CN102079934A - Anti-rustcoating - Google Patents
Anti-rustcoating Download PDFInfo
- Publication number
- CN102079934A CN102079934A CN2009102255324A CN200910225532A CN102079934A CN 102079934 A CN102079934 A CN 102079934A CN 2009102255324 A CN2009102255324 A CN 2009102255324A CN 200910225532 A CN200910225532 A CN 200910225532A CN 102079934 A CN102079934 A CN 102079934A
- Authority
- CN
- China
- Prior art keywords
- rust
- proof paint
- rust proof
- butyl ether
- alkali
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-rust coating. The coating is prepared from the following compositions in percentage by weight (wt.%): 0.4-0.6% of Tetrachloroisophthalonitrile, 0.3-0.5% of organo-silicone, 0.05-0.25% of alkali-soluble thickener, 1-3% of ethanol diphenyl ether, 2-4% of butanediol, 0.3-0.5% of carboxylic acid, 6-8% of aluminum phosphate, 1-3% of zinc oxide, 7-9% of titanium dioxide, 8-10% of talc, 40-50% of acrylic resin emulsion, 1-3% of film forming additive, 0.3-0.5% of dispersant and the balance of deionized water. The anti-rust paint has the advantages of faster speed of surface drying, long time of anti-rust, high hardness, high gloss and weather resistance, can meet the needs of automated assembly line production of large tubular or shaped materials like petroleum steel pipes and the needs of long anti-rust storage period in the open air.
Description
Technical field
The present invention relates to paint field, especially a kind of industrial rust proof paint.
Background technology
At present, the rust proof paint of domestic production great majority are solvent based coating, and its solvent includes iron red alcohol acid, iron oxide red phenolic aldehyde, iron oxide red epoxy ester, iron oxide red epoxy, chlorosulfonated polyethylene.The disadvantage of these coating is that price is very expensive, and contaminate environment is inflammable and harmful.Its rust-stabilising pigment component is generally the chromic salt of red lead, lead powder and zinc, lead or barium.These pigment all have very strong toxicity, can serious environment pollutions in the production of coating and use, and healthy with the constructing operation personnel produced in infringement.Therefore, many countries have all banned use of by legislation and have contained red lead, lead powder etc. and be the coating material production and the use of rust-stabilising pigment component.
People successively develop the rust proof paint with rust-stabilising pigment components such as zinc phosphate, aluminum phosphate, zinc molybdate, lime borates, and these coating have the low characteristics of toxicity, but rust-proof effect is bad, and the color development of film-forming resin and stability are not good enough yet.
Water-borne coatings or be called water-based paint is as the term suggests be exactly to be the coating that solvent or dispersion medium are made with water.It mainly comprises water soluble paint and water latex paint two classes.Its maximum characteristics are that whole or most of waters have replaced organic solvent, and filmogen is dispersed or dissolved in the water by different way uniformly, have the water-fast and physicals of similar solvent based coating at dry or curing back paint film.The maximum characteristics of water-borne coatings are to be primary solvent with water, have not only reduced production cost, significantly reduce the profit environmental pollution, and have fire prevention, are easy to transportation and characteristics such as storage, and therefore wide application prospect is arranged.
Summary of the invention
The objective of the invention is at above-mentioned deficiency of the prior art, a kind of environment-friendly antirust coating with long, advantages such as hardness is high, gloss is high, good weatherability of fast, antirust time of surface drying speed is provided.
For achieving the above object, the technical solution adopted for the present invention to solve the technical problems is:
A kind of rust proof paint comprises according to mass percent, daconil M 0.4-0.6wt.%, organo-siloxane 0.3-0.5wt.%, the molten thickening material 0.05-0.25wt.% of alkali, two phenylethyl alcohol butyl ether 1-3wt.%, butyleneglycol 2-4wt.%, carboxylic acid 0.3-0.5wt.%, aluminum phosphate 6-8wt.%, zinc oxide 1-3wt.%, titanium dioxide 7-9wt.%, talcum powder 8-10wt.%, CALCIUM ACRYLATE emulsion 40-50wt.%, film coalescence aid 1-3wt.%, dispersion agent 0.3-0.5wt.%, balance of deionized water.
The molten thickening material of described alkali is selected from a kind of among RM-8W, the WT-105A or their mixture.
Described film coalescence aid is selected from a kind of in 12 carbon alcohol esters, the ethylene glycol methyl-n-butyl ether or their mixture.
Described dispersion agent is selected from a kind of among P-19, the SN5040 or their mixture.
Rust proof paint of the present invention contains resin and activated feedstock calcium monofluorophosphate, and active iron rust is lost activity, and iron rust is separated to be enclosed in film, and makes deleterious iron rust be converted into useful protective layer, firmly attached to the metallic surface, forms persistent rustproof layer.
Compared with prior art, the invention has the beneficial effects as follows: rust proof paint of the present invention has long, advantages such as hardness is high, gloss is high, good weatherability of fast, antirust time of surface drying speed.Can satisfy large pipe or production of section bar automatic assembly line and the antirust needs of long-term outdoor storage such as petroleum steel pipe.
Embodiment
Disclosed all features in this specification sheets, or the step in disclosed all methods or the process except mutually exclusive feature and/or step, all can make up by any way.
Disclosed arbitrary feature in this specification sheets is unless special narration all can be replaced by other equivalences or the alternative features with similar purpose.That is, unless special narration, each feature is an example in a series of equivalences or the similar characteristics.
Embodiment 1: a kind of rust proof paint comprises daconil M 0.4wt.% according to mass percent, organo-siloxane 0.3wt.%, the molten thickening material 0.05wt.% of alkali, two phenylethyl alcohol butyl ether 3wt.%, butyleneglycol 4wt.%, carboxylic acid 0.3wt.%, aluminum phosphate 8wt.%, zinc oxide 1wt.%, titanium dioxide 9wt.%, talcum powder 10wt.%, CALCIUM ACRYLATE emulsion 40wt.%, 12 carbon alcohol ester 1wt.%, SN50400.5wt.%, balance of deionized water.
Embodiment 2: a kind of rust proof paint comprises daconil M 0.6wt.% according to mass percent, organo-siloxane 0.5wt.%, the molten thickening material 0.25wt.% of alkali, two phenylethyl alcohol butyl ether 1wt.%, butyleneglycol 2wt.%, carboxylic acid 0.5wt.%, aluminum phosphate 6wt.%, zinc oxide 3wt.%, titanium dioxide 7wt.%, talcum powder 8wt.%, CALCIUM ACRYLATE emulsion 50wt.%, 12 carbon alcohol ester 3wt.%, SN50400.3%, balance of deionized water.
Embodiment 3: a kind of rust proof paint comprises daconil M 0.5wt.% according to mass percent, organo-siloxane 0.4wt.%, the molten thickening material 0.15wt.% of alkali, two phenylethyl alcohol butyl ether 3wt.%, butyleneglycol 3wt.%, carboxylic acid 0.4wt.%, aluminum phosphate 7wt.%, zinc oxide 2wt.%, titanium dioxide 8wt.%, talcum powder 9wt.%, CALCIUM ACRYLATE emulsion 45wt.%, 12 carbon alcohol ester 2wt.%, SN50400.4wt.%, balance of deionized water.
Embodiment 4: a kind of rust proof paint comprises daconil M 0.4wt.% according to mass percent, organo-siloxane 0.3wt.%, RM-8W 0.05wt.%, two phenylethyl alcohol butyl ether 3wt.%, butyleneglycol 4wt.%, carboxylic acid 0.3wt.%, aluminum phosphate 8wt.%, zinc oxide 1wt.%, titanium dioxide 9wt.%, talcum powder 10wt.%, CALCIUM ACRYLATE emulsion 40wt.%, 12 carbon alcohol ester 1wt.%, SN50400.5wt.%, balance of deionized water.
Embodiment 5: a kind of rust proof paint comprises daconil M 0.6wt.% according to mass percent, organo-siloxane 0.5wt.%, RM-8W 0.25wt.%, two phenylethyl alcohol butyl ether 1wt.%, butyleneglycol 2wt.%, carboxylic acid 0.5wt.%, aluminum phosphate 6wt.%, zinc oxide 3wt.%, titanium dioxide 7wt.%, talcum powder 8wt.%, CALCIUM ACRYLATE emulsion 50wt.%, 12 carbon alcohol ester 3wt.%, SN50400.3%, balance of deionized water.
Embodiment 6: a kind of rust proof paint comprises daconil M 0.5wt.% according to mass percent, organo-siloxane 0.4wt.%, RM-8W 0.15wt.%, two phenylethyl alcohol butyl ether 3wt.%, butyleneglycol 3wt.%, carboxylic acid 0.4wt.%, aluminum phosphate 7wt.%, zinc oxide 2wt.%, titanium dioxide 8wt.%, talcum powder 9wt.%, CALCIUM ACRYLATE emulsion 45wt.%, 12 carbon alcohol ester 2wt.%, SN50400.4wt.%, balance of deionized water.
Embodiment 7: a kind of rust proof paint comprises daconil M 0.4wt.% according to mass percent, organo-siloxane 0.3wt.%, the molten thickening material 0.05wt.% of alkali, two phenylethyl alcohol butyl ether 3wt.%, butyleneglycol 4wt.%, carboxylic acid 0.3wt.%, aluminum phosphate 8wt.%, zinc oxide 1wt.%, titanium dioxide 9wt.%, talcum powder 10wt.%, CALCIUM ACRYLATE emulsion 40wt.%, ethylene glycol methyl-n-butyl ether 1wt.%, SN50400.5wt.%, balance of deionized water.
Embodiment 8: a kind of rust proof paint comprises daconil M 0.6wt.% according to mass percent, organo-siloxane 0.5wt.%, the molten thickening material 0.25wt.% of alkali, two phenylethyl alcohol butyl ether 1wt.%, butyleneglycol 2wt.%, carboxylic acid 0.5wt.%, aluminum phosphate 6wt.%, zinc oxide 3wt.%, titanium dioxide 7wt.%, talcum powder 8wt.%, CALCIUM ACRYLATE emulsion 50wt.%, ethylene glycol methyl-n-butyl ether 3wt.%, SN50400.3%, balance of deionized water.
Embodiment 9: a kind of rust proof paint comprises daconil M 0.5wt.% according to mass percent, organo-siloxane 0.4wt.%, the molten thickening material 0.15wt.% of alkali, two phenylethyl alcohol butyl ether 3wt.%, butyleneglycol 3wt.%, carboxylic acid 0.4wt.%, aluminum phosphate 7wt.%, zinc oxide 2wt.%, titanium dioxide 8wt.%, talcum powder 9wt.%, CALCIUM ACRYLATE emulsion 45wt.%, ethylene glycol methyl-n-butyl ether 2wt.%, SN50400.4wt.%, balance of deionized water.
The present invention is not limited to aforesaid embodiment.The present invention expands to any new feature or any new combination that discloses in this manual, and the arbitrary new method that discloses or step or any new combination of process.
Claims (4)
1. rust proof paint, it is characterized in that: comprise according to mass percent, daconil M 0.4-0.6wt.%, organo-siloxane 0.3-0.5wt.%, the molten thickening material 0.05-0.25wt.% of alkali, two phenylethyl alcohol butyl ether 1-3wt.%, butyleneglycol 2-4wt.%, carboxylic acid 0.3-0.5wt.%, aluminum phosphate 6-8wt.%, zinc oxide 1-3wt.%, titanium dioxide 7-9wt.%, talcum powder 8-10wt.%, CALCIUM ACRYLATE emulsion 40-50wt.%, film coalescence aid 1-3wt.%, dispersion agent 0.3-0.5wt.%, balance of deionized water.
2. rust proof paint according to claim 1 is characterized in that: the molten thickening material of described alkali is selected from a kind of among RM-8W, the WT-105A or their mixture.
3. rust proof paint according to claim 1 is characterized in that: described film coalescence aid is selected from a kind of in 12 carbon alcohol esters, the ethylene glycol methyl-n-butyl ether or their mixture.
4. rust proof paint according to claim 1 is characterized in that: described dispersion agent is selected from a kind of among P-19, the SN5040 or their mixture.