CN102106631A - Preparation method of for -sided embossed leaf metal souvenir badge - Google Patents
Preparation method of for -sided embossed leaf metal souvenir badge Download PDFInfo
- Publication number
- CN102106631A CN102106631A CN2009102009527A CN200910200952A CN102106631A CN 102106631 A CN102106631 A CN 102106631A CN 2009102009527 A CN2009102009527 A CN 2009102009527A CN 200910200952 A CN200910200952 A CN 200910200952A CN 102106631 A CN102106631 A CN 102106631A
- Authority
- CN
- China
- Prior art keywords
- preparation
- base cake
- blanking
- souvenir badge
- sheet metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a preparation method for a double-sided embossed leaf metal souvenir badge. The preparation method is characterized in that the preparation method of a thin blank cake adopts the production process of first blank cake blanking, blank cake performing and second blank cake blanking, the produced thin blank cake is dish-shaped with a thicker middle and a thinner edge, in the method, certain metal accumulation amount is preformed on the thin blank cake, thereby facilitating the stamping of double-sided embossed thin products. A thin printing mold adopts a female screw mold with different patterns, the surface of the mold has such surface processing effects of a mirror surface, sand blasting, and the like, and the layout and height of the patterns of the mold are limited appropriately. A novel double-sided embossed leaf metal souvenir badge is produced through the closed stamping method.
Description
Technical field:
The present invention relates to the technical field of metal coin (chapter), specifically a kind of preparation method of two-sided burr relief type sheet metal souvenir badge.
Background technology:
Sheet metal souvenir badge in the market (thickness of this series products thinnest part≤0.50mm) mostly is the sheet product of concave-convex type, and promptly product is just, the figure line at the back side is identical, and wherein one but positive line, and another side is an internal or female screw.Its preparation method be just, the figure line of back of the body mould makes equally, one of them mould is made positive line, another mould is made identical internal or female screw.It is after employing evenly is rolled down to certain thickness to silver that the base cake is made, and a blank-forming after the annealed cleaning, by the mode of impression, is finished the making of product again.This kind preparation method is quite ripe, sheet metal souvenir badge product on the market also is to adopt this method to make mostly, but it only limits to make the sheet product of concave-convex type, and just can not make, sheet metal product that the back side all has different burrs.Because if take above-mentioned preparation method, so can be owing to the thickness of base cake is too thin, the amount of flow of metal is abundant inadequately during the product impression, and product is difficult for being pressed foot fully.To press sufficient product fully in order wanting in addition, to strengthen force of impression, the service life that also can reduce mould if too pursue.Therefore above-mentioned preparation method is not suitable for making the two-sided sheet metal souvenir badge product that all has different burrs.
Through adopting keyword domestic and international patent database is retrieved, and the relevant patent that detects analyzed, the manufacturing technology (Chinese patent CN200610025289, U.S. Pat 2002154290, European patent EP 1718182 etc.) that relates to relief type coin or commemorative coin is all arranged in the existing as can be seen disclosed domestic and international patent, but the just manufacture craft of commemorative coin relief pattern, image that major part relates to, these patented technologies are because of the preparation method's that do not relate to ultra-thin type double face burr embossment commemorative coin (chapter) technical essential, and are little with this problem relation.So this problem has certain novelty in the claim at home and abroad.
Summary of the invention:
The purpose of this invention is to provide a kind of just, the back side has the preparation method of the slim souvenir badge of different burr relief patterns, adopt this method can produce a kind of novel just, the back side has the slim souvenir badge of different burr relief patterns.
To achieve these goals, technical scheme of the present invention is: a kind of preparation method of two-sided burr relief type sheet metal souvenir badge, it is characterized in that: described preparation method comprises the steps: a, to being rolling to certain thickness metal strip, carries out base cake blanking; B, the base cake is annealed; The optical mode that c, processing and fabricating preform are used; D, the base cake is carried out preform impression; E, the base cake is carried out the secondary blanking; F, the base cake behind the secondary blanking is annealed; G, the base cake behind the secondary blanking is cleaned light decorations; H, required printing die and the mould circle of making; I, employing coinage special equipment carry out multi-impression and are shaped.
The present invention is by adopting the thin slice base cake preparation method of blanking of base cake → base cake preform → base cake secondary blanking, and suitably control the figure line layout and the figure line height of mould, in conjunction with the production technology that adopts closed impression, be made into a kind of brand-new just, the back side has the ultrathin souvenir badge of different burr relief patterns.That such souvenir badge has is slim, burr, difficult imitated characteristics.At first this series products is extremely thin, and its thickness only is about 1/4 of same specification product; Secondly it not only just, the back side has different burr embossing patterns, but also have certain figure line height; This series products is also difficult imitated in addition, adopts conventional imprint process, can't press sufficient product at all.As seen, this kind preparation method has broken through the manufacture craft of traditional thin slice souvenir badge, has certain innovation.
Description of drawings:
Fig. 1 for the present invention to the base cake generalized section behind blanking
Fig. 2 is that the present invention is to base cake preform process schematic diagram
Fig. 3 is the base cake generalized section of the present invention after to preform
Fig. 4 is the base cake generalized section of the present invention after to the secondary blanking
Fig. 5 is a process chart of the present invention
The specific embodiment:
Below in conjunction with accompanying drawing the present invention is further described.
Thin slice base cake preparation method involved in the present invention is to adopt the production technology of blanking of base cake → base cake preform → base cake secondary blanking, its made thin slice base cake (Fig. 4) is that mid portion is thicker, the dish-shaped shape base cake that the marginal portion is thin, it is different from the thin slice base cake preparation method of an existing blanking and the thin slice base cake of its made uniform thickness, this kind method is made the preform mould of concave surface butterfly shape by adopting the surface, base cake behind blanking is carried out the preform impression, because metal can produce plastic deformation in the moulding process, the metal of base cake limit portion flows to the centre and fills, so just formed certain metal accumulation amount, helped the impression of two-sided burr sheet product in the centre of thin slice base cake.
Thin slice printing die involved in the present invention is the internal or female screw mould that adopts different figure lines, the surface grinding effect of mould is the same with traditional commemorative coin (chapter) mould, the treatment effect of minute surface is adopted in the baseplane, surface pattern adopts the treatment effect of sandblast, the main figure line of mould is placed in the middle, can there be some simple two-dimensional figure lines in limit portion, the figure line height in centre is with reference to the figure line height of same specification mould, figure line height by near part is about 1/2 of a central part bitmap line height, and it is different from existing thin slice printing die and adopts identical negative and positive line mould.
By the produced product of the present invention is the sheet metal souvenir badge of two-sided burr relief type, its be different from existing just, the back side all is the thin slice souvenir badge of identical asperities.
A kind of preparation method of two-sided burr relief type sheet metal souvenir badge is characterized in that: described preparation method comprises the steps: a, to being rolling to certain thickness metal strip, carries out base cake 1 blanking; B, base cake 1 is annealed; The optical mode 3 that c, processing and fabricating preform are used; D, base cake 1 is carried out preform impression; E, base cake 1 is carried out the secondary blanking; F, the base cake behind the secondary blanking is annealed; G, the base cake behind the secondary blanking is cleaned light decorations; H, required printing die and the mould circle of making; I, employing coinage special equipment carry out at least 2 impressions and are shaped.
In a step, adopt milling train that the thickness of metal strip is rolled to 0.70mm～0.90mm, adopt punch press to carry out base cake 1 blanking, base cake 1 blanking diameter amplifies 20%～30% according to the actual diameter of product;
In the b step, adopt chamber type electric resistance furnace that the base cake 1 behind blanking is carried out annealing softening and handle.Annealing temperature is 600 ℃～630 ℃, and annealing time is 10min～15min;
In the c step, the optical mode 3 that the processing and fabricating preform is used, concave surface butterfly shape (Fig. 2) is made on the surface of one of them preform optical mode, the radian of butterfly is 0.30mm-0.50mm, and carve locating slot 2 on the surface, the diameter of locating slot 2 is than product reduced 0.08mm～0.10mm, the width of locating slot 2 is 0.30mm～0.50mm, the height of locating slot 2 is 0.05mm～0.20mm, planar base surface is made on the surface of another one preform optical mode, and the diameter of preform optical mode 3 is identical with base cake 1 diameter behind blanking;
In the d step, adopt hydraulic press that the base cake 1 behind blanking is carried out the preform impression, impression tonnage is 30T～60T, and impressing number of times is 1～2 time;
In the e step, adopt the base cake after punch press impresses preform,, carry out the secondary blanking along locating slot 2;
In the f step, the base cake after adopting chamber type electric resistance furnace to the secondary blanking carries out annealing softening to be handled.Annealing temperature is 600 ℃～630 ℃, and annealing time is 10min～15min;
In the g step, base cake after adopting vertical light polishing machine to the secondary blanking cleans the light decorations, unified slight curving towards the one side of planar base surface before cleaning the base cake, cleansing medium is the stainless shot that φ 2mm and φ 4mm mix, cleaning fluid is the tumbling powder, the mixed solution of washing agent and deionized water, wherein the tumbling powder is the commercially available prod, produce with one-tenth Science and Technology Ltd. by Nanjing, model is NS-100, the ratio of its addition and deionized water is 1: 40～1: 60, and washing agent is a liquid detergent, and the ratio of its addition and deionized water is 1: 50～1: 70, the additional proportion of tumbling powder and washing agent is 1: 0.5～1: 1, and scavenging period is 5min～10min;
In the h step, processing and fabricating has the internal or female screw mould of different figure lines, and the baseplane of mould is made into minute surface, just, the figure line layout of back of the body mould is placed in the middle, just, the back of the body mould figure line height≤0.50mm, the mould circle is made the light centre circle, the clearance control between mould circle and the mould is at 0.08mm～0.10mm; The surface grinding effect of mould is the same with traditional commemorative coin (chapter) mould, the treatment effect of mould, and surface pattern adopts the treatment effect of sandblast, and the treatment effect that makes minute surface and sandblast about ground tackle belongs to prior art, is not described specifically at this;
In the i step, adopt the coinage special equipment to carry out thin slice souvenir badge finished product impression, the impression tonnage is set in 90T～150T, and the impression number of times is 2～4 times.
Embodiment 1
The preparation process and the step of the ultrathin golden chapter of φ 32mm (single piece of weight of product is 7.776 grams) are as follows:
(1) adopt milling train that the thickness of gold bar sheet is rolled to 0.90mm, adopt punch press to carry out base cake blanking, base cake blanking diameter is 40mm;
(2) adopting chamber type electric resistance furnace that the golden base cake behind blanking is carried out annealing softening handles.Annealing temperature is 610 ℃, and annealing time is 10min;
(3) optical mode used of processing and fabricating preform, concave surface butterfly shape is made on the surface of one of them preform optical mode, the radian of butterfly is 0.40mm, and carve locating slot on the surface, the diameter of locating slot is 39.90mm, and the width of locating slot is 0.50mm, and the height of locating slot is 0.10mm, planar base surface is made on the surface of another one preform optical mode, and the diameter of preform optical mode is 40mm;
(4) adopt hydraulic press that the base cake behind blanking is carried out the preform impression.The impression tonnage is 45T, and the impression number of times is 1 time;
(5) the base cake after the employing punch press impresses preform along locating slot, carries out the secondary blanking, and the base cake diameter behind the blanking is 31.90mm;
(6) the base cake after adopting chamber type electric resistance furnace to the secondary blanking carries out annealing softening and handles.Annealing temperature is 630 ℃, and annealing time is 15min;
(7) the base cake after adopting vertical light polishing machine to the secondary blanking cleans the light decorations, unified slight curving towards the one side of planar base surface before cleaning the base cake, cleansing medium is the stainless shot that φ 2mm and φ 4mm mix, cleaning fluid is the tumbling powder, the mixed solution of washing agent and deionized water, wherein the tumbling powder is the commercially available prod, produce with one-tenth Science and Technology Ltd. by Nanjing, model is NS-100, the ratio of its addition and deionized water is 1: 45, washing agent is a liquid detergent, the ratio of its addition and deionized water is about 1: 60, and the additional proportion of tumbling powder and washing agent is 1: 0.75, and scavenging period is 6min;
(8) required printing die and the mould circle of processing and fabricating, die surface has different internal or female screw figure lines, the surface grinding effect of mould is the same with traditional commemorative coin (chapter) mould, the baseplane of mould is made into the treatment effect of minute surface, surface pattern adopts the treatment effect of sandblast, just, the figure line layout of back of the body mould is placed in the middle, and just, the figure line height of back of the body mould is 0.50mm, the mould circle is made the light centre circle, and the clearance control between mould circle and the mould is at 0.10mm; The treatment effect that makes minute surface and sandblast about ground tackle belongs to prior art, is not described specifically at this;
(9) adopt the coinage special equipment to carry out thin slice souvenir badge finished product impression, the impression tonnage is set in 140T, and the impression number of times is 3 times.
Claims (10)
1. the preparation method of a two-sided burr relief type sheet metal souvenir badge is characterized in that: described preparation method comprises the steps: a, to being rolling to certain thickness metal strip, carries out base cake blanking; B, the base cake is annealed; The optical mode that c, processing and fabricating preform are used; D, the base cake is carried out preform impression; E, the base cake is carried out the secondary blanking; F, the base cake behind the secondary blanking is annealed; G, the base cake behind the secondary blanking is cleaned light decorations; H, required printing die and the mould circle of making; I, employing coinage special equipment carry out multi-impression and are shaped.
2. the preparation method of a kind of two-sided burr relief type sheet metal souvenir badge as claimed in claim 1, it is characterized in that: in a step, adopt milling train that the thickness of metal strip is rolled to 0.70mm～0.90mm, adopt punch press to carry out base cake blanking, base cake blanking diameter amplifies 20%～30% according to the actual diameter of product;
3. the preparation method of a kind of two-sided burr relief type sheet metal souvenir badge as claimed in claim 1 is characterized in that: in the b step, adopt chamber type electric resistance furnace that the base cake behind blanking is carried out annealing softening and handle; Annealing temperature is 600 ℃～630 ℃, and annealing time is 10min～15min.
4. the preparation method of a kind of two-sided burr relief type sheet metal souvenir badge as claimed in claim 1, it is characterized in that: in the c step, the optical mode that the processing and fabricating preform is used, concave surface butterfly shape is made on the surface of one of them preform optical mode, the radian of butterfly is 0.30mm-0.50mm, and carves locating slot on the surface, and the diameter of locating slot is than product reduced 0.08mm～0.10mm, the width of locating slot is 0.30mm～0.50mm, and the height of locating slot is 0.05mm～0.20mm; Planar base surface is made on the surface of another one preform optical mode, and the diameter of preform optical mode is identical with base cake diameter behind blanking;
5. the preparation method of a kind of two-sided burr relief type sheet metal souvenir badge as claimed in claim 1 is characterized in that: in the d step, adopt hydraulic press that the base cake behind blanking is carried out the preform impression; The impression tonnage is 30T～60T, and the impression number of times is 1～2 time.
6. the preparation method of a kind of two-sided burr relief type sheet metal souvenir badge as claimed in claim 1 is characterized in that: in the e step, adopt the base cake after punch press impresses preform, along locating slot, carry out the secondary blanking.
7. the preparation method of a kind of two-sided burr relief type sheet metal souvenir badge as claimed in claim 1 is characterized in that: in the f step, the base cake after adopting chamber type electric resistance furnace to the secondary blanking carries out annealing softening to be handled; Annealing temperature is 600 ℃～630 ℃, and annealing time is 10min～15min.
8. the preparation method of a kind of two-sided burr relief type sheet metal souvenir badge as claimed in claim 1, it is characterized in that: in the g step, base cake after adopting vertical light polishing machine to the secondary blanking cleans the light decorations, unified slight curving towards the one side of planar base surface before cleaning the base cake, cleansing medium is the stainless shot that φ 2mm and φ 4mm mix, cleaning fluid is the tumbling powder, the mixed solution of washing agent and deionized water, wherein the tumbling powder is the commercially available prod, produce with one-tenth Science and Technology Ltd. by Nanjing, model is NS-100, the ratio of its addition and deionized water is 1: 40～1: 60, washing agent is a liquid detergent, the ratio of its addition and deionized water is 1: 50～1: 70, and the additional proportion of tumbling powder and washing agent is 1: 0.5～1: 1, and scavenging period is 5min～10min;
9. the preparation method of a kind of two-sided burr relief type sheet metal souvenir badge as claimed in claim 1, it is characterized in that: in the h step, processing and fabricating has the internal or female screw mould of different figure lines, the baseplane of mould is made into minute surface, just, the figure line layout of back of the body mould is placed in the middle, just, the back of the body mould figure line height≤0.50mm, the mould circle is made the light centre circle, the clearance control between mould circle and the mould is at 0.08mm～0.10mm;
10. the preparation method of a kind of two-sided burr relief type sheet metal souvenir badge as claimed in claim 1, it is characterized in that: in the i step, adopt the coinage special equipment to carry out thin slice souvenir badge finished product impression, the impression tonnage is set in 90T～150T, and the impression number of times is 2～4 times.