CN102152566B - Plastic-plastic composite structure - Google Patents
Plastic-plastic composite structure Download PDFInfo
- Publication number
- CN102152566B CN102152566B CN2010106125002A CN201010612500A CN102152566B CN 102152566 B CN102152566 B CN 102152566B CN 2010106125002 A CN2010106125002 A CN 2010106125002A CN 201010612500 A CN201010612500 A CN 201010612500A CN 102152566 B CN102152566 B CN 102152566B
- Authority
- CN
- China
- Prior art keywords
- layer
- polypropylene film
- ethylene
- bidirectional stretching
- stretching polypropylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a composite film which is prepared by carrying out plastic-plastic thermal compounding on a plurality of layers of thin films. The composite structure is composed of an upper biaxially oriented polypropylene film, a middle printing ink film and a lower biaxially oriented polypropylene film, wherein the upper biaxially oriented polypropylene film comprises at least two layers, namely, an upper polypropylene substrate layer and a heat-seal layer arranged at the interior of the upper polypropylene substrate layer, and the heat-seal layer is prepared from a biopolymer or terpolymer or mixture of ethylene, propylene and butylene at an initial heat-seal temperature of less than or equal to 95 DEG C; and the lower biaxially oriented polypropylene film comprises at least two layers, namely, a lower polypropylene substrate layer and a function layer directly contacted with printing ink, and the function layer comprises the following compositions: 1) an ethylene-butylene copolymer; or 2) an ethylene-octylene copolymer; or 3) an MAH (maleic anhydride) grafted modifier of the ethylene-butylene copolymer; or 4) an MAH (maleic anhydride) grafted modifier of the ethylene-octylene copolymer; or 5) any mixture of the compositions 1), 2), 3) and 4); or 6) the mixture of the composition 5) and hydrogenated petroleum resin.
Description
Technical field
The present invention relates to a kind of moulding-plastic composite structure, specifically, relate to a kind of by plural layers through moulding-mould the laminated film that makes of the compound mode of heat.
Background technology
Through moulding-mould the flexible packing material that film that compound mode produces is used as article more, this laminated film carries out multiple film through the mode of having complementary advantages compound, thereby satisfies the demand of packing of product aspect between the plastic sheeting.
The complex technique of moulding-mould of existing film mainly carries out plural layers compound through adhesive.Generally be through online coating method, earlier on a kind of polar treatment surface of film, be coated with glue, through under uniform temperature and pressure condition, to carry out heat compound with another film or the film that is printed on ink lay after the drying tunnel drying.The laminated film that this mode obtains often contains a certain amount of residual solvent, and packed article or consumer are had a negative impact.
Summary of the invention
The present invention relates to a kind of novel moulding-plastic composite structure; The superficial layer of the thin film in this structure---bidirectional stretching polypropylene film can directly combine with ink lay; And through printing ink and other thin film---heat sealable bidirectional stretching polypropylene film, directly hot pressing is compound and need not to use adhesive under the certain temperature and pressure condition.
Of the present invention moulding-plastic composite structure has thoroughly been removed and has been used in the conventional composite membrane structure or negative effect that residual solvent causes, has simplified combination process.It not only has energy-conservation effect, and is particularly conducive to the health and the environmental protection of flexible packaging food.
Moulding among the present invention-plastic composite structure is to realize through the compound mode of hot pressing.This composite construction is made up of a upper strata bidirectional stretching polypropylene film, middle ink lay and lower floor's bidirectional stretching polypropylene film; Its upper strata bidirectional stretching polypropylene film is at least double-layer structure; It comprises base layer on the polypropylene and is positioned at its inboard heat sealable layer, and this heat sealable layer is less than or equal to 95 ℃ ethene, propylene, butylene two yuan or terpolymer and composition thereof for initial heat-sealing temperature.Lower floor's bidirectional stretching polypropylene film is at least double-layer structure, and it comprises polypropylene lower substrate layer and the functional layer that directly contacts with printing ink, and the composition of this functional layer is:
1). ethylene-butene copolymer
Or 2). ethylene-octene copolymer
Or 3). the modified by maleic acid anhydride graft thing of ethylene-butene copolymer
Or 4). the modified by maleic acid anhydride graft thing of ethylene-octene copolymer
Or 5) any mixture .1), 2), 3), 4)
Or 6) .5) with the blend again of hydrogenated petroleum resin
Description of drawings
Accompanying drawing is the sketch map of moulding among the present invention-plastic composite structure.Below in conjunction with accompanying drawing content of the present invention is explained further details.
Label 1 is the upper strata bidirectional stretching polypropylene film in the accompanying drawing, and label 3 is lower floor's bidirectional stretching polypropylene film, and label 2 is an ink lay.Upper strata bidirectional stretching polypropylene film 1 comprises base layer a and heat sealable layer b; Lower floor's bidirectional stretching polypropylene film 3 comprises lower substrate layer c and functional layer d.Heat sealable layer b be initial heat-sealing temperature less than, equal 95 ℃ ethene, propylene, two yuan or terpolymer or their mixture of butylene.The lower surface of this heat sealable layer b can be through the surface polarity processing.The composition of functional layer d in lower floor's bidirectional stretching polypropylene film is:
1). ethylene-butene copolymer
Or 2). ethylene-octene copolymer
Or 3). the modified by maleic acid anhydride graft thing of ethylene-butene copolymer
Or 4). the modified by maleic acid anhydride graft thing of ethylene-octene copolymer
Or 5) any mixture .1), 2), 3), 4)
Or 6) .5) with the blend again of hydrogenated petroleum resin.
The inner surface of this functional layer d also can be handled through polar.
The specific embodiment:
Embodiment 1:
A kind of moulding-plastic composite structure; This structure comprises a upper strata bidirectional stretching polypropylene film (1), middle ink lay (2) and lower floor's bidirectional stretching polypropylene film (3); Described upper strata bidirectional stretching polypropylene film (1) is a double-layer structure; It comprises base layer on the polypropylene (a) and is positioned at its inboard heat sealable layer (b); This heat sealable layer (b) is initial heat-sealing temperature less than the terpolymer of 95 ℃ ethene, propylene, butylene; Lower floor's bidirectional stretching polypropylene film (3) is a double-layer structure, and it comprises polypropylene lower substrate layer (c) and the functional layer (d) that directly contacts with printing ink, and the composition of this functional layer (d) is an ethylene-butene copolymer; Upper strata bidirectional stretching polypropylene film (1) and lower floor's bidirectional stretching polypropylene film (3) are combined with each other through the mode of heat seal, and described heat sealable layer (b) and/or functional layer (d) are handled through polar.
It moulds-and plastic composite structure processes in the following manner: (three-layer co-extrudedly go out the biaxial tension production line by means of the flat embrane method bidirectional stretching polypropylene film film line of German Bruckner (BRUECKNER); 4.2 meters of maximum rolling width; 280 meters/minute of maximum linear velocities) make the upper strata bidirectional stretching polypropylene film 1 that comprises base layer a and heat sealable layer b respectively, and the lower floor's bidirectional stretching polypropylene film 3 that comprises lower substrate layer c and functional layer d.On lower floor's bidirectional stretching polypropylene film 3, can carry out ink printing, ink lay 2 is adhered to above that.Again upper strata bidirectional stretching polypropylene film 1 and lower floor's bidirectional stretching polypropylene film 3 usefulness Hangzhou Wu Tai FM1050 types are not had the glue laminating machine in 5~15MPa pressure and 95~130 ℃ of following heat seals, can obtain of the present invention moulding-plastic composite structure.
Embodiment 2:
A kind of moulding-plastic composite structure; This structure comprises a upper strata bidirectional stretching polypropylene film (1), middle ink lay (2) and lower floor's bidirectional stretching polypropylene film (3); Described upper strata bidirectional stretching polypropylene film (1) is a double-layer structure; It comprises base layer on the polypropylene (a) and is positioned at its inboard heat sealable layer (b); This heat sealable layer (b) be initial heat-sealing temperature less than 95 ℃ ethene, two membered copolymers of propylene, lower floor's bidirectional stretching polypropylene film (3) is a double-layer structure, it comprises polypropylene lower substrate layer (c) and the direct functional layer (d) that contacts with printing ink; The composition of this functional layer (d) is the modified by maleic acid anhydride graft thing of ethylene-octene copolymer, and upper strata bidirectional stretching polypropylene film (1) and lower floor's bidirectional stretching polypropylene film (3) are combined with each other through the mode of heat seal.
Embodiment 3:
A kind of moulding-plastic composite structure; This structure comprises a upper strata bidirectional stretching polypropylene film (1), middle ink lay (2) and lower floor's bidirectional stretching polypropylene film (3); Described upper strata bidirectional stretching polypropylene film (1) is a double-layer structure; It comprises base layer on the polypropylene (a) and is positioned at its inboard heat sealable layer (b); This heat sealable layer (b) is initial heat-sealing temperature less than 95 ℃ ethene, propylene, two membered copolymers of butylene and the mixture of terpolymer; Lower floor's bidirectional stretching polypropylene film (3) is a double-layer structure; It comprises polypropylene lower substrate layer (c) and the functional layer (d) that directly contacts with printing ink, and the composition of this functional layer (d) is: the modified by maleic acid anhydride graft thing of ethylene-butene copolymer and ethylene-butene copolymer and the blend again of hydrogenated petroleum resin, upper strata bidirectional stretching polypropylene film (1) and lower floor's bidirectional stretching polypropylene film (3) are combined with each other through the mode of heat seal.Heat sealable layer (b) and functional layer (d) are all passed through polar and are handled.
Claims (2)
1. mould-plastic composite structure for one kind; This structure comprises a upper strata bidirectional stretching polypropylene film (1), middle ink lay (2) and lower floor's bidirectional stretching polypropylene film (3); It is characterized in that: described upper strata bidirectional stretching polypropylene film (1) is at least double-layer structure; It comprises base layer on the polypropylene (a) and is positioned at its inboard heat sealable layer (b); This heat sealable layer (b) is less than or equal to two yuan or the mixture of terpolymer of 95 ℃ ethene, propylene, butylene two yuan or terpolymer or ethene, propylene, butylene for initial heat-sealing temperature; Lower floor's bidirectional stretching polypropylene film (3) is at least double-layer structure, and it comprises polypropylene lower substrate layer (c) and the functional layer (d) that directly contacts with printing ink, and the composition of this functional layer (d) is:
1). ethylene-butene copolymer
Or 2). ethylene-octene copolymer
Or 3). the modified by maleic acid anhydride graft thing of ethylene-butene copolymer
Or 4). the modified by maleic acid anhydride graft thing of ethylene-octene copolymer
Or 5) any mixture .1), 2), 3), 4)
Or 6) .5) with the blend again of hydrogenated petroleum resin
Upper strata bidirectional stretching polypropylene film (1) and lower floor's bidirectional stretching polypropylene film (3) are combined with each other through the mode of heat seal.
2. as claimed in claim 1 moulding-plastic composite structure is characterized in that: described heat sealable layer (b) and/or functional layer (d) are handled through polar.