成分及重量份比例为：聚丙烯晴纤维20–40，聚酯纤维2–8，聚酰氨纤维5–15，聚烯烃纤维4–6，碳纤维10–30，玻璃纤维10–20，聚丙烯树脂10–20，该电磁波屏蔽纤维还包括电磁波吸收粉，电磁波吸收粉与聚丙烯树脂的重量比为1:5–1:4，电磁波吸收粉的组成成分及重量份比例为：铁氧体粉末40–50，二氧化硅粉末10–20，铁粉30–50。本发明不仅屏蔽效果较强，而且机械强度较高。
Description
技术领域
本发明涉及一种纤维材料，尤其涉及一种服装用电磁波屏蔽纤维，具体适用于高强度屏蔽纤维的制作。
背景技术
目前，电磁波屏蔽纤维的屏蔽方法一般包括两种：反射电磁波与吸收电磁波。所谓的反射电磁波就是采取金属等导电物质反射电磁波，从而实现屏蔽电磁波的目的，该种方法常用不锈钢等金属纤维及其与普通纤维混纺生产的材料以制作电磁波屏蔽织物，也可在普通纤维的表面镀金属膜以形成导电性能优良的导电层。采用的金属膜除了屏蔽作用外，还具有杀菌效果，如采用银离子就可以起到抑菌防臭的作用，对金葡菌、肺炎杆菌、绿浓杆菌、大肠杆菌等有抑制和防扩散作用。所谓的吸收电磁波就是采用陶瓷微粉、铁氧体微粉等吸收电磁波微粉共混制成电磁波屏蔽纤维。
中国专利公开号为CN1357664A，公开日为2002年7月10日的发明专利公开了一种具有电磁屏蔽功能的纤维及其制备方法，该纤维的特征在于：所述的纤维中和表面含有重量百分比为10－17％的成膜五硫九铜(分子式为Cu9S5)结晶层和83－90％的含氰基纤维，该纤维中的导电结晶层为100％的Cu9S5稳定结晶体，具有紧密，厚薄均匀，耐久性和耐化学性的特点。虽然该发明具有一定的电磁波屏蔽效果，但其仅仅依靠成膜的五硫九铜结晶层进行屏蔽，屏蔽效果较弱，而且其主体为含氰基纤维，机械强度较低，使用中易损坏。
发明内容
本发明的目的是克服现有技术中存在的屏蔽效果较弱、机械强度较低的缺陷与问题，提供一种屏蔽效果较强、机械强度较高的电磁波屏蔽纤维。
为实现以上目的，本发明的技术解决方案是：一种服装用电磁波屏蔽纤维，包括聚丙烯晴纤维，所述聚丙烯晴纤维的表面包裹有铜结晶层，所述电磁波屏蔽纤维的组成成分及重量份比例为：聚丙烯晴纤维20–40，聚酯纤维2–8，聚酰氨纤维5–15，聚烯烃纤维4–6，碳纤维10–30，玻璃纤维10–20，聚丙烯树脂10–20。
所述电磁波屏蔽纤维的组成成分及重量份比例为：聚丙烯晴纤维30，聚酯纤维5，聚酰氨纤维10，聚烯烃纤维5，碳纤维20，玻璃纤维15，聚丙烯树脂15。
所述电磁波屏蔽纤维还包括电磁波吸收粉，该电磁波吸收粉与聚丙烯树脂的重量比为1:5–1:4。
所述电磁波吸收粉的组成成分及重量份比例为：铁氧体粉末40–50，二氧化硅粉末10–20，铁粉30–50。
所述电磁波吸收粉的组成成分及重量份比例为：铁氧体粉末45，二氧化硅粉末15，铁粉40。
与现有技术相比，本发明的有益效果为：
1、由于本发明一种服装用电磁波屏蔽纤维的组成成分及重量份比例为：聚丙烯晴纤维20–40，聚酯纤维2–8，聚酰氨纤维5–15，聚烯烃纤维4–6，碳纤维10–30，玻璃纤维10–20，聚丙烯树脂10–20，其中，不仅仅通过镀有金属结晶膜的聚丙烯晴纤维起到反射电磁波的效果，还通过自身具有电磁波反射作用的聚酯纤维、聚酰氨纤维、聚烯烃纤维、碳纤维与玻璃纤维加强了本设计的屏蔽性，此外，玻璃纤维还能增强本设计的机械强度。因此本发明不仅屏蔽效果较强，而且机械强度较高。
2、由于本发明一种服装用电磁波屏蔽纤维还包括电磁波吸收粉，该电磁波吸收粉与聚丙烯树脂的重量比为1:5–1:4，电磁波吸收粉的组成成分及重量份比例为：铁氧体粉末40–50，二氧化硅粉末10–20，铁粉30–50，该设计通过在纤维中混有可吸收电磁波的铁氧体粉末、二氧化硅粉末与铁粉，具有极强的吸收效果，进一步增强了本设计的屏蔽效果。因此本发明的屏蔽效果较强。
具体实施方式
以下结合具体实施方式对本发明作进一步详细的说明。
一种服装用电磁波屏蔽纤维，包括聚丙烯晴纤维，所述聚丙烯晴纤维的表面包裹有铜结晶层，所述电磁波屏蔽纤维的组成成分及重量份比例为：聚丙烯晴纤维20–40，聚酯纤维2–8，聚酰氨纤维5–15，聚烯烃纤维4–6，碳纤维10–30，玻璃纤维10–20，聚丙烯树脂10–20。
所述电磁波屏蔽纤维的组成成分及重量份比例为：聚丙烯晴纤维30，聚酯纤维5，聚酰氨纤维10，聚烯烃纤维5，碳纤维20，玻璃纤维15，聚丙烯树脂15。
所述电磁波屏蔽纤维还包括电磁波吸收粉，该电磁波吸收粉与聚丙烯树脂的重量比为1:5–1:4。
所述电磁波吸收粉的组成成分及重量份比例为：铁氧体粉末40–50，二氧化硅粉末10–20，铁粉30–50。
所述电磁波吸收粉的组成成分及重量份比例为：铁氧体粉末45，二氧化硅粉末15，铁粉40。
实施例1：
一种服装用电磁波屏蔽纤维，包括聚丙烯晴纤维，所述聚丙烯晴纤维的表面包裹有铜结晶层，所述电磁波屏蔽纤维的组成成分及重量份比例为：聚丙烯晴纤维20，聚酯纤维8，聚酰氨纤维15，聚烯烃纤维6，碳纤维10，玻璃纤维20，聚丙烯树脂10。
所述电磁波屏蔽纤维还包括电磁波吸收粉，该电磁波吸收粉与聚丙烯树脂的重量比为1:5，电磁波吸收粉的组成成分及重量份比例为：铁氧体粉末50，二氧化硅粉末10，铁粉30。
实施例2：
一种服装用电磁波屏蔽纤维，包括聚丙烯晴纤维，所述聚丙烯晴纤维的表面包裹有铜结晶层，所述电磁波屏蔽纤维的组成成分及重量份比例为：聚丙烯晴纤维40，聚酯纤维2，聚酰氨纤维5，聚烯烃纤维4，碳纤维30，玻璃纤维10，聚丙烯树脂20。
所述电磁波屏蔽纤维还包括电磁波吸收粉，该电磁波吸收粉与聚丙烯树脂的重量比为1:4，电磁波吸收粉的组成成分及重量份比例为：铁氧体粉末45，二氧化硅粉末15，铁粉40。
实施例3：
一种服装用电磁波屏蔽纤维，包括聚丙烯晴纤维，所述聚丙烯晴纤维的表面包裹有铜结晶层，所述电磁波屏蔽纤维的组成成分及重量份比例为：聚丙烯晴纤维30，聚酯纤维5，聚酰氨纤维10，聚烯烃纤维5，碳纤维20，玻璃纤维15，聚丙烯树脂15。
所述电磁波屏蔽纤维还包括电磁波吸收粉，该电磁波吸收粉与聚丙烯树脂的重量比为1:5，电磁波吸收粉的组成成分及重量份比例为：铁氧体粉末45，二氧化硅粉末15，铁粉40。
实施例4：
一种服装用电磁波屏蔽纤维，包括聚丙烯晴纤维，所述聚丙烯晴纤维的表面包裹有铜结晶层，所述电磁波屏蔽纤维的组成成分及重量份比例为：聚丙烯晴纤维25，聚酯纤维4，聚酰氨纤维10，聚烯烃纤维6，碳纤维25，玻璃纤维12，聚丙烯树脂18。
所述电磁波屏蔽纤维还包括电磁波吸收粉，该电磁波吸收粉与聚丙烯树脂的重量比为1:4，电磁波吸收粉的组成成分及重量份比例为：铁氧体粉末40，二氧化硅粉末20，铁粉50。
实施例5：
一种服装用电磁波屏蔽纤维，包括聚丙烯晴纤维，所述聚丙烯晴纤维的表面包裹有铜结晶层，所述电磁波屏蔽纤维的组成成分及重量份比例为：聚丙烯晴纤维36，聚酯纤维7，聚酰氨纤维8，聚烯烃纤维5，碳纤维24，玻璃纤维15，聚丙烯树脂20。
所述电磁波屏蔽纤维还包括电磁波吸收粉，该电磁波吸收粉与聚丙烯树脂的重量比为1:4，电磁波吸收粉的组成成分及重量份比例为：铁氧体粉末45，二氧化硅粉末18，铁粉42。
Claims (5)
1.一种服装用电磁波屏蔽纤维，包括聚丙烯晴纤维，所述聚丙烯晴纤维的表面包裹有铜结晶层，其特征在于：所述电磁波屏蔽纤维的组成成分及重量份比例为：聚丙烯晴纤维20–40，聚酯纤维2–8，聚酰氨纤维5–15，聚烯烃纤维4–6，碳纤维10–30，玻璃纤维10–20，聚丙烯树脂10–20。
2.根据权利要求1所述的一种服装用电磁波屏蔽纤维，其特征在于：所述电磁波屏蔽纤维的组成成分及重量份比例为：聚丙烯晴纤维30，聚酯纤维5，聚酰氨纤维10，聚烯烃纤维5，碳纤维20，玻璃纤维15，聚丙烯树脂15。
3.根据权利要求1或2所述的一种服装用电磁波屏蔽纤维，其特征在于：所述电磁波屏蔽纤维还包括电磁波吸收粉，该电磁波吸收粉与聚丙烯树脂的重量比为1:5–1:4。
4.根据权利要求3所述的一种服装用电磁波屏蔽纤维，其特征在于：所述电磁波吸收粉的组成成分及重量份比例为：铁氧体粉末40–50，二氧化硅粉末10–20，铁粉30–50。
5.根据权利要求4所述的一种服装用电磁波屏蔽纤维，其特征在于：所述电磁波吸收粉的组成成分及重量份比例为：铁氧体粉末45，二氧化硅粉末15，铁粉40。