CN102120635A - Preparation method of water treatment coagulant - Google Patents
Preparation method of water treatment coagulant Download PDFInfo
- Publication number
- CN102120635A CN102120635A CN 201110020432 CN201110020432A CN102120635A CN 102120635 A CN102120635 A CN 102120635A CN 201110020432 CN201110020432 CN 201110020432 CN 201110020432 A CN201110020432 A CN 201110020432A CN 102120635 A CN102120635 A CN 102120635A
- Authority
- CN
- China
- Prior art keywords
- coagulant
- water treatment
- rare earth
- sodium hydroxide
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a preparation method of a water treatment coagulant, belonging to the field of water treatment. The preparation method comprises the following steps: mixing dried Baotou rare earth concentrate and sodium hydroxide solution in a proportion of (7-9g): (100-150mL), and carrying out boiling reaction for 3-5 hours at the temperature of 100 DEG C to prepare mother liquid, wherein the mole concentration of the sodium hydroxide solution is 3-5 mol/L, solid sodium hydroxide in one liter of solution is 120g-200g; and heating and curing the filtrated mother liquid for 1 hour-3 hours in a constant-temperature water bath at the temperature of 60-80 DEG C to obtain bright yellow transparent liquid. When the preparation method is used for water treatment, the coagulation effect of the coagulant prepared by the method is obviously superior to that of the conventional coagulant; compared with the traditional commercial coagulant, the prepared rare earth coagulant has the characteristics of less dosage, rapid flocculation speed, compact flocculation body, good sedimentation performance, and the like and ensures better treated water quality; and by using the coagulant provided by the method, sludge treatment expenditure can be saved.in the process of water treatment, which. The invention is another development of the application of rear earth in the field of water treatment.
Description
Technical field
The present invention relates to a kind of preparation method of water treatment coagulant, belong to water treatment field.
Background technology
The coagulating agent that water treatment is at present used is more, and the document of relevant coagulating agent is also a lot.Because rare earth has been obtained original achievement in the application of field of environment protection in recent years.Disclose in 2009101427751 as China and a kind ofly to be mixed with a kind of rare earth coagulant for water treatment according to corresponding proportion with rare earth ore concentrate and hydrochloric acid.But, in use has corrodibility because the coagulating agent mother liquor of its preparation is a strongly-acid.
Summary of the invention
The object of the present invention is to provide the preparation method of the water treatment coagulant that a kind of coagulation effect is good, drug dosage is few, settling velocity is fast, sludge volume is few.
Technical solution:
Preparation method of the present invention is as follows:
(1) Baotou rare earth ore concentrate is eluriated, and dries in the baking oven;
(2) Baotou rare earth ore concentrate after will drying mixes with sodium hydroxide solution, Baotou rare earth ore concentrate: sodium hydroxide solution=7-9g: 100-150mL, the volumetric molar concentration of sodium hydroxide solution: 3～5mol/L, containing solid sodium hydroxide in every liter of solution is 120g-200g, in temperature is 100 ℃ of following boiling reaction 3h-5h, makes mother liquor;
(3) reacted mother liquor leaches, filtrate for later use, filter residue recycling;
(4) mother liquor that leaches is put into thermostat water bath, and gained glassy yellow transparent liquid is prepared alkaline process rare earth coagulant after adding thermomaturation 1h-3h under 60 ℃ of-80 ℃ of temperature.
The present invention produces after mainly utilizing Baotou rare earth ore concentrate and alkali (NaOH) hybrid reaction.The prepared coagulating agent of the present invention is used for the processing of water, and coagulation effect obviously is better than conventional coagulating agent.Compare with the coagulating agent that tradition is commercially available, prepared rare earth coagulant has that consumption is few, flocculation rate is fast, flco is closely knit, settling property is good, the more excellent characteristics of effluent quality, especially in the removal of turbidity, significantly better than other coagulating agent; Also fine to subsequent disposal on mud forms, in water treatment technological process, can save the sludge treatment expense, be rare earth expanding again in water treatment field.
Embodiment
Embodiment 1:
Get the Baotou rare earth ore concentrate after 7 grams are dried, put it in the flask, and adding concentration is the sodium hydroxide solution 100ml (promptly containing solid sodium hydroxide is 12g) of 3mol/L; Make mother liquor at 100 ℃ of heating 4h that seethe with excitement down; Mother liquor vacuum suction filter after having reacted, filtrate concentrates the filter residue recycling in order to follow-up; Filtrate is put into thermostat water bath, add thermomaturation 2h under 70 ℃ of temperature, made glassy yellow transparent liquid is the gained coagulating agent.
With the Huanghe water is water quality treatment, post precipitation, and recording the supernatant liquor turbidity is 106NTU, gets its 1000ml and drops into prepared coagulating agent 4ml, carries out coagulation experiment, the turbidity that post precipitation records water outlet is 0.68NTU, goes turbid rate to reach 99.36%.
Embodiment 2:
Get the rare earth after 8 grams are dried, put it into the sodium hydroxide solution 100ml (promptly containing sodium hydroxide is 20g) that slowly adds 5mol/L in the flask; Make mother liquor at 100 ℃ of heating 4h that seethe with excitement down; Mother liquor vacuum suction filter after having reacted, filtrate concentrates in order to follow-up.The calculating dissolution rate of weighing after the filter residue oven dry, and reclaim in order to utilizing again.Filtrate is put into thermostat water bath, adds thermomaturation 3h under 70 ℃ of temperature.Made glassy yellow transparent liquid is the gained coagulating agent.
With the Huanghe water is water quality treatment, post precipitation, and recording the supernatant liquor turbidity is 102NTU, gets its 1000ml and drops into prepared coagulating agent 4ml, carries out coagulation experiment, the turbidity that post precipitation records water outlet is 0.80NTU, goes turbid rate to reach 99.21%.
Claims (1)
1. the preparation method of water treatment coagulant is characterized in that, comprises the steps:
(1) Baotou rare earth ore concentrate is eluriated, and dries in the baking oven;
(2) rare earth ore concentrate after will drying mixes rare earth ore concentrate with sodium hydroxide solution: sodium hydroxide solution=7-9g: 100-150mL, and the volumetric molar concentration of sodium hydroxide solution: 3～5mol/L, temperature: 100 ℃ of following boiling reaction 3h-5h, make mother liquor;
(3) reacted mother liquor leaches, filtrate for later use, filter residue recycling;
(4) mother liquor that leaches is put into thermostat water bath, gets the glassy yellow transparent liquid and be prepared alkaline process rare earth coagulant after adding thermomaturation 1h-3h under 60 ℃ of-80 ℃ of temperature.