CN102079891A - Petroleum-sulfonate antirust paint - Google Patents
Petroleum-sulfonate antirust paint Download PDFInfo
- Publication number
- CN102079891A CN102079891A CN2009102255254A CN200910225525A CN102079891A CN 102079891 A CN102079891 A CN 102079891A CN 2009102255254 A CN2009102255254 A CN 2009102255254A CN 200910225525 A CN200910225525 A CN 200910225525A CN 102079891 A CN102079891 A CN 102079891A
- Authority
- CN
- China
- Prior art keywords
- acid salt
- petroleum
- proof paint
- mahogany acid
- rust proof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a petroleum-sulfonate antirust paint which comprises the following components in percentage by mass: 10-15% of petroleum-sulfonate compound antirust agent, 40-50% of acrylic resin, 20-30% of aromatic solvent, 5-10% of phenolic resin and 5-10% of assistant. The petroleum-sulfonate antirust paint does not contain water bases or toxic and harmful substances, and can effectively prevent rust.
Description
Technical field
The present invention relates to paint field, especially a kind of mahogany acid salt rust proof paint.
Background technology
Most of rust proof paint of the prior art all is water-borne coatings or is called water-based paint, as the term suggests be the coating that solvent or dispersion medium are made with water exactly.It mainly comprises water soluble paint and water latex paint two classes.Its maximum characteristics are that whole or most of waters have replaced organic solvent, and filmogen is dispersed or dissolved in the water by different way uniformly, have the water-fast and physicals of similar solvent based coating at dry or curing back paint film.But the composition of water-borne coatings is more than the coatings volatile organic compounds complexity, and the water volatile ratio solvent evaporates in the water-borne coatings need absorb more heat, so energy consumption is higher.
And from antirust aspect, the water capacity in the water-borne coatings easily causes the hardware corrosion, and organic solvent is not easy to cause the hardware corrosion on the one hand, also can dissolve some water-fast materials on the other hand.
Summary of the invention
The objective of the invention is at above-mentioned deficiency of the prior art, a kind of low viscosity, non-foaming, nontoxic, the environment-friendly antirust coating that is difficult for corrosion are provided.
For achieving the above object, the technical solution adopted for the present invention to solve the technical problems is:
-kind of mahogany acid salt rust proof paint comprises according to mass percent, mahogany acid salt composite antirust agent 10-15%, methymethacrylate 40-50%, aromatic solvent 20-30%, Resins, epoxy 5-10%, auxiliary agent 5-10%.
Described aromatic solvent is selected from a kind of in trimethylbenzene, the sym-trimethylbenzene or their mixture.
Described auxiliary agent is a kind of in thickening material, the defoamer or their mixture.
Described thickening material is a polyacrylic acid.
Described defoamer is NXZ.
Industrial aqueous rust-proof coatings of the present invention contains resin and the agent of activated feedstock mahogany acid salt composite antirust; active iron rust is lost activity, iron rust is separated to be enclosed in film, make deleterious iron rust be converted into useful protective layer; firmly, form persistent rustproof layer attached to the metallic surface.
Compared with prior art, the invention has the beneficial effects as follows: the present invention does not contain water base, effectively antirust, no hazardous and noxious substances.
Embodiment
Disclosed all features in this specification sheets, or the step in disclosed all methods or the process except mutually exclusive feature and/or step, all can make up by any way.
Disclosed arbitrary feature in this specification sheets is unless special narration all can be replaced by other equivalences or the alternative features with similar purpose.That is, unless special narration, each feature is an example in a series of equivalences or the similar characteristics.
Embodiment 1: a kind of mahogany acid salt rust proof paint comprises mahogany acid salt composite antirust agent 15%, methymethacrylate 40%, aromatic solvent (trimethylbenzene) 25%, Resins, epoxy 10%, auxiliary agent (polyacrylic acid) 10% according to mass percent
Embodiment 2: a kind of mahogany acid salt rust proof paint comprises mahogany acid salt composite antirust agent 14%, methymethacrylate 49%, aromatic solvent (sym-trimethylbenzene) 20%, Resins, epoxy 9%, auxiliary agent (NXZ) 8% according to mass percent
Embodiment 3: a kind of mahogany acid salt rust proof paint comprises mahogany acid salt composite antirust agent 10% according to mass percent, methymethacrylate 50%, aromatic solvent (trimethylbenzene, sym-trimethylbenzene) 30%, Resins, epoxy 5%, auxiliary agent (polyacrylic acid, NXZ) 5%
The present invention is not limited to aforesaid embodiment.The present invention expands to any new feature or any new combination that discloses in this manual, and the arbitrary new method that discloses or step or any new combination of process.
Claims (5)
1. a mahogany acid salt rust proof paint is characterized in that: comprise mahogany acid salt composite antirust agent 10-15%, methymethacrylate 40-50%, aromatic solvent 20-30%, Resins, epoxy 5-10%, auxiliary agent 5-10% according to mass percent.
2. mahogany acid salt rust proof paint according to claim 1 is characterized in that: described aromatic solvent is selected from a kind of in trimethylbenzene, the sym-trimethylbenzene or their mixture.
3. mahogany acid salt rust proof paint according to claim 1 is characterized in that: described auxiliary agent is a kind of in thickening material, the defoamer or their mixture.
4. mahogany acid salt rust proof paint according to claim 3 is characterized in that: described thickening material is a polyacrylic acid.
5. rust proof paint according to claim 3 is characterized in that: described defoamer is NXZ.