CN102107509A - Method for manufacturing decorative strips - Google Patents
Method for manufacturing decorative strips Download PDFInfo
- Publication number
- CN102107509A CN102107509A CN2009102152756A CN200910215275A CN102107509A CN 102107509 A CN102107509 A CN 102107509A CN 2009102152756 A CN2009102152756 A CN 2009102152756A CN 200910215275 A CN200910215275 A CN 200910215275A CN 102107509 A CN102107509 A CN 102107509A
- Authority
- CN
- China
- Prior art keywords
- ornamental strip
- production method
- pvc
- mixture
- strip production
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The embodiment of the invention provides a method for manufacturing decorative strips. Environment-friendly decorative strips which are made from novel materials and are capable of replacing wood decorative strips, are manufactured by utilizing recovered PVC (polyvinyl chloride) materials, specifically treating the PVC materials, and using an extrusion forming method. The demand on the manufacturing technique is lowered and the wood waste is avoided by using the recovered PVC wastes as raw materials. The method for manufacturing decorative strips has the advantage of environmental protection.
Description
Technical field
The present invention relates to the decoration technical field, particularly a kind of furniture production method of ornamental strip.
Background technology
When making, furniture, usually can adopt ornamental strip that furniture is decorated in order to beautify the outward appearance of furniture.The tradition wood furniture generally all is to adopt the producing wood identical with furniture, this wooden ornamental strip adds and not only is difficult for processing man-hour, therefore and the waste to timber is more serious in the process, is necessary to provide a kind of ornamental strip production method of environmental protection of efficent use of resources.
Summary of the invention
For overcoming timber waste important disadvantages in the existing wooden ornamental strip manufacture process, provide a kind of ornamental strip production method of environmental protection that can efficent use of resources.
For solving the problems of the technologies described above, the purpose of the embodiment of the invention is achieved through the following technical solutions: a kind of ornamental strip production method is provided, the polyvinyl chloride that comprises the steps: to reclaim (Polyvinylchloride, PVC) material is ground into graininess, and washes, dries; PVC particle after will washing, drying is poured heating in the mixer into, is stirred; Add curing agent in mixer, be stirred to temperature and reach 90 degree, moisture is mixed dried; Mixture in the mixer is carried out the secondary extruding pelletization and carries out fragmentation; Pour the mixture after the fragmentation into homogenizer and carry out agitating heating; Mixture after the heating is poured into and carried out basic moulding in the moulding extruder, obtain ornamental strip.
Compared with prior art, adopt the method for the embodiment of the invention to produce the PVC material that ornamental strip is the utilization recovery, through specially treated, the ornamental strip that constitutes by new material of the environmental protection that utilizes the method for extrusion modling to produce to replace wooden ornamental strip, only reduced requirement to manufacture craft, and, avoided the waste of timber because raw material have adopted the PVC waste material of recycling, have environment-friendly advantage.
Description of drawings
Fig. 1 is the flow chart of ornamental strip production method of the present invention.
The specific embodiment
The pvc material that the production method utilization of the ornamental strip that the embodiment of the invention provides is reclaimed, through specially treated, the ornamental strip that constitutes by new material of the environmental protection that utilizes the method for extrusion modling to produce can to replace wooden ornamental strip.
Below in conjunction with accompanying drawing the embodiment of the invention is elaborated.
The production method of embodiment of the invention ornamental strip comprises the steps:
S01 is ground into graininess with the PVC material that reclaims, and washes, dries.This PVC material can be the waste pipe material.
S02 pours the graininess PVC material that S01 obtains heating in the mixer into, stirs.
S03 adds curing agent in mixer, be stirred to temperature and reach 90 degree, and moisture is mixed dried.This curing agent comprise plasticizer, stearic acid, compound lead stabilizer, calcium powder and hard PVC resin, each material is compared shared ratio with the PVC material be 8% plasticizer, 5% stearic acid, 3% compound lead stabilizer, 5%? powder and 5% hard PVC resin.
S04, the mixture that step S03 is obtained carries out the secondary extruding pelletization, carries out fragmentation then.
S05 pours the mixture after the fragmentation into homogenizer and carries out agitating heating about 7 minutes.
S06 carries out basic moulding with pouring into thing very much of heating in the moulding extruder, obtain the ornamental strip of environmental protection.
Compared with prior art, the ornamental strip that the method for the employing embodiment of the invention obtains has not only reduced the requirement to manufacture craft, and because raw material have adopted the PVC waste material of recycling, has avoided the waste of timber, has environment-friendly advantage.In addition, the ornamental strip that the method for utilizing the embodiment of the invention to provide obtains is plastic products, and it has curved tearing open property, and because added curing agent in the production process, have the strong characteristics of paint absorption affinity, arbitrarily moulding aborning improves designer's development space greatly.And this ornamental strip avirulence, technology is simple, has reduced cost, in use need not the operation of polishing, and therefore can not produce dust, very environmental protection.
The embodiment of the invention is described in detail the manufacture method of the ornamental strip that provided, used specific case herein principle of the present invention and embodiment are set forth, the explanation of above embodiment just is used for helping to understand method of the present invention and core concept thereof; Simultaneously, for one of ordinary skill in the art, according to thought of the present invention, the part that all can change in specific embodiments and applications, in sum, this description should not be construed as limitation of the present invention.
Claims (5)
1. an ornamental strip production method is characterized in that, comprises the steps:
The polyvinylchloride material that reclaims is ground into graininess, and washes, dry;
PVC particle after will washing, drying is poured heating in the mixer into, is stirred;
Add curing agent in mixer, be stirred to temperature and reach 90 degree, moisture is mixed dried;
Mixture in the mixer is carried out the secondary extruding pelletization and carries out fragmentation;
Pour the mixture after the fragmentation into homogenizer and carry out agitating heating;
Mixture after the heating is poured into and carried out basic moulding in the moulding extruder, obtain ornamental strip.
2. ornamental strip production method as claimed in claim 1 is characterized in that, described recovery PVC material is the waste pipe material.
3. ornamental strip production method as claimed in claim 1 is characterized in that, described curing agent comprise plasticizer, stearic acid, compound lead stabilizer,? powder and hard PVC resin.
4. ornamental strip production method as claimed in claim 1, it is characterized in that compare shared ratio with the PVC material be 8% plasticizer, 5% stearic acid, 3% compound lead stabilizer, 5% calcium powder and 5% hard PVC resin to each material in the described curing agent.
5. ornamental strip production method as claimed in claim 1 is characterized in that, described to pour the mixture after the fragmentation into time that homogenizer carries out agitating heating be about 7 minutes.